Synthesis, spectral and thermal studies on pyrazolate-bridged palladium(II) coordination polymers

Synthesis, spectroscopic characterization and thermal behavior of pyrazolate-bridged palladium complexes [Pd(mu-Pz)(2)](n) (1), [Pd(mu-mPz)(2)](n) (2), [Pd(mu-dmPz)(2)](n) (3), [Pd(mu-IPz)(2)](n) (4) {pyrazolate (Pz(-)), 4-methylpyrazolate (mPz(-)), 3,5-dimethylpyrazolate (dmPz(-)), 4-iodopyrazolate (IPz(-))} have been described in this work. The exobidentate coordination mode of pyrazolato ligands in 1-4 was inferred on basis of IR spectroscopic evidences. TG investigations indicated that the introduction of substituents at the 4 position in the pyrazolyl moiety into coordination polymers do not affect significantly their thermal stability, whereas at the 3 and 5 position reduced the stability of the main chain. Metal palladium was the final product of the thermal decompositions, which was identified by X-ray powder diffraction.

Study of the thermomechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work describes the preparation and characterization of composite materials obtained by the combination of natural rubber (NR) and carbon black (CB) in different percentages, aiming to improve their mechanical properties, processability, and electrical conductivity, aiming future applications as transducer in pressure sensors. The composites NR/CB were characterized through optical microscopy (OM), DC conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA), and stress-strain test. The electrical conductivity varied between 10(-9) and 10 S m(-1), depending on the percentage of CB in the composite. Furthermore, a linear (and reversible) dependence of the conductivity on the applied pressure between 0 and 1.6 MPa was observed for the sample with containing 80 wt % of NR and 20% of CB. (C) 2007 Wiley Periodicals, Inc.

Attainment of lead titanate - Through the thermal decomposition of coprecipitated 8-hydroxyquinolinate precursors

Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) Linder constant stirring at 3degreesC, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470degreesC, temperature lower than the tetragonal-cubic transition.

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

A PC compatible Brazilian software for obtaining thermal histories using apatite fission track analysis

In this work a software developed in the Instituto de Fisica Gleb Wataghin, IFGW, UNICAMP, Campinas, SP, Brazil for obtaining thermal histories using apatite fission track analysis is presented. This software works in Microsoft-Windows environment. It will be freely disposable in the web site of the Departamento de Raios Cosmicos, IFGW, UNICAMP. Thermal histories obtained through this software are compared with those deduced using Monte Trax the software compatible with Apple Macintosh developed by Gallagher. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Synthesis, characterization and thermal behaviour of solid state compounds of 4-methylbenzylidenepyruvate with lighter trivalent lanthanides

Solid state Ln-4-Me-BP compounds, where Ln stands for lighter trivalent lanthanides (lanthanum to europium) and 4-Me-BP is 4-methylbenzylidenepyruvate, have been synthesized. Elemental analysis, complexometry, X-ray powder diffractometry, infrared spectroscopy and simultaneous thermogravimetry-differential thermal analysis (TG-DTA), have been used to characterize and to study the thermal behaviour of these compounds. The results provided information concerning the stoichiometry, crystallinity, thermal stability and thermal decomposition. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Effective thermal conductivity of beans via a steady-state method

Steady-state concentric cylinder equipment was used to determine the effective thermal conductivity of beans (Phaseolus vulgaris). The measuring cell had no heated end guards and its length to diameter ratio was 10.5. Glass beads were employed to assess the accuracy and repeatability of the experimental system under heat transfer conditions. The results agree well with those reported in the literature so that the system can be considered reliable. Corn was used to verify the system's accuracy under heat and mass transfer conditions. Again the results were satisfactory. Moisture migration was observed and measured during the tests with beans, but this behavior does not compromise thermal conductivity values if both thermal and mass transfer steady-states are correctly interpreted. The effective thermal conductivity increases linearly with increasing grain moisture content. Statistical regression leads to good estimates of the fitted parameters.

Processing and properties of Ag/BSCCO PIT tapes containing different proportions of silver metal powder

Monofilamentary tapes (150 pm thickness) were prepared by swaging and rolling silver tubes containing the Bi:2212 ceramic (granulation below 20 mum) and the silver powder (about 0.8 mum). The study has been made, among other samples, on tapes with nominal proportions of 0, 10 and 20 wt.% of silver. The samples were characterized by SEM, and by electrical measurements under varying applied magnetic field. The measurements of J(c) showed that the addition of 10 wt.% silver powder is very beneficent to this property, doubling the obtained values at 60 K, while the 20 wt.% tape presented very low J(c). The tape with no silver content showed to have a J(c) as high as 2.2 x 10(5) A/cm(2), at 4.2 K, zero applied magnetic field. (C) 2004 Elsevier B.V. All rights reserved.

Thermal decomposition of crystalline Ni-II-Cr-III layered double hydroxide: A structural study of the segregation process

A structural study of the thermal evolution of Ni0.69Cr0.31(OH)(2)(CO3)(0.155)(.)nH(2)O into NiO and tetragonal NiCr2O4 is reported. The characteristic structural parameters of the two coexisting crystalline phases, as well as their relative abundance, were determined by Rietveld refinement of powder x-ray diffraction (PXRD) patterns. The results of the simulations allowed us to elucidate the mechanism of the demixing process of the oxides. It is demonstrated that nucleation of a metastable nickel chromite within the common oxygen framework of the parent Cr-III-doped bunsenite is the initial step of the cationic redistribution. The role that trivalent cations play in the segregation of crystalline spinels is also discussed.

Thermal study of cyclopalladated complexes of the type [Pd-2(dmba)(2)X-2(bpe)] - (X=NO3-, Cl-, N-3(-), NCO-, NCS-; bpe=trans-1,2-bis(4-pyridyl)ethylene)

The synthesis, characterization and thermal analysis of the novel cyclometallated compounds [Pd-2(dmba)(2)Cl-2(mu-bpe)] (1), [Pd-2(dmba)(2)(N-3)(2)(mu-bpe)] (2), [Pd-2(dmba)(2)(NCO)(2)(mu-bpe)] (3), [Pd-2(dmba)(2)(SCN)(2)(mu-bpe)] (4), [Pd-2(dmba)(2)(NO3)(2)(mu-bpe)] (5) (bpe=trans-1,2-bis(4-pyridyl)ethylene; dmba=N,N-dimethylbenzylamine) are described. The thermal stability of [Pd-2(dmba)(2)X-2(mu-bpe)] complexes varies in the sequence 1 > 4 > 3 > 2 > 5. The final residues of the thermal decompositions were characterized as metallic palladium by X-ray powder diffraction.

Synthesis and structural investigations on TeO2-PbF2-CdF2 glasses and transparent glass-ceramics

New glasses have been prepared in the oxifluoride mixed system TeO2-PbF2-CdF2. Starting from pure TeO2 the addition of the fluorides leads to a decrease in the glasses characteristic temperatures. Also from Raman scattering results a structural evolution was observed where the number of structural units described as [TeO3] trigonal pyramids and [TeO3+1] polyhedra increases at the expense of the [TeO4] trigonal bipyramids supposed to exist in the TeO2, rich samples. Transparent glass ceramics were obtained from the glass with composition 80TeO(2)-10PbF(2)-10CdF(2), (mol%) with the PbTe3O7 crystalline phase being identified by X-ray diffraction and EXAFS measurements performed at the Te K, Cd K and Pb L-III edges. Also from Exafs measurements it is proposed that cadmium ions are preferentially surrounded by oxygen atoms although they were in a fluoride anion environment in the starting material. (C) 2002 Published by Elsevier B.V. Ltd.

Solid-state compounds of 4-methoxybenzylidenepyruvate and cinnamylidenepyruvates with thorium (IV) - Preparation and thermal studies

By close control of experimental variables affecting precipitation, solid-state compounds of the type Th(OH)(m)L4-m.nH(2)O, where L stands for 4-methoxy-benzylidenepyruvate, cinnamylidenepyruvate or 4-dimethylaminocinnamylidene-pyruvate; m=0 to 3 and n=0.5-3 were isolated. Chemical analysis, TG, DTG, DSC and X-ray powder diffractometry have been employed to characterize and to study the thermal behavior of these compounds in dynamic air atmosphere. In all cases, hydration water is slowly lost between 30 and 160degreesC; a continuous, slow rate, mass loss is observed thereafter and beyond 280-400degreesC the rate of decomposition/oxidation increased rapidly, to give ThO2 as the final product, beginning at 412-510degreesC. The results associated with the hydroxo-compounds indicate that the loss of constitution water (OH ions) and the decomposition / oxidation of the organic moieties occur as simultaneous process.

Red, green, and blue upconversion luminescence in ytterbium-sensitized praseodymium-doped lead-cadmium-germanate glass

Blue, green, red, and near-infrared upconversion luminescence in the wavelength region of 480-740 nm in Pr3+/Yb3+-codoped lead-cadmium-germanate glass under 980 nm diode laser excitation, is presented. Upconversion emission peaks around 485, 530, 610, 645, and 725 nm which were ascribed to the P-3(0)-H-3(J) (J = 4, 5, and 6), and P-3(0)-F-3(J) (J = 2, 3, and 4), transitions, respectively, were observed. The population of the praseodymium upper P-3(0) emitting level was accomplished through a combination of ground-state absorption of Yb3+ ions at the F-2(7/2), energy-transfer Yb3+(2F(5/2))-Pr3+(H-3(4)), and excited-state absorption of Pr3+ ions provoking the (1)G(4)-P-3(0) transition. The dependence of the upconversion luminescence upon the Yb3+-concentration and diode laser power, is also examined, in order to subsidize the proposed upconversion excitation mechanism. (C) 2004 Elsevier B,V. All rights reserved.

Composites PVDF-TrFE/BT used as bioactive membranes for enhancing bone regeneration

In this paper a piezoelectric composite membranes were developed for charge generator to promoter bone regeneration on defects sites. Is known that the osteogenesis process is induced by interactions between biological mechanisms and electrical phenomena. The membranes were prepared by mixing Barium Titanate (BT) powders and PVDF-TrFE (PVDF:TrFE = 60:40 mol%) on dimethylformamide medium. This precursor solution was dried and crystallized at 100degreesC for 12 hours. Composites membranes were obtained by following methods: solvent casting (SC), spincoating (SP), solvent extraction by water addition (WS) and hot pressing (HP).The microstructural analysis performed by SEM showed connectivity type 3-0 and 3-1 with high homogeneity for samples of ceramic volume fraction major than 0.50. Powder agglomerates within the polymer matrix was evidenced were observed for composites with the BT volume fraction major than 40%. The composite of ceramic fraction of 0.55 presented the best values of remanent polarization (similar to33 muC/cm(2)), but the flexibility of these composites with the larger ceramic fraction was significantly affected.For in vivo evaluation PVDF-TrFE/BT 90/10 membranes with 3cm larger were longitudinally implanted under tibiae of male rabbit. After 21 days the animals were sacrificed. By histological analyses were observed neo formed bone with a high mitotic activity. In the interface bone-membrane was evidenced a pronounced callus formation. These results encourage further applications of these membranes in bone-repair process.