A comparison of photoluminescence properties of InGaAs GaAs quantum dots with a single quantum well

Variable temperature photoluminescence (PL) measurements for In0.3Ga0.7As(6 nm)/GaAs(34 nm) quantum dot superlattices with a period of 20 and an In0.3Ga0.7As(6 nm)/GaAs(34 nm) reference single quantum well have been conducted. It is found that the temperature dependence is different between the quantum dots and the reference single quantum well. The PL peak energy of the single quantum well decreases faster than that of the quantum dots with increasing temperature. The PL peak energy for the InGaAs/GaAs quantum dots closely follows the InAs band gap in the temperature range from 11 to 170 K, while the PL peak energy for the InGaAs/GaAs quantum well closely follows the GaAs band gap. In comparison with InAs/GaAs quantum dots, the InGaAs/GaAs quantum dots are more typical as a zero-dimensional system since the unusual PL results, which appear in the former, are not obvious for the latter. (C) 1999 American Institute of Physics. [S0021-8979(99)08615-6].

AlGaInP visible quantum well lasers for information technology

650 nm-range AlGaInP multi-quantum well (MQW) laser diodes grown by low pressure metal organic chemical vapor deposition (LP-MOCVD) have been studied and the results are presented in this paper. Threshold current density of broad area contact laser diodes can be as low as 350 A/cm(2). Laser diodes with buried-ridge strip waveguide structures were made, threshold currents and differential efficiencies are (22-40) mA and (0.2-0.7) mW/mA, respectively. Typical output power for the laser diodes is 5 mW, maximum output power of 15 mW has been obtained. Their operation temperature can be up to 90 degrees C under power of 5 mW. After operating under 90 degrees C and 5 mW for 72 hrs, the average increments for the threshold currents of the lasers at 25 degrees C and the operation currents at 5 mW (at 25 degrees C) are (2-3) mA and (3-5) mA, respectively. Reliability tests showed that no obvious degradation was observed after 1400 hours of CW operation under 50 degrees C and 2.5 mW.

Red luminescence from self-assembled InAlAs AlGaAs quantum dots with bimodal size distribution

Red-emitting at about 640 nm from self-assembled In0.55Al0.45As/Al0.5Ga0.5As quantum dots grown on GaAs substrate by molecular beam epitaxy are demonstrated, A double-peak structure of photoluminescence (PL) spectra from quantum dots was observed, and a bimodal distribution of dot sizes was also confirmed by an atomic force micrograph (AFM) image for uncapped sample. From the temperature and excitation intensity dependence of PL spectra, it is found that the double-peak structure of PL spectra from quantum dots is strongly correlated to the two predominant quantum dot families. Taking into account the quantum-size effect on the peak energy, it is proposed that the high (low) energy peak results from a smaller (larger) dot family, and this result is identical to the statistical distribution of dot lateral size from the AFM image.

Wavelength tuning in GaAsAlGaAs quantum wells by InAs submonolayer insertion

Wavelength tuning of exciton emissions has been achieved simply by inserting an InAs submonolayer at the centre of GaAs quantum wells during molecular beam epitaxy growth. Photoluminescence measurements show that the emission energy can be effectively tuned from the quantum-well-determined energy down to less than the band gap of GaAs, depending on the well width as well as the InAs layer thickness. Using the effective-mass approximation, the tuning effect can be well predicted theoretically The results reported here may provide an alternative way to tune the wavelength in optoelectronic devices.

Intraband absorption in the 8-12 mu m band from Si-doped vertically aligned InGaAs/GaAs quantum-dot superlattice

Normal-incident infrared absorption in the 8-12-mu m-atmospheric spectral window in the InGaAs/GaAs quantum-dot superlattice is observed. Using cross-sectional transmission electron microscopy, we find that the InGaAs quantum dots are perfectly vertically aligned in the growth direction (100). Under the normal incident radiation, a distinct absorption peaked at 9.9 mu m is observed. This work indicates the potential of this quantum-dot superlattice structure for use as normal-incident infrared imaging focal arrays application without fabricating grating structures. (C) 1998 American Institute of Physics. [S0003-6951(98)01151-6].

Lateral ordered InGaAs self-organized quantum dots grown on (311) GaAs by conventional molecular beam epitaxy

Self-assembled InxGa1-xAs quantum dots (QDs) on (311) and (100) GaAs surfaces have been grown by conventional solid source molecular beam epitaxy. Spontaneously ordering alignment of InxGa1-xAs QDs with lower In content around 0.3 has been observed on As-terminated (B type) surfaces. The direction of alignment orientation of the QDs formation differs from the direction of misorientation of the (311) B surface, and is strongly dependent upon the In content x. The ordering alignment becomes significantly deteriorated as the In content is increased to above 0.5 or as the QDs are formed on (100) and (311) Ga-terminated (A type) substrates.

Buried heterostructure InGaAsP/InP strain-compensated multiple quantum well laser with a native-oxidized InAlAs current blocking layer

An InAlAs native oxide is used to replace the p-n reverse-biased junction in a conventional buried heterostructure InP-based laser. This technique reduces the number of regrowth steps and eliminates leakage current under high-temperature operation. The InAlAs native oxide buried heterostructure (NOBH) laser with strain-compensated InGaAsP/InP multiple quantum well active layers has a threshold current of 5.6 mA, a slope efficiency of 0.23 mW/mA, and a linear power up to 22.5 mW with a HR-coated facet. It exhibits single transverse mode with lasing wavelength at 1.532 mu m. A characteristic temperature (T-0) of 50 K is obtained from the NOBH laser with a nonoptimized oxide layer width. (C) 1998 American Institute of Physics. [S0003-6951(98)01352-7].

Metamorphosis of self-organized quantum dots into quantum wires

Spontaneous formation of InAs quantum wires in InAlAs on InP(001) via sequential chain-like coalescence of quantum dots along [1 (1) over bar 0] is realized. Theoretical calculations based on the energetics of interacting steps provide a qualitative explanation for the experimental results. Sequential coalescence of initially isolated dots reduces the total free energy strikingly. Thus the wire-like structure is energetically favorable. (C) 1998 Elsevier Science B.V.

Structure and photoluminescence of InGaAs self-assembled quantum dots grown on InP(001)

Molecular beam epitaxy has been used for growing InGaAs self-assembled quantum dots (QDs) in InAlAs on an InP(001) substrate. Nominal deposition of 9.6 monolayers of In0.9Ga0.1As results in QDs of similar to 6.5 nm high with an areal density of 3.3 X 10(11) cm(-2). Conspicuous bimodal size distribution is identified, and is responsible for the observed QDs photoluminescence (PL) emission with two peaks at 0.627 and 0.657 eV. Good agreement is achieved between the observed PL peak energies and calculated results. (C) 1999 American Institute of Physics. [S00218979(99)00101-2].

Effects of annealing on self-organized InAs quantum islands on GaAs (100)

Self-organized InAs islands on (001) GaAs grown by molecular beam epitaxy were annealed and characterized with photoluminescence (PL) and transmission electron microscopy (TEM). The PL spectra from the InAs islands demonstrated that annealing resulted in a blueshift in peak energy, a reduction in intensity, and a narrower linewidth in the PL peak. In addition, the TEM analysis revealed the relaxation of strain in some InAs islands with the introduction of the network of 90 degrees dislocations. The correlation between the changes in the PL spectra and the relaxation of strain in InAs islands was discussed. (C) 1998 American Institute of Physics. [S0003-6951(98)01850-6].

Photovoltage and photoreflectance spectroscopy of InAs/GaAs self-organized quantum dots

We present a detailed study of the interband excitonic transitions of InAs/GaAs self-organized quantum dots (QDs) based on photovoltage (PV) photoreflectance (PR) and photoluminescence (PL) spectroscopy. At room temperature, the interband absorption transitions of QDs have been observed by using PV spectrum, which clearly exhibits four well-resolved excitonic absorption peaks. The absorption line shape is Gaussian-like. Furthermore, the corresponding excitonic transitions are also observed in PR experiment at 77 K. The first derivative of a Gaussian profile can fit the experimental data well. (C) 1998 American Institute of Physics. [S0003-6951(98)00743-8]

Electronic structures of cubic lattice quantum dots

In this article, we give the electronic structure and optical transition matrix elements of coupled quantum dots (QDs) arranged as different cubic lattices: simple cubic (sc), body-centered cubic (bcc), and face-centered cubic (fcc) superlattices. The results indicate that electron and hole energies of bcc, sc, and fcc superlattices are the lowest, the highest, and the middle, respectively, for the same subband under the same QD density or under the same superlattice constant. For a fixed QD density, the confinement effects in sc, fcc, and bcc superlattices are the strongest, the middle, and the weakest, respectively. There are only one, two, and four confined energy bands, with energies lower than the potential barrier for sc, bcc, and fcc QD superlattices, respectively. The results have great significance for researching and making semiconductor quantum dot devices. (C) 1998 American Institute of Physics. [S0021-8979(98)02119-7]

Normal-incidence intersubband (In, Ga)As/GaAs quantum dot infrared photodetectors

We report the device performance of normal-incidence (In, Ga)As/GaAs quantum dot intersubband infrared photodetectors. A primary intersubband transition peak is observed at the wavelength of 13 mu m (E-0 --> E-1) and a secondary peak at 11 mu m (E-0 --> E-2). The measured energy spacing in the conduction band of the quantum dots is in good agreement with low temperature photoluminescence measurement and calculations. A peak detectivity of 1 x 10(10) cm Hz(1/2)/W at 13 mu m was achieved at 40 K for these devices. (C) 1998 American Institute of Physics. [S0003-6951(98)01440-5].

Linewidth of the infrared absorption spectra due to bound-to-continuum transition in GaAs/AlxGa1-xAs multiple quantum well structures

We have observed an extremely narrow absorption spectrum due to bound-to-continuum transition in GaAs/AlxGa1-xAs multiple quantum wells (MQWs). Its linewidth is only about one tenth of the values reported previously. Our calculation indicates that the broadening of the excited state in the continuum has little contribution to the absorption linewidth. We have grown a sample whose MQW region contains two kinds of wells with a minor thickness inhomogeneity. Its resultant absorption linewidth is six times as large as that of homogeneous well sample, which is in good agreement with our theoretical analysis. Thus we can suggest that the wider absorption spectra reported by many authors may be due to the well width inhomogeneity. (C) 1998 American Institute of Physics. [S0003-6951(98)03430-5]

Photoluminescence investigation of GaInP/GaAs multiple quantum wells grown on (001) and (311) B GaAs surfaces by gas source molecular beam epitaxy

Photoluminescence (PL) investigation was carried out on GaInP/GaAs multiple quantum wells structures grown on (001) and (311) B surfaces of GaAs by gas source molecular beam epitaxy. Superlattice structures of GaAs/GaInP grown on (001) GaAs substrate were also studied in comparison. Deep-level luminescence was seen to dominate the PL spectra from the quantum wells and superlattice structures that were grown on (001) GaAs substrate. In contrast, superior optical properties were exhibited in the same structures grown on (311) B GaAs surfaces. The results suggested that GaAs/GaInP quantum well structures on (311) B oriented substrates could efficiently suppress the deep-level emissions, result in narrower PL peaks indicating smooth interfaces. (C) 1998 American Institute of Physics.