Electrochemical properties and intermediate-temperature fuel cell performance of dense yttrium-doped barium zirconate with calcium addition

Although BaZr 0.8Y 0.2O 3-δ(BZY) possesses large bulk proton conductivity and excellent chemical stability, its poor sinterability and grain boundaries block proton conduction. In this work, the effect of Ca as a co-dopant and as a sintering aid (as CaO), on the sinterability, proton conductivity, and fuel cell performance of BZY was investigated. The addition of 4 mol% CaO significantly improved the BZY sinterability: BZY pellets with densities of 92.7% and 97.5% with respect to the theoretical density were obtained after sintering at 1500°C and 1600°C, respectively. The improved BZY sinterability by CaO addition resulted also in a large proton conductivity; at 600°C, the total conductivity of BZY-CaO was 2.14 × 10 -3 S/cm, in wet Ar. Anode-supported fuel cells with 25 μm-thick BZY-CaO electrolyte membranes were fabricated by a dual-layer co-firing technique. The peak power density of the fuel cell with a BZY-Ni/BZY-4CaO/BZY-LSCF (La 0.6Sr 0.4Fe 0.8Co 0.2O 3-δ) configuration was 141 mW/cm 2 at 700°C, several times larger than the reported values of BZY electrolyte membrane fuel cells sintered with the addition of CuO or ZnO, demonstrating promising features for practical fuel cell applications.

Low-temperature synthesis and sintering of γ-Y2Si2O7

In this article, a novel pressureless solid-liquid reaction method is presented for preparation of yttrium disilicate (γ-Y2Si2O7). Single-phase γ-Y2Si2O7 powder was synthesized by calcination of SiO2 and Y2O3 powders with the addition of LiYO2 at 1400 °C for 4 h. The addition of LiYO2 significantly decreased the synthesis temperature, shortened the calcination time, and enhanced the stability of γ-Y2Si2O7. The sintering of these powders in air and O2 was studied by means of thermal mechanical analyzer. It is shown that the γ-Y2Si2O7 sintered in oxygen had a faster densification rate and a higher density than that sintered in air. Furthermore, single-phase γ-Y2Si2O7 with a density of 4.0 g/cm3 (99% of the theoretical density) was obtained by pressureless sintering at 1400 °C for 2 h in oxygen. Microstructures of the sintered samples are studied by scanning electron microscope.

Expanding the Peptide beta-Turn in alpha gamma Hybrid Sequences: 12 Atom Hydrogen Bonded Helical and Hairpin Turns

Hybrid peptide segments containing contiguous alpha and gamma amino acid residues can form C-12 hydrogen bonded turns which may be considered as backbone expanded analogues of C-10 beta-turns) found in alpha alpha segments. Exploration of the regular hydrogen bonded conformations accessible for hybrid alpha gamma sequences is facilitated by the use of a stereochemically constrained gamma amino acid residue gabapentin (1-aminomethylcyclohexaneacetic acid, Gpn), in which the two torsion angles about C-gamma-C-beta (theta(1)) and C-beta-C-alpha (theta(2)) are predominantly restricted to gauche conformations. The crystal structures of the octapeptides Boc-Gpn-Aib-Gpn-Aib-Gpn-Aib-Gpn-Aib-OMe (1) and Boc-Leu-Phe-Val-Aib-Gpn-Leu-Phe-Val-OMe (2) reveal two distinct conformations for the Aib-Gpn segment. Peptide 1 forms a continuous helix over the Aib(2)-Aib(6) segment, while the peptide 2 forms beta-hairpin structure stabilized by four cross-strand hydrogen bonds with the Aib-Gpn segment forming a nonhelical C-12 turn. The robustness of the helix in peptide 1 in solution is demonstrated by NMR methods. Peptide 2 is conformationally fragile in solution with evidence of beta-hairpin conformations being obtained in methanol. Theoretical calculations permit delineation of the various C-12 hydrogen bonded structures which are energetically feasible in alpha gamma and gamma alpha sequences.

Constitutive equation for elevated temperature flow behavior of plain carbon steels using dimensional analysis

Dimensional analysis using π-theorem is applied to the variables associated with plastic deformation. The dimensionless groups thus obtained are then related and rewritten to obtain the constitutive equation. The constants in the constitutive equation are obtained using published flow stress data for carbon steels. The validity of the constitutive equation is tested for steels with up to 1.54 wt%C at temperatures: 850–1200 °C and strain rates: 6 × 10−6–2 × 10−2 s−1. The calculated flow stress agrees favorably with experimental data.

Characterization of hot deformation behavior of Zr-1Nb-1Sn alloy

The hot deformation behavior of beta-quenched Zr-1 Nb-1Sn was studied in the temperature range 650-1050 degrees C and strain rate range 0.001-100 s(-1) using processing maps. These maps revealed three different domains: a domain of dynamic recovery at temperatures <700 degrees C and at strain rates <3 x 10(-3) s(-1), a domain of dynamic recrystallization in the temperature range 750-950 C-degrees and at strain rates <10(-2) S-1 with a peak at 910 degrees C and 10(-3) S-1 (in alpha + beta phase field), and a domain of large-grain superplasticity in the beta phase field at strain rates <10(-2) s(-1). In order to identify the rate controlling mechanisms involved in these domains, kinetic analysis was carried out to determine the various activation parameters. In addition, the processing maps showed a regime of flow instability spanning both alpha + beta and beta phase fields. The hot deformation behavior of Zr 1Nb-1Sn was compared with that of Zr, Zr-2.5Nb and Zircaloy-2 to bring out the effects of alloy additions. (C) 2006 Elsevier BN. All rights reserved.

Processing Response of Boron Modified Ti-6Al-4V Alloy In (alpha plus beta) Working Regime

Titanium alloys like Ti-6A-4V are the backbone materials for aerospace, energy and chemical industries. Hypoeutectic boron addition to Ti-6Al-4V alloy produces a reduction in as-cast grain size by roughly an order of magnitude resulting in the possibility of avoiding ingot breakdown step and thereby reducing the processing cost. In the present study, ISM processed as-cast boron added Ti-6Al-4V alloy is deformed in (alpha+beta)-phase field, where alpha-lath bending seemed to be the dominating deformation mechanism.

Expression of hyoscyamine 6 beta-hydroxylase in the root pericycle cells and accumulation of its product scopolamine in leaf and stem tissues of Datura metel L.

Hyoscyamine 60-hydroxylase (H6H: EC 1.14.11.11), a key enzyme at the terminal step of tropane alkaloid biosynthesis, converts hyoscyamine to scopolamine. The accumulation of scopolamine in different organs, in particular the aerial parts for storage, is subject to the expression of hyoscyamine 6-phydroxylase as well as its transport from the site of synthesis. To understand the molecular basis of this regulation, we have analyzed, in parallel, the relative levels of hyoscyamine and scopolamine, and the accumulation of H6H (both protein and transcript) in leaves, stems and roots of D. metel. The root, stem and leaf tissues all contain about 0.51-0.65 mg g(-1) dry weight of scopolamine. Hyoscyamine content was extremely low in leaf and stem tissues and was about 0.28 mg g(-1) dry weight in the root tissue. H6H protein and its transcript were found only in roots but not in the aerial parts viz. stems and leaves. The immunolocalization studies performed on leaf, stem, root as well as hairy root tissues showed that H6H was present only in the pericycle cells of young lateral and hairy roots. These studies suggest that the conversion of hyoscyamine to scopolamine takes place in the root pericycle cells, and the alkaloid biosynthesized in the roots gets translocated to the aerial parts in D. metel. (C) 2009 Elsevier Ireland Ltd. All rights reserved.

Effect of Polymer Grafting on the Bilayer Gel to Liquid-Crystalline Transition

Grafted polymers oil the surface of lipid membranes have potential applications in liposome-based drug delivery and Supported membrane systems. The effect of polymer grafting on the phase behavior of bilayers made up of single-tail lipids is investigated using dissipative particle dynamics. The bilayer is maintained in a tensionless state using a barostat. Simulations are carried Out by varying the grafting fraction, G(f), defined as the ratio of the number of polymer molecules to the number of lipid molecules, and the length of the lipid tails. At low G(f), the bilayer shows I sharp transition from the gel (L-beta) to the liquid-crystalline (L-alpha) phase. This main melting transition temperature is lowered as G(f) is increased, and above a critical value of G(f), the interdigitated L-beta I phase is observed prior to the main transition. The temperature range over which the intermediate phases are observed is a function of the lipid tail length and G(f). At higher grafting fractions, the presence of the L-beta I, phase is attributed to the increase in the area per head group due to the lateral pressure exerted by the polymer brush. The areal expansion and decrease in the melting temperatures as a function of G(f) were found to follow the scalings predicted by the self-consistent mean field theories for grafted polymer membranes. Our study shows that the grafted polymer density can be used to effectively control the temperature range and occurrence of a given bilayer phase.

Low-temperature Er3+ emission in Ge-S-Ga glasses excited by host absorption

The photoluminescence (PL) of a series of (GeS2)(80)(Ga2S3)(20) glasses doped with different amounts of Er (0.17, 0.35, 0.52, 1.05 and 1.39 at.%) at 77 and 4.2 K has been studied. The influence of the temperature on the emission cross-section of the PL bands at -> 1540, 980 and 820 nm under host excitation has been defined. A quenching effect of the host photoluminescence has been established from the compositional dependence of the PL intensity. It has been found that the present Er3+-doped Ge-S-Ga glasses posses PL lifetime values about 3.25 ms. (C) 2007 Elsevier B.V. All rights reserved.

Temperature monitoring of nonanaesthetised patients in a cardiac catheterisation laboratory

Aim and objectives To identify the prevalence that temperature reduced by more than 1°C from pre to post-procedure in a sample of non-anaesthetised patients undergoing procedures in a cardiac catheterisation laboratory. Background Advances in medical technology are minimising the invasiveness of diagnostic tests and treatments for disease, which is correspondingly increasing the number of medical procedures performed without sedation or anaesthesia. Procedural areas in which medical procedures are performed without anaesthesia are typically kept at a cool temperature for staff comfort. As such, there is a need to inform nursing practices in regard to the thermal management of non-anaesthetised patients undergoing procedures in surgical or procedural environments. Design Single-site observational study Methods Patients were included if they had undergone an elective procedure without sedation or anaesthesia in a cardiac catheterisation laboratory. Ambient room temperature was maintained between 18°C and 20°C. Passive warming with heated cotton blankets was applied. Nurses measured body temperature and thermal comfort before and after 342 procedures. Results Mean change in temperature was -0.08°C (Standard deviation 0.43). The reduction in temperature was more than 1°C after 11 procedures (3.2%). One patient whose temperature had reduced more than 1°C after their procedure reported thermal discomfort. A total of 12 patients were observed to be shivering post-procedure (3.6%). No demographic or clinical characteristics were associated with reduction in temperature of more than 1°C from pre to post-procedure. Conclusions Significant reduction in body temperature was rare in our sample of non-anaesthetised patients. Relevance to clinical practice Similar results would likely be found in other procedural contexts during procedures conducted in settings with comparable room temperatures where passive warming can also be applied with limited skin exposure.

Temperature-dependent infrared reflectivity studies of multiferroic TbMnO3: Evidence for spin-phonon coupling

We have measured near normal incidence far-infrared (FIR) reflectivity spectra of a single crystal of TbMnO3 from 10 K to 300 K in the spectral range of 50 cm(-1)-700 cm(-1). Fifteen transverse optic (TO) and longitudinal optic (LO) modes are identified in the imaginary part of the dielectric function epsilon(2)(omega) and energy loss function Im(-1/epsilon(omega)), respectively. Some of the observed phonon modes show anomalous softening below the magnetic transition temperature T-N (similar to 46 K). We attribute this anomalous softening to the spin-phonon coupling caused by phonon modulation of the superexchange integral between the Mn3+ spins. The effective charge of oxygen (Z(O)) calculated using the measured LO-TO splitting increases below TN.

Possible high-temperature superconducting state with a d plus id pairing symmetry in doped graphene

Motivated by a suggestion in our earlier work [G. Baskaran, Phys. Rev. B 65, 212505 (2002)], we study electron correlation driven superconductivity in doped graphene where on-site correlations are believed to be of intermediate strength. Using an extensive variational Monte Carlo study of the repulsive Hubbard model and a correlated ground state wave function, we show that doped graphene supports a superconducting ground state with a d+id pairing symmetry. We estimate superconductivity reaching room temperatures at an optimal doping of about 15%-20%. Our work suggests that correlations can stabilize superconductivity even in systems with intermediate coupling.

Highly biocompatible and water-dispersible, amine functionalized magnetite nanoparticles, prepared by a low temperature, air-assisted polyol process: a new platform for bio-separation and diagnostics

A low temperature polyol process, based on glycolaldehyde mediated partial reduction of FeCl3 center dot 6H(2)O at 120 degrees C in the presence of sodium acetate as an alkali source and 2,2'-(ethylenedioxy)-bis-(ethylamine) as an electrostatic stabilizer has been used for the gram-scale preparation of biocompatible, water-dispersible, amine functionalized magnetite nanoparticles (MNPs) with an average diameter of 6 +/- 0.75 nm. With a reasonably high magnetization (37.8 e.m.u.) and amine groups on the outer surface of the nanoparticles, we demonstrated the magnetic separation and concentration implications of these ultrasmall particles in immunoassay. MRI studies indicated that these nanoparticles had the desired relaxivity for T-2 contrast enhancement in vivo. In vitro biocompatibility, cell uptake and MR imaging studies established that these nanoparticles were safe in clinical dosages and by virtue of their ultrasmall sizes and positively charged surfaces could be easily internalized by cancer cells. All these positive attributes make these functional nanoparticles a promising platform for further in vitro and in vivo evaluations.

Gibbs Energy of Formation of MnO: Measurement and Assessment

Based on the measurements of Alcock and Zador, Grundy et al. estimated an uncertainty of the order of +/- 5 kJ mol(-1) for the standard Gibbs energy of formation of MnO in a recent assessment. Since the evaluation of thermodynamic data for the higher oxides Mn3O4, Mn2O3, and MnO2 depends on values for MnO, a redetermination of its Gibbs energy of formation was undertaken in the temperature range from 875 to 1300 K using a solid-state electrochemical cell incorporating yttria-doped thoria (YDT) as the solid electrolyte and Fe + Fe1-delta O as the reference electrode. The cell can be presented as Pt, Mn + MnO/YDT/Fe + Fe1+delta O, Pt Since the metals Fe and Mn undergo phase transitions in the temperature range of measurement, the reversible emf of the cell is represented by the three linear segments. Combining the emf with the oxygen potential for the reference electrode, the standard Gibbs energy of formation of MnO from alpha-Mn and gaseous diatomic oxygen in the temperature range from 875 to 980 K is obtained as: Delta G(f)(o)/Jmol(-1)(+/- 250) = -385624 + 73.071T From 980 to 1300 K the Gibbs energy of formation of MnO from beta-Mn and oxygen gas is given by: Delta G(f)(o)/Jmol(-1)(+/- 250) = -387850 + 75.36T The new data are in excellent agreement with the earlier measurements of Alcock and Zador. Grundy et al. incorrectly analyzed the data of Alcock and Zador showing relatively large difference (+/- 5 kJ mol(-1)) in Gibbs energies of MnO from their two cells with Fe + Fe1-delta O and Ni + NiO as reference electrodes. Thermodynamic data for MnO is reassessed in the light of the new measurements. A table of refined thermodynamic data for MnO from 298.15 to 2000 K is presented.