Understanding of the bainite transformation in a nano-structured bainitic steel

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to form a nano-scale bainitic microstructure consisting of nanobainitic ferrite laths with high dislocation density and retained austenite films. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with the parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. The presence of fine C-rich clusters and Fe-C carbides with a wide range of compositions in bainitic ferrite was revealed by Three-dimensional Atom Probe Tomography (APT). The high carbon content of bainitic ferrite compared to the para-equilibrium level of carbon in ferrite, absence of segregation of carbon to the austenite/bainitic ferrite interface and absence of partitioning of substitutional elements between the retained austenite and bainitic ferrite were also found using APT.

Application of advanced experimental techniques for the microstructural characterization of nanobainitic steels

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 350°C bainitic transformation temperature for 1 day to form fully bainitic structure with nano-layers of bainitic ferrite and retained austenite, while a 0.26C-1.96Si-2Mn-0.31Mo (wt%) steel was subjected to a successive isothermal heat treatment at 700°C for 300 min followed by 350°C for 120 min to form a hybrid microstructure consisting of ductile ferrite and fine scale bainite. The dislocation density and morphology of bainitic ferrite, and retained austenite characteristics such as size, and volume fraction were studied using Transmission Electron Microscopy. It was found that bainitic ferrite has high dislocation density for both steels. The retained austenite characteristics and bainite morphology were affected by composition of steels. Atom Probe Tomography (APT) has the high spatial resolution required for accurate determination of the carbon content of the bainitic ferrite and retained austenite, the solute distribution between these phases and calculation of the local composition of fine clusters and particles that allows to provide detailed insight into the bainite transformation of the steels. The carbon content of bainitic ferrite in both steels was found to be higher compared to the para-equilibrium level of carbon in ferrite. APT also revealed the presence of fine C-rich clusters and Fe-C carbides in bainitic ferrite of both steels.

Effect of composition and processing parameters on the formation of nano-bainite in advanced high strength steels

The nano-bainitic microstructures were compared in a 0.79C-1.5Si-1.98Mn-0.24Mo-1.06Al (wt%) steel after isothermal heat-treatment and a Fe-0.2C-1.5Mn-1.2Si-0.3M0-0.6Al-0.02Nb (wt%) steel after controlled thermo-mechanical processing. The microstructure for both steels consisted of bainite. The microstructural characteristics of bainite, such as the morphology of the nano-bainite and thicknesses of bainitic ferrite and retained austenite layers, as a function of steel composition and processing was studied using transmission electron microscopy (TEM). It was found that the nano-bainitic structure can be formed in the low alloy steel through thermomechanical processing. Atom probe tomography (APT) was employed as a powerful technique to determine local composition distributions in three dimensions with atomic resolution. The important conclusions from the APT research were that the carbon content of bainitic ferrite is higher than expected from paraequilibrium level of carbon in ferrite for both steels and that Fe-C clusters and fine particles are formed in the bainitic ferrite in both steels despite the high level of Si.

Effect of bake-hardening treatment on the mechanical properties of high strength bainitic steel produced by thermomechanical processing

The influence of pre-straining and bake-hardening on the mechanical properties of thermomechanically processed 0.2C-1.5Si-1.5Mn-0.2Mo-0.004Nb (wt%) steel was analysed using tensile test, transmission electron microscopy (TEM) and atom probe tomography (APT). This steel after processing had high strength (~1200MPa) and good ductility (~20%) due to the formation of fully bainitic microstructure with nano-layers of bainitic ferrite and retained austenite. The bake hardening (BH) of pre-strained (PS) samples increased the yield strength of steel up to 690MPa and showed the bake-hardening response of 220MPa due to the operation of several strengthening mechanisms such as transformation induced plasticity during pre-straining and pinning the dislocations by carbon during bake-hardening treatment. The carbon content of the bainitic ferrite and retained austenite before and after bake-hardening treatment, the solute distribution between these phases and the local composition of fine Fe-C clusters and particles formed during bake-hardening treatment was calculated using APT. The bainitic ferrite and retained austenite microstructural characteristics such as thickness of the layers and their dislocation density before and after bake-hardening treatment were studied using TEM.

Effects of Si on microstructural evolution and mechanical properties of hot-rolled ferrite and bainite dual-phase steels

Based on the thermo-mechanical controlled process, the effects of Si on microstructural evolution, tensile properties, impact toughness, and stretch-flangeability of ferrite and bainite dual-phase (FBDP) steels were systematically investigated. The addition of Si from 0 to 0.95% promoted the formation of fine and equiaxed ferrite grains, and high Si (0.95%) also resulted in the formation of blocky martensite islands and retained austenite. Yield and tensile strengths, and uniform and total elongations all increased with increasing Si content. Therefore, the tensile strength and ductility balance was improved by Si addition due to the increasing strain-hardening rate. The fractured morphologies after hole-expansion showed that the excellent stretch-flangeability of FBDP steels was associated with the micro-cracks propagating through in ferrite phase as well as the elongated ferrite grains along the direction perpendicular to the crack. 0.95% Si steel had a similar high combination of tensile strength and impact toughness to 0.55% Si steel, and especially 0.95% Si steel exhibited an excellent combination of tensile strength and stretch-flangeability.

Effect of baking process on microstructures and mechanical properties of low silicon TRIP steel sheet with niobium

After 2% predeformation, the baking treatment with different schedule was carried out for low silicon TRIP steel sheet with niobium. The effects of baking temperature and time on microstructures and mechanical properties were investigated. The results showed that with increasing the baking temperature and time, the volume fraction of retained austenite decreases, and the volume fraction of tempered martensite increases; as baking temperature ranges from 80°C to 170°C, the bake-hardening (BH) value increases obviously, while from 170°C to 230°C, the variation of BH value is very slight; as baking time ranges from 2 min to 20 min, the BH value increases significantly, while the BH value decreases when baking time exceeds 20 min. So that when the baking temperature is 170°C and the baking time is 20 min, the low silicon TRIP steel sheet exhibits good bake-hardening behavior, and the highest BH value is above 70 MPa.

Effect of prestrain on microstructures and properties of Si-Al-Mn TRIP steel sheet with niobium

Paint baking treatment was carried out in a silicon oil bath at 170 °C for 20 min for Si-Al-Mn TRIP Steel sheet with different prestrains, and effect of prestrain on microstructures and properties was studied before and after baking. The results show that with the increasing of prestrain amount during prestraining and baking, the volume fraction of retained austenite decreases, and the volume fraction of martensite and bainite increases as well as yield strength increases; as prestrain ranges from 0 to 4%, the baking-hardening (BH) value increases; while the prestrain ranges from 4% to 16%, the BH value decreases; when the prestrain amount is 4%, the highest BH value is about 70 MPa for Si-Al-Mn TRIP steel sheet with niobium, which displays excellent baking-hardening behavior.

Characterization of nano-structured bainitic steel

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to produce a nano-structured bainitic steel. The microstructure consisted of nanobainitic ferrite laths with a high dislocation density and retained austenite films having extensive twins. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. Atom Probe Tomography (APT) revealed that the carbon content of nanobainitic ferrite laths was much higher than expected from the para-equilibrium level. This was explained due to the long heat treatment time, which led to the formation of fine Fe-C clusters on areas with high dislocation densities in bainitic ferrite laths.

On the low temperature strain aging of bainite in the TRIP steel

The aging behavior of a thermomechanically processed Mo-Al-Nb transformation-induced plasticity steel with ultrafine microstructure was investigated using transmission electron microscopy and atom probe tomography (APT). Strain aging at 73 K (200 °C) for 1800 seconds led to a significant bake-hardening response (up to 222 MPa). Moreover, aging for 1800 seconds at room temperature after 4 pct pre-strain also revealed a bake-hardening response (~60 MPa). The experimental results showed the formation of carbon Cottrell atmospheres around dislocations and the formation of carbon clusters/fine carbides in the bainitic ferrite during aging. It is proposed that this is associated with the high dislocation density of bainitic ferrite with formation of a complex dislocation substructure after pre-straining and its high average carbon content (~0.35 at. pct). The segregation of carbon and substitutional elements such as Mn and Mo to the retained austenite/bainitic ferrite interface during aging was observed by APT. This segregation is likely to be the preliminary stage for Mo-C particles’ formation. The aging after pre-straining also induced the decomposition of retained austenite with formation of ferrite and carbides.

Atomic scale investigation of solutes and precipitates in high strength steels

Two steels, ferritic, high strength with interphase precipitation and nano-bainitic, were used to show the advances in and application of atom probe. The coexistence of the nano-scale, interphase Nb-Mo-C clusters and stoichiometric MC nano particles was found in the high strength steel after thermomechanical processing. Moreover, the segregation of carbon at different heterogeneous sites such as grain boundary that reduces the solute element available for fine precipitation was observed. The APT study of the solutes redistribution between the retained austenite and bainitic ferrite in the nano-bainitic steel revealed: (i) the presence of two types of the retained austenite with higher and lower carbon content and (ii) segregation of carbon at the local defects such as dislocations in the bainitic ferrite during the isothermal hold.

A case study on effect of feed rate on machinability of austempered ductile iron

Austempered Ductile Iron (ADI) is a type of nodular, ductile cast iron subjected to heat treatments - austenitising and austempering. Whilst machining is conducted prior to heat treatment and offers no significant difficulty, machining post heat treatment is demanding and often avoided. Phase transformation of retained austenite to martensite leading to poor machinability characteristics is a common problem experienced during machining. This case study explains the effect of feed rate on machinability of ADI using cutting force analysis and tool failure analysis. The experimental design consists of conducting drilling trials on grade 1200 and 1400 at constant depth of cut, 25mm; constant speed, 45m/min; no coolant and variable feed rates from 0.2 to 0.35 mm/rev (increment of 0.025mm/rev). Metallography and X-ray diffraction technique was carried out in order to identify and quantify the microstructural phases before and after drilling. The results from the trial infer that the best way to machine ADI efficiently without tool failure is using low feeds and high speeds and without coolant.

Machinability and phase transformation study of nanobainite steels

There is an increasing demand for high strength materials with the development of technology and critical applications. Nano materials are newly developed materials with extremely high strength for this purpose. Nanobainite is a dual phase material containing alternate layers of bainitic ferrite in nano dimensions and retained austenite. Nanobainite is produced by isothermally holding austenitized steel at a temperature of 200°C or less, depending on the chemical composition, for 6 10 days until bainite forms and then cooling to room temperature using austempering. The experimental design consisted of face milling under 12 combinations of Depth of Cut (DOC)-1, 2 and 3mm; cutting speed-100 and 150m/min; constant feed-0.15mm/rev and coolant on/off. The machinability of the material is assessed by means of analysis, such as surface texture and microhardness. The assessment also involves microstructural comparisons before and after milling. Future work involves quantifying the microstructural phase before and after milling using XRD. The results obtained are used to assess the most favorable condition to cut this new variety of steel.

A Novel Mo and Nb Microalloyed Medium Mn TRIP Steel with Maximal Ultimate Strength and Moderate Ductility

The multi-phase, metastable, and multi-scale (M3) constitution of a novel transformation-induced plasticity (TRIP) steel (Fe-0.17C-6.5Mn-1.1Al-0.22Mo-0.05Nb, wt pct) was designed through thermodynamic calculations combined with experimental analysis. In this study, Mo and Nb microalloying was used to control the fraction of retained austenite and its mechanical stability during tensile deformation and to improve the yield strength. Thermodynamic calculations were developed to determine the critical annealing temperature, at which a large fraction of retained austenite (~38 pct) would be obtained through the effects of solute enrichment. The experimental observation was in good agreement with the predicted results. According to the critical annealing temperature, such an ultrafine (<200 nm) M3, microstructure with optimum mechanical stability was successfully achieved. The results of this work demonstrated the superior performance with improved yield strength of 1020 to 1140 MPa and excellent ductility (>30 pct), as compared with other TRIP steels. Both angle-selective backscatter and electron backscatter diffraction techniques were employed to interpret the transformation from the deformed martensitic laths to the ultrafine austenite and ferrite duplex structure.

Characterization of microstructures and tensile properties of TRIP-aided steels with different matrix microstructure

Three different heat treatment processes have been proposed as a fundamental method to produce three kinds of TRIP-aided steels with polygonal ferritic matrix (F-TRIP), bainitic matrix (B-TRIP) and martensitic matrix (M-TRIP) in a newly designed low alloy carbon steel. By means of dilatometry study and detailed characterization, the relationships among transformation, microstructure and the resulting mechanical behavior were compared and analyzed for the three cases. The work hardening of the samples was evaluated by calculating the instantaneous n value as a function of strain. The M-TRIP sample exhibits the highest strength with the highest work hardening rate at low strains and subsequent rapid descending at high strains. In contrast, the B-TRIP sample has relatively high continuously constant work hardening behavior over strain levels greater than 0.067. The difference in work hardening behavior corresponds directly to the rate of the retained austenite-martensitic transformation during straining, which can be attributed to the carbon content, the morphology of the retained austenite and the matrix microstructure in the respective TRIP-aided samples. © 2014 Elsevier B.V.