Porous titanium for biomedical applications: An experimental study on rabbits

Objective: The aim of this study was to carry out an in vivo assessment of bone ingrowth in two different types of porous titanium -the first being completely porous, and the second with a porous surface and dense nucleus, manufactured by powder metallurgy- and to evaluate their mechanical properties. Study design: Ten scaffolds from each group were submitted to metallographic analysis and compression tests. Next, two scaffolds of each type were inserted into 14 rabbits, which were sacrificed 8 weeks after surgery. The samples were submitted for histological examination. Results: Metallographic analysis revealed interconnected pores, and the average interconnected pore diameter was about 360 mm, with 36% total porosity. The totally porous titanium samples and the titanium samples with porous surface and dense nucleus showed an average compressive strength of 16.19 MPa and 69.27 MPa, respectively. After 8 weeks, the animals showed bone ingrowth, even into the most internal pores. Conclusions: The pore morphology was effective in permitting bone ingrowth in both groups. Titanium scaffolds with a porous surface and dense nucleus showed the best mechanical properties and most adequate interface.

Effects of Dimerization on the Structure and Biological Activity of Antimicrobial Peptide Ctx-Ha

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo da secagem de materiais híbridos siloxano-PMMA preparados pelo processo sol-gel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mass fractal characteristics of wet sonogels as determined by small-angle x-ray scattering and differential scanning calorimetry

Low density silica sonogels were prepared from acid sonohydrolysis of tetraethoxysilane. Wet gels were studied by small-angle x-ray scattering (SAXS) and differential scanning calorimetry (DSC). The DSC tests were carried out under a heating rate of 2 degrees C/min from -120 degrees C up to 30 degrees C. Aerogels were obtained by CO(2) supercritical extraction and characterized by nitrogen adsorption and SAXS. The DSC thermogram displays two distinct endothermic peaks. The first, a broad peak extending from about -80 degrees C up to practically 0 degrees C, was associated to the melting of ice nanocrystals with a crystal size distribution with pore diameter ranging from 1 or 2 nm up to about 60 nm, as estimated from Thomson's equation. The second, a sharp peak with onset temperature close to 0 degrees C, was attributed to the melting of macroscopic crystals. The DSC incremental nanopore volume distribution is in reasonable agreement with the incremental pore volume distribution of the aerogel as determined from nitrogen adsorption. No macroporosity was detected by nitrogen adsorption, probably because the adsorption method applies stress on the sample during measurement, leading to a underestimation of pore volume, or because often positive curvature of the solid surface is in aerogels, making the nitrogen condensation more difficult. According to the SAXS results, the solid network of the wet gels behaves as a mass fractal structure with mass fractal dimension D=2.20 +/- 0.01 in a characteristic length scale below xi=7.9 +/- 0.1 nm. The mass fractal characteristics of the wet gels have also been probed from DSC data by means of an earlier applied modeling for generation of a mass fractal from the incremental pore volume distribution curves. The results are shown to be in interesting agreement with the results from SAXS.

2-Mercaptoimidazole covalently bonded to a silica gel surface for the selective separation of mercury(II) from an aqueous solution

Silica gel with a specific surface area of 365 m(2).g(-1) and an average pore diameter of 60 Angstrom was chemically modified with 2-mercaptoimidazole. The degree of functionalization of the covalently attached molecule, (drop SiO)(3)(CH2)(3) - MI, where MI is the 2-mercaptoimidazole bound to the silica surface by a propyl group, was 0.58 mmolg.(-1). In individual metal adsorption experiments from aqueous solutions by the batch procedure, the affinity order was Hg(II)much greater than Cd-II > Cu-II approximate to Zn-II approximate to Pb-II > Mn-II at solution pHs between 4 and 7. Due to the high affinity by the sulfur atom, Hg-II is strongly bound to the functional groups. When solution containing a mixture of Hg-II, Cd-II, Cu-II, Zn-II, Pb-II, and Mn-II ions was passed through a column packed with the adsorbent, Hg-II was the only one whose adsorption and elution was not affected by the presence of other ions.

Sol-gel entrapped cobalt complex

This work describes optimized conditions for preparation of a cobalt complex entrapped in alumina amorphous materials in the form of powder. The hybrid materials, CoNHG, were obtained by a nonhydrolytic sol-gel route through condensation of aluminum chloride with diisopropylether in the presence of cobalt chloride. The materials were calcined at various temperatures. The presence of cobalt entrapped in the alumina matrix is confirmed by ultraviolet visible spectroscopy. The materials have been characterized by X-ray diffraction (XRD), surface area analysis, thermogravimetric analysis (TGA), differential thermal analyses (DTA) and transmission electron microscopy (TEM). The prepared alumina matrix materials are amorphous, even after heat treatment up to 750 degreesC. The XRD, TGA/DTA and TEM data support the increase of sample crystallization with increasing temperature. The specific surface area, pore size and pore diameter changed as a function of the heat treatment temperature employed. Different heat treatment temperatures result in materials with different compositions and structures, and influence their catalytic activity. The entrapped cobalt materials calcined at 750 degreesC efficiently catalyzed the epoxidation of (Z)-cyclooctene using iodozylbenzene as the oxygen donor. (C) 2003 Elsevier B.V. All rights reserved.

PREPARATION AND CHARACTERIZATION OF TI(IV) OXIDE GRAFTED ONTO SILICA ON A SILICA-GEL SURFACE

Silica gel with a surface area of 500 m2g-1 and an average pore diameter of 60 angstrom was chemically modified with Ti(IV) oxide using the grafting method. The amount of metal oxide attached to the surface was 1.8.10(-3) mol g-1. The X-ray photoelectron spectra showed that the metal ion species on the surface are Ti(IV) in TiO2 and MTiO3 (M = Ca2+, Sr2+, Ba2+ and Pb2+), i.e. they have the binding energy of Ti2p3/2 = 458.7 eV. The dehydration of the solid at higher temperature increased the O(II)/Ti (O(II) = oxygen bound to titanium atom) ratio, presumably due to a reticulation of the hydrous Ti(IV) oxide on the silica surface at higher temperatures. Migration of Ti(IV) into the silica gel matrix was observed but the specific surface area was not significantly changed.

Influence of the morphology and microstructure on the photocatalytic properties of titanium oxide films obtained by sparking anodization in H3PO4

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A Semi-Continuous Analyzer for the Fluorimetric Determination of Atmospheric Formaldehyde

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

On the specific filtration mechanism of a mesoporous silica membrane, prepared with non-connecting parallel pores

We report the singular filtration properties of an ultrafiltration membrane made with mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst [Boissière et al., An ultrafiltration membrane made with mesoporous MSU-X silica, Chem. Mater. 15 (2003) 460-463]. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80% and a steep cut-off at 2000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2004 Elsevier B.V. All rights reserved.

An ultrafiltration membrane, prepared with MSU-type mesoporous silica: Preparation and specific filtration behavior

We report preparation and the singular filtration properties of an ultrafiltration membrane made with MSU-type mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80 % and a steep cut-off at 2,000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2005 Elsevier B.V. All rights reserved.

Preparation of a silica gel modified with 2-amino-1,3,4-thiadiazole for adsorption of metal ions and electroanalytical application

Silica gel with a specific area of 382 m2 g-1 and an average pore diameter of 60 Å was chemically modified with 2-amino-1,3,4-thiadiazole, for the purpose of selective adsorption of heavy metals ions and possible use as a chemically modified carbon paste electrode (CMCPE). The following properties of this functionalized silica gel are discussed: selective adsorption of heavy metal ions measured by batch and chromatographic column techniques, and utilization as preconcentration agent in a chemically modified carbon paste electrode (CMCPE) for determination of mercury(II). The chemical selectivity of this functional group and the selectivity of voltammetry were combined for preconcentration and determination. ©2006 Sociedade Brasileira de Química.

Preparação e caracterização de sílicas mesoporosas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Calcinação e estabilidade térmica de Sílicas mesoporoas preparadas com Pluronic P123

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Perfis de polietileno reciclado carregado com fibra de açaí

Foram obtidos perfis tubulares porosos de polietileno (PE) e de polietileno/fibra de açaí (PE/PA) 80/20 extrudados a partir de partículas granuladas de polietileno de alta densidade reciclado de embalagens pós-consumo de 600 μm, e deste com fibra de açaí de 300 μm. Para o processamento das peças foi desenvolvida uma extrusora mono-rosca de bancada, com sistema mecânico acionado por um motor elétrico de ½ CV (0,37 kw) controlado por um inversor de freqüência, com canhões, roscas, matriz e sistema de aquecimento substituíveis. Para permitir uma visualização didática de condições de operação do equipamento de modo simplificado foram realizados testes com parafina em canhão de vidro variando-se a velocidade de rotação do parafuso e perfil de temperatura, ajustando vazão mássica e pressão na saída. Para a extrusão dos perfis porosos foram realizados ensaios reológicos de PE e PE/FA sendo selecionado rosca, barril e matriz de alumínio; rosca com passo de 9 mm e relação comprimento diâmetro (L/D) 22, composta de um elemento misturador e um elemento de flutuação na zona de controle de vazão; ângulo entre o filete e o eixo da rosca 17º, folga entre a rosca e o barril 0,15 mm; rotação de 1,3 rpm; aquecimento ao longo do canhão de 120ºC; matriz tubular com 21 mm de diâmetro interno e mandril de 19 mm de diâmetro externo. Os perfis PE e PE/FA apresentaram poros com diâmetros médios de 0,7 e 0,6 mm; densidade relativa à água a 28ºC de 0,77 e 0,73; módulo de elasticidade de 1,002 e 2,601 GPa e máximo inchamento aparente do extrudado de 100 e 80%.