Relationship between viscoelastic transition and yield behavior of phenolphthalein poly(ether ketone)

The viscoelastic behavior of phenolphthalein poly(ether ketone) (PEK-C) and its relationship to yielding was studied. The following phenomena were observed: (1) The relaxation behavior at strain near yield closely approximated that at low strain but near the T-g; (2) the temperature and strain rate dependence of yield stress could be modeled by the one-process Eyring theory and the value of the activation volume was the same as that of the glass transition; and (3) according to the Zhurkov-Bueche equation, the cu transition was related to the yield behavior. All these results indicated that the glass transition was the main factor that controlled the yield behavior. (C) 1996 John Wiley & Sons, Inc.

Application of coupling model for stress relaxation of phenolphthalein polyether ketone

According to stress relaxation curves of phenolphthalein polyether ketone (PEK-C) at different temperatures and the principle of the time-temperature equivalence, the master curve of PEK-C at arbitrary reference temperature is obtained. A coupling model is applied to explain quantitatively stress relaxation behaviour of PEK-C at different temperatures. The parameters obtained from the coupling model have important physical meaning. Copyright (C) 1996 Elsevier Science Ltd.

Dynamic light-scattering characterization of the molecular weight distribution of a broadly distributed phenolphthalein poly(aryl ether ketone)

Using a recently developed laser light-scattering (LLS) procedure, we accomplished the characterization of a broadly distributed unfractionated phenolphthalein poly(aryl ether ketone) (PEK-C) in CHCl3 at 25 degrees C. The laplace inversion of precisely measured intensity-intensity time correlation function from dynamic LLS leads us first to an estimate of the characteristic line-width distribution G(Gamma) and then to the translational diffusion coefficient distribution G(D). By using a previously established calibration of D (cm(2)/s) = 2.37 X 10(-4)M(-0.57), were able to convert G(D) into a differential weight distribution f(w)(M). The weight-average molecular weight M(w) calculated from f(w)(M) agrees well with that directly measured in static LLS. Our results indicate that both the calibration and LLS procedure used in this study are ready to be applied as a routine method for the characterization of the molecular weight distribution of PEK-C. (C) 1996 John Wiley & Sons, Inc.

Laser light-scattering study of novel thermoplastics .2. Phenolphthalein poly(ether sulfone) (PES-C)

Five narrowly distributed fractions of phenolphthalein poly(ether sulfone) (PES-C) were studied in CHCl3 by both static and dynamic laser light scattering (LLS) at 25 degrees C. The dynamic LLS showed that the PES-C samples contain some large polymer clusters as in previously studied phenolphthalein poly(ether ketone)(PEK-C). These large clusters can be removed by a 0.1-mu m filter. Our results showed that [R(g)(2)](1/2)(z) = (3.35 +/- 0.13) x 10(-2) M(w)((0.52 +/- 0.03)) and [D] = (2.26 +/- 0.02) x 10(-4)M(w)-((0.54) +/- 0.03)) with [R(g)(2)](1/2)(z), M(w) and [D] being the z-average radius of gyration, the weight-average molecular weight, and the z-average translational diffusion coefficient, respectively. A combination of static and dynamic LLS results enabled us to determine D = (2.45 +/- 0.04) x 10(-4)M-((0.55 +/- 0.05)), where D and M correspond to monodisperse species. Using this scaling relationship, we have successfully converted the translational diffusion coefficient distribution into the molecular weight distribution for each of the five PES-C fractional The weight-average molecular weights obtained from dynamic light scattering have a good agreement with that obtained from static laser light-scattering measurements.

Sulfonation of polyetheretherketone and its effects on permeation behavior to nitrogen and water vapor

The novel polyetheretherketone (PEK-C) prepared from phenolphthalein in our institute is an amorphous, rigid, tough material with good mechanical properties over a wide temperature range. To improve its water vapor permeability for the application of gas drying, PEK-C was sulfonated with concentrated sulfuric acid and transferred in sodium, cupric, and ferric salt forms. Sulfonation degree can be regulated by controlling the temperature and reaction time. Characterization of sulfonated PEK-C in sodium form was made by infrared spectroscopy. Some properties of the sulfonated PEK-C, such as solubility, glass transition temperature, thermal stability, mechanical properties, and transport properties to nitrogen and water vapor, are also discussed. (C) 1996 John Wiley & Sons, Inc.

Miscibility and phase behavior in blends containing random copolymers of poly(ether ether ketone) and phenolphthalein poly(ether ether ketone)

The miscibility and phase behavior of polysulfone (PSF) and poly(hydroxyether of bisphenol A) (phenoxy) with a series of copoly(ether ether ketone) (COPEEK), a random copolymer of poly(ether ether ketone) (PEEK), and phenolphthalein poly(ether ether ketone) (PEK-C) was studied using differential scanning calorimetry. A COPEEK copolymer containing 6 mol % ether ether ketone (EEK) repeat units is miscible with PSF, whereas copolymers containing 12 mol % EEK and more are not. COPEEK copolymers containing 6 and 12 mol % EEK are completely miscible with phenoxy, but those containing 24 mol % EEK and more are immiscible with phenoxy. Moreover, a copolymer containing 17 mol % EEK is partially miscible with phenoxy; the blends show two transitions in the midcomposition region and single transitions at either extreme. Two T(g)s were observed for the 50/50 blend of phenoxy with the copolymer containing 17 mol % EEK, whereas a single composition-dependent T-g appeared for all the other compositions. An FTIR study revealed that there exist hydrogen-bonding interactions between phenoxy and the copolymers. The strengths of the hydrogen-bonding interactions in the blends of the COPEEK copolymers containing 6 and 12 mol % EEK are the same as that in the phenoxy/PEK-C blend. However, for the blends of copolymers containing 17, 24, and 28 mol % EEK, the hydrogen-bonding interactions become increasingly unfavorable and the self-association of the hydroxyl groups of phenoxy is preferable as the content of EEK units in the copolymer increases. The observed miscibility was interpreted qualitatively in terms of the mean-field approach. (C) 1996 John Wiley & Sons, Inc.

Laser light-scattering study of novel thermoplastics .1. Phenolphthalein poly(aryl ether ketone)

Five different molecular weight phenolphthalein poly(aryl ether ketone) (PEK-C) fractions in CHCl3 were studied by static and dynamic laser light scattering(LLS). The dynamic LLS revealed that the PEK-C samples contain some large polymer clusters. These large clusters can be removed by filtering the solution with a 0.1-mu m filter. We found that the persistence length of PEK-C in CHCl3 at 25 degrees C is similar to 2 nm and the Flory characteristic ratio, C-infinity is similar to 25. Our results showed that [R(g)(2)](1/2)(z) = (3.50+/-0.20) x 10(-2)M(w)(0.54+/-0.01) and [D] = (2.37+/-0.05) x 10(-4)M(w)(-0.55+/-0.01), with [R(g)(2)](1/2)(z), M(w), and [D] being the z-average radius of gyration, the weight-average molecular weight, and the z-average translational diffusion coefficient, respectively. A combination of static and dynamic LLS results enabled us to determine D = (2.20+/-0.10) x 10(-4)M(-0.555+/-0.015), where D and M correspond to monodisperse species. Using this calibration between D and M,we have determined molecular weight distributions of five PEK-C fractions from their corresponding translational diffusion coefficient distribution.

Plastic zone in front of mode I crack in phenolphthalein polyether ketone

The plastic zone size and crack opening displacement of phenolphthalein polyether ketone (PEK-C) at various conditions were investigated. Both of them increase with increasing temperature (decreasing strain rate), i.e. yield stress steadily falls. Thus, the mechanism increasing the yield stress leads to increased constraint in the crack tip and a corresponding reduction in the crack opening displacement and the plastic deformation zone. The effect of the plastic deformation on the fracture toughness is also discussed.

Enhanced glass fiber-reinforced phenolphthalein poly(ether ketone) composites by blending poly(phenylene sulfide)

The mechanical properties of glass fiber-reinforced phenolphthalein poly(ether ketone)/poly(phenylene sulfide) (PEK-C/PPS) composites have been studied. The morphologies of fracture surfaces were observed by scanning electron microscope. Blending a semicrystalline component, PPS, can improve markedly the mechanical properties of glass fiber-reinforced PEK-C composites. These results can be attributed to the improvement of fiber/matrix interfacial adhesion and higher fiber aspect ratio. (C) 1996 John Wiley & Sons, Inc.

酞侧基聚芳醚酮屈服应力与杨氏模量及断裂韧性关系的研究

研究了酞侧基聚芳醚酮（ＰＥＫ－Ｃ）的屈服应力、杨氏模量和断裂韧性等对温度的依赖性，给出了本文所用ＰＥＫ－Ｃ的屈服应力与杨氏模量及屈服应力与断裂韧性间的定量关系．研究表明，在１２℃～１９０℃的温度范围内，随温度的升高，材料的屈服应力、杨氏模量降低．断裂韧性Ｋ１ｃ和Ｇ１ｃ的对数与屈服应力间存在很好的线性关系．

酞侧基聚芳醚酮冲击断裂韧性的研究

本文用仪器化冲击仪研究了酞侧基聚芳醚酮（ＰＥＫ－Ｃ）的冲击断裂韧性对温度的依赖性。依据线弹性断裂力学原理，通过１．５ＹＰＬ／ＢＤ２对ａ－１／２作图，所得直线斜率即为应力强度因子Ｋｃ；用Ｕ对ＢＤΦ作图，所得直线斜率即为扩展裂纹所需的能量Ｇｃ。在不同温度下测试，便可得到Ｋｃ－Ｔ，Ｇｃ－Ｔ的依赖关系图。温度对冲击断裂韧性的影响，是ｔａｎδ损耗和裂尖前缘热钝化共同作用的结果。在１００～１４０℃之间，断裂韧性的升高主要是由于β转变作用的结果。通常ｔａｎδ对能量吸收过程的影响，要比裂尖前缘热钝化的影响小，只有当裂尖前缘区域的有效温度Ｔｅ低于软化温度Ｔｓ时，ｔａｎδ才起作用。当Ｔ＝１８０℃，Ｔｅ＝２０２．４３℃，大于软化温度Ｔｓ时，裂尖前缘热钝化开始起作用，冲击断裂韧性随温度升高而升高

TEMPERATURE AND STRAIN-RATE DEPENDENCE OF FRACTURE-TOUGHNESS OF PHENOLPHTHALEIN POLYETHER KETONE

A strong strain-rate and temperature dependence was observed for the fracture toughness of phenolphthalein polyether ketone (PEK-C). Two separate crack-blunting mechanisms have been proposed to account for the fracture-toughness data. The first mechanism involves thermal blunting due to adiabatic heating at the crack tip for the high temperatures studied. In the high-temperature range, thermal blunting increases the fracture toughness corresponding to an effectively higher test temperature. However, in the low-temperature range, the adiabatic temperature rise is insufficient to cause softening and Jic increases with increasing temperature owing to viscoelastic losses associated with the p-relaxation there. The second mechanism involves plastic blunting due to shear yield/flow processes at the crack tip and this takes place at slow strain testing of the single-edge notched bending (SENB) samples. The temperature and strain-rate dependence of the plastic zone size may also be responsible for the temperature and strain-rate dependence of fracture toughness.

FRACTURE-TOUGHNESS OF PHENOLPHTHALEIN POLYETHER KETONE

The static and impact fracture toughness of phenolphthalein polyether ketone (PEK-C) were studied at different temperatures. The static fracture toughness of PEK-C was evaluated via the linear elastic fracture mechanics (LEFM) and the J-integral analysis. Impact fracture toughness was also analyzed using the LEFM approach. Temperature and strain rate effects on the fracture toughness were also studied. The enhancement in static fracture toughness at 70 degrees C was thought to be caused by plastic crack tip blunting. The increase in impact fracture toughness with temperature was attributed two different mechanisms, namely, the relaxation process in a relatively low temperature and thermal blunting of the crack tip at higher temperature. The temperature-dependent fracture toughness data obtained in static tests could be horizontally shifted to match roughly the data for impact tests, indicating the existence of a time-temperature equivalence relationship. (C) 1995 John Wiley & Sons, Inc.

SIMPLE-MODELS FOR STRESS-RELAXATION AND YIELD PHENOMENON OF PHENOLPHTHALEIN POLY(ETHER KETONE)

According to stress relaxation curves of phenolphthalein poly(ether ketone) (PEK-C) at different temperatures and the principle of time-temperature equivalence, the master curves of PEK-C at arbitrary reference temperatures are obtained. A coupling model (Kohlrausch-Williams-Watts) is applied to explain quantitatively the different temperature dependence of stress relaxation behavior and the relationship between stress relaxation and yield phenomenon is established through the coupling model.

THE IZOD IMPACT FRACTURE-BEHAVIOR OF PHENOLPHTHALEIN POLY(ETHER KETONE)

The Izod impact fracture behaviour of notched specimens of phenolphthalein poly(ether ketone) (PEK-C) has been studied over a temperature range from room temperature to 240 degrees C by using an instrumented impact tester. The temperature dependence of the maximum load, total impact energy, initiation energy, propagation energy, ductility index (DI) and the relationships between these parameters and the relaxation processes have been investigated.