Thermal influence on excimer-laser-induced electrical conductivity on polyimide film surfaces

The thermal influence on the electrical conductivity of polyimide film surfaces induced by KrF-laser irradiation was investigated, The formation of conducting phases was demonstrated to be highly temperature sensitive, as evidenced by strong dependence of the electrical conductivity on repetition rate and ambient temperature. XPS and Raman studies showed that the efficiency of the formation of conducting phases could be enhanced by the increase of temperature on irradiated polyimide film surfaces. After the disruption of polymeric chain, the carbon-enriched clusters remained on the irradiated polyimide film surfaces organized into polycrystalline graphite-like clusters responsible for electrical conductivity. The resulting dangling bonds from the decomposition process of polyimide acted as centers for the rearrangement of carbon-enriched clusters. It is suggested that the motion of radicals was promoted with increasing the temperature. Therefore the formation of polycrystalline graphite-like clusters benefited from high remaining temperature on the irradiated polyimide film surfaces. These results revealed that thermal influence played a dominant role on the formation of conducting phases.

Structural studies of excimer laser-induced percolative phase transition on polyimide thin film surfaces

The behavior of electrical conductivity for excimer laser irradiated polyimide films in the vicinity of the critical number of laser shots was described by three-dimensional percolative phase transition model. It is: found that electrical conductivity changed more rapidly than that predicted by the percolation model. Thus, the change in microstructure with increasing number of laser shots was analyzed by FT-IR Raman spectrometry and laser desorption time-of-flight mass spectrometry. It is demonstrated that not only the number but also the average size of graphite particles on the irradiated polyimide film surfaces increased with increasing number of laser shots. These results were helpful to better understand the critical change in electrical conductivity on the irradiated polyimide film surfaces. (C) 2001 Elsevier Science B.V. All rights reserved.

Diffusion-limited kinetics modeling of one-step polyimide formation

A diffusion-limited kinetic model was developed to describe the imidization of one-step polythioetherimide formation based on an endgroup diffusion model. The changes of conversion and viscosity during the imidization were monitored with thermogravimetric analysis and dynamic stress rheometry, respectively. It was observed that the imidization rate began to decelerate after a fast early stage, whereas the viscosity in the system increased dramatically after a period of low value. Amic acid and imide formations concurrently take place in the one-step polyimide formation, but the formation of amic acid is much slower than that of imide and is the rate-limiting step of imidization. When a second-order kinetic model was used to describe the imidization, the effect of viscosity on the diffusion resistance of reactive groups needed to be included. In order to predict the change of viscosity during the imidization, the Lipshitz-Macosko model was modified and introduced into the diffusion-limited kinetic model by the Stokes-Einstein equation. The comparison of the modeled results with experimental data indicated that the diffusion-limited kinetic model and the modified Lipshitz-Macosko model were able to efficiently predict the changes of conversion and viscosity with temperature and time during the one-step polythioetherimide formation. (C) 2001 John Wiley & Sons, Inc.

Preparation of polyimide-BaTiO3 hybrid films by a dispersion process and their microstructure

Barium titanate (BaTiO3) powders with particle sizes of 30 similar to 50 nm were prepared from barium stearate, titanium alkoxides and stearic acid by stearic acid-gel method. Dispersing the agglomerate of BaTiO3 nanoparticles into poly(amic acid) solution followed by curing led to the formation of polyimide hybrid films. The hybrid films were transparent and well distributed with BaTiO3 nanoparticles when the BaTiO3 content was less than 1 wt%. Highly loaded hybrid film containing 30 wit % BaTiO3 was tough, had a smooth surface and possessed much higher dielectric and piezoelectric constants than the parent polyimide.

Syntheses of novel macrocyclic polyarylate oligomers based on phenolphthalein and m-phthaloyl-dichloride

Novel macrocyclic oligomers were synthesized through the condensation of phenolphthalein and m-phthaloyl-dichloride with triethylamine as catalyst in the mixed solution of methylene chloride and THF via pseudo-high-dilution technique. The oligomers were characterized by IR, H-1 NMR, MS, WAXD, TGA and DSC. It was found that the 3 : 3 adduct (molar ratio of phenolphthalein to m-phthaloyl-dichloride) and the 4 : 4 adduct were the main products and there was a small amount of crystalline in the macrocyclic mixtures. When the mixtures were heated to 360 degrees C, the crystalline disappeared.

Novel macrocyclic aryl thioether ester oligomers: structure characterization and free-radical ring opening polymerization

Novel macrocyclic aryl thioether ester oligomers have been synthesized in high yield from phthaloyl dichloride and 4,4'-thiodiphenol under pseudo high dilution conditions. The cyclic nature was unambiguously confirmed by a combination of MALDI-TOF MS, gel permeation chromatography and NMR analyses. Single-crystal X-ray diffraction of cyclic ester dimer reveals no severe strain on the cyclic structure. The free-radical ring opening polymerization (ROP) of the macrocyclic oligomers was achieved to give high molecular weight polymers via a transthioetherification reaction. The molecular weight of the polymer resulting from ROP decreases as the conversion of cyclic oligomers increases after a polymerization period of 30 min.

Ester-type precursor of polyimide and photosensitivity

In order to investigate the influence of the main chain structure and molecular weight on the sensitivity of photosensitive ester-type precursor of polyimide (photo-PAE), an improved method was used to synthesize several kinds of photo-PAEs with relatively high molecular weight. Their sensitivities (at 365 nm) were investigated, and it was found that some additives such as sensitizer and photoinitiator had the greatest influence on the sensitivity of photo-PAE, that the photo-PAE with BPDA and mPDA as the main chain structure had the best sensitivity (D-0.5: 5-10 mJ/cm(2)) among the studied photo-PAEs, and that the sensitivity did not significantly change with the change of inherent viscosity of photo-PAE. Meanwhile, the thermal imidization of these photo-PAEs was also investigated by means of TGA and IR analyses. Additionally, a discussion was made for formulation of PSPI resist. (C) 1999 Elsevier Science Ltd. All rights reserved.

New optically active aromatic polyimides II: Synthesis and properties of optically active aromatic polyimide based on (R)-(+)-2,2 '-bis(2-trifluoro-4-aminophenoxy)-1,1 '-binaphthyl

Optically active (R)-(+)-2, 2'-bis(2-trifluoro-4-aminophenoxy)-1, 1'-binaphthyl was prepared from 1, 1'-bi-2-naphthol. The optically active aromatic polyimide was also successfully synthesized. This new polymer has good solubility, thermal stability etc. Its specific rotation was found to be +174 degrees, and its chiroptical property was also studied.

Fluorescence and aggregation behavior of a polyimide in solutions

The UV-visible absorption and fluorescence spectra of a soluble polyimide, YS-30, in several organic solvents were measured over a wide range of concentration. The experimental results show that there exist both intramolecular and intermolecular electron donor acceptor interactions for YS-30 molecules. The fluorescence behavior of YS-30 in N,N-dimethylacetamide and in chloroform solutions is similar in general, except that its ground-state intermolecular charge transfer emission is more obvious in N,N-dimethylacetamide solution. This difference is attributed to the greater extent of disruption of the chain packing by solvent or/and the more efficient radiationless energy dissipation process from the excited state complexes to chloroform. The intensity ratio of intermolecular charge transfer emission to intramolecular charge transfer emission is used to characterize the state of aggregation of YS-30 molecules in solutions. The plot of this ratio versus concentration indicates the existence of two critical concentrations. It is also found from the same plot that the decrease of coil size is very pronounced during the initial stage of shrinkage.

A comparative study of insoluble and soluble polyimide thin films

Physical properties of thin films of soluble and insoluble aromatic polyimides were compared by d.s.c., u.v.-visible and fluorescence spectroscopy, and prism coupler technique. D.s.c. results showed that the thermal properties of insoluble polyimides are superior to those of soluble ones, owing to the specific molecular interactions of insoluble polyimides, revealed by fluorescence spectroscopy. However, the specific molecular interactions sacrifice the transparency in their thin films, shown by u.v.-visible transmission spectra. Negative birefringence of thin films, not only for soluble polimides but also for polyamic acids of insoluble polyimides, was confirmed by prism coupler, while thin films of insoluble polyimides thermally imidized lack high levels of negative birefringence. It is regarded that thin films of insoluble polyimides thermally imidized are likely to be isotropic because of molecular relaxation above their glass transition temperatures (T-g) in the course of thermal imidization, according to Flory's principle. On the contrary, thin films of insoluble poyimide chemically imidized keep the same levels of negative birefringence as those of the relevant polyamic acid thin films. Judging from the opposite cases, it is recognized that molecular relaxation above T-g weakens the optical anisotropy of polyimide thin films. (C) 1998 Elsevier Science Ltd. All rights reserved.

Polyimide structure-property relationships - I. Polyimide properties vs dianhydride configuration

X-ray crystal structures of 2,2',3,3'-and 3,3',4,4'-biphenyltetracarboxylic dianhydride (2,2',3,3'- and 3,3',4,4'-BPDA) were determined. The dianhydride isomers have different symmetry caused by difference in two anhydride group positions and the dihedral angles between the two phenyl rings are 62.9 degrees for 2,2',3,3',-BPDA and 0 degrees for 3,3',4,4'-BPDA respectively. The polyimides from 2,2',3,3'-BPDA exhibit enhanced solubility, higher thermal stability, and higher glass transition temperature (T-g) compared with those from 3,3',4,4'-BPDA.

Synthesis of novel cyclic aryl ether thioether ketone (Sulfone) oligomers

Two kinds of macrocyclic oligomers containing aromatic sulfide linkages have been synthesized by the solution polycondensation in high yield. The cyclic compounds were characterized by H-1 and C-13 NMR, by and MALDI - TOF MS.

Synthesis of cyclic aryl ether sulfone oligomers through interfacial polycondensation method

Novel cyclic aryl ether sulfone oligomers have been synthesized in high yield based on bisphenol A and 4-fluoro-3-nitrophenyl sulfone firstly through interfacial polycondensation reaction under a pseudo-high-dilution condition. Detailed structural characterization of the oligomers by MS, GPC, NMR and IR analyses confirmed the cyclic nature.

Synthesis and polymerization of some macrocyclic (arylene ether sulfone) containing cardo groups and macrocyclic (arylene ether ketone sulfone) oligomers

Some novel macrocyclic (arylene ether sulfone) containing cardo groups and (arylene ether ketone sulfone) oligomers have been synthesized in high yields by a nucleophilic aromatic substitution reaction of 4,4'-difluorophenylsulfone with bisphenols in the presence of anhydrous potassium carbonate under a pseudo-high-dilution condition. Detailed structural characterization of these oligomers by matrix-assisted laser desorption/ionization-time of flight-mass spectrometry (MALDI-TOF-MS), fast atom bombardment mass spectrometry (f.a.b.-m.s.), nuclear magnetic resonance spectrometry (n.m.r.) and single-crystal X-ray structure analysis confirms their cyclic nature, and the composition of the oligomeric mixtures is provided by g.p.c. analysis. Ring polymerization of cyclic oligomers 3a to a high molecular weight polymer with M-w of 59.1 k was achieved by heating at 290 degrees C for 40 min in the presence of a nucleophilic initiator. (C) 1998 Elsevier Science Ltd. All rights reserved.

Optical properties of organo-soluble polyimide thin films and their applications in liquid crystal displays

Three organo-soluble polyimide powders have been synthesized. Their imidization was verified by Fourier transform infrared (FTIR) and thermal gravimetric analysis (TGA) techniques. The amorphous morphology of their thin films were confirmed by X-ray diffraction. Polyimide thin films were prepared by solution casting or spin coating. UV-visible transmission spectra of thin films revealed that they are almost transparent in the range of visible light. With in-plane orientation, revealed by FTIR spectra, negative birefringence (Delta n) of thin films were observed, and refractive indices of the thin films along the film plane (n(TE)) and normal to the plane (n(TM)) were measured by a prism coupler. Because of negative birefringence of the thin films, they tan be substituted for the compensation films for twisted nematic liquid crystal displays (TN-LCDs) to extend their viewing angles. In this paper, a 90 degrees C TN-LCD and 120 degrees C TN-LCD were taken as examples to show the compensation effect of thin films of a qualified polyimide. (C) 1998 Elsevier Science S.A. All rights reserved.