Síntese, caracterização de ferritas espinélio com propriedades magnéticas e absorvedoras de microondas

Were synthesized spinel-type ferrites with general formula Ni0,8Mg0.2-xMxFe2O4, where M represents the doping Mn, Co or Mn + Co simultaneously, x ranges for the values 0.02, 0.05 and 0.1. The value of x was divided by 2 in cases where M equals Mn and Co conjugates. We used the citrate precursor method and heat treatment to obtain the phases at 1100°C. The materials were characterized by XRD, TGA/ DTGA, SEM, MAV and reflectivity measurements by the method of waveguide. Powders to 350°C/3.5 h were crystalline and nanosized. According to the results this temperature all powders have a percentage of ferrite phase over 90%. The composition had the addition of Mn and Co simultaneously showed a higher percentage of secondary phase NiO, 5.8%. The TGA/DTGA curves indicate that this sample reached phase (s) crystalline (s) at lowest temperatures. The X-ray diffractograms of the samples calcined at 350°C and 1100°C were treated with the Rietveld refinament technique. The powders calcined at 1100 °C/3h in air show to be 100% except spinel phase composition with 0.02 doping. The micrographs show clusters of particles with sizes smaller than 1 μm in calcination temperature of 1100°C which agreed with the result of Rietveld refinement. In the compositions doped with Mn were higher values of magnetization (45.90 and 53.20 Am2/kg), which did not cause high microwave absorption. The theoretical calculation of magnetization (MT) was consistent with the results, considering that there was agreement between the increase of magnetization experimental and theoretical. It was observed that there was the interrelation of the final effect of absorption with the thickness of MARE, the composition of ferrimagnetic materials and in particular the specific values of frequency. The analysis shows that the reflectivity increases in the concentration of cobalt increased the frequency range and also for absorption 10.17 GHz and 84%, respectively. The best result of chemical homogeneity and the value of 2.96 x 10-2 tesla coercive field were crucial for high performance ferrite absorber with 0.1 cobalt. The Cobalt has high magnetocrystalline anisotropy, it is associated with an increased coercive field, Hc. Therefore, this property improves the results of reflectivity of spinel ferrites

Síntese e caracterização estrutural e magnética da ferrita de cálcio

The calcium ferrite (Ca2Fe2O5) has a perovskite-type structure with oxygen deficiency and is used as a chemical catalyst. With the advent of nanoscience and nanotechnology, methods of preparation, physical and chemical characterizations, and the technological applications of nanoparticles have attracted great scientific interest. Calcium nanostructured ferrites were produced via high-energy milling, with subsequent heat treatment. The milling products were characterized by X-ray diffraction, magnetization and Mössbauer spectroscopy. Samples of the type Ca2Fe2O5 were obtained from the CaCO3 and Fe2O3 powder precursors, which were mixed stoichiometrically and milled for 10h and thermally treated at 700ºC, 900ºC and 1100ºC. The Mössbauer spectra of the treated samples were adjusted three subespectros: calcium ferrite (octahedral and tetrahedral sites) and a paramagnetic component, related to very small particles of calcium ferrite, which are in a superparamagnetic state. For samples beats in an atmosphere of methyl alcohol, there is a significant increase in area associated with the paramagnetic component. Hysteresis curves obtained are characteristic of a weak ferromagnetic-like material

Síntese, sinterização e caracterização de ferrita de níquel

In this work we obtain nickel ferrite by the combustion synthesis method whcih involves synthesising in an oven at temperatures of 750oC, 950oC and 125oC. The precursors oxidizing used were nickel nitrate, ferric as an oxidizing and reducing urea (fuel). After obtaining the mixture, the product was deagglomerated and past through a 270 mesh sieve. To assess the structure, morphology, particle size, magnetic and electrical properties of nanoparticles obtained the samples were sintered and characterized by x-ray distraction (XRD), x-ray fluorescence spectroscopy (FRX); scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), vibrating sample magnetometer (MAV ) and electrical permittivity. The results indicated the majority of phase inverse spinel ferrite and Hematite secondary phase nickel and nickel oxide. Through the intensity of the distraction, the average size of the crystallization peaks were half-height width which was calculated using the Scherrer equation. From observing the peaks of all the reflections, it appears that samples are crystal clear with the formation of nanoparticles. Morphologically, the nanoferritas sintered nickel pellet formation was observed with three systems of particle size below 100mn, which favored the formation of soft pellets. The average size of the grains in their micrometric scale. FRX and EDS showed qualitatively the presence of iron elements nickel and oxygen, where through quantitative data we can observe the presence of the secondary phase. The magnetic properties and the saturation magnetization and the coercive field are in accordance with the nickel, ferrite where the curve of hysteresis has aspects of a soft material. Dielectric constant values are below 10 and low tangent loss

New Nanostructured Silica Adjuvant (SBA-15) Employed to Produce Antivenom in Young Sheep Using Crotalus durissus terrificus and Apis mellifera Venoms Detoxified by Cobalt-60

Equine antivenom is considered the only treatment for animal-generated envenomations, but it is costly. The study aimed to produce Apis mellifera (Africanized honeybee) and Crotalus durissus terrificus (C.d.t.) antivenoms using nanostructured silica (SBA-15) as adjuvant and cobalt-60 (60Co)-detoxified venoms utilizing young sheep. Natural and 60Co-irradiated venoms were employed in four different hyperimmunization protocols. Thus, 8 groups of 60- to 90-d-old sheep were hyperimmunized, enzyme-linked immunosorbent assay (ELISA) serum titers collected every 14 d were assessed clinically daily, and individual weight were measured, until d 84. Incomplete Freund's (IFA) and nanostructured silica (SBA15) adjuvants were compared. The lethal dose (LD50) for both venoms was determined following intraperitoneal (ip) administration to mice. High-performance liquid chromatography on reversed phase (HPLC-RP) was used also to measure the 60Co irradiation effects on Apis venom. At the end of the study, sheep were killed in a slaughterhouse. Kidneys were histologically analyzed. LD50 was 5.97 mg/kg Apis and 0.07 mg/kg C.d.t. for native compared to 13.44 mg/kg Apis and 0.35 mg/kg C.d.t. for irradiated venoms. HPLC revealed significant differences in chromatographic profiles between native and irradiated Apis venoms. Native venom plus IFA compared with SBA-15 showed significantly higher antibody titers for both venoms. Apis-irradiated venom plus IFA or SBA-15 displayed similar antibody titers but were significantly lower when compared with native venom plus IFA. Weight gain did not differ significantly among all groups. 60Co irradiation decreased toxicity and maintained venom immunogenic capacity, while IFA produced higher antibody titers. SBA-15 was able to act as an adjuvant without producing adverse effects. Hyperimmunization did not affect sheep weight gain, which would considerably reduce the cost of antiserum production, as these sheep were still approved for human consumption even after being subjected to hyperimmunization.

Silver nanoparticles: influence of stabilizing agent and diameter on antifungal activity against Candida albicans and Candida glabrata biofilms

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Silver colloidal nanoparticles: antifungal effect against adhered cells and biofilms of Candida albicans and Candida glabrata

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Silver Distribution and Release from an Antimicrobial Denture Base Resin Containing Silver Colloidal Nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Tissue Reaction to Silver Nanoparticles Dispersion as an Alternative Irrigating Solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of Candida albicans adhesion and biofilm formation on a denture base acrylic resin containing silver nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of silica-carbon mesoporous matrix with embedded nickel nanoparticles synthesized by the polymeric precursor method

Nickel nanoparticles into silica-carbon matrix composites were prepared by using the polymeric precursor method. The effects of the polyester type and the time of pyrolysis on the mesoporosity and nickel particle dispersion into non-aqueous amorphous silica-carbon matrix were investigated by thermogravimetric analysis, adsorption/desorption isotherms and TEM. A well-dispersed metallic phase could be only obtained by using ethylene glycol. Weightier polyesters affected the pyrolysis process due to a combination of more amounts of carbonaceous residues and delaying of pyrolysis process. The post-pyrolyzed composites were successfully cleaned at 200 degrees C for I h in oxygen atmosphere leading to an increase in the surface area and without the occurrence of carbon combustion or nickel nanoparticles oxidation. The matrix composites presented predominantly mesoporous with pore size well defined in 38 angstrom, mainly when tetraethylene glycol was used as polymerizing agent. (C) 2007 Elsevier B.V. All rights reserved.

Ultrastructural characterization of CD133(+) stem cells bound to superparamagnetic nanoparticles: possible biotechnological applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In vitro study of CD133 human stem cells labeled with superparamagnetic iron oxide nanoparticles

Superparamagnetic iron oxide nanoparticles (SPIONs) are applied in stem cell labeling because of their high magnetic susceptibility as compared with ordinary paramagnetic species, their low toxicity, and their ease of magnetic manipulation. The present work is the study of CD133(+) stem cell labeling by SPIONs coupled to a specific antibody (AC133), resulting in the antigenic labeling of the CD133+ stem cell, and a method was developed for the quantification of the SPION content per cell, necessary for molecular imaging optimization. Flow cytometry analysis established the efficiency of the selection process and helped determine that the CD133 cells selected by chromatographic affinity express the transmembrane glycoprotein CD133. The presence of antibodies coupled to the SPION, expressed in the cell membrane, was observed by transmission electron microscopy. Quantification of the SPION concentration in the marked cells using the ferromagnetic resonance technique resulted in a value of 1.70 x 10 (13) mol iron (9.5 pg) or 7.0 x 10 (6) nanoparticles per cell ( the measurement was carried out in a volume of 2 mu L containing about 6.16 x 10 5 pg iron, equivalent to 4.5 x 10 (11) SPIONs). (c) 2008 Elsevier B.V. All rights reserved.

A systematic study of transfection efficiency and cytotoxicity in HeLa cells using iron oxide nanoparticles prepared with organic and inorganic bases

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Physicochemical characterization of nanoparticles formed between DNA and phosphorylcholine substituted chitosans

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrofluid dynamic (EFD) energy conversion in gas flows with suspended nanoparticles

This work presents simulations of the Electrofluid Dynamic energy conversion process in slender channel devices having very small particles (in both micro and nano scales) as charge carriers. Solutions are discussed for a system composed by coupled differential equations, which includes the equation for the total current along the channel, the equations for total energy and momentum of the mixture (gas and solid particles), the continuity equation and the equations for energy and momentum of a single particle. Results for suspended particles of higher diameters have been previously published in the Literature, but the simulations here presented exhibit an appreciable increase in the values for output currents.