SrBi2Nb2O9 thin films deposited by dip coating using aqueous solution

A new approach for SrBi2Nb2O9 (SBN) thin films synthesis using aqueous solution was successfully experienced. The deposition solution was prepared from Sr-Bi-Nb mixed-citrate solution, requiring no special atmosphere and using common reagents. Films were deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates and hear treated at temperatures ranging from 300 to 700 degrees C. The process of formation and crystallization of SrBi2Nb2O9 thin films, prepared by the aqueous solution method have been studied with particular emphasis on the microstructure of crystallized films. Crystalline phases formation were followed by grazing incident X-ray diffraction (GIXRD), microstructure characterization was evaluated by scanning electron microscopy (SEM) and surface roughness were observed using atomic for ce microscopy (AFM). To reach the desired thickness, substrates were dipped in the deposition solution twice, forming double-layered films. The thickness of each layer ranged from 80 to 100 nm. (C) 1999 Elsevier B.V. Limited. All rights reserved.

Upconversion fluorescence spectroscopy of Er3+/Yb3+-doped heavy metal Bi2O3-Na2O-Nb2O5-GeO2 glass

Upconversion fluorescence emission of Er3+/Yb3+-doped Bi2O3-Na2O-Nb2O5-GeO2 heavy metal glass samples excited at 1.06 mu m is experimentally investigated. The results reveal the existence of intense emission bands centered around 520, 545, and 655 nm. The germano-niobate based host glass presents high transparency in the region of 400-2700 nm, the capability of incorporating high dopant concentrations, high melting temperature, and large resistance to atmospheric moisture. The observed intensity of the green fluorescence emission, suggested that the niobium based host glass material plays an important role in the efficiency of the upconversion process. Emission lines centered at 425, 483, 503, 608, and 628 nm were also observed. (C) 1997 American Institute of Physics.

Quantitative structural analysis of the transition from LT-LixCoO2 to HT-LixCoO2 using the rietveld method: correlation between structure and electrochemical performance

A quantitative phase analysis was made of LiXCoO2 powders obtained by two distinct chemical methodologies at different temperatures (from 400 to 700degreesC). A phase analysis was made using Rietveld refinements based on X-ray diffraction data, considering the LiXCoO2 powders as a multiphase system that simultaneously contained two main phases with distinct, layered and spinel-type structures. The sults showed the coexistence of both structures in LiXCoO2 obtained at low temperature (400 and 500degreesC), although only the layered structure was detected at higher temperatures (600 and 700degreesC, regardless of the chemical powder process employed. The electrochemical performance, evaluated mainly by the cycling reversibility of LiXCoO2 in the form of cathode insertion electrodes, revealed that there is a close correlation between structural features and the electrochemical response, with one of the redox processes (3.3 v/3.9 v) associated only with the presence of the spinel-type structure. (C) 2003 Elsevier B.V. All rights reserved.

Electrodeposited thin mercury films on Pt-Ir alloy electrodes

Mercury thin films prepared by electrochemical deposition on Pt-Ir alloy and after partial removing of mercury at different temperatures were studied by means of an interferometric surface mapping microscope and by X-ray photoelectronic spectroscopy. Mercury film samples having mercury partially removed by anodic stripping at a potential more positive than the corresponding peak in the voltammogram were also studied using the same techniques. For blank samples the surface topographic studies showed well defined grain boundaries. Mercury film samples when heated up to different temperatures showed as material is removed and that the surface roughness decreases as the temperature increases. For samples heated up to 800 degrees C the surface roughness is approximately the same that for the blank. A model for the interphase of volumetric mercury electrodeposited on a Pt-Ir alloy has been proposed using samples both electrochemically and thermally removed of their Hg coatings. The model includes a layered three-region structure, containing at least two Pt-Hg intermetallics: PtHg4 and PtHg2. A substrate modified region, iridium rich, has also been detected. (C) 1999 Elsevier B.V. S.A. All rights reserved.

An approach to analyzing synthesis, structure and properties of bismuth titanate ceramics

The family of bismuth titanate, Bi(4)Ti(3)O(12) (BIT) layered-structured ferroelectrics materials is attractive from the viewpoint of such as their application as electronic materials dielectrics, piezoelectrics and pyroelectrics, because they are characterized by good stability of piezoelectric properties, a high Curie temperature and a good resistance vs temperature. Bismuth titanate (Bi(4)Ti(3)O(12)) powders can be prepared using different methods, depending if the creation will be film coating or ceramics. The structure and properties of bismuth titanate materials show a significance dependence on the applied synthesis method. In this review paper, we made an attempt to give an approach to analyszing the structure, synthesis methods and properties of bismuth titanate ferroelectrics materials.

Dielectric properties of Na1-xLixNbO3 ceramics from powders obtained by chemical synthesis

Ultra-fine powders of Na1-xLixNbO3 (x=0; 0.06; 0.09; 0.12) were synthesized by the Polymeric Precursors Method. Such powders had their orthorhombic structures determined by X-ray diffraction and their surface area determined by BET isotherms (less than 10 m(2) g(-1)). Densification was followed by dilatometric study. The powders, calcined at 700 degrees C for 5 h, were sintered at 1290 degrees C during 2 h under ambient atmosphere with no application of extra pressure. The samples with relative densities higher than 95% were analyzed by impedance spectroscopy at room temperature, under a signal amplitude of 1 V-rms. Dielectric constants of about 180 and dielectric loss factor of about 0.03 were measured showing small dependence with frequency. The electrical properties were similar to those obtained for samples sintered by hot pressing. (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Photo-induced transformations in chalcogenide composite layers

Investigations of photo-induced structural transformations (PST) and related changes of optical parameters in the light-sensitive amorphous chalcogenides were extended to composite layers, which consist of a wide band-gap material and an active material, Se60Te40 with a smaller band gap. Photo-stimulated interdiffusion and/or crystallization in layered Se0.6Tc0.4/As0.6Se0.94 and Se0.6Te0.4/SiOx were investigated with respect to their dependence on the compositional modulation of the multilayer at scale-dimensions (similar to3-10nm). It was established that PST due to the interdiffusion and crystallization can be efficiently operated by the composition of the adjacent layers of the multilayer which results in the change of the transformation rate and of the optical relief type (positive or negative). The comparison with a single Se0.6Te0.4 layer and with the known data for amorphous-Se/As2S3 multilayers supports the advantages of composite layers for amplitude-phase optical recording. (C) 2004 Published by Elsevier B.V.

Ferroelectric state analysis in grain boundary of Na0.85Li0.15NbO3 ceramic

The electric and dielectric properties of the grain boundary of Na0.85Li0.15NbO3 lead-free ferroelectric-semiconductor perovskite were investigated. The impedance spectroscopy was carried out as a function of a thermal cycle. The sodium lithium niobate was synthesized by a chemical route based on the evaporation method. Dense ceramic, relative density of 97%, was prepared at 1423 K for 2 h in air atmosphere. ac measurements were carried out in the frequency range of 5 Hz-13 MHz and from 673 to 1023 K. Theoretical adjust of the impedance data was performed to deriving the electric parameters of the grain boundary. The electric conductivity follows the Arrhenius law, with activation energy values equal to 1.55 and 1.54 eV for heating and cooling cycle, respectively. The nonferroelectric state of the grain boundary and its correlation with symmetry are discussed in the temperature domain. (C) 2003 American Institute of Physics.

Growth and characterization of BaBi2Nb2O9 thin films made by RF-magnetron sputtering

The RF-magnetron sputtering technique has been used to deposit polycrystalline thin films of layered-structured ferroelectric BaBi2Nb2O9 (BBN). The XRD patterns for the films annealed at 700degreesC for 1 hour show the presence of the BBN phase as well as the BaNb2O6 secondary phase. A better crystallization of the BBN phase and an inhibition of the secondary phase is obtained with the increase of temperature. The surface of the prepared films was rather dense and smooth with no cracks. The 300 nm thick BBN thin films exhibited a room-temperature dielectric constant of about 779 with a dissipation factor of 0.09 at a frequency of 100 kHz.

Effect of oxygen atmosphere on the morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate (LiTaO3) thin films with (50:50) stoichiometry were prepared using polymeric organic solution. The 5-layered films were deposited on silicon (100) substrates by spin coating method. The coated substrates were thermally treated at 500degreesC for 3 h under several oxygen atmospheres in order to study the influence of oxygen flow on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction results showed that an oxygen flow of 100 cm(3)/min leads to LiTaO3 thin films with higher crystallinity, without preferential orientation. It was observed by scanning electron microscopy (SEM) that the thickness of thin films decreases when the oxygen flow increases. The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by oxygen flow.

Embryology and seed development of Syngonanthus caulescens (Poir.) Ruhland (Eriocaulaceae-Poales)

The embryology and the seed development of Syngonanthus caulescens are presented. This species possesses: a bithecous and tetrasporangiate anther, with a four-layered wall, a conspicuous endothecium of the baseplate type, a secretory tapetum formed by uninucleate cells, successive microsporogenesis resulting in isobilateral microspore tetrads, spiraperturate and binucleate pollen grains, an orthotropous, pendulous, bitegmic and terminucellate ovule, with a micropyle formed only by the inner integument, a megagametophyte of the Polygonum type, with formation of an antipodal cyst, free-nuclear and starchy endosperm, a broad and bell-shaped embryo, operculate and endotestal seeds, a seed coat derived from the inner layers of both integuments, and tanniniferous endotegmen. These embryological aspects are characteristic not only for Syngonanthus, but for the whole family, with few differences between genera. Furthermore, the pollen grain of the spiraperturate type and the cystic arrangement of the antipodals in the megagametophyte are peculiar and very distinctive features of Eriocaulaceae within the other Poales (commelinids). (c) 2006 Elsevier B.V. All rights reserved.

Ultrastructure and histochemistry of the mineral concretions in the midgut of bees (Hymenoptera: Apidae)

Mineral concretions in the digestive cells of bees were examined under transmission electron microscope and histochemically. Ultrastructure shows two types of mineral deposits: 1) mineral concretions which are organized in granules with a striking concentrically layered organization of opaque and clear zones and 2) electron dense granules which appear inside small vacuoles (0.4-0.7 mu m). These two structures are present in the apex of the digestive cells of the posterior midgut. Histochemical data reveal that mineral concretions are composed of calcium, iron and uric acid or its salts while calcium determination gives a positive reaction for electron dense granules. Morphological and chemical similarities between the mineral concretions of bees and those described for other insects suggest that they have an important physiological role regulating the composition of the internal environment and to avoid intoxication. Since concretions and granules are structurally distinct, it is suggested that they are functionally different.

Seeding of PMN powders made by the Pechini method

The partial oxalate method, with the columbite route, associated with the Pechini method, was used to obtain a very fine ceramic powder at low temperature. Using this route it was possible to obtain a very reactive powder and to synthesize a lead magnesium niobate (PMN) powder with up to 100% of perovskite phase at a lower temperatures than the PbO melting point. The influence of the BaTiO3 and PbTiO3 seeds in the phase formation, along with time and temperature during the PMN calcination, was also investigated. The amount of 2% of BaTiO3 seeds promoted PMN powder formation with 100% of perovskite phase and a very narrow particle size distribution. (C) 2001 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Structure and ontogeny of Swartzia langsdorffii (Leguminosae) pericarp

In order to elucidate the position of the Swartzieae in Leguminosae, Swartzia langsdorffii was chosen as a representative of this tribe type genus and subjected to structural studies of immature ovaries (in the floral bud and flowers) and developing and mature fruits. The external epidermis of the ovary is characterized by one layer of thin-walled polyhedral cells with a thin cuticle. Parenchyma cells have a large quantity of tannin-containing idioblasts located inside a procambial ring. The one-layered inner epidermis consists of flattened cells. In fruits the one-layered exocarp is covered by a thick cuticle. The mesocarp consists of three distinct regions, the middle region being a sclerenchymatous layer. The one-layered endocarp shows cells with little cohesion. The occurrence of canals consisting of a net of resinous cells was also observed in the mesocarp. Secretion was of an elaborate composition. Differentiation of the secretory structures begin in the floral bud ovary, where they appear as idioblasts containing tannin. The taxonomic position of this tribe, as well as the function of the mesocarp secreting canals, are discussed.

Comparative study of ovule and fruit development in species of Hypolytrum and Rhynchospora (Cyperaceae, Poales)

The development of the ovule and of the fruit of Hypolytrum bullatum and H. schraderianum (Mapanioideae) and of Rhynchospora consanguinea and R. rugosa (Cyperoideae) are described. All species share anatropous, bitegmic and crassinucellate ovules, funicular obturator, megagametophyte of the Polygonum type, presence of starch grains in the mature megagametophyte, free-nuclear endosperm, Onagrad-type embryogeny, testal-tegmic seed, and a simple fruit of the achene type. Rhynchospora species have characters typical of the family: micropyle formed by the inner integument alone; 3-4-layered parietal tissue; and hard achene. Hypolytrum species differ in those characters by presenting a slightly zigzag micropyle formed by both integuments connected with the funicular obturator, 5-8-layered parietal tissue, and fibrous-spongy achene. The peculiar formation of the micropyle in Hypolytrum is a feature reported here for the first time in the family. The ontogeny provides evidence for a better understanding of the dispersal unit in Hypolytrum supporting the classification as a true achene, like that of Rhynchospora, which is characteristic of the family.