Effect of heat input on the mechanical properties of welded joints in high strength steels

Experiments were carried out to determine the properties of the welded joints in 8mm thick high-strength steels produced by quenching and tempering and thermomechanical rolling with accelerated cooling (tensile strength 821–835 MPa). The dependence of the strength, elongation, hardness, impact energy and crack opening displacement on the heat input in the range 1.0–0.7 kJ mm21 was determined. The results show that the dependence of the strength of the welded joints decreases and that of the elongation increases. The heat input has only a slight effect on the impact energy and crack opening displacement in the heat-affected zone.

Paineventtiilien hitsauksen laadunhallinnan kehittäminen

Diplomityössä tarkastellaan keinoja Temet Oy:n valmistamien paineventtiilien hitsauksen laadunhallinnan kehittämiseen. Työn avulla hitsauksen laadunhallinta on tarkoitus saada vastaamaan paremmin yrityksen asiakkaiden vaatimuksia sekä samalla parantaa yrityksen kilpailukykyä. Työn alkupuolella perehdytään laatuun ja laadunhallintaan, erityisesti hitsauksen näkökulmasta. Lisäksi tutustutaan laadunhallinnan työkaluihin, ISO 9001- ja ISO 3834 -standardeihin sekä tarkemmin jälkimmäisen vaatimuksiin. Lisäksi työhön sisältyy kahden erityyppisen paineventtiilin hitseille tehtävä makrohietutkimus. Työssä haetaan myös paineventtiilien valmistukselle vaatimuksia antavia viranomaismääräyksiä tai standardeja. Oleellinen osa hitsauksen laadunhallinnan kehitystyötä on yrityksen hitsaustoiminnan nykytilanteen kartoittaminen ja tarvittavien kehitystoimien suunnittelu tehtyihin selvityksiin perustuen. Työn valmistuttua yrityksellä on ehdotus siitä, miten toteuttaa ISO 3834-2 kattavien laatuvaatimusten mukaisen hitsauksen laadunhallintajärjestelmä paineventtiilien hitsaukseen. Yrityksellä on myös laadunhallintajärjestelmän kannalta oleelliset asiakirjat ja ehdotus siitä, miten hitsauksen laadunhallinnan kehitystyötä kannattaisi tulevaisuudessa jatkaa.

Weldability of powder bed fusion fabricated stainless steel 316L sheets to cold rolled sheet metal

Weldability of powder bed fusion (PBF) fabricated components has come to discussion in past two years due to resent developments in the PBF technology and limited size of the machines used in the fabrication process. This study concentrated on effects of energy input of welding on mechanical properties and microstructural features of welds between PBF fabricated stainless steel 316L sheets and cold rolled sheet metal of same composition by the means of destructive testing and microscopic analysis. Optical fiber diameter, laser power and welding speed were varied during the experiments that were executed following one variable at a time (OVAT) method. One of the problems of welded PBF fabricated components has been lower elongations at break comparing to conventionally manufactured components. Decreasing energy input of the laser keyhole welding decreased elongations at break of the welded specimens. Ultimate tensile strengths were not affected significantly by the energy input of the welding, but fracturing of the specimens welded using high energy input occurred from the weld metal. Fracturing of the lower energy input welds occurred from the PBF fabricated base metal. Energy input was found to be critical factor for mechanical properties of the welds. Multioriented grain growth and formation of neck at fusion zone boundary on the cold rolled side of the weld was detected and suspected to be result from weld pool flows caused by differences in molten weld pool behaviour between the PBF fabricated and cold rolled sides of the welds.

Inclusion or Exclusion? Trade union strategies and Labor migration

Inclusion or Exclusion? Trade Union Strategies and Labor Migration This research identified and analyzed immigration-related strategies of the Finnish Construction Trade Union (FCTU) and the Service Union United (SUU); e.g. how the unions react to labor immigration, whether unions seek to include migrants in the unions, and what is migrants’ position in the unions. The two unions were chosen as the focus of the research because the workforce in the sectors they represent is migrant-dense. The study also analyzed the experiences that migrants who work in these sectors have with trade unions. The Estonian labor market situation –including the role of Estonian trade unions– was also examined as it has a considerable impact on the operating environment of the FCTU. The results of the study indicate that immigration is a contradictory issue for both unions. On the one hand, they strive to include migrants as trade union members and to defend migrants’ labor rights. On the other hand, they, together with their umbrella organization the Central Organisation of Finnish Trade Unions (SAK), seek to prevent labor immigration from outside the EU and EEA countries. They actively defend current labor immigration restrictions by drawing atten- tion to high unemployment figures and to the breaches of working conditions migrants encounter. In contrast, the employer organizations promote a more liberal state policy on labor immigration because they see it as a boost for business. Both the unions and the employer organizations ground their arguments on national interest. However, the position of the trade union movement is not uniform: unions belonging to the Confederation of Unions for Professionals and Managerial Staff in Finland (Akava) embrace more liberal labor immigration stances than the SAK. A key trade union strategy is to try to guarantee that migrants’ working condi- tions do not differ from those of the natives. The FCTU and the SUU inform migrants about Finnish collective agreements and trade union membership in the most common migrant languages. This is important for the unions because it is not in their interest that migrants’ working conditions are undercut. The interviewed migrants said that natives had more negotiating power with employers, which is often negatively portrayed in migrants’ working conditions. Migrants perceive that trade unions have an important role in protecting their working conditions. However, they stressed that migrants’ knowledge of unions is often very limited. The number of migrants in both two unions studied here is increasing. Espe- cially in the SUU, a considerable proportion of the new members are migrants. The FCTU is in a more challenging situation than the SUU because migrant construc- tion workers often work only for short periods in Finland and are consequently not interested in becoming union members. The unions’ strategies partly differ: the FCTU was the first Finnish trade union to establish a trade union branch/lo- cal for migrant members. The goal is to facilitate migrants’ inclusion in the union and to highlight the specific problems they face. The SUU, for its part, insists that such a special strategy would exclude migrants within the union organization. Despite the unions’ strategies, migrants are still underrepresented as union members and officials, which some of the interviewed migrants saw as a problem. Immigrants’ perception of trade unions was pragmatic: they had joined unions when membership yielded concrete benefits. In spite of the unions’ strategies, migrants –and temporary migrants– encoun- ter specific problems in terms of working conditions. Both unions demand more state intervention to protect migrants’ labor rights because overseeing working conditions consumes union resources. However, without the unions’ intervention, these problems would be more common than is currently the case. For instance, some of the interviewed migrants had received trade union assistance in claim- ing unpaid wages. The study demonstrated with the help of building on Walter Korpi’s power resources theory, that immigration is a power resource issue for the unions: suc- cessful immigration-related strategies strengthen unions –and vice versa. The research also showed how the unions’ operating environments constrain and enable their immigration-related strategies. This study has illuminated a previously ignored dimension: the immigrant- inclusive strategies of the Finnish trade unions. The research material consists of 78 qualitative interviews, observation in trade union events, and trade unions’ and employer organizations’ public state- ments.

Kuparin hitsaus kattavilla laatuvaatimuksilla

Kuparin ja kupariseosten hitsaus eroaa merkittävästi esimerkiksi terästen hitsauksesta. Suuri lämmönjohtavuus, lämpölaajeneminen, pehmeneminen ja kuparin taipumus liuottaa kaasuja sulaan asettavat hitsaukselle haasteita. Kuparia on perinteisesti hitsattu kaasuhitsaamalla ja kaasukaarihitsausprosesseilla, mutta uudemmat menetelmät kuten laserhitsaus, elektronisuihkuhitsaus ja FSW-hitsaus tarjoavat uudenlaisia käyttökohteita korkealla laadulla. ISO 3834-2 asettaa noudatettavat vaatimukset hitsaustoiminnalle laatuvaatimusten ollessa kattavia. Ydinvoimalaitoksella hitsauksessa tulee lisäksi noudattaa Säteilyturvakeskuksen YVL-ohjeita, joissa on määritetty lisävaatimuksia liitosten materiaalivalinnoille, pätevöittämiselle ja tarkastamiselle. Tässä työssä tutkittiin kuparimetallien hitsauksen mahdollisuutta Loviisan ydinvoimalaitoksella juottamisen sijasta siten, että kattavat laatuvaatimukset täyttyisivät. Hitsauskokeissa ja laboratoriotutkimuksissa testattiin hitsausta erilaisilla hitsausaineilla ja hitsausprosesseilla. Koetulosten pohjalta toteutettiin hitsausmenetelmä deoksidoidun kupariputken ja tinapronssilaipan TIG-hitsaukselle.

Finnish perceptions on management accounting systems: towards an upgraded sophistication model

This study is based on a large survey study of over 1500 Finnish companies’ usage, needs and implementation difficulties of management accounting systems. The study uses quantitative, qualitative and mixed methods to answer the research questions. The empirical data used in the study was gathered through structured interviews with randomly selected companies of varying sizes and industries. The study answers the three research questions by analyzing the characteristics and behaviors of companies working in Finland. The study found five distinctive groups of companies according to the characteristics of their cost information and management accounting system use. The study also showed that the state of cost information and management accounting systems depends on the industry and size of the companies. It was found that over 50% of the companies either did not know how their systems could be updated or saw systems as inadequate. The qualitative side also highlighted the needs for tailored and integrated management accounting systems for creating more value to the managers of companies. The major inhibitors of new system implementation were the lack of both monetary and human resources. Through the use of mixed methods and design science a new and improved sophistication model is created based on previous research results combined with the information gathered from previous literature. The sophistication model shows the different stages of management accounting systems in use and what companies can achieve with the implementation and upgrading of their systems.

Simulation and material calibration of ultra high strength steel (UHSS) S960 welded joint under static tensile test utilizing finite element method (FEM)

The aim of this work was to calibrate the material properties including strength and strain values for different material zones of ultra-high strength steel (UHSS) welded joints under monotonic static loading. The UHSS is heat sensitive and softens by heat due to welding, the affected zone is heat affected zone (HAZ). In this regard, cylindrical specimens were cut out from welded joints of Strenx® 960 MC and Strenx® Tube 960 MH, were examined by tensile test. The hardness values of specimens’ cross section were measured. Using correlations between hardness and strength, initial material properties were obtained. The same size specimen with different zones of material same as real specimen were created and defined in finite element method (FEM) software with commercial brand Abaqus 6.14-1. The loading and boundary conditions were defined considering tensile test values. Using initial material properties made of hardness-strength correlations (true stress-strain values) as Abaqus main input, FEM is utilized to simulate the tensile test process. By comparing FEM Abaqus results with measured results of tensile test, initial material properties will be revised and reused as software input to be fully calibrated in such a way that FEM results and tensile test results deviate minimum. Two type of different S960 were used including 960 MC plates, and structural hollow section 960 MH X-joint. The joint is welded by BöhlerTM X96 filler material. In welded joints, typically the following zones appear: Weld (WEL), Heat affected zone (HAZ) coarse grained (HCG) and fine grained (HFG), annealed zone, and base material (BaM). Results showed that: The HAZ zone is softened due to heat input while welding. For all the specimens, the softened zone’s strength is decreased and makes it a weakest zone where fracture happens while loading. Stress concentration of a notched specimen can represent the properties of notched zone. The load-displacement diagram from FEM modeling matches with the experiments by the calibrated material properties by compromising two correlations of hardness and strength.

Robottihitsauksen toimintojen kehittäminen hitsaustuotannossa

Tämän diplomityön tarkoituksena oli kehittää robottihitsauksen toimintoja KKR Steel Oy:ssä. Tärkeimmät tutkimuskohteet olivat robottisolujen toiminnan tehostaminen ja uusien robottihitsaukseen sopivien tuotteiden kartoittaminen. Työ on jaettu teoreettiseen ja käytännön osuuteen. Teoriaosassa perehdytään kirjallisuuskatsauksen kautta robottihitsauksen perusteisiin, hitsauksen robotisointiin sekä tuottavuuteen ja laatuun. Robottihitsauksen osuudessa käsitellään hitsausrobotin rakennetta, siihen liittyviä oheislaitteita ja robottien ohjelmointia. Hitsauksen robotisoinnissa selvitetään syitä robottihitsauksen käyttöönotolle, robotisoitavilta tuotteilta vaadittavia ominaisuuksia sekä erilaisia toimenpiteitä robottiaseman toiminnan tehostamiseksi. Tuottavuuteen liittyvässä osuudessa selvitetään erilaisten laskentakaavojen ja tunnuslukujen käyttöä ja merkitystä hitsauksessa. Käytännön osuudessa kartoitettiin yrityksen robottihitsauksen lähtötilanne ja selvitettiin ongelmakohtien perusteella kehittämistoimenpiteitä. Tutkimuksissa seurattiin ja havainnoitiin hitsaustuotannon eri vaiheita, minkä perusteella laadittiin erilaisia parannuskeinoja. Toimenpiteistä saatavan hyödyn arviointiin käytettiin yrityksen tuotantoon sopivia mittareita kuten läpimenoaikaa ja kaariaikasuhdetta. Havaittujen ongelmakohtien perusteella ryhdyttiin kehittämään hitsauskiinnittimien suunnittelua ja käsittelylaitteiden käyttöä hitsaustuotannossa sekä hyödyntämään etäohjelmointia tuotteiden viennissä robottiasemille. Lisäksi robottiasemien käyttöastetta pyrittiin nostamaan tutkimalla käsinhitsattavia tuotteita ja siirtämällä niistä robotille soveltuvimmat robottiasemille hitsattavaksi.

Modifioidun MAG-kaarihitsausprosessin hyödyntäminen railotilavuuden pienentämisessä mekanisoidussa orbitaalihitsauksessa.

Länsimaisen työn hinta luo jatkuvan paineen hitsauksen tuottavuuden parantamiseen. MIG/MAG-hitsauksen tuottavuutta voidaan parantaa tehostamalla hitsausprosessia, vähentämällä hitsien lukumäärää ja pienentämällä hitsiaineen tarvetta. Eri virtalähdevalmistajat tuovat markkinoille hitsausprosesseja hitsauksen tehostamiseen, joilla pystytään korvata vähemmän tuottavia hitsaustyövaiheita. Hitsien lukumäärän vähentäminen on rakenteen suunnitteluun liittyvä tekijä ja hitsiaineen tarpeen pienentäminen voidaan toteuttaa railogeometrian muutoksilla tai tuotteen sopivalla suunnittelulla. Diplomityössä on tutkittu 30 mm paksujen S355 rakenneteräsputkien hitsauksen tuottavuuden kasvattamista käyttäen nykyaikaisia modifioituja kaarihitsausprosesseja ja railotilavuutta pienentämällä. Työssä vertailtiin 30o ja 60o railokulmalla tehtyjä liitoksia. Railogeometrian muutoksen lisäksi diplomityössä vertailtiin eri menetelmien tehokkuutta putken pohjapalon hitsauksessa.

Weldability of high strength aluminium alloys

The need for reduced intrinsic weight of structures and vehicles in the transportation industry has made aluminium research of interest. Aluminium has properties that are favourable for structural engineering, including good strength-to-weight ratio, corrosion resistance and machinability. It can be easily recycled saving energy used in smelting as compared to steel. Its alloys can have ultimate tensile strength of up to 750 MPa, which is comparable to steel. Aluminium alloys are generally weldable, however welding of high strength alloys like the 7xxx series pose considerable challenges. This paper presents research on the weldability of high strength aluminium alloys, principally the 7xxx series. The weldability with various weld processes including MIG, TIG, and FSW, is discussed in addition to consideration of joint types, weld defects and recommendations for minimizing or preventing weld defects. Experimental research was carried out on 7025-T6 and AW-7020 alloys. Samples were welded, and weld cross sections utilized in weld metallurgy studies. Mechanical tests were carried out including hardness tests and tensile tests. In addition, testing was done for the presence of Al2O3 on exposed aluminium alloy. It was observed that at constant weld heat input using a pulsed MIG system, the welding speed had little or no effect on the weld hardness. However, the grain size increased as the filler wire feed rate, welding current and welding speed increased. High heat input resulted in lower hardness of the weld profile. Weld preheating was detrimental to AW- 7020 welds; however, artificial aging was beneficial. Acceptable welds were attained with pulsed MIG without the removal of the Al2O3 layer prior to welding. The Al2O3 oxide layer was found to have different compositions in different aluminium alloys. These findings contribute useful additional information to the knowledge base of aluminium welding. The application of the findings of this study in welding will help reduce weld cost and improve high strength aluminium structure productivity by removing the need for pre-weld cleaning. Better understanding of aluminium weld metallurgy equips weld engineers with information for better aluminium weld design.

Effects of Fabrication Processes on the Behavior of S960 Ultra High Strength Steel (UHSS)

Strenx® 960 MC is a direct quenched type of Ultra High Strength Steel (UHSS) with low carbon content. Although this material combines high strength and good ductility, it is highly sensitive towards fabrication processes. The presence of stress concentration due to structural discontinuity or notch will highlight the role of these fabrication effects on the deformation capacity of the material. Due to this, a series of tensile tests are done on both pure base material (BM) and when it has been subjected to Heat Input (HI) and Cold Forming (CF). The surface of the material was dressed by laser beam with a certain speed to study the effect of HI while the CF is done by bending the specimen to a certain angle prior to tensile test. The generated results illustrate the impact of these processes on the deformation capacity of the material, specially, when the material has HI experience due to welding or similar processes. In order to compare the results with those of numerical simulation, LS-DYNA explicit commercial package has been utilized. The generated results show an acceptable agreement between experimental and numerical simulation outcomes.

Hitsatun alumiinirakenteen suunnittelu

Alumiiniseosten käyttö konstruktiomateriaalina lisääntyy johtuen sen lukuisista variaatioista lujuuden ja muovattavuuden suhteen. Alumiinin keveys on merkittävä kilpailuetu teräkseen nähden. Alumiiniseosten hitsattavuus on parantunut hitsausmenetelmien kehittyessä. Uusilla menetelmillä lämmöntuontia hallitaan paremmin, kuten myös alumiinin huokoisuutta sekä lujuuden laskua hitsauksen yhteydessä. Tässä diplomityössä tutkitaan alumiinin metallurgiaa, hitsausmenetelmiä, sekä alumiinin ja teräksen sekaliitoksen toteutusta. Tutkimuksella pyritään tekemään hitsatun alumiinirakenteen suunnittelua ymmärrettävämmäksi. SFS-EN standardit antavat perustuksen alumiinirakenteen suunnittelulle. Tässä diplomityössä tehdään suunnitteluesimerkki hitsatun alumiinirakenteen hitsien suunnittelusta. Suunnitteluesimerkissä tutkitaan alumiiniseoksen lujuuden laskua hitsattaessa, ja etsitään standardien antamia ratkaisuja toimivan hitsatun rakenteen toteuttamiseksi.

Modulaarinen arkkitehtuuri tuoteperheen kehittämisessä

Modulaarisen tuotteen kehittäminen tehostaa yrityksen kilpailukykyä ja helpottaa asiakkaiden tarpeiden tyydyttämistä. Tuoteperheen edut verrattaessa massatuotantoon ovat laajempi tuotevalikoima sekä parempi tuotettavuus massaräätälöintiin verrattuna. Eri tuotevaihtoehtoja ja moduuleja on mahdollista kehittää rinnakkain. Moduloitava tuoteperhe helpottaa yrityksen eri vaiheita aina tuotteen suunnittelusta huoltotoimenpiteisiin ja lopulta tuotteen purkamiseen. Asiakkaille tärkeitä hyötyjä moduloinnin osalta ovat tuotteiden parempi laatu ja huollettavuus. Täysin uuden modulaarisen tuoteperheen kehittäminen vaatii runsaasti resursseja suunnitteluosastolla. Modulaarisessa tuotteessa suunnittelutyö voidaan kohdistaa vain tietyn moduulin kohdalle ja suunnitteluaikoja saadaan täten lyhennettyä. Tässä kandidaatintyössä tutkittiin, miten hitsausautomaatiosovelluksissa modulaarisuus on toteutettu sekä pohditaan kehityskohteita, koska hitsausautomaatiosovelluksia tuotetaan runsaasti asiakasräätälöintinä. Tarkasteltavana tuoteperheenä oli robottihitsausportaalit ja hitsaustornit.