Aplicação de Zr/Ti-PILC no processo de adsorção de Cu(II), Co(II) e Ni(II) utilizando modelos físico-químicos de adsorção e termodinâmica do processo

The aim of this investigation is to study how Zr/Ti-PILC adsorbs metals. The physico-chemical proprieties of Zr/Ti-PILC have been optimized with pillarization processes and Cu(II), Ni(II) and Co(II) adsorption from aqueous solution has been carried out, with maximum adsorption values of 8.85, 8.30 and 7.78 x10-1 mmol g-1, respectively. The Langmuir, Freundlich and Temkin adsorption isotherm models have been applied to fit the experimental data with a linear regression process. The energetic effect caused by metal interaction was determined through calorimetric titration at the solid-liquid interface and gave a net thermal effect that enabled the calculation of the exothermic values and the equilibrium constant.

Degradação fotoeletroquímica de corantes dispersos em efluente têxtil utilizando fotoanodos de Ti/TiO2

The degradation of disperses dyes in aqueous solution and in effluents from textile industry has been investigated by photoelectrocatalytic oxidation using nanoporous thin films electrodes of Ti/TiO2. Samples of dispersil black dye and dispersil blue dye after 300 min of photoelectrolyzed at applied potential of +1.0 V and UV irradiation exhibited 100% of discoloration and 90% and 64% reduction total organic carbon, respectively. The proposed method was applied with success in a textile industry effluent containing residues of these dyes, which after 300 min of treatment leads to reduction of 60% of COD and 64% removal of TOC.

Vanadium-modified molecular sieves: preparation, characterization and catalysis

Vanadium-containing molecular sieves are redox catalysts and are good candidates as substitutes for oxide-supported V2O5 in a number of reactions. These materials have the advantage of presenting better dispersion of vanadium species, as well as shape-selective properties and controllable acidities. They may be prepared by one-pot synthesis or by post-synthesis methods and a number of techniques such as diffuse reflectance UV-visible spectroscopy, 51V nuclear magnetic resonance and electron paramagnetic resonance, to name but a few, have been used to characterize these materials. In this review, methods of preparation of vanadium-modified molecular sieves, their characterization and applications in catalysis are discussed.

On-line preconcentration system using a microcolumn packed with Alizarin Red S-modified alumina for zinc determination by flame atomic absorption spectrometry

A simple and sensitive on-line flow injection system for determination of zinc with FAAS has been described. The method is based on the separation and preconcentration of zinc on a microcolumn of immobilized Alizarin Red S on alumina. The adsorbed analyte is then eluted with 250 µL of nitric acid (1 mol L-1) and is transported to flame atomic absorption spectrometer for quantification. The effect of pH, sample and eluent flow rates and presence of various cations and anions on the retention of zinc was investigated. The sorption of zinc was quantitative in the pH range of 5.5-8.5. For a sample volume of 25 mL an enrichment factor of 144 and a detection limit (3S) of 0.2 µg L-1 was obtained. The precision (RSD, n=7) was 3.0% at the 20 µg L-1 level. The developed system was successfully applied to the determination of zinc in water samples, hair, urine and saliva.

Estudo da fotocatálise heterogênea sobre Ti/TiO2 na descoloração de corantes sintéticos

The main goal of this paper was to study the degradation of synthetic dyes using photoelectrocatalytic properties of particulate films of TiO2 supported on plates of titanium and stimulated by UV-Vis radiation. The dyes decolorizations were measured using spectrophotometric methods to verify which the conditions on Ti/TiO2 electrode was the best for the photoelectrodegradation of them. The results showed that decolorization rates were higher than 90% during a period of 270 min. FT-IR spectroscopy showed that intermediate substances were formed after the decolorization and N=N group/aromatic structures were preserved independently of the specific structure of the dyes.

Separation and preconcentration trace amounts of gold by using modified organo nanoclay closite 15A

The application of organo nanoclay 5-(4-dimethylamino-benzylidene) rhodanine-immobilized as a new, easily prepared, and stable solid sorbent for preconcentration trace amounts of Au(III) ions in aqueous solution is presented. The sorption of Au(III) ions was quantitative in the pH range of 2-4, and quantitative desorption occurred instantaneously with 10.0 mL of a mixture containing 0.5 mol L-1 Na2S2O3 and KSCN. Various parameters, such as the effect of pH, breakthrough volume, extraction time, and interference of a large number of anions and cations have been studied. The proposed method has been applied for determination of trace amount of gold in water samples.

Arylation of β,γ-unsaturated lactones by a Heck-Matsuda reaction: an unexpected route to aryldiazene butenolides and pyridazinones

The palladium catalysed coupling of aryldiazonium salts with β-γ-unsaturated lactones under basic conditions has been investigated. Both (3H)-furanone and α-angelicalactone were evaluated as substrates in the Heck Matsuda reaction but both failed to afford the desired arylated butenolides. Under basic conditions, β-γ-unsaturated lactones generate highly nucleophilic enolates that preferentially undergo azo coupling reactions with arenediazonium salts to afford aryldiazene butenolides. The electronic and steric effect of the substituents on the aryldiazonium salt in the azo coupling reaction is described. Aryldiazene-lactone derivatives were obtained in good yields from a highly facile and straightforward procedure. An aminoisomaleimide was formed from (3H)-furanone and cyclised to the corresponding pyridazinones in modest yield.

A comparison of electrodeposited Ti/β-PbO2 and Ti-Pt/β-PbO2 anodes in the electrochemical degradation of the direct yellow 86 dye

The electrochemical performance of electrodeposited Ti/β-PbO2 and Ti-Pt/β-PbO2 anodes was galvanostatically evaluated (batch mode, 50 mA cm-2) to degrade the Direct Yellow 86 dye (100 or 200 mg L-1 in 0.1 mol L-1 Na2SO4 + 1.5 g L-1 NaCl), investigating the effect of pH and temperature. Similar results were obtained for both electrodes and the best conditions for removal of color and chemical oxygen demand are pH 7 and 40 °C, when 90% decolorization is attained by passing a charge of only ~0.13 A h L-1 and total mineralization is achieved with expenditure of ~5 kW h m-3.

Diesel/biodiesel soot oxidation with ceo2 and ceo2-zro2-modified cordierites: a facile way of accounting for their catalytic ability in fuel combustion processes

CeO2 and mixed CeO2-ZrO2 nanopowders were synthesized and efficiently deposited onto cordierite substrates, with the evaluation of their morphologic and structural properties through XRD, SEM, and FTIR. The modified substrates were employed as outer heterogeneous catalysts for reducing the soot originated from the diesel and diesel/biodiesel blends incomplete combustion. Their activity was evaluated in a diesel stationary motor, and a comparative analysis of the soot emission was carried out through diffuse reflectance spectroscopy. The analyses have shown that the catalyst-impregnated cordierite samples are very efficient for soot oxidation, being capable of reducing the soot emission in more than 60%.

Materiais híbridos orgânico-inorgânicos (ormosil) obtidos por sol-gel com potencial uso como filtro solar

This work aimed at the synthesis and characterization of particles of modified silica containing the organic filter dibenzoylmethane (DBM) by the hydrolytic sol-gel method, with modifications to the Stöber route. The structures of the resulting Xerogels were characterized by diffuse reflectance UV-VIS spectroscopy in the solid state, infrared absorption spectroscopy, Scanning Electron Microscopy (SEM) and 29Si Nuclear Magnetic Resonance (29Si NRM). The results showed favorable formation of hybrid organic-inorganic nanoparticles with efficient absorption/reflectance of radiation in the UV / VIS range, which enables their potential use as sunscreen.

Poly(o-methoxyaniline) modified electrode for detection of lithium ions

This paper reports the use of an electrode modified with poly(o-methoxyaniline) for detecting lithium ions. These ions are present in drugs used for treating bipolar disorder and that requires periodical monitoring of the concentration of lithium in blood serum. Poly(o-methoxyaniline) was obtained electrochemically by cyclic voltammetry on the surface of a gold electrode. The results showed that the electrode modified with a conducting polymer responded to lithium ions in the concentration range of 1 x 10-5 to 1 x 10-4 mol L-1 . The results also confirmed that the performance of the modified electrode was comparable to that of the standard method (atomic emission spectrophotometry).

Highly improved chromium (III) uptake capacity in modified sugarcane bagasse using different chemical treatments

The present paper focuses on improving chromium (III) uptake capacity of sugarcane bagasse through its chemical modification with citric acid and/or sodium hydroxide. The chemical modifications were confirmed by infrared spectroscopy, with an evident peak observed at 1730 cm-1, attributed to carbonyl groups. Equilibrium was reached after 24 h, and the kinetics followed the pseudo-second-order model. The highest chromium (III) maximum adsorption capacity (MAC) value was found when using sugarcane bagasse modified with sodium hydroxide and citric acid (58.00 mg g-1) giving a MAC value about three times greater (20.34 mg g-1) than for raw sugarcane bagasse.

Eletrodegradação de Ponceau 2R utilizando ânodos dimensionalmente estáveis e Ti/Pt

This paper reports the electrochemical degradation of the azo dye Ponceau 2R under galvanostatic electrolysis in the 1 to 200 mA cm-2 range at room temperature using dimensionally-stable anodes of oxygen (DSA-O2), chlorine (DSA-Cl2) and a titanium electrode of platinum coated with platinum oxide (Ti/Pt). The methodology applied was efficient for removing the color of the Ponceau 2R and the highest percentage removal of total organic carbon was obtained at 200 mA cm-2. Despite not having been observed complete mineralization, approximately80% removal of aromatic rings was estimated, resulting in drastic reduction of toxicity of the sample.

Sodium dodecyl sulfate coated γ-alumina support modified by a new Schiff base for solid phase extraction and flame-AAS determination of lead and copper ions

A simple and fast approach for solid phase extraction is herein described, and used to determine trace amounts of Pb2+ and Cu2+ metal ions. The solid phase support is sodium dodecyl sulfate (SDS)-coated γ-alumina modified with bis(2-hydroxy acetophenone)-1,6-hexanediimine (BHAH) ligand. The adsorbed ions were stripped from the solid phase by 6 mL of 4 M nitric acid as eluent. The eluting solution was analyzed by flame atomic absorption spectrometry (FAAS). The sorption recovery of metal ions was investigated with regard to the effects of pH, amount of ligand, γ-alumina and surfactant and the amount and type of eluent. Complexation of BHAH with Pb2+ or Cu2+ ions was examined via spectrophotometry using the HypSpec program. The detection limit for Cu2+ was 7.9 µg L-1 with a relative standard deviation of 1.67%, while that for Pb2+ was 6.4 µg L-1 with a relative standard deviation of 1.64%. A preconcentration factor of 100 was achieved for these ions. The method was successfully applied to determine analyte concentrations in samples of liver, parsley, cabbage, and water.

Preparation and evaluation of magnetic chitosan particles modified with ethylenediamine and Fe(III) for the removal of Cr(VI) from aqueous solutions

The adsorption of Cr(VI) in aqueous solution by magnetic particles of crosslinked chitosan-ethylenediamine-Fe(III) (MPCh-EDA-FeCL) was studied in a batch system. Fe3+ in the MPCh-EDA-FeCL permitted that adsorption of Cr(VI) occurred with maximum efficiency between pH 3 and 11. The maximum adsorption capacity at pH 7.0 was 81.04 mg g-1 at 25 ºC. The adsorption kinetic process was described by the pseudo-second-order model. Thermodynamic parameters indicated spontaneous, exothermic and chemical adsorption nature. The adsorbent was successively regenerated using a 0.1 mol L-1 NaOH solution. Results were satisfactory for treatment of wastewater from the electroplating industry.