连续可调纳秒脉冲LD驱动电源的研制

为了满足单模尾纤输出脉冲半导体激光器及其后级光放大的要求,研制了一种重频、脉宽及峰值电流均连续可调的纳秒脉冲驱动电源。该电源使用功率场效应管作为开关,通过分析其驱动特性,采用合适的栅极驱动电路,从而缩短了脉冲宽度,增加了带负载能力;同时电源中的保护电路采用自断电等保护措施,能有效保证LD的安全工作。实验结果表明,该驱动电源工作稳定,能满足单模尾纤输出脉冲LD重频、脉宽、峰值可调的要求。

LD泵浦的镱铒共掺磷酸盐玻璃的光谱性质和激光性质

制备了Er^3＋/Yb^3＋共掺磷酸盐玻璃. 通过分析其吸收光谱, 根据McCumber理论计算得到了Er^3＋离子在波长1533 nm处的峰值发射截面为0.84×10^-20 cm^2, ^4I13/2能级的荧光寿命为8.5 ms. 利用激光二极管作为泵浦源, 成功地实现了Er^3＋/Yb^3＋共掺磷酸盐玻璃激光器的连续运转. 在室温下, 获得最大激光输出功率为80 mW, 斜率效率为16.5%.

Er3+ and Yb3+ codoped phosphate laser glass for high power flashlamp pumping

A novel Vb(3+)-Er-(3+) codoped phosphate glass for high power flashlamp pumping and high repetition rate laser at 1.54 mu m, designated EAT5-2, is developed. The weight-loss rate of is 1.3 x 10(-5) gcm(-2) h(-1) in boiling water, which is comparable to Kigre's QX-Er glass. Some spectroscopic parameters are analysed by Judd-Ofelt theory and McCumber theory The emission cross section is calculated to be 0.73 x 10(-20) cm(2). The thermo-mechanical properties of EAT5-2 are modified after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. The thresholds for optical damage from the flashlamp pumping are tested on glass rods. A repetition rate of 15 Hz is achieved for chemically strengthened glass. The laser experimental results at. 1.54 mu m from flashlamp pumping are also reported.

铒镱共掺磷酸盐玻璃的激光性质

制备了镱铒共掺的磷酸盐玻璃并研究了室温下LD泵浦的连续激光输出性质。在泵浦功率为496mW时实现了最大输出功率77mW。讨论了在不同玻璃样品厚度和谐振腔长度时的斜率效率的变化以及在不同玻璃样品厚度，泵浦功率和谐振腔长度时的不同激光模式竞争的动力学行为。结果表明：激光光谱受到光学增益和光学损耗相对大小的限制。

Infrared (1.2-1.6 mu m) luminescence in Yb, Cr : YAG with 940 nm diode pumping

Infrared (1.2-1.6 mum) luminescence in a yttrium aluminium garnet (YAG) crystal, co-doped with Yb (10 at.%) and Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.35 mum and measured to be about 6% with respect to Yb3+ IR luminescence (lambda = 1.03 mum). Analysis of the crystal absorption and luminescence spectra allows one to conclude that Yb3+-Cr4+ energy transfer is a mechanism responsible for the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as an efficient source of the near infrared emission. (C) 2004 Elsevier B.V. All rights reserved.

Infrared (1.2-1.6 mu m) luminescence in Cr4+: Yb3Al5O12 single crystal with 940 nm diode pumping

Infrared (1.2-1.6 mu m) luminescence in a ytterbium aluminium garnet (YbAG) crystal, doped with Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.34 mu m and measured to be about 1.3 times with respect to Yb3+ IR luminescence (lambda = 1.03 mu m). We demonstrate that for the excitation wavelength of 940 nm Yb3+ ions act as sensitizers of the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as a high-efficient system for tunable laser (1.2-1.6 mu m) output. (c) 2004 Elsevier B.V. All rights reserved.

LD抽运Yb:GSO实现1090nm低阈值激光运转

We report what we believe to be the first demonstration of laser operation with a novel laser material of Yb3(+) -doped Gd-2 SiO2 (Yb: GSO) pumped by a laser diode at 940 nm. We obtained a low lasing threshold of 1.27 kW/cm(2) with the center wavelength of 1090 nm, which is lower than the value of 1.53 kW/cm(2) predicted for Yb: YAG. The maximal output power of 360 mW was obtained with a 2% output, which corresponds to a slope efficiency up to 19%.

激光二极管抽运Na，Yb共掺CaF2晶体自调Q激光特性的研究

利用激光二极管（LD）抽运新型Na．Yb共掺CaF2（Na．Yb：CaF2）晶体，获得了1．05μm的自调Q激光输出。利用透射率1％的耦合输出镜，得到最低激光输出的抽运阈值功率仅为70mW。在透射率为2％的输出镜条件下，得到最大输出激光功率为390mw，此时激光的斜度效率达到20%。实验详细记录了自调Q脉冲的周期和宽度随抽运功率的变化关系，随着抽运功率的增加，自调Q脉冲的周期和宽度呈指数衰减。同时，还采用单棱镜进行光谱调谐实验，获得了1036～1059nm的自调Q激光调谐输出。

LD抽运新型Yb：LYSO晶体实现1085nm激光输出

Yb^3＋激光材料在900～980nm范围具有较强的吸收，能与高效的InGaAs激光二极管（波长为9001100nm）有效地耦合，且能级简单，抽运波长与振荡波长相近，量子效率高。这些优点十分有利于在1000nm附近实现超快高功率激光输出。而随着高性能InGaAs激光二极管的发展和成本的降低，近年来，掺Yb^3＋激光介质的研究受到人们的极大关注，并研制出了许多新型激光晶体，如Yb：YAG，Yb：KYW，Yb：GdVO4，Yb：SYS，Yb：YAB，

利用窄得-奥菲特理论研究Tm:Lu_2SiO_5晶体的光谱特性

采用丘克拉斯基(Czochralski)技术生长了掺铥硅酸镥(Tm∶Lu2SiO5,Tm∶LSO)晶体;测量了LSO晶体在室温下的非偏振吸收光谱和非偏振荧光光谱;利用窄得-奥菲特(Judd-Ofelt)理论计算了Tm∶LSO晶体的窄得-奥菲特强度参数、振子强度、自发辐射概率、辐射寿命、积分吸收截面和积分发射截面.Tm∶LSO晶体的强度参数为Ω2=9.1355×10-20cm2,Ω4=8.4103×10-20cm2,Ω6=1.5908×10-20cm2;Tm∶LSO晶体在1.9μm附近有明显的发射峰(3F4→3H6跃迁),相应的辐射寿命为2.03 ms,积分发射截面为5.81×10-18cm2,半峰全宽(FWHM)为250 nm.用Tm∶LSO晶体在77 K温度下实现了激光运转.利用792 nm的激光二极管(LD)作为抽运源,获得中心波长为1960 nm的激光输出,抽运阈值为2.13 kW/cm2.