Nd3+螯合物的含氢有机溶液光谱性能研究

Tris-thenoyltrifluroacetonate of Nd3+ has been prepared and dissolved in DMF solation with very high concentration, and the contained hydrogen has not been substituted by deuterium. The absorption spectrum, emission spectrum, and fluorescence lifetime of the solution were measured. Very obvious characteristic fluorescence peaks were observed at 898 and 1058 nm. Based on Judd-Ofelt theory, three intensity parameters were obtained: Omega(2) = 4.9 x 10(-20) cm(2), Omega(4) = 5.1 x 10(-20) cm(2) and Omega(6) = 2.5 x 10(-20) cm(2). Line strengths S-cal, oscillator strengths f(cal), radiative transition probabilities A(ed), radiative lifetimes tau(r) and branch ratios beta were calculated too. The measured lifetime tau of 1058 nm peak is 460 mu s, and that of 898 nm 505 mu s. Comparison between theoretically computed radiative lifetime tau(r)(682 mu s) and the measured lifetime indicates that the non-radiative transition probability of the solution is very low and the fluorescence quantum efficiency very high. High values of three intensity parameters prove the high asymmetric surroundings of Nd3+, which is important for Nd3+ to absorb the excitation energy. Spectropic quality factor Omega(4)/Omega(6) > 1 makes radiation at 898 nm stronger than at 1058 nm.

掺铒高硅氧玻璃光谱性质的研究

应用Judd-Oflet理论计算了新型掺铒高硅氧玻璃中铒离子的强度参量Ωt（t=2，4，6），Ω2=8．15×10^-20,Ω4=1．43×10^-20,Ω6=1．22×10^-20，相比于其他氧化物玻璃，表现出较大的Ω2,6值，反映了铒离子周围的近邻结构不对称性和Er-O键的离子键成分较高．利用McCumber理论计算得到了能级4I13/2→4I15/2跃迁的受激发射截面为σc=O．51pm^2．这种高硅氧玻璃掺铒离子浓度尽管高于石英光纤的掺杂浓度10倍左右，其荧光寿命和量子效率仍达到6．0ms和66．

Effect of network modifiers on spectroscopic properties of erbium-doped phosphate glasses

The integrated absorption cross section Sigma(abs), I peak emission cross section sigma(cmi), Judd-Ofeld intensity parameters Omega(iota) ( t = 2,4,6), and spontaneous emission probability A(R) of Er3+ ions were determined for Erbium doped alkali and alkaline earth phosphate glasses. It is found the compositional dependence of sigma(emi) 5 almost similar to that of Sigma(abs), which is determined by the sum, of Omega(1) (3 Omega(2) + 10 Omega(4) + 21 Omega(6)). In addition, the compositional dependence of Omega(1) was studied in these glass systems. As a result, compared with. Omega(4) and Omega(6) the Omega(2) has a stronger compositional dependence on the ionic radius and content of modifers. The covalency of Er-O bonds in phosphate glass is weaker than that in silicate glass, germanate glass, aluminate glass, and tellurate glass, since Omega(6) of phosphate glass is relatively large. A(R) is affected by the covalency of the Er3+ ion sites and corresponds to the Omega(6) value.

Effect of alkaline-earth metal composition on spectroscopic properties of Er3+ in fluorophosphate glasses

Optical spectroscopic properties of Er3+-doped alkaline-earth metal modified fluoropho sphate glasses have been investigated experimentally for developing broadband fiber and planar amplifiers. The results show a strong correlation between the alkaline-earth metal content and the spectroscopic parameters such as absorption and emission cross sections, full widths at half-maximum and Judd-Ofelt intensity parameters. It is found that strontium ions could have more influences on the Judd-Ofelt intensity parameters and the absorption and emission cross sections than other alkaline-earth metal ions such as Mg2+, Ca2+, Ba2+. The sample containing 23 mol% strontium fluoride exhibits the maximum emission cross section of 7.58 x 10(-21) cm(2), the broadest full width at half-maximum of 65 nm and the longer lifetime of 8.6 ms among the alkaline-earth metal modified fluorophosphates glasses studied. The Judd-Ofelt intensity parameter Omega(6)s, the emission cross sections and the full widths at half-maximum in the Er3+-doped fluorophosphate glasses studied are larger than in the silicate and phosphate glasses.

掺铒碲酸盐玻璃的热力学稳定性和光谱性质的研究

分析了掺Er^3+碲酸盐玻璃的热力学稳定性能，研究了掺Er^3+碲酸盐玻璃的吸收和荧光光谱性质；应用Judd-Ofelt理论计算了碲酸盐玻璃中Er^3+离子的强度参数Ω(Ω2=4．79×10^-20cm^2,Ω4=1．52×10^-20cm^2，Ω6=0．66×10^-20cm^2)，计算了离子的自发跃迁几率，荧光分支比；应用McCumber理论计算了Er^3+的受激发射截面(σe=10．40×10^-21cm^2)、Er^3+离子^4I13／2→^4I15／2发射谱的荧光半高宽(FWHM=65．5nm)

Effect of lithium-potassium mixed alkali on spectroscopic properties of Er3+-doped aluminophosphate glasses

Er3+-doped lithium-potassium mixed alkali aluminophosphate glasses belonging to the oxide system xK(2)O-(15x)Li2O-4B(2)O(3)-11Al(2)O(3)-5BaO-65P(2)O(5) are obtained in a semi-continuous melting quenching process. Spectroscopic properties of Er3+-doped glass matrix have been analysed by fitting the experimental data with the standard Judd-Ofelt theory. It is observed that Judd-Ofelt intensity parameters-Omega(t)(t=2, 4 and 6) of Er3+ change when the second alkali is introduced into glass matrix. The variation of line strength S-ed[I-4(13/2),I-4(15/2)] follows the same trend as that of the Omega(6) parameter. The effect of mixed alkali on the spectroscopic properties of the aluminophosphate glasses, such as absorption cross-section, stimulated emission cross-section, spontaneous emission probability, branching ratio and the radiative lifetime, has also been investigated in this paper.

Judd-Ofelt intensity parameters of Er3+ doped mixed alkali aluminophosphate glasses

Lithium sodium mixed alkali aluminophosphate glasses of the composition xNa(2)O-(15-x)Li2O-4B(2)O(3)-11Al(2)O(3)-5BaO-65P(2)O(5) (where x=0, 3.75, 7.5, 11.25 and 15 mol%) containing 0.5 mol% Er2O3 were prepared by melt quenching. The absorption spectra of Er3+ were studied from the experimental oscillator strengths and the Judd-Ofelt intensity parameters were obtained. The variations of Judd-Ofelt intensity parameters (Omega(2), Omega(4) and Omega(6)), experimental oscillator strengths of certain excited states of Er3+ and hypersensitive band positions with different mixed alkali content have been discussed in detail. It was found that there were similar effects of mixed alkali on both Judd-Ofelt intensity parameter 02 and the experimental oscillator strength of the hypersensitive transition, I-4(15/2) -> H-2(11/2). No shifts in the peak wavelength of the studied transitions were found in different glasses. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties and Judd-Ofelt theory analysis of Dy3+ doped oxyfluoride silicate glass

Dy3+ doped oxyfluoride silicate glass was prepared and its optical absorption, 1.3 mu m emission, and upconversion luminescence properties were studied. Furthermore, the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] intensity parameters, oscillator strengths, spontaneous transition probability, fluorescence branching ratio and radiative lifetime were calculated by Judd-Ofelt theory, while stimulated emission cross section of H-6(9/2)+F-6(11/2)-> H-6(15/2) transition was calculated by McCumber theory [Phys. Rev. A. 134, 299 (1964)]. According to the obtained Judd-Ofelt intensity parameters Omega(2)=2.69x10(-20) cm(2), Omega(4)=1.64x10(-20) cm(2), and Omega(6)=1.64x10(-20) cm(2), the radiative lifetime was calculated to be 810 mu s for 1.3 mu m emission, whose full width at half maximum and sigma(e) were 115 nm and 2.21x10(-20)cm(2), respectively. In addition, near infrared to visible upconversion luminescence was observed and evaluated. The results suggest that Dy3+ doped oxyfluoride silicate glass can be used as potential host material for developing broadband optical amplifiers and laser applications.

Stability against crystallization and spectroscopic properties of Tm3+ doped fluorophosphate glasses

Fluorophosphate glasses with various content of Al(PO3)(3) were prepared. With the increment of Al(PO3)(3) content, density decreases while refractive index increases, and transition temperature, crystallization peak temperature and melt temperature increase which were suggested by differential scanning calorimetry. These glasses exhibit the best stability against crystallization with 7-9 mol'Yo Al(PO3)(3) content. Normalized Raman spectra were used to analyze structure and phonon state. The increment of Al(PO3)(3) content does not affect phonon energy but results in the augment of phonon density. Absorption spectra were measured. H-3(6) -> F-3(4) transition exhibits absorption at L band of the third communication window. Compared with the energy of Tm3+ excited states in other glass system, F-3(4) energy of Tm3+ in these glasses is considerable higher and H-3(4) energy is considerable lower, and it can be predicted that emission band of H-3(4) -> F-3(4) transition is close to the amplified band of gain-shift Tm3+ doped fiber amplifier. Analyses of Judd-Ofelt theory suggest when Al(PO3)(3) content is no more than 7 mol%, Judd-Ofelt parameters Omega(t) and the lifetime of H-3(4) energy level of TM3+ vary little with the increment of Al(PO3)(3) content, and when Al(PO3)(3) content is more than 7 mol%, Omega(2) and Omega(6) increase and radiative lifetime of H-3(4) energy level of Tm3+ drops sharply with the increment of Al(PO3)(3) content. (c) 2006 Elsevier B.V. All rights reserved.

Efficient frequency upconversion emission in Er3+-doped novel strontium lead bismuth glass

Er3+ -doped strontium lead bismuth glass for developing upconversion lasers has been fabricated and characterized. The Judd-Ofelt intensity parameters Omega(1) (t = 2,4,6), calculated based on the experimental absorption spectrum and Judd-Ofelt theory, were found to be Omega(2) = 2.95 x 10(-20), Omega(4) = 0-91 X 10(-20), and Omega(6) = 0.36 x 10(-20) cm(2). Under 975 nm excitation, intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions H-2(11/2) --> I-4(15/2), S-4(3/2) I-4(15/2), and F-4(9/2) --> I-4(15/2) respectively were observed. The upconversion mechanisms are discussed based oil the energy matching and quadratic dependence on excitation power, and the dominant mechanisms are excited state absorption and energy transfer upconversion for the green and red emissions. The long-lived I-4(11/2) level is supposed to serve as the intermediate state responsible for the upconversion processes. (C) 2004 Published by Elsevier B.V.

Broadband amplification and upconversion luminescence properties of Er3+/Yb3+ co-doped fluorophosphate glass

Broadband and upconversion properties were studied in Er3+/Yb3+ co-doped fluorophosphate glasses. Large Omega(6) and S-ed/(S-ed + S-md) values and the flat gain profile over 1530-1585 nm indicate the good broadband properties of the glass system. And a premise of using Omega(6) as a parameter to estimate the broadband properties of the glasses is proposed for the first time to our knowledge. Results showed that fluorescence intensity, upconversion luminescence intensity, the intensity ratio of red/green light (656 nm/545 nm) are closely related to the Yb3+:Er3+ ratio and Er3+ concentration, and the corresponding calculated lifetime of F-4(9/2) and S-4(3/2) states for red and green upconversion samples proves this conclusion. The upconversion mechanism is also discussed. (c) 2005 Elsevier Ltd. All rights reserved.

Host dependent frequency upconversion of Er3+-doped oxyfluoride germanate glass

Er3+-doped oxyfluoride germanate glasses have been synthesized by the conventional melting and quenching method. The Judd-Ofelt intensity parameters were calculated based on the Judd-Ofelt theory and absorption spectra measurements. With the substitution of PbF2 for PbO, the Omega(2) parameter decreases, while the Omega(6) parameter increases. These change trends indicate that fluoride anions come to coordinate erbium cations and the covalency of the Er-O bond decreases. Structural and thermal stability properties were obtained by Raman spectra and differential thermal analysis, indicating that PbF2 plays an important role in the formation of glass network and has an important influence on the maximum phonon energy and thermal stability of host glasses. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions H-2(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2), respectively, were simultaneously observed at room temperature. With increasing PbF2 content, the intensity of red (657nm) emissions increases significantly, while that of the green (525 and 546nm) emission increases slightly. The results indicate that PbF, has more influence on the red (657nm) emission than the green (525 and 546nm) emissions in oxyfluoride germanate glasses. The possible upconversion luminescence mechanisms have also been estimated and discussed. (c) 2005 Elsevier B.V. All rights reserved.

Infrared-to-visible upconversion fluorescence of Er3+-doped novel lithium-barium-lead-bismuth glass

Er3+-doped lithium-barium-lead-bismuth glass for developing upconversion lasers has been fabricated and characterized. The Judd-Ofelt intensity parameters Omega(t) (t = 2, 4, 6), calculated based on the experimental absorption spectrum and Judd-Ofelt theory, were found to be Omega(2) = 3.05 x 10(-20) cm(2), Omega(4) = 0.95 x 10(-20) cm(2), and Omega(6) = 0.39 x 10(-20) cm(2). Under 975 nm excitation, intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions H-2(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2), respectively, were observed at room temperature. The upconversion mechanisms are discussed based on the energy matching and quadratic dependence on excitation power, and the dominant mechanisms are excited state absorption and energy transfer upconversion for the green and red emissions. The long-lived I-4(11/2) level is supposed to serve as the intermediate state responsible for the intense upconversion processes. The intense upconversion luminescence of Er3+-doped lithium-barium-lead-bismuth glass may be a potentially useful material for developing upconversion optical devices. (c) 2004 Elsevier B.V. All rights reserved.

Impacto da dieta hiperlipídica contendo óleo de canola ou de soja no desenvolvimento da adiposidade abdominal e estrutura óssea

A baixa relação de ômega-6/ômega-3 esta relacionada com propriedades benéficas para a saúde óssea. No entanto, a dieta rica nestes compostos pode levar a obesidade. Adipócitos e osteoblastos derivam de células progenitoras comuns, e o consumo de óleo de canola pode ter ação adipogênica e osteogênica. Nosso objetivo foi avaliar a adiposidade abdominal, insulina e estrutura óssea em ratos tratados com dieta contendo baixa relação ômega-6/ômega-3, proveniente do óleo de canola. Após desmame, os ratos foram divididos em grupos alimentados com dieta normocalórica: Controle (S) e experimental (C), contendo 7ml/100g de óleo de soja ou de canola e grupos tratados com dieta rica em lipídios: Controle (7S) ou hiperlipídico contendo 19ml/100g de óleo de soja (19S) ou de canola (19C), até completarem 60 dias de idade. Os dados foram significativos com P<0,05. No primeiro modelo, o grupo C apresentou redução de: Massa e área do adipócito intra-abdominal; Colesterol; Insulina; Densidade mineral (DMO) e massa óssea total e na coluna vertebral; Massa do fêmur; Espessura da diáfise; DMO do fêmur e das vértebras lombares e radiodensidade da cabeça do fêmur. No segundo modelo, os grupos 19S e 19C apresentaram maior ingestão calórica, densidade corporal, massa de gordura intra-abdominal, e maior massa e comprimento do fêmur e da coluna lombar. O grupo 19S apresentou maior área e menor número de adipócitos da região retroperitoneal. Glicose e a insulina foram aumentadas no grupo 19C vs. 7S. A tomografia do fêmur revelou maior radiodensidade na região proximal e da coluna lombar, no grupo 19C. Sugerimos que a quantidade e o tipo de lipídio consumido, após o desmame, induzem não somente o desenvolvimento corporal e os depósitos de gordura, além de afetarem a resistência insulínica e a saúde óssea

Upconversion emission in Er3+ doped novel bismuthate glass

Novel Er3+-doped bismuth lead strontiam glass was fabricated and characterized, and the absorption spectrum and upconversion spectrum of the glass were studied. The Judd-Ofelt intensity parameters Omega(t)(t = 2, 4, 6) were found to be Omega(2) = 3.27 x 10(-20) cm(2), Omega(4) = 1.15 x 10(-20) cm(2), and Omega(6) = 0.38 x 10(-20) cm(2). The oscillator strength, the spontaneous transition probabilities, the fluorescence branching ratios, and excited state lifetimes were also measured and calculated. The upconversion emission intensity varies with the power of infrared excitation intensity. A plot of log I-up vs log I-IR yields a straight line with slope 1.86, 1.88 and 1.85, corresponding to 525, 546, and 657 nm emission bands, respectively, which indicates that a two-photon process for the red and green emission.