Bacterial sterilization by a dielectric barrier discharge (DBD) in air

Cold atmospheric plasma treatment of microorganisms and living tissues has become a popular topic in modern plasma physics and in medical science. The plasma is capable of bacterial inactivation and noninflammatory tissue modification, which makes it an attractive tool for treatment of skin diseases, open injuries and dental caries. Because of their enhanced plasma chemistry, Dielectric Barrier Discharges (DBDs) have been widely investigated for some emerging applications such as biological and chemical decontamination of media at ambient conditions. Despite the high breakdown voltage in air at atmospheric pressure, the average current of DBD discharges is low. Therefore, a DBD can be applied in direct contact with biological objects without causing any damage. In this work a 60 Hz DBD reactor, which generates cold atmospheric plasma inside Petri dishes with bacterial culture, is investigated. Samples of Staphylococcus aureus, a Gram-positive bacterium and Escherichia coil a Gram-negative bacterium were selected for this study. The bacterial suspensions were evenly spread on agar media planted in Petri dishes. The reactor electrodes were placed outside the Petri dish, thus eliminating the risk of samples microbial contamination. The covered Petri dish with agar medium in it serves as dielectric barrier during the treatment. The plasma processing was conducted at same discharge power (similar to 1.0 W) with different exposure time. Sterilization of E. coil and S. aureus was achieved for less than 20 min. Plasma induced structural damages of bacteria were investigated by Scanning Electron Microscopy. (C) 2010 Elsevier B.V. All rights reserved.

Properties of hydrogenated amorphous carbon films deposited by PECVD and modified by SF6 plasma

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Fatigue strength of HVOF sprayed Cr(3)C(2)-25NiCr and WC-10Ni on AISI 4340 steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Progression of experimental chronic peri-implantitis in dogs: Clinical and radiographic evaluation

Background: the aim of this study was to evaluate the progression of experimental peri-implantitis in dogs using implants with different surface coatings.Methods: Thirty-six dental implants with four different surface coatings, commercially pure titanium (cpTi), titanium plasma-sprayed (TPS), hydroxyapatite (HA), and acid-etched (AE), were placed in six mongrel dogs. Five months after implantation, peri-implantitis was induced by cotton ligatures to facilitate plaque accumulation for 60 days. After 60 days, the ligatures were removed and supragingival plaque control was initiated for 12 months. Probing depth (PD), clinical attachment level (CAL), vertical bone level (VBL), horizontal bone level (HBL), and mobility were obtained at baseline, and 20, 40, 60 (acute phase), and 425 days (chronic phase) after ligature removal.Results: PD and CAL changed around all implant surfaces after ligature placement (P < 0.0001). However, the means of PD and CAL were not statistically significant among the different surfaces (P > 0.05). The range of CAL variation, calculated between baseline and 60 days (acute phase) and between 60 and 425 days (chronic phase), decreased (P < 0.05). Bone loss increased during the entire experiment (P < 0.0001). The HA surface showed the greatest bone loss measurement (5.06 +/- 0.38 mm) and the TPS showed the smallest bone loss (4.27 +/- 0.62 mm). However, statistical significance was not assessed for different coatings (P > 0.05).Conclusions: the clinical data at the initial phase showed rapid and severe peri-implant tissue breakdown. However, removal of ligatures did not convert the acute destructive peri-implant phase to a non-aggressive lesion and the progression of peri-implantitis was observed at chronic phase. The,experimental peri-implantitis in dogs may be a useful model to evaluate the progression of peri-implantitis.

Lethal photosensitization and guided bone regeneration in treatment of peri-implantitis: an experimental study in dogs

The purpose of this study was to evaluate the effect of lethal photosensitization and guided bone regeneration (GBR) on the treatment of ligature-induced peri-implantitis in different implant surfaces. The treatment outcome was evaluated by clinical and histometric methods. A total of 40 dental implants with four different surface coatings (10 commercially pure titanium surface (cpTi); 10 titanium plasma-sprayed (TPS); 10 acid-etched surface; 10 surface-oxide sandblasted) were inserted into five mongrel dogs. After 3 months, the animals with ligature-induced peri-implantitis were subjected to surgical treatment using a split-mouth design. The controls were treated by debridment and GBR, while the test side received an additional therapy with photosensitization, using a GaAlAs diode laser, with a wavelength of 830 nm and a power output of 50 mW for 80 s (4 J/cm(2)), and sensitized toluidine blue O (100 mu g/ml). The animals were sacrificed 5 months after therapy. The control sites presented an earlier exposition of the membranes on all coating surfaces, while the test group presented a higher bone height gain. Re-osseointegration ranged between 41.9% for the cpTi surface and 31.19% for the TPS surface in the test sites; however differences were not achieved between the surfaces. The lethal photosensitization associated with GBR allowed for better re-osseointegration at the area adjacent to the peri-implant defect regardless of the implant surface.

Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu-Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm(-2). However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained gal vanostatic ally. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Calculation of the vacuum pressure gradient in field emission displays

The usual design of field-emission displays (FEDs) often results in high vacuum pressure gradients inside the glass plates of the device, and this is the main limitation to the widespread availability of large area FEDs. In this paper, we perform theoretical calculations using the finite element method for determining the pressure distributions in several pumping configurations, including a new FED configuration known as porous FED or pFED. The approach here is capable of clarifying the design issues influencing the final pressure relevant to the field-emission display devices. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Study on the orientation degree of Pb1-xLaxTiO3 thin films by the rocking curve technique and its morphological aspects

Thin films of perovskite-type materials such as PbTiO3, BaTiO3, (Pb,La)TiO3, (Pb, La)(ZrTi)O-3, KNbO3, and Pb(Mg,Nb)03 have been attracting great interest for applications like non-volatile memories, ultrasonic sensors and optical devices. Thin film should be epitaxially grown or at least highly textured since the properties of this anisotropic material depend on the crystallographic orientation. For optical devices, in particular, an epitaxial thin film without defects are essential to reduce optical propagation losses. Pb1-xLaxTiO3 (PLT) where x=0, 13 and 27% thin films were prepared by a chemical method (polymeric precursors method), and deposited by the spin coating technique onto substrates of SrTiO3 (STO) and LaAlO3 (LAO). The films were then beat treated at 500 degrees C in a controlled atmosphere of 0,. The orientation degree of the thin films was obtained from rocking curve technique, by means of X-ray difftaction analysis. A microstructural study revealed that the films were crack-free, homogeneous and have low roughness. (c) 2006 Elsevier B.V. All rights reserved.

Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy

The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due to their lower manufacturing and operated production infrastructure. In landing gear components, wear and corrosion control of many components is accomplished by surface treatments of chrome electroplating on steel or anodizing of aluminum. One of the most interesting environmentally safer and cleaner alternatives for the replacement of hard chrome plating or anodizing is tungsten carbide thermal spray coating, applied by the high velocity oxy fuel (HVOF) process. However, it was observed that residual stresses originating from these coatings reduce the fatigue strength of a component.An effective process as shot peening treatment, considered to improve the fatigue strength, pushes the crack sources beneath the surface in most of medium and high cycle cases, due to the compressive residual stress field induced. The objective of this research is to evaluate a tungsten carbide cobalt (WC-Co) coating applied by the high velocity oxy fuel (HVOF) process, used to replace anodizing. Anodic films were grown on 7050-T7451 aluminum alloy by sulfuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on axial fatigue strength of anodic films grown on the aluminum alloy surface is to degrade the stress-life performance of the base material. Three groups of specimens were prepared and tested in axial fatigue to obtain S-N curves: base material, base material coated by HVOF and base material shot peened and coated.Experimental results revealed increase in the fatigue strength of Al 7050-T7451 alloy associated with the WC 17% Co coating. on the other hand, a reduction in fatigue life occurred in the shot peened and coated condition. Scanning electron microscopy technique and optical microscopy were used to observe crack origin sites, thickness and coating/substrate adhesion. (c) 2007 Elsevier B.V. All rights reserved.

The influence of residual stress and crystallite size on the magnetic properties of electrodepo sited nanocrystalline Pd-Co alloys

Nanocrystalline Pd-Co alloys were obtained by electrodeposition from an ammoniacal chloride bath. The influence of the crystallite size and the residual stress on the magnetic properties of the alloys was investigated. The residual stress increased as the applied current density was increased. It was associated to the high nucleation rate during electrodeposition and correlated to the lattice strain, estimated from the XRD patterns. Also from the XRD patterns the average crystallite size and the lattice constant were determined by Scherrer's and Rietveld's methods, respectively. Both parameters were directly influenced by the applied current density. Magnetic properties such as coercivity, remanence, saturation magnetization and squareness showed strong dependence on the residual stress and crystallite size. Coercivity higher than 1 kOe was achieved when a high current density was applied. High coercivity was attributed to the presence of residual stress and to the small crystallite size of deposits. (C) 2007 Elsevier B.V. All rights reserved.

Treatment of ligature-induced peri-implantitis by lethal photosensitization and guided bone regeneration: A preliminary histologic study in dogs

Background: the purpose of this pilot study was to evaluate the healing potential and reosseointegration in ligature-induced peri-implantitis defects adjacent to various dental implant surfaces following lethal photosensitization.Methods: A total of 36 dental implants with 4 different surface coatings (9 commercially pure titanium surface [CPTi]; 9 titanium plasma-sprayed [TPS]; 9 hydroxyapatite [HA]; and 9 acid-etched [AE]) were inserted in 6 male mongrel dogs 3 months after extraction of mandibular premolars. After a 2-month period of ligature-induced peri-implantitis and 12 months of natural peri-implantitis progression, only 19 dental implants remained. The dogs underwent surgical debridement of the remaining dental implant sites and lethal photosensitization by combination of toluidine blue O (100 mug/ml) and irradiation with diode laser. All exposed dental implant surfaces and bone craters were meticulously cleaned by mechanical means, submitted to photodynamic therapy, and guided bone regeneration (GBR) using expanded polytetrafluoroethylene (ePTFE) membranes. Five months later, biopsies of the implant sites were dissected and prepared for ground sectioning and analysis.Results: the percentage of bone fill was HA: 48.28 +/- 15.00; TPS: 39.54 +/- 12.34; AE: 26.88 +/- 22.16; and CPTi: 26.70 +/- 16.50. The percentage of reosseointegration was TPS: 25.25 +/- 11.96; CPTi: 24.91 +/- 17.78; AE: 17.30 +/- 15.41; and HA: 15.83 +/- 9.64.Conclusion: These data suggest that lethal photosensitization may have potential in the treatment of peri-implantitis.

Plasma nitriding of sintered AISI 316L at several temperatures

Samples of sintered AISI 316L stainless steel were plasma nitrided in a mixture of H-2-20% N-2, for 3 or 4 h. The treatment temperature was selected in 400-550 degreesC interval, in steps of 50 degreesC. X-ray diffraction (glancing angle geometry-GAXRD), conversion electron Mossbauer spectroscopy (CEMS), optical microscopy and Vickers microhardness were used as analytical techniques. For T greater than or equal to 500 degreesC and t = 4 h, a 40-mum layer is formed. The GAXRD results showed a transformation of the austenite gamma phase to the martensite in the sinterization process and showed as well, that the gamma' (Fe4N) phase is the predominant nitride besides small amounts of epsilon-Fe2N, gamma(N) CrN, Cr2O3 and the fcc nitrogen supersatured solid phase gamma(N). The CrN phase seems to decrease with temperature while the gamma(N) phase fraction is almost less than or equal to10%, independently on the temperature. The CEMS results indicated that while the gamma(N) fraction decreases with temperature of plasma nitriding, the gamma' fraction increases proportionally. (C) 2003 Elsevier B.V. All rights reserved.

Effects of nitrogen ion irradiation on plasma polymerized films produced from titanium tetraiso pro poxide-oxygen-helium mixtures

In this work films were produced by the plasma enhanced chemical vapor deposition (PECVD) of titanium tetraisopropoxide-oxygen-helium mixtures and irradiated with 150 keV singly-charged nitrogen ions (N(+)) at fluences, phi, between 10(14) and 10(16) cm(-2). Irradiation resulted in compaction, which reached about 40% (measured via the film thickness) at the highest fluence. Infrared reflection-absorption spectroscopy (IRRAS) revealed the presence of Ti-O bonds in all films. Both O-H and C-H groups were present in the as-deposited films, but the density of each of these decreased with increasing phi and was absent at high phi, indicating a loss of hydrogen. X-ray photoelectron spectroscopy (XPS) analyses revealed an increase in the C to Ti atomic ratio as phi increased, while the O to Ti ratio hardly altered, remaining at around 2.8. The optical gap of the films, derived from data obtained by ultraviolet-visible spectroscopy (UVS), remained at about 3.6 eV for all fluences except the highest, for which an abrupt fall to around 1.0 eV was observed. For the irradiated films, the electrical conductivity, measured using the two-point method, showed a systematic increase with increasing phi. (c) 2008 Elsevier B.V. All rights reserved.

Preparation of Fe-Cr-P-Co amorphous alloys by electrodeposition

The effects of bath composition and electroplating conditions on structure, morphology, and composition of amorphous Fe-Cr-P-Co deposits on AISI 1020 steel substrate, priorly plated with a thin Cu deposit, were investigated. The increase of charge density activates the inclusion of Cr in the deposit. However, above specific values of the charge density, which depend on the deposition current density, the Cr content in the deposit decreases. This Cr content decreasing is probably due to the significant hydrogen evolution with the increasing of deposition cur-rent and charge density. The effect of charge density on the content of Fe and Co is not clear. However, there is a tendency of increasing of Fe content and decreasing of Co content with the raising of current density. The Co is more easily deposited than the P, and its presence results in a more intense inhibition effect on the Cr deposition than the inhibition effect caused by P presence. Scanning electron microscope (SEM) analysis showed that Co increasing in the Fe-Cr-P-Co alloys analyzed does not promote the susceptibility to microcracks, which led to a good quality deposit. The passive film of the Fe-Cr-P-Co alloy shows a high ability formation and high protective capacity, and the results obtained by current density of corrosion, j(cor), show that the deposit with addition of Co, Fe31Cr11P28Co30, presents a higher corrosion resistance than the deposit with addition of Ni, Fe54Cr21P20Ni5. (C) 2004 Published by Elsevier B.V.

Effects of helium ion irradiation on fluorinated plasma polymers

The effects of ion irradiation on fluorinated plasma polymer films are investigated using profilometry, surface contact-angle measurements, infrared reflection absorption spectroscopy (IRRAS) and X-ray photoelectron spectroscopy (XPS). Remarkably, helium plasma immersion ion implantation (PIII) of several amorphous hydrogenated fluorinated plasma polymers deposited from C(2)H(2)-SF(6), C(6)H(6)-SF(6) or C(6)F(6) produces film compactions of up to 40%, and modifies the surface energy in the 35 to 65 dyn cm(-1) range. As revealed by IRRAS and XPS, the films contain C-H, C-C, C=C, C=O, O-H and C-F groups. XPS spectra confirm the presence of N (typically similar to 5%). The films produced from SF(6)-containing plasmas also contain S. For irradiation times of 80 min, the film carbon content is increased, and the fluorine content is greatly reduced, by factors of about 3 to 15, depending on the initial film composition. (C) 2010 Elsevier B.V. All rights reserved.