Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

三倍频分光膜在1064 nm的破斑特性研究

采用电子束蒸发方式制备了两种不同材料组合的分光膜,分别对其在波长1064 nm激光辐照下的损伤阈值进行了测试,用Alpha-Step 500台阶仪对破斑进行了深度测量。实验结果表明,破斑呈现出表面层的剥落和深坑破坏两种形态。表面层的剥落深度在一定范围内不随能量密度的变化而变化；深坑破坏深浅不一,是膜内缺陷融化、汽化及喷发的综合作用的结果,是损伤阈值降低的主要原因。

短脉冲激光辐照下熔融石英薄膜的损伤机理

激光诱导薄膜损伤过程中，雪崩离化（AI）和多光子离化（MPI）的性质和作用到目前仍然存在争议。基于STUART等人的电子密度演化方程，运用数值模拟方法，研究了脉宽为τ∈[0．01，5]ps范围内单脉冲激光作用下熔融石英薄膜中电子密度演化过程；讨论了初始电子密度、激光脉冲宽度对阈值功率密度和阈值能量的影响；分析了初始电子密度、激光脉冲宽度对多光子离化及雪崩离化的影响。研究结果表明，在所研究的脉宽范围内，对于熔融石英光学薄膜、飞秒激光诱导损伤以雪崩离化为主导，多光子离化的影响随着脉宽的降低而增强，雪崩离化所需种子电子主要来源于多光子离化。

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

355nm增透膜的设计、制备与性能

用热舟蒸发法结合修正挡板技术制备了355 nm LaF3/MgF2增透膜,并对部分样品进行了真空退火。采用Lambda 900光谱仪测试了增透膜的低反光谱和透射光谱,并考察了其光谱稳定性;使用脉冲8 ns的355 nm激光测试了增透膜的激光损伤阈值(LIDT);采用Normarski显微镜对增透膜的表面缺陷密度和破斑形貌进行了观察。实验结果表明,制备得到的增透膜的剩余反射率较低,光谱稳定性好;真空退火对增透膜的激光损伤阈值没有改善;增透膜的破环形貌为散点形式,结合破斑深度测试表明薄膜的破坏源于薄膜和基底界面的缺陷点。JGS1熔石英基底由于有好的表面状况、固有的高激光损伤阈值和以其为基底的增透膜具有更低的表面场强,使得其上的增透膜有更高的抗激光损伤能力。

Thermal-mechanical modeling of nodular defect embedded within multilayer coatings

The initiation of laser damage within optical coatings can be better understood by thermal-mechanical modeling of coating defects. The result of this modeling shows that a high-temperature rise and thermal stress can be seen just inside the nodular defect compared to surrounding coating layers. The temperature rise and thermal stress tend to increase with seed diameter. Shallower seed tend to cause higher temperature rise and greater thermal stress. There is a critical seed depth at which thermal stress is largest. The composition of the seed resulting from different coating-material emission during evaporation can affect the temperature rise and thermal stress distribution.

Retinal and choroidal responses to panretinal photocoagulation: an ultrastructural perspective

BACKGROUND: There have been few histological or ultrastructural studies of the outer retina and choriocapillaris following panretinal photocoagulation therapy. This investigation examines the long-term morphological effects of panretinal photocoagulation in two patients with type II diabetes who had received laser treatment more than 6 months prior to death.

METHODS: Regions of retina and choroid from each patient were fixed in 2.5% glutaraldehyde, dissected out and examined using light microscopy and scanning and transmission electron microscopy.

RESULTS: After removing the neural retina, scanning electron microscopy of non-photocoagulated areas of the eye cups revealed normal cobblestone-like retinal pigment epithelial (RPE) cells. Regions with laser scars showed little RPE infiltration into the scar area, although large rounded cells often appeared in isolation within these areas. Sections of the retina and choroid in burn regions showed a complete absence of the outer nuclear layer and photoreceptor cells, with the inner retinal layers lying in close apposition to Bruch's membrane. Non-photocoagulated regions of the retina and choroid appeared normal in terms of both cell number and cell distribution. The RPE layer was absent within burn scars but many RPE-like cells appeared markedly hypertrophic at the edges of these regions. Bruch's membrane always remained intact, although the underlying choriocapillaris was clearly disrupted at the point of photocoagulation burns, appearing largely fibrosed and non-perfused. Occasional choroidal capillaries occurring in this region were typically small in profile and had plump non-fenestrated endothelium.

CONCLUSIONS: This study outlines retinal and choroidal cell responses to panretinal photocoagulation in diabetic patients and demonstrates an apparent reduction in the capacity of these tissues to repair laser damage.

Spray Pyrolysed Zinc Oxide Thin Films : Effects of Doping and Ion Beam Irradiation

In recent years scientists have made rapid and significant advances in the field of semiconductor physics. One of the most important fields of current interest in materials science is the fundamental aspects and applications of conducting transparent oxide thin films (TCO). The characteristic properties of such coatings are low electrical resistivity and high transparency in the visible region. The first semitransparent and electrically conducting CdO film was reported as early as in 1907 [1]. Though early work on these films was performed out of purely scientific interest, substantial technological advances in such films were made after 1940. The technological interest in the study of transparent semiconducting films was generated mainly due to the potential applications of these materials both in industry and research. Such films demonstrated their utility as transparent electrical heaters for windscreens in the aircraft industry. However, during the last decade, these conducting transparent films have been widely used in a variety of other applications such as gas sensors [2], solar cells [3], heat reflectors [4], light emitting devices [5] and laser damage resistant coatings in high power laser technology [6]. Just a few materials dominate the current TCO industry and the two dominant markets for TCO’s are in architectural applications and flat panel displays. The architectural use of TCO is for energy efficient windows. Fluorine doped tin oxide (FTO), deposited using a pyrolysis process is the TCO usually finds maximum application. SnO2 also finds application ad coatings for windows, which are efficient in preventing radiative heat loss, due to low emissivity (0.16). Pyrolitic tin oxide is used in PV modules, touch screens and plasma displays. However indium tin oxide (ITO) is mostly used in the majority of flat panel display (FPD) applications. In FPDs, the basic function of ITO is as transparent electrodes. The volume of FPD’s produced, and hence the volume of ITO coatings produced, continues to grow rapidly. But the current increase in the cost of indium and the scarcity of this material created the difficulty in obtaining low cost TCOs. Hence search for alternative TCO materials has been a topic of active research for the last few decades. This resulted in the development of binary materials like ZnO, SnO2, CdO and ternary materials like II Zn2SnO4, CdSb2O6:Y, ZnSO3, GaInO3 etc. The use of multicomponent oxide materials makes it possible to have TCO films suitable for specialized applications because by altering their chemical compositions, one can control the electrical, optical, chemical and physical properties. But the advantages of using binary materials are the easiness to control the chemical compositions and depositions conditions. Recently, there were reports claiming the deposition of CdO:In films with a resistivity of the order of 10-5 ohm cm for flat panel displays and solar cells. However they find limited use because of Cd-Toxicity. In this regard, ZnO films developed in 1980s, are very useful as these use Zn, an abundant, inexpensive and nontoxic material. Resistivity of this material is still not very low, but can be reduced through doping with group-III elements like In, Al or Ga or with F [6]. Hence there is a great interest in ZnO as an alternative of ITO. In the present study, we prepared and characterized transparent and conducting ZnO thin films, using a cost effective technique viz Chemical Spray Pyrolysis (CSP). This technique is also suitable for large area film deposition. It involves spraying a solution, (usually aqueous) containing soluble salts of the constituents of the desired compound, onto a heated substrate.

Nanosecond optical limiting response of sandwich-type neodymium dyphthalocyanine in a co-polymer host

The nanosecond optical limiting characteristics of sandwich-type neodymium diphthalocyanine in a co-polymer matrix of polymethyl methacrylate (PMMA) and methyl-2-cyanoacrylate have been studied for the first time. The measurements were performed using 9 ns laser pulses generated from a frequency-doubled Nd:YAG laser at 532 nm wavelength. The optical limiting performance of neodymium diphthalocyanine in co-polymer host was studied at different linear transmission. Laser damage threshold was also measured for the doped and undoped co-polymer samples. The optical limiting response is attributed to reverse saturable absorption which is due to excited-state absorption.

Optical-limiting response of rare-earth metallo-phthalocyanine-doped copolymer matrix

The nanosecond optical-limiting characteristics (at 532 nm) of some rare-earth metallo-phthalocyanines (Sm(Pc)2, Eu(Pc)2, and LaPc) doped in a copolymer matrix of poly(methyl methacrylate) and methyl-2-cyanoacrylate have been studied for the first time to our knowledge. The optical-limiting response is attributed to reverse saturable absorption due to excited-state absorption. The performance of LaPc in a copolymer host is studied at different linear transmissions. The laser damage thresholds of all the samples are also reported.

Investigations on Nonlinear and Radiative Properties of Certain Phatonic Materials

Light in its physical and philosophical sense has captured the imagination of human mind right from the dawn of civilization. The invention of lasers in the 60’s caused a renaissance in the field of optics. This intense, monochromatic, highly directional radiation created new frontiers in science and technology. The strong oscillating electric field of laser radiation creates a. polarisation response that is nonlinear in character in the medium through which it passes and the medium acts as a new source of optical field with alternate properties. It was in this context, that the field of optoelectronics which encompasses the generation, modulation, transmission etc. of optical radiation has gained tremendous importance. Organic molecules and polymeric systems have emerged as a class of promising materials of optoelectronics because they offer the flexibility, both at the molecular and bulk levels, to optimize the nonlinearity and other suitable properties for device applications. Organic nonlinear optical media, which yield large third-order nonlinearities, have been widely studied to develop optical devices like high speed switches, optical limiters etc. Transparent polymeric materials have found one of their most promising applicationsin lasers, in which they can be used as active elements with suitable laser dyes doped in it. The solid-matrix dye lasers make possible combination of the advantages of solid state lasers with the possibility of tuning the radiation over a broad spectral range. The polymeric matrices impregnated with organic dyes have not yet widely used because of the low resistance of the polymeric matrices to laser damage, their low dye photostability, and low dye stability over longer time of operation and storage. In this thesis we investigate the nonlinear and radiative properties of certain organic materials and doped polymeric matrix and their possible role in device development