Sol-gel deposition of calcium silicate red-emitting luminescent films doped with Eu3+

Eu3+-activated calcium silicate (CaO-SiO2:Eu3+) luminescent films were prepared by the sol-gel method. The structural evolution of the film was studied by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and the luminescence properties of the phosphor films were investigated as a function of heat treatment temperature. The XRD study indicates that a kilchoanite phase forms in the film sintered at 800 degreesC, which is different from that in gel powder treated under the same conditions. The SEM results show that the film thickness decreases and the particles in the film become smaller with increasing heat treatment temperature. The CaO-SiO2:Eu film shows the characteristic emission of Eu3+ under UV excitation, with the Eu3+ D-5(0)-->F-7(2) band (616 nm) being the most prominent. A large difference in the Eu3+ lifetime is observed between the film samples treated at 500 and 700 degreesC (or above). Concentration quenching occurs when the Eu3+ doping concentration is above 6 mol% of Ca2+ in the film.

Luminescence properties of rare-earth (Eu3+ and Tb3+) complexes with paraaminobenzoic acid and 1,10-phenanthroline incorporated into a silica matrix by sol-gel method

Ternary complexes of europium and terbium with paraaminobenzoic acid and 1,10-phenanthroline (Eu(p-ABA)(3). phen . 2H(2)O and Tb(p-ABA)(3). phen . 2H(2)O, where p-HABA = paraaminobenzoic acid and phen = 1,10-phenanthroline) were introduced into a silica matrix by sol-gel method. The luminescence behavior of the complexes in silica gels was studied in comparison with the. corresponding solid-state complexes by means of emission, excitation spectra, and Lifetimes. Within the range of effective dopant concentrations, the luminescence intensities of rare-earth complexes in silica gel increase with the increasing of their dopant concentration. The lifetimes of rare-earth ions (Eu3+ and-Tb3+) in silica gel doped with europium and terbium complexes become longer than those in pure complexes. Very small amounts of rare-earth complexes doped in silica gel matrix can exhibit excellent luminescence properties, (C) 1998 Elsevier Science Ltd.

Luminescence properties of rare earth (Eu3+ and Tb3+) complexes with conjugated carboxylic acids and 1,10-phenanthroline incorporated in silica matrix

Binary and ternary complexes of europium and terbium with conjugated carboxylic acid (nicotinic acid and 3,4-furandicarboxylic acid) and 1,10-phenanthroline were introduced into silica gel by the sol-gel method. The luminescence behavior of the complexes in silica gels was studied compared with the corresponding solid state complexes by means of emission, excitation spectra and lifetimes. The result indicated that the rare earth ions (EU3+ and Tb3+) showed fewer emission lines and slightly lower emission intensities in the silica gel than those in pure rare earth complexes. The lifetimes of rare earth ions (EU3+ and Tb3+) in silica gel doped with rare earth complexes became longer than those in pure rare earth complexes. (C) 1998 Elsevier Science S.A.

Luminescence properties of sol-gel derived silica gels doped and undoped with RE-complexes (RE=Eu, Tb)

The luminescence properties of silica gels and silica gels doped with two rare earth complexes, Eu(TTA)(3) and Tb(o-CBA)(3) (TTA=thenoyltriffuocetate, o-CBA=o-chlorobenzoic acid) are reported and discussed. Pure silica gels show a blue luminescence, and the maximum excitation and emission wavelengths depend strongly on the solvents used. Both of the studied rare earth complexes exhibit the characteristic emissions of the rare earth ions in silica gels, i.e., Eu3+5D0-->F-7(J)(J=0,1,2,3,4), Tb3+5D4-->F-7(J)(J=3,4,5,6) transitions. Compared with the pure RE-complexes powder, the silica gels doped with RE-complexes show fewer emission lines of the rare earth ions. Furthermore the rare earth ion (Tb3+) presents a longer lifetime (1346 mu s) in silica gel doped with Tb(o-CBA)3 than in pure Tb((o-CBA)(3) powder (744 mu s). The reasons responsible for these results are discussed in the context.

LUMINESCENCE AND ENERGY MIGRATION IN THE OXYAPATITE CA2GD8(SIO4)6O2 DOPED WITH SEVERAL RARE-EARTH AND MERCURY-LIKE IONS

Energy transfer phenomena have been observed by activating the oxyapatite host-lattice Ca2Gd8(SiO4)6O2 with Eu3+, Tb3+, Dy3+, Sm3+. This is based on the energy migration in the Gd3+ sublattice and trapping by the activators. The trapping efficiency for G

Effects of gamma radiation on the photoluminescence properties of polycarbonate matrices doped with terbium complex

Luminescent films containing terbium complex [Tb(acac)(3)(H(2)O)(3)] (acac = acetylacetonate) doped into a polycarbonate (PC) matrix were prepared and irradiated at low-dose gamma radiation with ratio of 5 and 10 kGy. The PC polymer was doped with 5% (w/w) of the Tb(3+) complex. The thermal behavior was investigated by utilization of differential scanning calorimetry (DSC) and thermogravimetry analysis (TGA). Changes in thermal stability due to the addition of doping agent into the polycarbonate matrix. Based on the emission spectra of PC:5% Tb(acac)(3) film were observed the characteristic bands arising from the (5)D(4) -> (7)F(J) transitions of Tb(3+) ion (J = 0-6), indicating the ability to obtain the luminescent films. Doped samples irradiated at low dose of gamma irradiation showed a decrease in luminescence intensity with increasing of the dose. (C) 2009 Elsevier Ltd. All rights reserved.

Excitation mechanisms and effects of dopant concentration in Gd2O2S : Tb3+ phosphor

Gadolinium oxysulfide powders doped with different Tb3+ concentrations were prepared from sulfur vaporization on rare earths' basic carbonate precursors. Single-phase Gd2O2S samples were obtained, with Tb3+ doping up to 9 at%. The study of the excitation mechanisms revealed that the Tb3+ emission might occur after the direct Tb3+ excitation either by energy transfer from Gd3+ or from the phosphor host. The characteristic terbium emission lines were observed, resulting from the radiative decay from D-5(3) or D-5(4), to F-7(j) levels. The cross-relaxation phenomenon was observed and its effects on the materials emission color were discussed based on the CIE diagram. By using time-resolved spectroscopy, D-5(3) -> F-7(J) and D-5(4) -> F-7(J) transitions were separated. (c) 2007 Elsevier B.V. All rights reserved.

Thermally enhanced cooperative energy-transfer frequency upconversion in terbium and ytterbium doped tellurite glass

Infrared-to-visible frequency upconversion through cooperative energy-transfer and thermal effects in Tb3+/Yb3+-codoped tellurite glasses excited at 1.064 mum is investigated. Bright luminescence emission around 485, 550, 590, 625 and 65 nm, identified as due to the D-5(4) --> F-7(J) (J= 6, 5, 4, 3, and 2) transitions of the terbium ions, respectively, was recorded. The excitation of the D-5(4) emitting level of the Tb3+ ions is assigned to cooperative energy-transfer from pairs of ytterbium ions.. The effect of temperature on the upconversion process was examined and the results revealed a fourfold upconversion enhancement in the 300-500 K interval. The enhancement of the upconversion process is due to the temperature dependence of the Yb3+-sensitizer absorption cross-section under anti-Stokes excitation. A rate-equation. model using multiphonon-assisted absorption for the ytterbium excitation combined with the energy migration effect between Yb-Yb pair, and Tb3+ ground-state depopulation via multiphonon excitation of the F-7(J) excited states describes quite well the experimental results. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Low voltage electroluminescence of terbium- and thulium-doped zinc oxide films

Strong interest in developing technology for visual information. stimulates research for thin film electroluminescent devices. Here, for the first time, we report that thulium- and terbium-doped zinc-oxide films are suitable for electroluminescence applications. Two different devices were assembled as lTO/LiF/ZnO:RE/LiF/Al or ITO/SiO2/ZnO:RE/SiO2/Al, where ZnO:RE is a film of zinc oxide containing 10 at% of Tb3+ or Tm3+. Electroluminescence spectra show that besides a broad emission band with maximum around 650 nm assigned to ZnO, also emission lines from Tb3+ at 484 nm (D-5(4) -> F-7(6)), 543 nm (D-5(4) -> F-7(6)), and 589 nm (D-5(4) -> F-7(4)), or from Tm3+ at 478 nm ((1)G(4) -> H-3(6)), and 511 mn (D-1(2) -> H-3(5)) were detected. Intensity of emission as function of applied voltage and current-voltage characteristic are shown and discussed. (c) 2005 Elsevier B.V. All rights reserved.

Frequency upconversion in rare-earth doped fluoroindate glasses

We present recent results on frequency upconversion (UPC) obtained in fluoroindate glasses (FIG) doped with Ho3+, Tm3+ and Nd3+ ions and codoped with Pr3+/Nd3+ and Yb3+/Tb3+ ions. The results for the Ho3+-doped samples show strong evidence of energy transfer (ET) between Ho3+ ions resonantly excited at 640 nm. The origin of the blue-green upconverted fluorescence observed was identified and the dynamics of the signals revealed the pathways involved in the UPC process. In the case of Tm3+-doped FIG, the samples were resonantly excited at 650 nm and the main mechanism that contributes for the red-to-blue upconversion is excited-state absorption (ESA). The FIG samples codoped with Pr3+/Nd3+ were excited at 588 nm in resonance with transitions starting from the ground state of the Nd 3+ and the Pr3+ ions. It was observed that the presence of Nd3+ ions enhanced the Pr3+ emission at 480 nm by two orders of magnitude. Multiphonon (MP)-assisted upconversion is also discussed for Nd3+-doped FIG pumped at 866 nm. Emission at 750 nm with a peculiar linear dependence with the laser intensity was observed and explained. A rate-equation model that includes MP absorption via thermally coupled electronic excited states of Nd3+ was developed and describes well the experimental results. The role played by effective phonon modes is clearly demonstrated. MP-assisted UPC process was also studied in Yb3+/ Tb3+-codoped FIG samples excited at 1064 nm, which is off-resonance with electronic transitions starting from the ground state. It was determined that the mechanism leading to Tb3+ emission in the blue is due to ET from a pair of excited Yb3+ ions followed by ESA in the Tb 3+ ions. © 2002 Académie des sciences/Éditions scientifiques et médicales Elsevier SAS.

Effects in the population inversion of3H4 level in Tm, Tm-Tb and Tm-Eu doped germanate glasses for amplifiers applications

The population inversion of the Tm3+ in GLKZ glass involved in the 1470 nm emission (3H4 → 3F 4) as a function of Tb (or Eu) concentration was calculated by computational simulation for a CW laser pumping at 792 nm. These calculations were performed using the experimental Tm→Tb an Tm→Eu transfer rates and the spectroscopic parameters of the Tm (0.1 mol %) system. The result shows that 0.2 mol % (Tb3+) and 0.4 mol % of Eu3+ ions propitiate best population inversion of Tm3+ (0.1 mol %) maximizing the amplification coefficient of germanate (GLKZ) glass when operating as laser intensity amplification at 1470 nm. Besides the effective deactivation of the 3F4 level, the presence of Tb3+ or Eu 3+ ions introduce a depopulation of the 3H4 emitting level by means of a cross relaxation process with Tm3+ ions. In spite of this, the whole effect is verified to be benefic for using Tm-doped GLKZ glass codoped with Tb3+ or Eu3+ as a suitable material for confectioning optical amplifiers that operates in the S-band for telecommunication.

Tb3+-> Eu3+ Energy Transfer in Mixed-Lanthanide-Organic Frameworks

In this work, we report a theoretical and experimental investigation of the energy transfer mechanism in two isotypical 2D coordination polymers, (infinity)[(Tb1-xEux)(DPA)(HDPA)], where H(2)DPA is pyridine 2,6-dicarboxylic acid and x = 0.05 or 0.50. Emission spectra of (infinity)[(Tb0.95Eu0.05)(DPA)(HDPA)] and (infinity)[(Tb0.5Eu0.5)(DPA)(HDPA)], (I) and (2), show that the high quenching effect on Tb3+ emission caused by Eu3+ ion indicates an efficient Tb3+-> Eu3+ energy transfer (ET). The k(ET) of Tb3+-> Eu3+ ET and rise rates (k(r)) of Eu3+ as a function of temperature for (1) are on the same order of magnitude, indicating that the sensitization of the Eu3+5D0 level is highly fed by ET from the D-5(4) level of Tb3+ ion. The eta(ET) and R-0 values vary in the 67-79% and 7.15 to 7.93 angstrom ranges. Hence, Tb3+ is enabled to transfer efficiently to Eu3+ that can occupy the possible sites at 6.32 and 6.75 angstrom. For (2), the ET processes occur on average with eta(ET) and R-0 of 97% and 31 angstrom, respectively. Consequently, Tb3+ ion is enabled to transfer energy to Eu3+ localized at different layers. The theoretical model developed by Malta was implemented aiming to insert more insights about the dominant mechanisms involved in the ET between lanthanides ions. Calculated single Tb3+-> Eu3+ ETs are three orders of magnitude inferior to those experimentally; however, it can be explained by the theoretical model that does not consider the role of phonon assistance in the Ln(3+)-> Ln(3+) ET processes. In addition, the Tb3+-> Eu3+ ET processes are predominantly governed by dipole-dipole (d-d) and dipole-quadrupole (d-q) mechanisms.

Doped poly(vinylidene fluoride) as solid polymer electrolyte in nanocrystalline dye-sensitized solar cell

A new solid composite polymer electrolyte was reported by incorporating Azino-bis-(3-ethyl benzo thiazoline-6-sulphonate) ion [ABTS] as dopant in poly(vinylidene flouride) along with redox couple (1-/13-). Under certain conditions, the electrolyte composition forms brush like nano-rods while it is doped with Azino-bis-(3-ethly) benzo thiazoline-6-sulphonate) ion [ABTS], a pi-electron donor. The polymer electrolyte forms nanoscale interpenetrating network with the crystalline order of the polymer electrolyte that seems to be a desirable architecture for the active layer of the photoelectrochemical cell. With this new polymer electrolyte, dye-sensitized solar cell was fabricated using N3 dye absorbed over Ti02- nonoparticles (photoanode) and conducting carbon cement coated on the conducting press (FTO, photocathode). This polymer composite has been successfully used as a promising candidate as solid polymer electrolyte in nanocrystalline dye-sensitized solar cell.

Solid-state nanocrystalline dye-sensitized solar cell using 2-mercapto benzimidazole doped poly(ethylene oxide) as a new polymer electrolyte

New composite doped poly (ethylene oxide) polymer electrolyte was developed using 2-mercapto benzimidazole as plasticizer and iodide/triiodide as redox couple. The fabrication of the cell involves Poly(ethylene oxide)/ 2-mercapto benzimidazole / iodide/triiodide as polymer electrolyte in dye-sensitized solar cell fabricated with N3 dye and TiO2 nanoparticles as the photoanode and Platinum coated FTO (fluorine doped SnO2) as counter electrode. The current-volatage characteristics under simulated sunlight AM1.5 shows a short circuit current Isc of 8.7mA and open circuit photovoltage 508 mV. The conductivity measurements for the new polymer electrolyte and the photoelectrochemical measurments were carried out systematically. In 2-mercapto benzimidazole the electron rich sulphur and nitrogen atoms, act as pi-electron donors that form good interaction with iodine which plays a vital role in the performance of the fabricated dye-sensitized solar cells. The resonance effect increases the stability of the cell to a considerable extent. These results suggest that the new composite polymer electrolyte performs as a promising new doped polymer-electrolyte.