Effect of OH^- content on emission properties in Er³⁺-doped tellurite glasses

A series of tellurite glasses of composition, 75TeO(2)-20ZnO-(5 - x)La2O3-xEr(2)O(3) (x = 0.05, 0.1, 0.3, 0.6, 1.0, 2.0, and 3.0 mol%) with different hydroxl content were prepared. The effect of Er3+ and OH- groups concentration on the emission properties of Er3+: I-4(13/2) -> I-4(15/2) transition in tellurite glasses was investigated. The constant KOH-Er for Er3+ in tellurite glasses, which represents the strength of interaction between Er3+ and OH- groups in the case of energy migration, was about 14 x 10(-19) cm(4) s(-1). The interaction parameter C-Er,C-Er for the migration rate of Er3+ : 4I(13/2) -> I-4(13/2) transition in tellurite glass was 46 x 10(-40) cm(2), which indicates that concentration quenching in Er3+-doped modified tellurite glass for a given Er3+ concentration is much stronger than in silicate and phosphate glasses. (c) 2007 Elsevier B.V. All rights reserved.

Effects of thermal treatment on broadband near-infrared emission from Bi-doped chalcohalide glasses

GeGaSKBr glass with Bi ions as emission centers were fabricated. An intense emission centered at around 1230 nm with the width of more than 175 nm was observed by 808 nm photo-excitation of the glass. Lower quenching rate and thermal treatment promote micro-crystallization process, thus strengthening the emission. Crown Copyright (c) 2008 Published by Elsevier Ltd. All rights reserved.

Broadband infrared luminescence of bismuth-doped borosilicate glasses

We prepare bismuth-doped borosilicate glasses and the luminescence properties in infrared wavelength region are investigated. Transmission spectrum, fluorescence spectrum and fluorescence decay curve are measured. The glasses exhibit a broad infrared luminescence peaking at 1340nm with the full width at half maximum of about 205nm, and lifetime of 273 mu s when excited by an 808-nm laser diode. The glasses are promising materials for broadband optical amplifiers and tunable lasers.

High quantum efficiency and high concentration erbium-doped silica glasses fabricated by sintering nanoporous glasses

A new method was used to prepare erbium-doped high silica (SiO2% > 96%) glasses by sintering nanoporous glasses. The concentration of erbium ions in high silica glasses can be considerably more than that in silica glasses prepared by using conventional methods. The fluorescence of 1532 nm has an FWHM (Full Wave at Half Maximum) of 50 nm, wider than 35 nm of EDSFA (erbium-doped silica fiber amplifer), and hence the glass possesses potential application in broadband fiber amplifiers. The Judd-Ofelt theoretical analysis reflects that the quantum efficiency of this erbium-doped glass is about 0.78, although the erbium concentration in this glass (6 x 103) is about twenty times higher than that in silica glass. These excellent characteristics of Er-doped high silica glass will be conducive to its usage in optical amplifiers and microchip lasers.

Diode-pumped room-temperature continuous wave Tm3+ doped Lu2SiO5 laser

We report on room temperature laser actions of a novel thulium-doped crystal Tm center dot Lu2SiO5 (LSO) under diode pumping. An optical optical conversion efficiency of 12% and a slope efficiency of 21% were obtained with the maximum continuous wave (CW) output power of 0.67 W. The emission wavelengths of Tm LSO laser were centered at 2058.4 nm with bandwidth of similar to 13.6 nm.