A hydrothermally stable transition alumina by condensation-enhanced self-assembly and pyrolysis crystallization:application in the steam reforming of methane

The preparation of a steam-based hydrothermally stable transition alumina is reported. The gel was derived from a synthetic sol-gel route where Al-tri-sec-butoxide is hydrolysed in the presence of a non-ionic surfactant (EO20PO70EO20), HCl as the catalyst and water (H2O/Al = 6); the condensation was enhanced by treating the hydrolysed gel with tetrabutylammonium hydroxide (TBAOH), after which it was dried at 60 °C by solvent evaporation. The so-obtained mesophase was crystallized under argon at 1200 °C (1 h) producing a transition alumina containing δ/α, and possibly θ, alumina phases. Due to its surface acidity, the pyrolysis conditions transform the block copolymer into a cross-linked char structure that embeds the alumina crystallites. Calcination at 650 °C generates a fully porous material by burning the char; a residual carbon of 0.2 wt.% was found, attributed to the formation of surface (oxy)carbides. As a result, this route produces a transition alumina formed by nanoparticles of about 30 nm in size on average, having surface areas in the range of 59-76 m2 g-1 with well-defined mesopores centered at 14 nm. The material withstands steam at 900 °C with a relative surface area rate loss lower than those reported for δ-aluminas, the state-of-the-art MSU-X γ-alumina and other pure γ-aluminas. The hydrothermal stability was confirmed under relevant CH4 steam reforming conditions after adding Ni; a much lower surface area decay and higher CH4 conversion compared to a state-of-the-art MSU-X based Ni catalyst were observed. Two effects are important in explaining the properties of such an alumina: the char protects the particles against sintering, however, the dominant effect is provided by the TBAOH treatment that makes the mesophase more resistant to coarsening and sintering. This journal is © the Partner Organisations 2014.

Thermal detemplation of SBA-15 mesophases. Effect of the activation protocol on the framework contraction

The potential use of the solvothermal extraction (SE) as a preliminary step to calcination for detemplating SBA-15 mesophases is investigated; aiming to reduce the amount of organics to be burnt and thereby the corresponding structural shrinkage. A systematic study was carried out by soxhlet extraction on mesophases hydrothermally aged between 90 and 130 C. The mesophases containing variable amounts of template were then treated by calcination or pyrolysis/calcination. TGA was applied to quantify the template amount after the various treatments. The as obtained materials were characterized by SAXS and Ar ad/desorption for structural and textural information while 1H NMR gave information about the integrity of the as-recycled template. The study shows that solvothermal conditions remove considerably the template, typically from 50 to 10-20 wt.%, mainly extracted from the primary mesopores. Possible reuse of the extracted template is questionable as it is poor in polyethyleneoxide compared to the synthesis block-copolymer, Pluronic P123. For all thermal protocols applied (direct calcination, calcination after solvent-extraction or pyrolysis/calcination after solvent extraction), the thermal shrinkage decreases with the aging temperature; that is consistent with the condensation degree of the silica. For each mesophase, it was found that the thermal shrinkage becomes less pronounced when the material is fully templated; thus the template can serve as structural support or can control the mass transfer of O2 and thereby the oxidation rate of the template burning. © 2013 Elsevier Inc. All rights reserved.

Identification of the degradation mechanisms of organic solar cells:active layer and interfacial layers

Organic Solar Cells (OSCs) represent a photovoltaic technology with multiple interesting application properties. However, the establishment of this technology into the market is subject to the achievement of operational lifetimes appropriate to their application purposes. Thus, comprehensive understanding of the degradation mechanisms occurring in OSCs is mandatory in both selecting more intrinsically stable components and/or device architectures and implementing strategies that mitigate the encountered stability issues. Inverted devices can suffer from mechanical stress and delamination at the interface between the active layer, e.g. poly(3-hexylthiophene):[6,6]-phenyl-C61-butyric acid methyl ester (P3HT:PCBM), and the hole transport layer, e.g. poly(3,4-ethylenedioxythiophene):poly(p-styrene sulfonate) (PEDOT:PSS). This work proposes the incorporation of a thin adhesive interlayer, consisting of a diblock copolymer composed of a P3HT block and a thermally-triggerable, alkyl-protected PSS block. In this context, the synthesis of poly(neopentyl p-styrene sulfonate) (PNSS) with controlled molar mass and low dispersity (Ð ≤ 1.50) via Reversible Addition-Fragmentation chain Transfer (RAFT) polymerisation has been extensively studied. Subsequently, Atomic Force Microscopy (AFM) was explored to characterise the thermal deprotection of P3HT-b-PNSS thin layers to yield amphiphilic P3HT-b-PSS, indicating that surface deprotection prior to thermal treatment could occur. Finally, structural variation of the alkyl protecting group in PSS allowed reducing the thermal treatment duration from 3 hours (P3HT-b-PNSS) to 45 minutes for the poly(isobutyl p-styrene sulfonate) (PiBSS) analogous copolymer. Another critical issue regarding the stability of OSCs is the sunlight-driven chemical degradation of the active layer. In the study herein, the combination of experimental techniques and theoretical calculations has allowed identification of the structural weaknesses of poly[(4,4’- bis(2-ethylhexyl) dithieno [3,2-b:2’,3’-d]silole)-2,6-diyl-alt-(4,7-bis(2-thienyl)-2,1,3-benzothiadiazole)-5,5’-diyl], Si-PCPDTBT, upon photochemical treatment in air. Additionally, the study of the relative photodegradation rates in air of a series of polymers with systematically modified backbones and/or alkyl side chains has shown no direct correlation between chemical structure and stability. It is proposed instead that photostability is highly dependent on the crystalline character of the deposited films. Furthermore, it was verified that photostability of blends based on these polymers is dictated by the (de)stabilising effect that [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) has over each polymer. Finally, a multiscale analysis on the degradation of solar cells based on poly[4,4' bis(2- ethylhexyl) dithieno[3,2-b:2',3'-d]silole)-2,6-diyl-alt-[2,5 bis(3 tetradecylthiophen 2-yl)thiazole[5,4-d]thiazole)-1,8-diyl] and PCBM, indicated that by judicious selection of device layers, architectures, and encapsulation materials, operational lifetimes up to 3.3 years with no efficiency losses can be successfully achieved.

Physicochemical properties of hydrogels for use in ophthalmology

This chapter deals with the physicochemical aspects of structure-property relationships in synthetic hydrogels, with particular reference to their application in optometry and ophthalmology. It demonstrates the ways in which the amount of water contained in the hydrogel network can be manipulated by changes in copolymer composition and illustrates the advantages and limitations imposed by use of water as a means of influencing surface, transport and mechanical properties of the gel. The chapter then illustrates how this basic understanding has formed a platform for the development of synthetic interpenetrating networks and macroporous materials, and of hybrids of natural and synthetic hydrogels. The behaviour of these more complex systems is not so centrally dominated by the equilibrium water content as is the case with homogeneous synthetic hydrogels, thus providing advantageous ways of extending the properties and applications of these interesting materials.

Stabilization of troponin I for applications in clinical chemistry and forensic medicine. Cardiac troponin I: A time of death marker

Cardiac troponin I (cTnI) is one of the most useful serum marker test for the determination of myocardial infarction (MI). The first commercial assay of cTnI was released for medical use in the United States and Europe in 1995. It is useful in determining if the source of chest pains, whose etiology may be unknown, is cardiac related. Cardiac TnI is released into the bloodstream following myocardial necrosis (cardiac cell death) as a result of an infarct (heart attack). In this research project the utility of cardiac troponin I as a potential marker for the determination of time of death is investigated. The approach of this research is not to investigate cTnI degradation in serum/plasma, but to investigate the proteolytic breakdown of this protein in heart tissue postmortem. If our hypothesis is correct, cTnI might show a distinctive temporal degradation profile after death. This temporal profile may have potential as a time of death marker in forensic medicine. The field of time of death markers has lagged behind the great advances in technology since the late 1850's. Today medical examiners are using rudimentary time of death markers that offer limited reliability in the medico-legal arena. Cardiac TnI must be stabilized in order to avoid further degradation by proteases in the extraction process. Chemically derivatized magnetic microparticles were covalently linked to anti-cTnI monoclonal antibodies. A charge capture approach was also used to eliminate the antibody from the magnetic microparticles given the negative charge on the microparticles. The magnetic microparticles were used to extract cTnI from heart tissue homogenate for further bio-analysis. Cardiac TnI was eluted from the beads with a buffer and analyzed. This technique exploits banding pattern on sodium dodecyl sulfate polyacrylamide gel electrophoresis (SDS-PAGE) followed by a western blot transfer to polyvinylidene fluoride (PVDF) paper for probing with anti-cTnI monoclonal antibodies. Bovine hearts were used as a model to establish the relationship of time of death and concentration/band-pattern given its homology to human cardiac TnI. The final concept feasibility was tested with human heart samples from cadavers with known time of death. ^

Design and performance assessment of aortic heart valve for tissue engineering

Current artificial heart valves are classified as mechanical and bioprosthetic. An appealing pathway that promises to overcome the shortcomings of commercially available heart valves is offered by the interdisciplinary approach of cardiovascular tissue engineering. However, the mechanical properties of the Tissue Engineering Heart Valves (TEHV) are limited and generally fail in the long-term use. To meet this performance challenge novel biodegradable triblock copolymer poly(ethylene oxide)-polypropylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO or F108) crosslinked to Silk Fibroin (F108-SilkC) to be used as tri-leaflet heart valve material was investigated. ^ Synthesis of ten polymers with varying concentration and thickness (55 µm, 75 µm and 100 µm) was achieved via a covalent crosslinking scheme using bifunctional polyethylene glycol diglycidyl ether (PEGDE). Static and fatigue testing were used to assess mechanical properties of films, and hydrodynamic testing was performed to determine performance under a simulated left ventricular flow regime. The crosslinked copolymer (F108-Silk C) showed greater flexibility and resilience, but inferior ultimate tensile strength, by increasing concentration of PEGDE. Concentration molar ratio of 80:1 (F108: Silk) and thickness of 75 µm showed longer fatigue life for both tension-tension and bending fatigue tests. Four valves out of twelve designed satisfactorily complied with minimum performance requirement ISO 5840, 2005. ^ In conclusion, it was demonstrated that the applicability of a degradable polymer in conjugation with silk fibroin for tissue engineering cardiovascular use, specifically for aortic valve leaflet design, met the performance demands. Thinner thicknesses (t<75 µm) in conjunction with stiffness lower than 320 MPa (80:1, F108: Silk) are essential for the correct functionality of proposed heart valve biomaterial F108-SilkC. Fatigue tests were demonstrated to be a useful tool to characterize biomaterials that undergo cyclic loading. ^

Síntese, caracterização e estudo da associação em meio aquoso de copolímeros responsivos de carboximetilcelulose-g-Jeffamine®

This thesis presents the synthesis, characterization and study of the associative behaviour in aqueous media of new responsive graft copolymers, based on carboxymethylcellulose as the water-soluble backbone and Jeffamine® M-2070 e Jeffamine® M-600 (commercial polyetheramines) as the thermoresponsive grafts with high cloud point temperatures in water. The synthesis was performed on aqueous medium, by using 1-ethyl-3- (3-(dimethylamino)-propyl)carbodiimide hydrochloride and N-hydroxysuccinimide as activators of the reaction between carboxylategroupsfrom carboxymethylcellulose and amino groups from polyetheramines. The grafting reaction was confirmed by infrared spectroscopy and the grafting percentage by 1H NMR. The molar mass of the polyetheramines was determined by 1H NMR, whereas the molar mass of CMC and graft copolymers was determined by static light scattering. The salt effect on the association behaviour of the copolymers was evaluated in different aqueous media (Milli-Q water, 0.5M NaCl, 0.5M K2CO3 and synthetic sea water), at different temperatures, through UV-vis, rheology and dynamic light scattering. None of the copolymers solutions, at 5 g/L, turned turbid in Milli-Q water when heated from 25 to 95 °C, probably because of the increase in hydrophibicity promoted by CMC backbone. However, they became turbid in the presence of salts, due to the salting out effect, where the lowest cloud point was observed in 0.5M K2CO3, which was attributed to the highest ionic strength in water, combined to the ability of CO3 2- to decrease polymer-solvents interactions. The hydrodynamic radius and apparent viscosity of the copolymers in aqueous medium changed as a function of salts dissolved in the medium, temperature and copolymer composition. Thermothickening behaviour was observed in 0.5M K2CO3 when the temperature was raised from 25 to 60°C. This performance can be attributed to intermolecular associations as a physical network, since the temperature is above the cloud point of the copolymers in this solvent.

Bioengineered Approaches to Prevent Hypertrophic Scar Contraction

Burn injuries in the United States account for over one million hospital admissions per year, with treatment estimated at four billion dollars. Of severe burn patients, 30-90% will develop hypertrophic scars (HSc). Current burn therapies rely upon the use of bioengineered skin equivalents (BSEs), which assist in wound healing but do not prevent HSc. HSc contraction occurs of 6-18 months and results in the formation of a fixed, inelastic skin deformity, with 60% of cases occurring across a joint. HSc contraction is characterized by abnormally high presence of contractile myofibroblasts which normally apoptose at the completion of the proliferative phase of wound healing. Additionally, clinical observation suggests that the likelihood of HSc is increased in injuries with a prolonged immune response. Given the pathogenesis of HSc, we hypothesize that BSEs should be designed with two key anti-scarring characterizes: (1) 3D architecture and surface chemistry to mitigate the inflammatory microenvironment and decrease myofibroblast transition; and (2) using materials which persist in the wound bed throughout the remodeling phase of repair. We employed electrospinning and 3D printing to generate scaffolds with well-controlled degradation rate, surface coatings, and 3D architecture to explore our hypothesis through four aims.

In the first aim, we evaluate the impact of elastomeric, randomly-oriented biostable polyurethane (PU) scaffold on HSc-related outcomes. In unwounded skin, native collagen is arranged randomly, elastin fibers are abundant, and myofibroblasts are absent. Conversely, in scar contractures, collagen is arranged in linear arrays and elastin fibers are few, while myofibroblast density is high. Randomly oriented collagen fibers native to the uninjured dermis encourage random cell alignment through contact guidance and do not transmit as much force as aligned collagen fibers. However, the linear ECM serves as a system for mechanotransduction between cells in a feed-forward mechanism, which perpetuates ECM remodeling and myofibroblast contraction. The electrospinning process allowed us to create scaffolds with randomly-oriented fibers that promote random collagen deposition and decrease myofibroblast formation. Compared to an in vitro HSc contraction model, fibroblast-seeded PU scaffolds significantly decreased matrix and myofibroblast formation. In a murine HSc model, collagen coated PU (ccPU) scaffolds significantly reduced HSc contraction as compared to untreated control wounds and wounds treated with the clinical standard of care. The data from this study suggest that electrospun ccPU scaffolds meet the requirements to mitigate HSc contraction including: reduction of in vitro HSc related outcomes, diminished scar stiffness, and reduced scar contraction. While clinical dogma suggests treating severe burn patients with rapidly biodegrading skin equivalents, these data suggest that a more long-term scaffold may possess merit in reducing HSc.

In the second aim, we further investigate the impact of scaffold longevity on HSc contraction by studying a degradable, elastomeric, randomly oriented, electrospun micro-fibrous scaffold fabricated from the copolymer poly(l-lactide-co-ε-caprolactone) (PLCL). PLCL scaffolds displayed appropriate elastomeric and tensile characteristics for implantation beneath a human skin graft. In vitro analysis using normal human dermal fibroblasts (NHDF) demonstrated that PLCL scaffolds decreased myofibroblast formation as compared to an in vitro HSc contraction model. Using our murine HSc contraction model, we found that HSc contraction was significantly greater in animals treated with standard of care, Integra, as compared to those treated with collagen coated-PLCL (ccPLCL) scaffolds at d 56 following implantation. Finally, wounds treated with ccPLCL were significantly less stiff than control wounds at d 56 in vivo. Together, these data further solidify our hypothesis that scaffolds which persist throughout the remodeling phase of repair represent a clinically translatable method to prevent HSc contraction.

In the third aim, we attempt to optimize cell-scaffold interactions by employing an anti-inflammatory coating on electrospun PLCL scaffolds. The anti-inflammatory sub-epidermal glycosaminoglycan, hyaluronic acid (HA) was used as a coating material for PLCL scaffolds to encourage a regenerative healing phenotype. To minimize local inflammation, an anti-TNFα monoclonal antibody (mAB) was conjugated to the HA backbone prior to PLCL coating. ELISA analysis confirmed mAB activity following conjugation to HA (HA+mAB), and following adsorption of HA+mAB to the PLCL backbone [(HA+mAB)PLCL]. Alican blue staining demonstrated thorough HA coating of PLCL scaffolds using pressure-driven adsorption. In vitro studies demonstrated that treatment with (HA+mAB)PLCL prevented downstream inflammatory events in mouse macrophages treated with soluble TNFα. In vivo studies using our murine HSc contraction model suggested positive impact of HA coating, which was partiall impeded by the inclusion of the TNFα mAB. Further characterization of the inflammatory microenvironment of our murine model is required prior to conclusions regarding the potential for anti-TNFα therapeutics for HSc. Together, our data demonstrate the development of a complex anti-inflammatory coating for PLCL scaffolds, and the potential impact of altering the ECM coating material on HSc contraction.

In the fourth aim, we investigate how scaffold design, specifically pore dimensions, can influence myofibroblast interactions and subsequent formation of OB-cadherin positive adherens junctions in vitro. We collaborated with Wake Forest University to produce 3D printed (3DP) scaffolds with well-controlled pore sizes we hypothesized that decreasing pore size would mitigate intra-cellular communication via OB-cadherin-positive adherens junctions. PU was 3D printed via pressure extrusion in basket-weave design with feature diameter of ~70 µm and pore sizes of 50, 100, or 150 µm. Tensile elastic moduli of 3DP scaffolds were similar to Integra; however, flexural moduli of 3DP were significantly greater than Integra. 3DP scaffolds demonstrated ~50% porosity. 24 h and 5 d western blot data demonstrated significant increases in OB-cadherin expression in 100 µm pores relative to 50 µm pores, suggesting that pore size may play a role in regulating cell-cell communication. To analyze the impact of pore size in these scaffolds on scarring in vivo, scaffolds were implanted beneath skin graft in a murine HSc model. While flexural stiffness resulted in graft necrosis by d 14, cellular and blood vessel integration into scaffolds was evident, suggesting potential for this design if employed in a less stiff material. In this study, we demonstrate for the first time that pore size alone impacts OB-cadherin protein expression in vitro, suggesting that pore size may play a role on adherens junction formation affiliated with the fibroblast-to-myofibroblast transition. Overall, this work introduces a new bioengineered scaffold design to both study the mechanism behind HSc and prevent the clinical burden of this contractile disease.

Together, these studies inform the field of critical design parameters in scaffold design for the prevention of HSc contraction. We propose that scaffold 3D architectural design, surface chemistry, and longevity can be employed as key design parameters during the development of next generation, low-cost scaffolds to mitigate post-burn hypertrophic scar contraction. The lessening of post-burn scarring and scar contraction would improve clinical practice by reducing medical expenditures, increasing patient survival, and dramatically improving quality of life for millions of patients worldwide.

Fabrication of sub-10 nm lamellar structures by solvent vapour annealing of block copolymers

Fabrication of nanoscale patterns through the bottom-up approach of self-assembly of phase-separated block copolymers (BCP) holds promise for nanoelectronics applications. For lithographic applications, it is useful to vary the morphology of BCPs by monitoring various parameters to make “from lab to fab” a reality. Here I report on the solvent annealing studies of lamellae forming polystyrene-blockpoly( 4-vinylpyridine) (PS-b-P4VP). The high Flory-Huggins parameter (χ = 0.34) of PS-b-P4VP makes it an ideal BCP system for self-assembly and template fabrication in comparison to other BCPs. Different molecular weights of symmetric PS-b-P4VP BCPs forming lamellae patterns were used to produce nanostructured thin films by spin-coating from mixture of toluene and tetrahydrofuran(THF). In particular, the morphology change from micellar structures to well-defined microphase separated arrangements is observed. Solvent annealing provides a better alternative to thermal treatment which often requires long annealing periods. The choice of solvent (single and dual solvent exposure) and the solvent annealing conditions have significant effects on the morphology of films and it was found that a block neutral solvent was required to realize vertically aligned PS and P4VP lamellae. Here, we have followed the formation of microdomain structures with time development at different temperatures by atomic force microscopy (AFM). The highly mobilized chains phase separate quickly due to high Flory-Huggins (χ) parameter. Ultra-small feature size (~10 nm pitch size) nanopatterns were fabricated by using low molecular weight PSb- P4VP (PS and P4VP blocks of 3.3 and 3.1 kg mol-1 respectively). However, due to the low etch contrast between the blocks, pattern transfer of the BCP mask is very challenging. To overcome the etch contrast problem, a novel and simple in-situ hard mask technology is used to fabricate the high aspect ratio silicon nanowires. The lamellar structures formed after self-assembly of phase separated PS-b-P4VP BCPs were used to fabricate iron oxide nanowires which acted as hard mask material to facilitate the pattern transfer into silicon and forming silicon nanostructures. The semiconductor and optical industries have shown significant interest in two dimensional (2D) molybdenum disulphide (MoS2) as a potential device material due to its low band gap and high mobility. However, current methods for its synthesis are not ‘fab’ friendly and require harsh environments and processes. Here, I also report a novel method to prepare MoS2 layered structures via self-assembly of a PS-b-P4VP block copolymer system. The formation of the layered MoS2 was confirmed by XPS, Raman spectroscopy and high resolution transmission electron microscopy.

BLOCK COPOLYMERS CONTAINING A LOW-SURFACE-ENERGY BLOCK AND THEIR APPLICATIONS

This thesis reports the synthesis and/or applications of three types of block copolymers that each bear a low-surface-energy block. First, poly(dimethylsiloxane)-block-poly(2-cinnamoyloxyethyl acrylate) (PDMS-b-PCEA) was synthesized and characterized. Cotton coating using a micellar solution of this block copolymer yielded superhydrophobic cotton fabrics. X-ray photoelectron spectroscopy (XPS) and surface property analyses indicated that the PDMS block topped the polymer coating. Photocuring the cotton swatches crosslinked the underlying PCEA layer and yielded permanent coatings. More interestingly, hydrophilically patterned superhydrophobic cotton fabrics were produced using photolithography that allowed the crosslinking of the coating around irradiated fibers but the removal, by solvent extraction, of the coating on fibers that were not irradiated. Since water-based ink only permeated the uncoated regions, such patterned fabric was further used to print ink patterns onto substrates such as fabrics, cardboard, paper, wood, and aluminum foil. Then, another PDMS-based diblock copolymer poly(dimethylsiloxane)-block-poly(glycidyl methacrylate) (PDMS-b-PGMA) was prepared. Different from PCEA that photocrosslinked around cotton fibers, PGMA reacted with hydroxyl groups on cotton fiber surfaces to get covalently attached. Further, different PGMA chains crosslinked with each other. PDMS-b-PGMA-coated cotton fabrics have been used for oil-water separations. In addition, polymeric nanoparticles were grafted onto cotton fiber surface before PDMS-b-PGMA was used to cover the surfaces of the grafted spheres and the residual surfaces of the cotton fibers. These two types of fabrics, coated by the block copolymer alone or by the polymer nanospheres and then the copolymer, were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), and water repellency analyses. A comprehensive comparative study was made of their performances in oil-water separation. Finally, a fluorinated ABC triblock copolymer poly(acrylic acid)-block-poly(2-cinnamoyloxyethyl methacrylate)-block-poly(2-perfluorooctylethyl methacrylate) (PAA-b-PCEMA-b-PFOEMA) was used to iii encapsulate air nanobubbles. The produced air nanobubbles were thermodynamically stable in water and were some 100 times more stable than commercially available perfluorocarbon-filled microbubbles under ultrasound. These nanobubbles, due to their small sizes and thus ability to permeate the capillary networks of organs and to reach tumors, may expand the applications of microbubbles in diagnostic ultrasonography and find new applications in ultrasound-regulated drug delivery.

Development of a Composite ion-exchange membrane for PDMS-based microfluidic devices

The purpose of this research is to investigate potential methods to produce an ion-exchange membrane that can be integrated directly into a polydimethylsiloxane Lab-on-a-Chip or Micro-Total-Analysis-System. The majority of microfluidic membranes are based on creating microporous structures, because it allows flexibility in the choice of material such that it can match the material of the microfluidic chip. This cohesion between the material of the microfluidic chip and membrane is an important feature to prevent bonding difficulties which can lead to leaking and other practical problems. However, of the materials commonly used to manufacture microfluidic chips, there are none that provide the ion-exchange capability. The DuPont product Nafion{TM} is chosen as the ion-exchange membrane, a copolymer with high conductivity and selectivity to cations and suitable for many applications such as electrolysis of water and the chlor-alkali process. The use of such an ion-exchange membrane in microfluidics could have multiple advantages, but there is no reversible/irreversible bonding that occurs between PDMS and Nafion{TM}. In this project multiple methods of physical entrapment of the ion-exchange material inside a film of PDMS are attempted. Through the use of the inherent properties of PDMS, very inexpensive sugar granulate can be used to make an inexpensive membrane mould which does not interfere with the PDMS crosslinking process. After dissolving away this sacrificial mould material, Nafion{TM} is solidified in the irregular granulate holes. Nafion{TM} in this membrane is confined in the irregular shape of the PDMS openings. The outer structure of the membrane is all PDMS and can be attached easily and securely to any PDMS-based microfluidic device through reversible or irreversible PDMS/PDMS bonding. Through impedance measurement, the effectiveness of these integrated membranes are compared against plain Nafion{TM} films in simple sodium chloride solutions.

Nanotechnology in the food industry I: applications

Nanotechnology is a multidisciplinary science that is having a boom today, providing new products with attractive physicochemical properties for many applications. In agri/feed/food sector, nanotechnology offers great opportunities for obtaining products and innovative applications for agriculture and livestock, water treatment and the production, processing, storage and packaging of food. To this end, a wide variety of nanomaterials, ranging from metals and inorganic metal oxides to organic nanomaterials carrying bioactive ingredients are applied. This review shows an overview of current and future applications of nanotechnology in the food industry. Food additives and materials in contact with food are now the main applications, while it is expected that in the future are in the field of nano-encapsulated and nanocomposites in applications as novel foods, additives, biocides, pesticides and materials food contact.

Développement de matériaux à base de protéines extraites du byssus de la moule bleue Mytilus edulis

Le byssus est un amas de fibres que les moules produisent afin de s’ancrer aux surfaces immergées sous l’eau. Ces fibres sont pourvues de propriétés mécaniques impressionnantes combinant rigidité, élasticité et ténacité élevées. De plus, elles possèdent un comportement d’auto-guérison de leurs propriétés mécaniques en fonction du temps lorsque la contrainte initialement appliquée est retirée. Les propriétés mécaniques de ces fibres sont le résultat de l’agencement hiérarchique de protéines de type copolymère blocs riches en collagène et de la présence de métaux formant des liens sacrificiels réversibles avec certains acides aminés comme les DOPA et les histidines. Bien que cette fibre soit très intéressante pour la production de matériaux grâce à son contenu élevé en collagène potentiellement biocompatible, cette ressource naturelle est traitée comme un déchet par les mytiliculteurs. L’objectif de cette thèse était de valoriser cette fibre en extrayant les protéines pour générer une nouvelle classe de matériaux biomimétiques. Un hydrolysat de protéines de byssus (BPH) riche en acides aminés chargés, i.e. ~30 % mol, et permettant de former des films a pu être généré. Lorsque solubilisé à pH 10.5, le BPH forme un hydrogel contenant des structures en triple hélice de collagène et des feuillets β anti-parallèles intra- et inter-moléculaires. Suite à l’évaporation de l’eau, le film de BPH résultant est insoluble en milieu aqueux à cause des structures secondaires très stables agissant comme points de réticulation effectifs. Les propriétés mécaniques des films de BPH sont modulables en fonction du pH. Au point isoélectrique (pI = 4.5), les interactions électrostatiques entre les charges opposées agissent comme points de réticulation et augmentent la rigidité des films et leur contrainte à la rupture sans affecter la déformation à la rupture. À pH plus élevé ou plus bas que le pI, les performances mécaniques des films sont plus faibles à cause de la répulsion entre les groupements fonctionnels de même charge qui interagissent plutôt avec les molécules d’eau et causent le gonflement de la matrice protéique des films. Le BPH contenant un nombre élevé d’acides aminés chargés et réactifs, nous avons pu réticuler les films de manière covalente à l’aide d’EDC ou de glutaraldéhyde. Les propriétés mécaniques des films sont modulables en fonction de la concentration d’EDC utilisée lors de la réticulation ou en employant du glutaraldéhyde comme agent réticulant. Les films sont à la fois plus rigides et plus forts avec un degré de réticulation élevé, mais perdent leur extensibilité à mesure que les segments libres de s’étirer lors d’une traction deviennent entravés par les points de réticulation. La réticulation augmente également la résistance à la dégradation enzymatique par la collagénase, les films les plus fortement réticulés lui étant pratiquement insensibles. La spectroscopie infrarouge montre enfin que la réticulation entraîne une transition de feuillets β anti-parallèles inter-moléculaires vers des structures de type hélices de collagène/PPII hydratées. Des liens sacrificiels ont été formés dans les films de BPH par traitement au pI et/ou avec différents métaux, i.e. Na+, Ca2+, Fe3+, afin de moduler les propriétés mécaniques statiques et d’évaluer le rôle de ces traitements sur le comportement d’auto-guérison lors de tests mécaniques cycliques avec différents temps de repos. Plus la valence des ions métalliques ajoutés augmente, plus les propriétés mécaniques statiques affichent un module, une contrainte à la rupture et une ténacité élevés sans toutefois affecter la déformation à la rupture, confirmant la formation de liens sacrificiels. Les tests mécaniques cycliques montrent que les traitements au pI ou avec Ca2+ créent des liens sacrificiels ioniques réversibles qui mènent à un processus d’auto-guérison des performances mécaniques dépendant du pH. L’ajout de Fe3+ à différentes concentrations module les performances mécaniques sur un plus large intervalle et la nature plus covalente de son interaction avec les acides aminés permet d’atteindre des valeurs nettement plus élevées que les autres traitements étudiés. Le Fe3+ permet aussi la formation de liens sacrificiels réversibles menant à l’auto-guérison des propriétés mécaniques. Les spectroscopies Raman et infrarouge confirment que le fer crée des liaisons avec plusieurs acides aminés, dont les histidines et les DOPA. Les résultats dans leur ensemble démontrent que les films de BPH sont des hydrogels biomimétiques du byssus qui peuvent être traités ou réticulés de différentes façons afin de moduler leurs performances mécaniques. Ils pourraient ainsi servir de matrices pour des applications potentielles dans le domaine pharmaceutique ou en ingénierie tissulaire.

Studio del comportamento di poli-alfa-olefine come modificatori di viscosità negli oli lubrificanti

Il buon funzionamento di una qualsiasi tipologia di motore prevede l’utilizzo di un componente che abbia il compito di lubrificare le parti meccaniche in movimento, come, ad esempio, l’olio motore per l’automobile. Un fattore determinante nella scelta dell’olio è la variazione della sua viscosità in relazione alla variazione di temperatura, poiché la temperatura di esercizio di un macchinario è solitamente diversa dalla temperatura di avviamento. Tale valore viene identificato in maniera assoluta dal Viscosity Index (VI). L’olio motore è una formulazione complessa in cui sono presenti l’olio base ed una serie di additivi, tra cui molto importante è il modificatore di viscosità (Viscosity Index Improver, VII), che migliora il VI e permette di utilizzare lo stesso olio a basse ed alte temperature (olio multigrade). Come VII possono essere utilizzate diverse tipologie di polimeri solubili in olio, che variano per caratteristiche e target di mercato. La famiglia presa in esame in questa tesi è quella delle poli-alfa-olefine, utilizzate prevalentemente con oli base minerali, e più precisamente copolimeri etilene/propilene. Sono state analizzate le proprietà che questa famiglia ben nota di OCP (Olefin CoPolymer) ingenera nel sistema base-polimero. In particolare si è cercato di correlare le proprietà molecolari del polimero (composizione, peso molecolare e paracristallinità) con le proprietà “tecnologico-applicative” di ispessimento, stabilità meccanica al taglio, punto di non scorrimento, avviamento a freddo, pompabilità a freddo. L’attività è proseguita con la progettazione di un modello fisico, con l’obiettivo di predire il comportamento tecnologico del sistema olio-polimero in funzione delle proprietà molecolari di polimeri appartenenti alla classe delle poli-alfa-olefine lineari, esaminando anche le proprietà tecnologiche di un omopolimero sperimentale.

The effect of poly(lactide)-poly(carbonate) based block copolymers on the morphology and crystallization of double crystalline poly(lactide)/poly(ε-caprolactone) blends

Block copolymers of poly(lactide) and poly(carbonate) were synthetized in three different compositions and characterized by 1H-NMR and ATR analyses. The compatibilization effect of this copolymers on 80/20 (w/w%) PLA/PCL blend was evaluated. SEM micrographs show that all the blends exhibit the typical sea-island morphology characteristic of immiscible blends with PCL finely dispersed in droplets on a PLA matrix. Upon the addiction of the copolymers a reduction on PCL droplets size is observable. At the same time, a Tg depression of the PLA phase is detected when the copolymers are added in the blend. These results indicate that these copolymers are effective as compatibilizers. The copolymer that acts as the best compatibilizer is the one characterized by the same amount of PLA and PC as repeating units. As result, in the blend containing this copolymer PLA phase exhibits the highest spherulitic growth rate. An analyses on PLA phase crystallization behaviour from the glassy state within the blends was evaluated by DSC experiments. Isothermal cold crystallization of the PLA phase is enhanced up an order of magnitude upon the blending with PCL. Annealing experiments demonstrated that the crystallization of the PCL phase induces the formation of active nuclei in PLA when cooled above cooled below Tg. When the crystallization rate of PCL is retarded, a reduction on PLA nucleation is observed.