磷酸盐激光玻璃聚（CH3）2SiO／SiO2防潮膜改性研究

采用溶胶-凝胶方法制备的（CH2）2Si（OC2H5）2预聚体涂膜液中，掺入碱催化的SiO2悬胶体涂膜液，采用旋涂法在掺钕磷酸盐激光玻璃棒端面涂制了改性的防潮膜。当涂膜液中（CH2）2Si（OC2H5）2和SiO2物质的量之比为1：1时。热处理后的膜层耐摩擦性能明显改善；表面粗糙度的均方根值为1．245nm；膜层激光破坏阈值大于15J／cm^2（1053nm，1ns）；在80℃和95％RH的封闭环境中静置336h，膜层的透过率、接触角基本不变。结果证明膜层具有稳定的疏水结构和很好的防潮性能，膜层强度增加，

Optical transmission larger than 1 (T > 1) through ZnS-SiO2/AgOx/ZnS-SiO2 sandwiched thin films

Optical transmission through flat media should be smaller than 1. However, we have observed optical transmission up to T=1.18. The samples were ZnS-SiO2/AgOx/ZnS-SiO2 sandwiched thin films on glass substrate. The supertransmission could only be observed in the near field. We attribute the supertransmission to the lateral propagation relayed by the laser activated and decomposed Ag nanoparticles. (c) 2006 American Institute of Physics.

SiO2 对Bi2O3-B2O3 玻璃体系光学、热学及结构的 影响

Glasses with compositions 50Bi2O3-xB2O3- (50-x)SiO2(x=0, 10, 20, 30, 40, 50) in mol% have been prepared by using a normal melt-quench technique. The effect of SiO2 addition on thermal stability, optical properties and structural characteristic on Bi2O3-B2O3 glass were systematically investigated by using XRD, DTA, ultraviolet-visible transmittance spectra, midinfrared transmittance spectra and Raman spectra. The experimental results demonstrate that, with the addition of SiO2, thermal stability of glass samples has been obviously improved. Once the amount of SiO2 is too much, the glass samples tend to be phase seperation which results in the decrease of thermal stability. With increasing SiO2 content, the UV cutoff edge firstly shifts to short-wave band and then shifts to long-wave band, and the transmittance of mid-infrared has been greatly improved. With substitution of SiO2 for B2O3, the [BO3] triangles and [BO4] tetrahedral groups are gradually replaced by [SiO4]. [BiO6] octahedral and [SiO4] tetrahedral units are connected forming a vibrational mode of Bi-O-Si. The physical chemistry and optical performance of Bi2O3-B2O3 glass were greatly improved by addition of SiO2.

Effect of water content in sol on optical properties of hybrid sol-gel derived TiO2/SiO2/ormosil film

Sol-gel derived TiO2/SiO2/ormosil hybrid planar waveguides have been deposited on soda-lime glass slides and silicon substrates, films were heat treated at 150 degreesC for 2 h or dried at room temperature. Different amounts of water were added to sols to study their impacts on microstructures and optical properties of films. The samples were characterized by m-line spectroscopy, Fourier transform infrared spectroscopy (FT-IR), UV/VIS/NIR spectrophotometer (UV-vis), atomic force microscopy (AFM), thermal analysis instrument and scattering-detection method. The refractive index was found to have the largest value at the molar ratio H2O/OR = 1 in sol (OR means -OCH3, -OC2H5 and -OC4H9 in the sol), whereas the thickest film appears at H2O/OR = 1/2. The rms surface roughness of all the films is lower than 1.1 nm, and increases with the increase of water content in sol. Higher water content leads to higher attenuation of film. (C) 2004 Elsevier B.V. All rights reserved.

Transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics with broadband infrared luminescence

We report on transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics with broadband infrared luminescence. Ni2+-doped MgO-Al2O3-SiO2 glass is Prepared by using the conventional method. After heat treatment at high temperature, MgAl2O4 crystallites are precipitated, and their average size is about 4.3nm. No luminescence is detected in the as-prepared glass sample, while broadband infrared luminescence centred at around 1315nm with full width at half maximum (FWHM) of about 300nm is observed from the glass ceramics. The observed infrared emission could be attributed to the T-3(2g)(F-3) -> (3)A(2g)(F-3) transition of octahedral Ni2+ ions in the MgAl2O4 crystallites of the transparent glass ceramics. The product of the fluorescence lifetime and the stimulated emission cross section is about 1.6 X 10(-24) s cm(2).

Spectroscopic and fluorescence decay behaviors of Yb3+ -doped SiO2-PbO-Na2O-K2O glass

The spectroscopic and fluorescent decay behaviors of Yb3+-doped SiO2-PbO-Na2O-K2O glass is reported in this work. Yb2O3 contents of 1, 1.5 and 2mol% are added into the glass. Through the measurement of absorption and fluorescence spectra, and fluorescent decay rate at room temperature and at low temperature (18 K), it is found that the nonradiative decay rate of Yb3+ ions is mainly determined by the interaction between residual hydroxyl groups and Yb3+ ions. Concentration quenching effect can be omitted in this glass up to the Yb3+ ion concentration of 8.98 x 10(20)/cm(3). Multiphonon decay rate is also very small because of the large energy gap between F-2(5/2) and F-2(7/2) levels of Yb3+ ions. (c) 2004 Elsevier B.V. All rights reserved.

Broadband infrared luminescence from Li2O-Al2O3-ZnO-SiO2 glasses doped with Bi2O3

The broadband emission in the 1.2 similar to 1.6 mu m region from Li2O-Al2O3-ZnO-SiO2 ( LAZS) glass codoped with 0.01mol.% Cr2O3 and 1.0mol.% Bi2O3 when pumped by the 808nm laser at room temperature is not initiated from Cr4+ ions, but from bismuth, which is remarkably different from the results reported by Batchelor et al. The broad similar to 1300nm emission from Bi2O3-containing LAZS glasses possesses a FWHM ( Full Width at Half Maximum) more than 250nm and a fluorescent lifetime longer than 500 mu s when excited by the 808nm laser. These glasses might have the potential applications in the broadly tunable lasers and the broadband fiber amplifiers. (c) 2005 Optical Society of America.