Does Adhesive Thickness Affect Resin-dentin Bond Strength After Thermal/Load Cycling?

This study evaluated the influence of adhesive layer thickness (ADL) on the resin-dentin bond strength of two adhesive systems (AS) after ther-mal and mechanical loading (TML). A flat superficial dentin surface was exposed with 600-grit SiC paper on 40 molars. After primer application, the adhesive layer of Scotchbond Multipurpose (SBMP) or Clearfil SE Bond (CSEB) was applied in one or two layers to a delimited area (52 mm(2)) and resin blocks (Filtek 2250) were built incrementally: Half of the sample was stored in distilled water (37 C, 24 hours) and submitted to thermal (1,000; 5 degrees-55 degrees C) and mechanical cycles (500,000; 10kgf) [TML]. The other half was stored in distilled water (72 hours). The teeth were then sectioned to obtain sticks (0.8 mm(2)) to be tested under tensile mode (1.0 mm/minute). The fracture mode was analyzed at 400x. The BS from all sticks from the same tooth was averaged for statistical purposes. The data was analyzed by three-way ANOVA. The x(2) test was used (p<0.05) to compare the frequency of pre-testing failure specimens. Higher BS values were observed for SBMP regardless of the ADL. The TML reduced the BS values irrespective of the adhesive employed and the ADL. A higher frequency of pre-testing failure specimens was observed for the cycled groups. A thicker adhesive layer, acting as an intermediate flexible layer, did not min-imize the damage caused by thermal/mechanical load cycling for a three-step etch-and-rinse and two-step self-etch system.

Early and 24-hour bond strength and degree of conversion of etch-and-rinse and self-etch adhesives

Purpose: To evaluate early and 24-hour microtensile bond strength (mu TBS) and the degree of conversion (DC) of one representative adhesive system from each of the four current bonding approaches. Methods: 40 human molars were sectioned occluso-gingivally into two halves. Resin composite was bonded incrementally to flat, mid-coronal dentin, using the adhesives Adper Scotchbond MP (MP); Adper Scotchbond 2 (SB); Clearfil SE Bond (SE); and Adper Prompt L-Pop (LP) according to the respective manufacturer`s instructions (n= 10). One half was immediately sectioned into sticks and subjected to mu TBS test. As the sectioning process took approximately 1 hour, the results were designated as 1-hour bond strengths. The other half was stored in distilled water at 37 degrees C for 24 hours before being sectioned and tested. The DC of these systems was measured using Fourier Transform-Raman spectroscopy in three periods: immediately, 1 and 24 hours after polymerization. Data were analyzed with ANOVA and Tukey`s tests. Results: There were no significant differences between the 1-hour and 24-hour bond strengths (P> 0.05), or among the DC measured immediately, 1 hour and 24 hours after polymerization (P> 0.05). However, significant differences were observed among adhesives (P< 0.05). mu TBS values obtained, in MPa (1 hour/24 hour), were: SB (48.6 + 1.3/48.4 + 3.5) = SE (51.9 + 4.7/53.3 +/- 2.9) > MP (35.3 +/- 10.9/38.6 + 6.7) > LP (25.5 + 1.1/26.0 + 1.5). The DC, in percentage (immediately/1 hour/24 hour), were: SE (81/82/87) > MP (79/77/81) > SB (60/63/65) > LP (39/37/42).

Adhesive Temperature: Effects on Adhesive Properties and Resin-Dentin Bond Strength

Objectives: To evaluate the effect of adhesive temperature on the resin-dentin bond strength (mu TBS), nanoleakage (NL), adhesive layer thickness (AL), and degree of conversion (DC) of ethanol/water- (SB) and acetone-based (PB) etch-and-rinse adhesive systems. Methods: The bottles of the two adhesives were kept at each temperature (5 degrees C, 20 degrees C, 37 degrees C, and 50 degrees C) for 2 hours before application to demineralized dentin surfaces of 40 molars. Specimens were prepared for mu TBS testing. Bonded sticks (0.8 mm(2)) were tested under tension (0.5 mm/min). Three bonded sticks from each tooth were immersed in silver nitrate and analyzed by scanning electron microscopy. The DC of the adhesives was evaluated by Fourier transformed infrared spectroscopy. Results: Lower mu TBS was observed for PB at 50 degrees C. For SB, the mu TBS values were similar for all temperatures. DC was higher at 50 degrees C for PB. Higher NL and thicker AL were observed for both adhesives in the 5 degrees C and 20 degrees C groups compared to the 37 degrees C and 50 degrees C groups. The higher temperatures (37 degrees C or 50 degrees C) reduced the number of pores within the adhesive layer of both adhesive systems. Conclusions: It could be useful to use an ethanol/water-based adhesive at 37 degrees C or 50 degrees C and an acetone-based adhesive at 37 degrees C to improve adhesive performance.

Compromised Bond Strength after Root Dentin Deproteinization Reversed with Ascorbic Acid

Introduction: The present study evaluated the effect of a reducing agent on the bond strength of deproteinized root canal dentin surfaces when using a self-adhesive versus dual-cured cement. Regional differences were also evaluated. Methods: A total of 45 bovine incisor roots were divided into 3 groups: irrigation with physiologic solution (control), 10-minute deproteinization with 5% NaOCl, and 10-minute deproteinization with 5% NaOCl followed by 10 minutes of 10% ascorbic acid. Fiber posts were cemented with either RelyX 0100 or RelyX ARC (with SingleBond 2 or Clearfil SE Bond). The push-out bond strength was evaluated after 24 hours of storage. Data were submitted to three-way analyses of variance and Dunnett 13 tests (alpha = 0.05). Results: No differences between cements were observed within the testing conditions, regardless of the adhesive (P < .05). Deproteinization reduced bond strengths. Subsequent treatment with ascorbic acid was capable of reversing bond strength value changes to levels similar to those of controls. Regional radicular differences were also found, where coronal > middle > apical. Conclusions: The reducing agent was capable. of reversing the effect of dentin deproteinization, and RelyX U100 behaved similarly to RelyX ARC. (J Endod 2010;36:130-134)

Influence of glutaraldehyde priming on bond strength of an experimental adhesive system applied to wet and dry dentine

Objectives: This study tested the following null hypotheses: (1) there is no difference in resin-dentine bond strength when an experimental glutaraldehyde primer solution is added prior to bonding procedures and (2) there is no difference in resin-dentine bond strength when experimental glutaraldehyde/adhesive system is applied under dry or wet demineralized dentine conditions. Methods: Extracted human maxillary third molars were selected. Flat, mid-coronal dentine was exposed for bonding and four groups were formed. Two groups were designated for the dry and two for the wet dentine technique: DRY: (1) Group GD: acid etching + glutaraldehyde primer (primer A) + HEMA/ethanol primer (primer B)-under dried dentine + unfilled resin; (2) Group D: the same as GD, except for primer A application; WET: (3) Group GW: the same as GD, but primer B was applied under wet dentine condition; (4) Group W: the same as GW, except for primer A application. The bonding resin was light-cured and a resin core was built up on the adhesive layer. Teeth were then prepared for microtensile bond testing to evaluate bond strength. The data obtained were submitted to ANOVA and Tukey`s test (alpha = 0.05). Results: Glutaraldehyde primer application significantly improved resin-dentine bond strength. No significant difference was observed when the same experimental adhesive system was applied under either dry or wet dentine conditions. These results allow the first null hypothesis to be rejected and the second to be accepted. Conclusion: Glutaraldehyde may affect demineralized dentine properties leading to improved resin bonding to wet and dry substrates. (C) 2008 Elsevier Ltd. All rights reserved.

Effect of different surface treatments on the repair bond strength of indirect composites

Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surface treatments and direct composites. Methods: 180 specimens were prepared with Targis, belleGlass HP and Sculpture indirect composites, light-activated and post-cured according to the manufacturers` recommendations. The specimens were stored in distilled water for 24 hours at 37 degrees C. The bonding surfaces were prepared with air abrasion, hydrofluoric acid or hydrofluoric acid followed by a neutralizing solution. All the treated surfaces were subject to the application of a silane and a bonding agent before the repair procedures with Tetric Ceram and Tetric Flow for the Targis specimens, Herculite XRV and Revolution for the belleGlass HP specimens and Sculp-It and Flow-It for Sculpture specimens. The tensile bond strength tests were carried out using a universal testing machine at cross-head speed of 0.5 mm/minute. The type of fracture was observed under a light microscope at x40 magnification. Data were analyzed by a two-way ANOVA and Tukey`s post-hoc tests (P<0.05). Results: Targis showed a statistically higher repair bond strength than belleGlass HP and Sculpture, which were not significantly different from each other. Air abrasion increased the repair bond strength of belleGlass HP and Sculpture. For Targis, all the surface treatments resulted in similar repair bond strength. The different viscosity of repair composites did not affect the repair of indirect composites. Fractured surfaces showed mostly adhesive failures, mainly with hydrofluoric acid treatment.

Influence of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and bond strength

Statement of the Problem: Adhesive systems can spread differently onto a substrate and, consequently, influence bonding. Purpose: The purpose of this study was to evaluate the effect of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and microtensile bond strength (MTBS). Materials and Methods: Twenty-four molars were sectioned mesiodistally to expose flat buccal and lingual halves. Standardized drop volumes of adhesive systems (Single Bond [SB] and Prime & Bond 2.1 [PB2.1]) were applied to dentin according to the manufacturer`s instructions. Teeth halves were randomly divided into groups: 1A-SB/parallel to gravity; 1B-SB/perpendicular to gravity; 2A-PB2.1/parallel to gravity; and 2B-PB2.1/perpendicular to gravity. The bonded assemblies were stored in 37 degrees C distilled water for 24 hours and then sectioned to obtain dentin sticks (0.8 mm(2)). The adhesive layer thickness was determined in a light microscope (x200), and after 48 hours the specimens were subjected to MTBS test. Data were analyzed by one-way and two-way analysis of variance and Student-Newman-Keuls tests. Results: Mean values (MPa +/- SD) of MTBS were: 39.1 +/- 12.9 (1A); 32.9 +/- 12.4 (1B); 52.9 +/- 15.2 (2A); and 52.3 +/- 16.5 (2B). The adhesive systems` thicknesses (mu m +/- SD) were: 11.2 +/- 2.9 (1A); 18.1 +/- 7.3 (1B); 4.2 +/- 1.8 (2A); and 3.9 +/- 1.3 (2B). No correlation between bond strength and adhesive layer thickness for both SB and PB2.1 (r = -0.224, p = 0.112 and r = 0.099, p = 0.491, respectively) was observed. Conclusions: The differently oriented dentin surfaces and the regional variation of specimens on the adhesive layer thickness are material-dependent. These variables do not influence the adhesive systems` bond strength to dentin. CLINICAL SIGNIFICANCE Adhesive systems have different viscosities and spread differently onto a substrate, influencing the bond strength and also the adhesive layer thickness. Adhesive thickness does not influence dentin bond strength, but it may impair adequate solvent evaporation, polymer conversion, and may also determine water sorption and adhesive degradation over time. In the literature, many studies have shown that the adhesive layer is a permeable membrane and can fail over timebecause ofits continuous plasticizing and degradation when in contact with water. Therefore, avoiding thick adhesive layers may minimize these problems and provide long-term success for adhesive restorations.

Enamel Wetness Effects on Bond Strength Using Different Adhesive Systems

Objective: To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. Methods: This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive systems (Clearfil SE Bond; and Xeno IV). Flat bovine enamel surfaces were either air-dried for 30 seconds or blotted with absorbent paper after acid-etching for the conventional bonding agents or before the application of self-etching bonding agents. The resin composite EsthetX was bonded to flat surfaces that had been treated with one of the adhesives, following the manufacturer`s instructions. After being stored in water at 37 degrees C for one week, bonded specimens were broken in shear. Data were evaluated with two-way analysis of variance (ANOVA) and Student-Newman-Keuls tests (alpha=0.05). For comparing each condition individually, regardless of the adhesive or wetness condition, a one-way ANOVA and a Student-Newman-Keuls test (alpha=0.05) were applied. Results: The two-way ANOVA showed significant differences among adhesive systems. An interaction effect was also observed (p < 0.05), but wetness did not influence shear bond strength (p=0.98). The one-way ANOVA showed that the all-in-one adhesive was the only material influenced by the presence of water at the enamel`s surface. Conclusion: The all-in-one adhesive behaved differently depending on whether the enamel surface was dry or wet.

SEM observation of the bond integrity of fiber-reinforced composite posts cemented into root canals

Objectives. To test the null hypothesis that continuity of resin cement/dentin interfaces is not affected by location along the root canal walls or water storage for 3 months when bonding fiber posts into root canals. Methods. Fiber posts were luted to bovine incisors using four resinous luting systems: Multilink, Variolink II, Enforce Dual and Enforce PV. After cementation, roots were longitudinally sectioned and epoxy resin replicas were prepared for SEM analysis (baseline). The original halves were immersed in solvent, replicated and evaluated. After 3 months water storage and a second solvent immersion, a new set of replicas were made and analyzed. The ratio (%) between the length (mm) of available bonding interface and the actual extension of bonded cement/dentin interface was calculated. Results. Significant lower percent values of bond integrity were found for Multilink (8.25%) and Variolink 11 (10.08%) when compared to Enforce Dual (25.11%) and Enforce PV (27.0%) at baseline analysis. The same trend was observed after immersion in solvent, with no significant changes. However, bond integrity was significantly reduced after 3 months water storage and a second solvent immersion to values below 5% (Multilink = 3.31%, Variolink=1.87%, Enforce Dual=1.20%, and Enforce PV=0.75%). The majority of gaps were depicted at the apical and middle thirds at baseline and after immersion in solvent. After 3 months, gaps were also detected at the cervical third. Significance. Bond integrity at the cement/dentin interface was surprisingly low after cementation of fiber posts to root canals with all resin cements. That was not significantly altered after immersion in solvent, but was further compromised after 3 months water storage. Gaps were mainly seen at middle and apical thirds throughout the experiment and extended to the cervical third after water storage for 3 months. Bond integrity of fiber posts luted to root canals was affected both by location and water storage. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of 2% Chlorhexidine Digluconate on the Bond Strength to Normal Versus Caries-affected Dentin

This study evaluated the effect of 2% chlorhexidine digluconate (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesives to normal (ND) and caries-affected (CAD) dentin. Forty extracted human molars with coronal carious lesions, surrounded by normal dentin, were selected for this study. The flat surfaces of two types of dentin (ND and CAD) were prepared with a water-cooled high-speed diamond disc, then acidetched, rinsed and air-dried. In the control groups, the dentin was re-hydrated with distilled water, blot-dried and bonded with a three-step (Scotchbond Multi-Purpose-MP) or two-step (Single Bond 2-SB) etch-and-rinse adhesive. In the experimental groups, the dentin was rehydrated with 2% CHX (60 seconds), blot-dried and bonded with the same adhesives. Resin composite build-ups were made. The specimens were prepared for microtensile bond testing in accordance with the non-trimming technique, then tested either immediately or after six-months storage in artificial saliva. The data were analyzed by ANOVA/Bonferroni tests (alpha=0.05). CHX did not affect the immediate bond strength to ND or CAD (p>0.05). CHX treatment significantly lowered the loss of bond strength after six months as seen in the control bonds for ND (p<0.05), but it did not alter the bond strength of CAD (p>0.05). The application of NIP on CHX-treated ND or CAD produced bonds that did not change over six months of storage.

Push-out Bond Strength of Fiber Posts Luted with Unfilled Resin Cement

Purpose: The study evaluates the behavior of different adhesive systems and resin cements in fiber post placement, with the intent to clarify the possible role of unfilled resin as a luting material for fiber posts. Materials and Methods: Two luting agents (Dual-Link and Unfilled Resin) for cementing fiber posts into root canals were applied either with All-Bond 2 or One-Step Plus, or without an adhesive system, and challenged with the push-out test. Slices of roots restored with posts were loaded until post segment extrusion in the apical-coronal direction. Failure modes were analyzed under SEM. Results: Push-out strength was significantly influenced by the luting agent (p < 0.05), but not by the bonding strategy (p > 0.05). The best results were obtained in combination with Unfilled Resin with One-Step Plus. Dual-Link groups failed mainly cohesively within the cement, while Unfilled Resin demonstrated more adhesive fracture at the post interface. Conclusion: The results of this study support the hypothesis that adhesive unfilled resin application is essential for achieving high bond strength to radicular dentin.

Microtensile vs Microshear Bond Strength of All-in-One Adhesives to Unground Enamel

Purpose To determine the bond strength to unground enamel of all in one adhesives in comparison with an etch and rinse system and to compare the reliability of microtensile and microshear methods in providing such measurements Materials and Methods The bonding procedure was performed on enamel of 64 extracted molars The tested all in one adhesives were Bond Force (Tokuyama), AdheSE One (Ivoclar Vivadent) and Xeno V (Dentsply) Prime&Bond NT (Dentsply) served as control Microtensile specimens were obtained from 4 teeth per group Twelve teeth per group were used for microshear testing Microtensile specimens that failed prior to testing were included in statistical calculations, they were assigned the lowest value measured in the respective group Failure modes were observed under light microscope and classified (cohesive within substrates, adhesive mixed) Statistically significant differences in bond strength were assessed among the adhesives within each testing method and between microshear and microtensile data for each adhesive Failure mode distributions were compared using the chi square test Results All in-one adhesives had similar microshear and microtensile bond strengths In both testing methods, the etch and rinse system achieved the strongest bond For all adhesives significantly higher bond strengths were measured with the microshear test In microtensile testing specimens bonded with the etch and rinse adhesive exhibited a significantly different distribution of failure modes The coefficients of variation were extremely high for microtensile bond strength data, particularly of all in one adhesives Conclusion The adhesive potential to intact enamel of recently introduced all in-one adhesives was inferior to that of an etch and rinse system When testing bond strength to enamel of all in one adhesives, microshear testing may be a more accurate method than microtensile

Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a `monoblock` effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey`s post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Bond Strength of Fiber Posts to Weakened Roots After Resin Restoration With Different Light-Curing Times

Introduction: This study evaluated the bond strength of translucent fiber posts to experimentally weakened radicular dentin restored with composite resin and polymerized with different light-exposure time. Methods: Roots of 60 maxillary incisors were used. Twenty-four hours after obturation, the filling materials of root canals were removed to a depth of 12 mm, and 4 groups were randomly formed. In 3 groups, root dentin was flared to produce a space between fiber post and canal walls. In the control group, the roots were not experimentally weakened. The flared roots were bulk restored with composite resin, which was light-activated through the translucent post for 40, 80, or 120 seconds. Posts were cemented, and after 24 hours, all roots were sectioned transversely in the coronal, middle, and apical regions, producing 1-mm-thick slices. Push-out test was performed, and failure modes were observed. Results The quantitative analysis showed significant statistical difference only among groups (P <.001). Comparing the weakened/restored groups, composite light-exposure time did not influence the results. Overall, adhesive failures occurred more frequently than other types of failures. Cohesive failures occurred only in the weakened/restored roots. Conclusions Intracanal root restoration with composite resin and translucent fiber posts provided similar or higher bond strength to dentin than the control group, regardless of the light-exposure time used for polymerization. (J Endod 2009;35:1034-1039)

Bond Strength of Epiphany Sealer Prepared with Resinous Solvent

This study evaluated in vitro the bond strength of Epiphany sealer prepared with resinous solvent of Epiphany system (Thinning resin) by using a push-out test. Forty maxillary canines were sectioned transversally below the cementoenamel junction to provide 4-mm-thick dentin disks that were centered in aluminum rings and embedded in acrylic resin. Root canals were prepared with tapered diamond bur. Intraradicular dentin was treated with 1% NaOCl for 30 minutes, 17% ethylenediaminetetraacetic acid for 5 minutes, and flushed with distilled water for 1 minute. The specimens were randomly distributed into 4 groups (n = 10) according to the filling material: GI, Epiphany without photoactivation; GII, Epiphany prepared with solvent without photoactivation; Gill, Epiphany followed by photoactivation; and GIV, Epiphany prepared with solvent followed by photoactivation. After the setting time, the specimens were submitted to the push-out test. The highest mean value (14.91 +/- 2.82 MPa) was obtained with Epiphany prepared with solvent followed by photoactivation (GIV), which was statistically different (P < .01) from the other groups. Groups I (8.15 +/- 2.47 MPa), II (9.46 +/- 2.38 MPa), and III (9.80 +/- 2.51 MPa) had inferior bond strength values and were statistically similar among themselves (P > .01). The resinous solvent of Epiphany system increased the bond strength of Epiphany sealer to dentin walls when followed by photoactivation. (J Endod 2009;35: 251-255)