The effect of mold temperature on castability of CPTi and Ti-6Al-4V castings into phosphate bonded investment materials

Objective. The aim of this study was to evaluate the castability of CP titanium and Ti-6Al-4V alloy castings into Rematitan Plus investment at three different mold temperatures.Methods. A nylon mesh pattern (20 mm with 64 squares and wire of 0.7 mm in diameter) was used for the castability testing. Initially, an image of the wax pattern was obtained by means of a digital camera and the total extension of filaments (mm) was then measured, using the Leica Qwin image analysis system. The mesh sprued was placed in the Rematitan Plus investment material and the castings were made in a Discovery Plasma machine at three different mold temperatures: 430 degrees C (control group), 480 degrees C or 530'C. Ten castings were made for each temperature. The images of the castings were analyzed (Leica Qwin) and the castability index determined by the number of the completely cast segments as a percentage of the wax pattern. Data were analyzed by two-way ANOVA and Tukey's multiple comparison test (a = 0.05) using materials and temperatures as discriminating variables.Results. The Ti-6Al-4V alloy (60.86%) presented a better castability index than CP Ti (48.44%) (p < 0.000001). For CP Ti, the temperature of 530 degrees C (23.96%) presented better castability than at other temperatures, 480 degrees C (14.66%) and 430 degrees C (12.54%), with no difference between them (p < 0.001). For Ti-6Al-4V alloy, there was a statistically significant difference among the three temperatures: 530 degrees C (28.36%) > 480 degrees C (19.66%) > 430 degrees C (15.97%) (p < 0.002).Significance. Within the limitations of this study, the increase in the mold temperature of the Rematitan Plus investment resulted in a better castability index for both materials, and Ti-6Al-4V presented a better castability index than CP Ti. (c) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Heating titanium structures is assumed to relieve tensions induced by the casting process as well as possibly optimizing some mechanical properties. The aim of this investigation was to evaluate the effect of thermal treatments on tensile strength of commercially pure titanium (CP Ti) and Ti-6Al-4V alloy. Thirty dumbbell rods, with diameters of 3.0 mm at the central segment and lengths of 42 mm, were cast for each metal using the Rematitan System. CP Ti and Ti-6Al-4V specimens were randomly divided into three groups of ten: a control group that received no thermal treatment and two test groups. One (T1) was heated at 750°C for 2 h and the other (T2) was annealed at 955°C for 1 h and aged at 620°C for 2 h. Tensile strength was measured with a universal testing machine (MTS model 810). Tensile strength means and standard deviations were statistically compared using a Kruskal-Wallis test at a α = 0.05 significance level. No statistically significant differences in tensile strength were observed among CP Ti groups. For the Ti-6Al-4V alloy, the control and T1 groups revealed statistically higher tensile strengths when compared to the T2 group, with no significant difference between the control and T1 groups. © 2005 Springer Science + Business Media, Inc.

Crystallographic structure of Ti-6Al-4V, Ti-HP and Ti-CP under high-pressure

The phase stability of a commercial purity (Ti-CP), high purity (Ti-HP) and Ti-6Al-4V alloy were investigated in a diamond anvil cell up to 32 GPa and 298 K using a polychromatic X-ray beam. The Ti-CP and Ti-HP shown the same HCP (c/a∼0.632) to Hexagonal (c/a∼1.63) non reversible martensitic transition at about 9 GPa. The as received Ti-6Al-4V shows a very low relative volume fraction β-Ti / α-Ti. No phase changes were observed in the Ti-6Al-4V alloy in the pressure range of this study. The α phase of the Ti-6Al-4V shows monotonic volume cell pressure dependence. This volume change is reversible and non-hysteretic. The cell of the a phase recovered its original volume when the pressure was released. © 2010 IOP Publishing Ltd.

Analysis on turning Ti-6Al-4V with different cooling methods

The aim of this paper is to optimize the machining of Ti-6Al-4V alloy, by studying the chip formation, roughness and tool wear for different cooling conditions. The results were compared between cooling methods, minimal quantity of fluid (MQF) and flooding, and also without fluid for the tool H13A. The turning of Ti-6Al-4V has shown good results on roughness (0, 8μm) and tool life, which was 11% lower with MQF than with the flooding method. The tool wear causes variation of the shear angle, which promotes strength hardening of the chip. As a result, the machined surface could be damaged. The use of the cutting fluid helps to save the cutting edge and could reduce the strength hardening. Nevertheless, it could also facilitate the formation of built-up edge. The nucleation of alpha lamellar colonies can occur due to a combination of deformation rates and temperature, mainly when the flooding is used, but it's not conclusive. The lamellar colonies were also found with the MQF in some regions, however, this structure did not show hardness variation compared to equiaxial. For all this reasons, the machining parameters might be carefully chosen.

Obtenção de fosfatos de cálcio pelo método biomimético sobre a superfície da liga Ti-6Al-4V modificada pelo laser Nd:YAG

In this work, surface modification of the Ti-6Al-4V alloy by irradiation with a Nd:YAG laser beam was studied. The matrix spacing was varied and the other parameters were kept constant. After theirradiation, the samples were immersed into SBF solution (Simulated Body Fluid) for 7 days at 37 ° C for nucleation and formation of calcium phosphates. After this period, the samples were subjected to a heat treatment at 600 °C. X-ray diffraction results indicated the formation of a mixture of phases containing hydroxyapatite and tricalcium phosphate. Infrared analysis demonstrated the presence of bands related to hydroxyapatite. SEM micrographs showed that different matrix spacing used leads to the formation of different morphologies.The 0.01 cm spacing induced the formation of microspheres, characteristic of the hydroxyapatite phase, while for 0.02 cm spacing, only a non-homogeneous coating was obtained. Therefore, the use of laser in the production of active surfaces for deposition of bioceramics proved to be viable, and the final coating has potential for applications in the field of dental implants.

Estudo in vitro das alterações na superfície do titânio comercialmente puro e da liga de titânio Ti -6Al-4V submetida a diferentes tratamentos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito de tratamentos térmicos na resistência à tração e na dureza Vickers do Ti c.p. e da liga Ti-6Al-4V obtidos por fundição odontológica

Pós-graduação em Reabilitação Oral - FOAR

Processamento, caracterização microestrutural e propriedades elásticas de metais celulares do sistema Ti-6Al-4V para fins de regeneração óssea

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloys in different storage environments

Statement of problem. Removable partial dentures are affected by fatigue because of the cyclic mechanism of the masticatory system ansi frequent insertion and removal. Titanium and its alloys have been used in the manufacture of denture frameworks; however, preventive agents with fluorides are thought to attack titanium alloy surfaces.Purpose. This study evaluated, compared, analyzed the corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloy in different storage environments.Material and methods. For each metal, 33 dumbbell rods, 2.3 mm in diameter at the central segment, were cast in the Rematitan system. Corrosion-fatigue strength test was carried out through a universal testing machine with a load 30% lon er than the 0.2% offset yield strength and a combined influence of different: environments: in air at room temperature, with synthetic saliva, and with fluoride synthetic saliva. After failure, the number of cycles were recorded, and fracture surfaces were examined with on SEM.Results. ANOVA and Tukey's multiple comparison rest indicated that Ti-6Al-4V alloy achieved 21,269 cycles (SD = 8,355) against 19,157 cycles (SD = 3,624) for the commercially purr Ti. There were no significant differences between either metal in the corrosion-fatigue life for dry specimens, but when the solutions were present, the fatigue life was significantly reduced, probably because of the product-ion of corrosion pits caused by superficial reactions.

Modificação da superfície do titânio e de sua liga Ti-6Al-4V por recobrimento com TiO2 e hidroxiapatita

In this work, the influence of modifications of the cp-Ti and Ti 6Al 4V alloy, by treating the surface with NaOH and depositing titanium oxide and hydroxyapatite by sol-gel method, on their biocompatibility was studied. The coatings were characterized by scanning electron microscopy and X-ray diffraction which showed that the coatings on Ti 6Al 4V are better than on cp-Ti. Adhesion tests showed that adhesion strength of the coatings on cp-Ti substrate is less than on Ti 6Al 4V as well as cytotoxicity for L929 fibroblast cells is higher

The effect of thermal cycling on the shear bond strength of porcelain/Ti-6Al-4V interfaces

The aim of the study was to evaluate the effect of thermal cycling on the shear bond strength of the porcelain/Ti-6Al-4V interfaces prepared by two different processing routes and metallic surface conditions. Polished and SiO2 particle abraded Ti-6Al-4V alloy and Triceram bonder porcelain were used to produce the interfaces. Porcelain-to-metal specimens were processed by conventional furnace firing and hot pressing. Thermal cycling was performed in Fusayama's artificial saliva for 5000 cycles between 5 +/- 1 and 60 +/- 2 degrees C. After thermal cycling, shear bond tests were carried out by using a custom-made stainless steel apparatus. The results were analyzed using t-Student test and non-parametric Kruskal-Wallis test (p<0.01). Most of the polished-fired specimens were fractured during thermal cycling; thus, it was not possible to obtain the shear bond strength results for this group. Sandblasted-fired, polished-hot pressed, and sandblasted-hot pressed specimens presented the shear bond strength values of 76.2 +/- 15.9, 52.2 +/- 23.6, and 59.9 +/- 22.0 MPa, respectively. Statistical analysis indicated that thermal cycling affected the polished specimens processed by firing, whereas a significant difference was not observed on the other groups. (C) 2015 Elsevier Ltd. All rights reserved.

Micromechanisms of damage in a hypereutectic Ti-6Al-4V-B alloy

The tensile stress–strain response and fracture in a hypereutectic Ti–6Al–4V–1.7B (weight percent) alloy were investigated by employing interrupted tensile tests combined with acoustic emission measurements, with the aim to identify the cause for the observed low ductility in this alloy. These tests were complemented with microscopy. The alloy contains TiB whiskers of different length scales, the majority of which include micro-whiskers ( 5–10 μm length) and a few primary-whiskers ( 200–300 μm length). Although the fracture of both types of whiskers occur during deformation, the former leads to a gradual decrease in the secant modulus whereas initiation of the latter leads to a drastic drop in the modulus along with failure of the specimen, limiting the ductility.

The influence of temperature and strain rate on the deformation response and microstructural evolution during hot compression of a titanium alloy Ti-6Al-4V-0.1B

Hot deformation behavior of a hypoeutectic Ti-6Al-4V-0.1B alloy in (alpha + beta) phase field is investigated in the present study with special reference to flow response, kinetics and microstructural evolution. For a comparison, the base alloy Ti-6Al-4V was also studied under identical conditions. Dynamic recovery of alpha phase occurs at low temperatures while softening due to globularization and/or dynamic recrystallization dominates at high temperatures irrespective of boron addition. Microstructural features for both the alloys display bending and kinking of alpha lamellae for near alpha test temperatures. Unlike Ti-6Al-4V, no sign of instability formation was observed in Ti-6Al-4V-0.1B for any deformation condition except for cavitation around TiB particles, due to deformation incompatibility and strain accumulation at the particle-matrix interface. The absence of macroscopic instabilities and early initiation of softening mechanisms as a result of boron addition has been attributed to microstructural features (e.g. refined prior beta grain and alpha colony size, absence of grain boundary alpha layer, presence of TiB particles at prior beta boundaries, etc.) of the respective alloys prior to deformation. (C) 2012 Elsevier B.V. All rights reserved.

Deformation mechanisms during superplastic testing of Ti-6Al-4V-0.1B alloy

Superplastic tensile tests on warm rolled and optimally annealed boron modified alloy Ti-6Al-4V-0.1B at a temperature of 850 degrees C and initial strain rate of 3 x 10(-4) s(-1) results in a higher elongation (similar to 500%) compared to the base alloy Ti-6Al-4V (similar to 400%). The improvement in superplasticity has been attributed to enhanced contribution from interfacial boundary sliding to the overall deformation for the boron modified alloy. The boundary sliding was facilitated by the starting microstructure which predominantly contains small equiaxed primary a grains with narrow size distribution. Dynamic processes such as coarsening and globularization of primary a phase occur under the test condition but do not significantly contribute to the observed difference in superplasticity between the two alloys. In spite of cavitation takes place around the TiB particles during deformation, they do not cause macroscopic cracking and early fracture by virtue of the cavities being extremely localized. Localized cavitation is found to correlate with increased material transfer due to faster diffusion.