Strain status in ZnO film on sapphire substrate with a GaN buffer layer grown by metal-source vapor phase epitaxy

ZnO film of 8 mu m thickness was grown on a sapphire (0 0 1) substrate with a GaN buffer layer by a novel growth technique called metal-source vapor phase epitaxy (MVPE). The surface of ZnO film measured by scanning electron microscope (SEM) is smooth and shows many regular hexagonal features. The full width at half maximum (FWHM) of ZnO(0 0 2) and (1 0 2) omega-scan rocking curves are 119 and 202 arcsec, corresponding a high crystal quality. The status of the strain in ZnO thick film was particularly analyzed by X-ray diffraction (XRD) omega-20 scanning. The results show that the strain in ZnO film is compressive, which is also supported by Raman scattering spectroscopy. The compressive strain can solve the cracking problem in the quick growth of ZnO thick film. (c) 2008 Elsevier Ltd. All rights reserved.

Growth of crack-free GaN films on Si(111) substrate by using Al-rich AlN buffer layer

GaN epilayers were grown on Si(111) substrate by metalorganic chemical vapor deposition. By using the Al-rich AlN buffer which contains Al beyond stoichiometry, crack-free GaN epilayers with 1 mum thickness were obtained. Through x-ray diffraction (XRD) and secondary ion mass spectroscopy analyses, it was found that a lot of Al atoms have diffused into the under part of the GaN epilayer from the Al-rich AlN buffer, which results in the formation of an AlxGa1-xN layer at least with 300 nm thickness in the 1 mum thick GaN epilayer. The Al fraction x was estimated by XRD to be about 2.5%. X-ray photoelectron spectroscopy depth analysis was also applied to investigate the stoichiometry in the Al-rich buffer before GaN growth. It is suggested that the underlayer AlxGa1-xN originated from Al diffusion probably provides a compressive stress to the upper part of the GaN epilayer, which counterbalances a part of tensile stress in the GaN epilayer during cooling down and consequently reduces the cracks of the film effectively. The method using the Al diffusion effect to form a thick AlGaN layer is really feasible to achieve the crack-free GaN films and obtain a high crystal quality simultaneously. (C) 2004 American Institute of Physics.

Thermal annealing effect on InAs/InGaAs quantum dots grown by atomic layer molecular beam epitaxy

The effect of rapid thermal annealing on the InAs quantum dots (QDs) grown by atomic layer molecular beam epitaxy and capped with InGaAs layer has been investigated using transmission electron microscopy and photoluminescence (PL). Different from the previously reported results, no obvious blueshift of the PL emission of QDs is observed until the annealing temperature increases up to 800 degreesC. The size and shape of the QDs annealed at 750 degreesC have hardly changed indicating the relatively weak Ga/In interdiffusion, which is characterized by little blueshift of the PL peak of QDs. The QD size increases largely and a few large clusters can be observed after 800 degreesC RTA, implying the fast interdiffusion and the formation of InGaAs QDs. These results indicate that the delay of the blueshift of the PL peak of QDs is correlated with the abnormal interdiffusion process, which can be explained by two possible reasons: the reduction of excess-As-induced defects and the redistribution of In, Ga atoms around the InAs QDs resulted from the sub-monolayer deposition of InGaAs capping layer. (C) 2004 Elsevier B.V. All rights reserved.

The influence of AlN buffer layer thickness on the properties of GaN epilayer

The influence of low-temperature AlN buffer layer thickness on GaN epilayer was investigated by triple-axis X-ray diffraction (XRD) and photoluminescence measurements. A method was proposed to measure the screw and edge dislocation densities by XRD. It was found that the buffer layer thickness was a key parameter to affect the quality of GaN epilayer and an appropriate thickness resulted in the best structural and optical properties except the lateral grain size. After the thickness exceeding the appropriate value, the compressive stress in the epilayer decreased as the thickness increased, which led to the redshift of the near-band edge luminescence. The experimental results showed the buffer layer thickness had more influence on edge dislocation than screw type and the former was perhaps the main source of the yellow band. (C) 2004 Elsevier B.V. All rights reserved.

Luminescence properties of self-assembled InAs/GaAs quantum dots covered by InAlAs and InGaAs combination strain-reducing layer

We report the photoluminescence (PL) and structural properties of self-assembled InAs/GaAs quantum dots (QDs) covered by In0.2Al0.8As and In0.2Ga0.8As combination strain-reducing layer (SRL). By introducing a thin InAlAs layer, the ground state emission wavelength redshifts, and the energy splitting between the ground and first-excited states increases to 85 meV at 10 K. The energy splitting further increases to 92 meV and the temperature dependence of full width at half maximum (FWHM) changes for QDs with different SRL after the multi-stacking. These results are attributed to the fact that the combination layer has different effects on QDs compared to the InGaAs SRL.

Effect of the InAlAs and InGaAs combination strain-reducing layer on 1.3 mu m emission self-assembled InAs/GaAs quantum dots

Self-assembled InAs quantum dots (QDs) with differing deposition thicknesses covered by InxAl1-xAs (x = 0.2, 0.3) and In0.2Ga0.8As combination strain-reducing layers (CSRLs) were grown by molecular beam epitaxy. Their structural and optical properties were investigated by atomic force microscopy and photoluminescence spectroscopy, respectively. The emission peak position of InAs QDs capped by CSRL can reach 1.34 mum at room temperature with a relatively larger energy splitting of 93 meV between the ground and first excited states.

Ordering growth of InAs quantum dots on ultra-thin InGaAs strained layer

InAs quantum dots (QDs) were grown On Ultra-thin In0.15Ga0.85As strained layers by molecular beam epitaxy on GaAs (00 1) substrates. Combining reflection high-energy electron diffraction, atomic force microscopy and transmission electron microscopy, we analyzed the stress field of dislocations in the strained layer/substrate interface. Specially, we revealed the relative position of QDs and dislocations. We found that the difference of the stress field around dislocations is prominent when the strained layer is ultra-thin and the stress field will directly affect the following growth. On the strained layer surface, In0.15Ga0.85As ridges will form at the inclined upside of dislocations. Then, InAs QDs will prefer nucleating on the ridges, there is relatively small stress between InAs and In0.15Ga0.85As. By selecting ultra-thin In0.15Ga0.85As layer (50 nm) and controlling the QD layer at just form QDs, we obtained ordered InAs QDs. (C) 2004 Elsevier B.V. All rights reserved.

1.3 mu m InAs/GaAs self-assembled quantum dots grown on In0.2Ga0.8As-GaAs combined strain-buffer layer

Optical properties and surface structures of InAs/CaAs self-assembled quantum dots (QDs) grown on 2 nm In-0.2 Ga0.8As and x ML GaAs combined strain-buffer layer were investigated systematically by photoluminescence ( PL) and atomic force microscopy (AFM). The QD density increased from similar to 1.7 x 10(9) cm(-2) to similar to 3.8 x 10(9) cm(-1) due to the decreasing of the lattice mismatch. The combined layer was of benefit to increasing In incorporated into dots and the average height-to-width ratios, which resulted in the red-shift of the emission peaks. For the sample of x = 10 ML, the ground state transition is shifted to 1350 nm at room temperature.

Epitaxial SiC grown on silicon-on-insulator substrate with ultra-thin silicon-over-layer

We report on the comparative studies of epitaxial SiC films grown on silicon-on-insulator (SOI) and Si bulk substrates. The silicon-over-layer (SOL) on the SOI has been thinned down to different thicknesses, with the thinnest about 10 nm. It has been found that the full-width-at-half-maxim in the X-ray diffraction spectrum from the SiC films decreases as the SOL thickness decreases, indicating improved quality of the SiC film. A similar trend has also been found in the Raman spectrum. One of the potential explanations for the observation is strain accommodation by the ultra-thin SOI substrate. (c) 2005 Elsevier B.V. All rights reserved.

The effect of a combined InAlAs and GaAs strained buffer layer on the structure and optical property of InAs quantum dots

The character of InAs quantum dots (QD) directly deposited on a combined InAlAs-GaAs (XML) strained buffer layer (SBL) has been investigated. This growth technique realizes high-density QD (5.88 x 10(10) cm(-2)) by changing the thickness of GaAs in InAlAs-GaAs SBL. The dependence of the density and the aspect ratio of QD on the GaAs thickness has been discussed in detail. The photoluminescence (PL) measurements demonstrate an obvious redshift with the increase of GaAs thickness. In addition, the deposition of InAs QDs grown on the combined InAlAs-GaAs SBL has an important effect of the QD properties. The ordered QD array can be observed from the sample deposited by atomic layer epitaxy, of which the PL peak shows an obvious redshift in comparison to the molecular beam epitaxy (MBE) QDs when the GaAs thicknesses are equal. (c) 2004 Elsevier B.V. All rights reserved.

InAs0.3Sb0.7 films grown on (100) GaSb substrates with a buffer layer by liquid-phase epitaxy

The growth of InAsxSb1-x films on (100) GaSb substrates by liquid-phase epitaxy (LPE) has been investigated and epitaxial InAs0.3Sb0.7 films with InAs0.9Sb0.09 buffer layers have been successfully obtained. The low X-ray rocking curve FHWM values of InAs0.3Sb0.7 layer shows the high quality of crystal-orientation structure. Hall measurements show that the highest electron mobility in the samples obtained is 2.9 x 10(4) cm(2) V-1 s(-1) and the carrier density is 2.78 x 10(16)cm(-3) at room temperature (RT). The In As0.3Sb0.7 films grown on (10 0) GaSb substrates exhibit excellent optical performance with a cut-off wavelength of 12 mu m. (c) 2007 Elsevier B.V. All rights reserved.

The influence of V/III ratio in the initial growth stage on the properties of GaN epilayer deposited on low temperature AlN buffer layer

The V/III ratio in the initial growth stage of metalorganic chemical vapor deposition has an important influence on the quality of a GaN epilayer grown on a low-temperature AIN buffer layer and c-plane sapphire substrate. A weaker yellow luminescence, a narrower half-width of the X-ray diffraction peak, and a higher electron mobility result when a lower V/III ratio is taken. The intensity of in situ optical reflectivity measurements indicates that the film surface is rougher at the beginning of GaN growth, and a longer time is needed for the islands to coalesce and for a quasi-two dimensional mode growth to start. A comparison of front- and back-illuminated photoluminescence spectra confirms that many threading dislocations are bent during the initial stage, leading to a better structural quality of the GaN layer. (C) 2007 Elsevier B.V. All rights reserved.

Growth and characterization of AlGaN/AlN/GaN HEMT structures with a compositionally step-graded AlGaN barrier layer

A new AlGaN/AlN/GaN high electron mobility transistor (HEMT) structure using a compositionally step-graded AlGaN barrier layer is grown on sapphire by metalorganic chemical vapour deposition (MOCVD). The structure demonstrates significant enhancement of two-dimensional electron gas (2DEG) mobility and smooth surface morphology compared with the conventional HEMT structure with high Al composition AlGaN barrier. The high 2DEG mobility of 1806 cm(2)/Vs at room temperature and low rms surface roughness of 0.220 nm for a scan area of 5 mu m x 5 mu m are attributed to the improvement of interfacial and crystal quality by employing the step-graded barrier to accommodate the large lattice mismatch stress. The 2DEG sheet density is independent of the measurement temperature, showing the excellent 2DEG confinement of the step-graded structure. A low average sheet resistance of 314.5 Omega/square, with a good resistance uniformity of 0.68%, is also obtained across the 50 mm epilayer wafer. HEMT devices are successfully fabricated using this material structure, which exhibits a maximum extrinsic transconductance of 218 mS/mm and a maximum drain current density of 800 mA/mm.

Extremely low density InAs quantum dots with no wetting layer

Extremely low density InAs quantum dots (QDs) are grown by molecular beam droplet epitaxy, The gallium deposition amount is optimized to saturate exactly the excess arsenic atoms present on the GaAs substrate surface during growth, and low density InAs/GaAs QDs (4x10(6) cm(-2)) are formed by depositing 0.65 monolayers (ML) of indium. This is much less than the critical deposition thickness (1.7 ML), which is necessary to form InAs/GaAs QDs with the conventional Stranski-Krastanov growth mode. The narrow photoluminescence line-width of about 24 meV is insensitive to cryostat temperatures from 10 K to 250 K. All measurements indicate that there is no wetting layer connecting the QDs.

AlGaN/AlN/GaN/SiC HEMT structure with high mobility GaN thin layer as channel grown by MOCVD

Enhancement of the electrical properties in an AlGaN/GaN high electron mobility transistor (HEMT) structures was demonstrated by employing the combination of a high mobility GaN channel layer and an AlN interlayer. The structures were grown on 50 mm semi-insulating (SI) 6H-SiC substrates by metalorganic chemical vapor deposition (MOCVD). The room temperature (RT) two-dimensional electron gas (2DEG) mobility was as high as 2215 cm(2)/V s, with a 2DEG concentration of 1.044 x 10(13)cm(-2). The 50 mm HEMT wafer exhibited a low average sheet resistance of 251.0 Omega/square, with a resistance uniformity of 2.02%. The 0.35 Pin gate length HEMT devices based on this material structure, exhibited a maximum drain current density of 1300 mA/mm, a maximum extrinsic transconductance of 314 mS/mm, a current gain cut-off frequency of 28 GHz and a maximum oscillation frequency of 60 GHz. The maximum output power density of 4.10 W/mm was achieved at 8 GHz, with a power gain of 6.13 dB and a power added efficiency (PAE) of 33.6%. (c) 2006 Elsevier B.V. All rights reserved.