Mechanochemical synthesis of lead magnesium niobate ceramics in iron media

The possibility of mechanochemical synthesis of the lead magnesium niobate (PMN) powders of the composition Pb(Mg(1/3)Nb(2/3))O(3) in iron vials was investigated. According to X-ray and energy-dispersive spectroscopy (EDS) analysis of the obtained powder mixtures, milling in iron vials resulted in incorporation of Fe and formation of PFN of composition Pb(Fe(1/2)Nb(1/2))O(3) simultaneously with formation of PMN. Relative amounts of PMN and PFN were determined based on values of Curie temperature and lattice constant of perovskite phase. Although only 1 wt pct of Fe was incorporated, a stoichiometry of the system was significantly changed, resulting in formation of pyrochlore phase and excess MgO. Single-phase perovskite was obtained when the excess of PbO and Nb(2)O(5) was added during mechanochemical synthesis. Because the dielectric properties were worse than expected, the alternative ways for improvement of dielectric properties were tried and discussed.

New chelate complexes of trivalent Y and lanthanides (Eu, Ho, Yb) with a triazene N-oxide: Synthesis, structural characterization and luminescence properties

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

On the stability of the extracellular hemoglobin of Glossoscolex paulistus, in two iron oxidation states, in the presence of urea

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mössbauer spectroscopic study of the early crystallization stage of iron(III) hydroxide particles

Mössbauer spectroscopy was used to investigate the early aging stage of iron(III) hydroxide sols prepared by oxidation of Fe(CO)5 in ethanolic solution, followed by vacuum drying at room temperature. One sample was composed of amorphous particles, while two other samples were partially crystallized, either as a result of solvent change or of spontaneous aging. The main results of Mössbauer measurements in the 80-320 K temperature range are: (a) partially crystallized particles exhibit a strong, S-shaped temperature dependence of the quadrupole splitting, in contrast to a weak and linear variation for amorphous particles; (b) the recoilless fraction temperature dependence is affected by vibration of the particles as a whole, with an effective force constant which is smaller for crystallized particles than for amorphous ones. Furthermore, the former exhibit anf-factor discontinuity near 0°C, which is attributed to melting of a surface layer built up during the crystallization process. © 1986.

The determination of iron, lead, copper and zinc in the hair of children between 22 and 85 months old

In this study the levels of Cu, Fe, Pb and Zn, determined in hair of healthy children (25-85 months), living at Araraquara (São Paulo, Brasil) are reported. Analytical determinations were carried out by using atomic absorption spectrometry employing an air acetylene flame. The results obtained are discussed with regard to effect of sex and age, as well compared with others analogous studies.

Gold-bearing iron duricrust in Central Brazil

In the Cuiabá region-State of Mato Grosso, Central Brazil-primary gold mineralization is hosted by two generations of quartz veins in Precambrian metamorphic terrains of the Cuiabá Group. Gold is mined from the veins and mainly from the eluvial horizons that cover the deeply altered basement. In the lodes gold occurs as small particles (less than 1 mm) associated with pyrite and contains up to 5% Ag. Larger particles and nuggets of almost pure gold are found in the iron duricrust which caps the upper levels of the weathering profile. It is difficult to determine the average grade of this kind of deposit but some prospects in the Cuiabá region produce up to 2 g gold per ton of ore. Lateritization is responsible for both the formation of the iron crust and the concentration of gold within the regolith. Under a tropical climate, the supergene alteration of phyllites of the Cuiabá Group has led to the formation of a weathering profile consisting typically of saprolite, mottled clay zone and duricrust, from bottom to top. The duricrust is directly derived form the in situ weathering of phyllites. Geochemical balance calculations indicate that in the transition from the saprolite to the duricrust lateritization has promoted a progressive loss of Si, Al and K, and more than 500% of absolute Fe enrichment. Gold underwent a supergene evolution related to the development of the weathering profile. In the saprolite and mottled clay zone, associated with quartz and oxidized sulfides, gold dissolves as demonstrated by corrosion features at the surface of the particles. The formation of secondary gold in the duricrust is indicated by the larger size of the nuggets, their higher fineness and the close relationship between gold and the neoformed iron oxy-hydroxides. © 1991.

Fortificação do leite fluido na prevenção e tratamento da anemia carencial ferropriva em crianças menores de 4 anos

The effectiveness of the use of chelate aminoacid iron fortified fluid milk in the treatment of iron deficiency in children under four years of age was studied. The 269 children included in this trial received 1 liter/day of fluid milk fortified with 3 mg of chelate aminoacid iron and were evaluated at six monthly intervals. At the beginning of the study 62.3% of the children presented anemia. After 6 months, this percentage had decreased to 41.8% and at the end of one year to 26.4%. The greatest decreases occurred in the groups comprising the subjects who were of 12 to 23 months of age and those under one year of age. Among the children who presented initial hemoglobin levels under 9.5 g/ dl, 59.3% were free of anemia after one year of follow-up. Of those presenting initial hemoglobin levels between 9.5 and 10.9 g/dl, 66.7% recovered from their anemia. There was also greater hematological improvement in the children that ingested over 750 ml/day of fortified milk in those families that did not share the supply of supplement among their other members and in those families that had only one child under five years of age. These findings led to the conclusion that the fortification of fluid milk is a viable and effective method for the treatment of iron deficiency in pre-school children.

Electrolytic treatment of wastewater from a fowl slaughterhouse using cast-iron electrodes

A viability study of an electrolytic process for the transformation of organic matter and free sulphide contained in wastewater from a fowl slaughterhouse in order to minimise odours was carried out Cast iron and aluminium electrodes were tried at 7.09 mA/cm2, under strong agitation, at 297 K. Conductivity, pH, chemical oxygen demand (COD), amount of settleable solids, and sulphide content were monitored with electrolysis duration. The cast iron electrodes were found to be viable for the elimination of soluble sulphides in the wastewater, leading to the elimination of its strong odour after short times of electrolysis. A significant decrease in COD was also attained.

Formation of colloidal particles of hydrous iron oxide by forced hydrolysis

The mechanism of formation and growth of hydrous iron oxide (FeOOH) during the initial stages of forced hydrolyses of ferric chloride aqueous solution was studied by small angle X-ray scattering (SAXS). The effect of the hydrolysis temperature (60°C, 70°C and 80°C) and of the addition of urea on the formation of colloidal particles under isothermal conditions were investigated. Based on the experimental scattering functions in the Guinier range, we suggest the presence of elongated colloidal particles. The particle diameter and length, and their variation with time, were determined by fitting the form factor of prolate ellipsoids to the experimental scattering functions. We have assumed that our solutions are in a dilute state and that all colloidal particles are approximately of the same size. The colloidal particles have geometrical shapes similar to those of the subcrystals that build up the superstructure of β-FeOOH crystals, indicating that the formation of this hydrous iron oxide is governed by an aggregation process. Otherwise, the addition of urea hinders the growth and yields smaller particles, with a reduction in size greater than 50%. © 2000 Elsevier Science B.V. All rights reserved.

Protected magnetic particles: Silica on yttrium iron garnet

The formation of silica on core yttrium iron garnet presents a variety of different applications as corrosion resistance and stabilization of magnetic properties. Well-defined magnetic particles were prepared by heterocoagulating silica on yttrium iron garnet to protect the core. Yttrium iron garnet was obtained using a homogeneous nucleation process by controlling the chemical routes from cation hydrolysis in acid medium. The heterocoagulation was induced by tetraethyl orthosilicate hydrolysis in appropriate yttrium iron garnet dispersion medium. The presence of silica on yttrium iron garnet was characterized by vibrating sample magnetometry, X-ray photoemission spectroscopy, transmission electron microscopy, small area electron diffraction and differential thermal analysis. © 2001 Elsevier Science B.V. All rights reserved.

Magnetic properties of spindle-type iron fine particles obtained from hematite

Spindle-type iron fine particles have been prepared by reduction of silica-coated-hematite particles. Hydrogen reduction of the coated-hematite cores yielded uniform spindle-type iron particles, which were stabilized by surface oxidation. Narrow particle distributions are observed from TEM measurements. X-ray, Mössbauer and magnetization data are in agreement with the presence of nanosized α-Fe particles, having surface layer of spinel structure oxide. Mössbauer spectra show that the oxide surface is superparamagnetic at room temperature. © 2001 Elsevier Science B.V. All rights reserved.

Preparation and characterization of spherical yttrium iron garnet via coprecipitation

The purpose of this work is to obtain spherical particles yttrium iron garnet (YIG) by coprecipitation technique. The spherical particles were obtained from either nitrate or chloride salt solutions by controlling the precipitation medium. Different agents of dispersion such as PVP and ammonium iron sulfate were used to optimize the shape and size of YIG. Samples were characterized by X-ray diffraction, scanning electron microscopy and vibrating sample magnetometry. The results show that the samples phase transition takes place at 850°C (orthorhombic phase) and at 1200°C (cubic phase). Spherical shape particles, with diameter of around 0.5 μm, present magnetization values close to the bulk value (26 emu g -1). © 2001 Elsevier Science B.V. All rights reserved.

Yttrium iron garnet heterocoagulated by silica

Coated purpose of homogeneous distribution as a second phase is introduced in magnetic systems. Yttrium iron garnet (YIG) shows special interest as magnetic dye, microwave absorber, and magnetic fluids when heterocoagulated by other material. Surface and interface magnetic properties are intimately connected with the new properties of the silica on YIG system. Néel first introduced the concept of surface anisotropy, and Chen et al. developed a model that describes the anisotropy effects at the boundary surface particle, which was applied in this work. Spherical YIG particles were prepared by coprecipitation method and coated with silica using the tetraethylorthosilicate (TEOS) hydrolysis process. The silica-YIG boundary was investigated by transmission electron microscopy. Hysteresis loops comparatively show the profile of the naked and silica-covered YIG particles. The surface anisotropies were calculated using the Chen et al. approach. Indeed, in heterocoagulation systems, the surface anisotropy is a result of the interface symmetry breaking, as observed.