Upconversion emission in Er3+ doped novel bismuthate glass

Novel Er3+-doped bismuth lead strontiam glass was fabricated and characterized, and the absorption spectrum and upconversion spectrum of the glass were studied. The Judd-Ofelt intensity parameters Omega(t)(t = 2, 4, 6) were found to be Omega(2) = 3.27 x 10(-20) cm(2), Omega(4) = 1.15 x 10(-20) cm(2), and Omega(6) = 0.38 x 10(-20) cm(2). The oscillator strength, the spontaneous transition probabilities, the fluorescence branching ratios, and excited state lifetimes were also measured and calculated. The upconversion emission intensity varies with the power of infrared excitation intensity. A plot of log I-up vs log I-IR yields a straight line with slope 1.86, 1.88 and 1.85, corresponding to 525, 546, and 657 nm emission bands, respectively, which indicates that a two-photon process for the red and green emission.

Spectroscopic properties of Er3+-doped tellurite glass for 1.55 mu m optical amplifier

Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 tellurite glass system was prepared and their density, characteristic temperatures and optical properties were determined and investigated. For the TeO2-BaO-La2O3-Er2O3 system, composition with 10 mol% BaO presented the highest thermal stability and good infrared transmittance. Intense and broad 1.53 mu m infrared fluorescence were observed under 977 nm diode laser excitation and the most full width at half-maximum (FWHM) is similar to 60nm. According to absorption spectrum, we calculated the optical parameters by means of Judd-Ofelt and McCumber theory such as the fluorescence lifetimes which are about 2.72-3.25 ms and the maximum emission cross-sections which are similar to 1.0pm(2) at 1.531 mu m. The sigma(e) x FWHM value of composition with 10 mol% BaO for gain bandwidth is similar to 600 exceeding those in silicon and phosphate glasses. Our results indicated this kind of tellurite glasses could be used as an ideal host glass for optical amplifier. (c) 2005 Elsevier B.V. All rights reserved.

Inhomogeneous broadening, luminescence origin and optical amplification in bismuth-doped glass

Absorption and luminescence spectra and optical amplification in bismuth-doped germanate silicate glass were investigated. Two kinds of bismuth ion valence states could exist in the glass. One is Bi2+, which has shown red luminescence, another might be Bi+, which is the active center for infrared luminescence. The infrared luminescence excited at 700, 800, and 980 nm should be ascribed to the electronic transition P-3(1) --> P-3(0) of Bi+ ions in three distinct sites. The shifting, broadening, and multiple configuration of the luminescence could be due to the randomly disorder of local environment and multiple sites of the active centers. In this glass, obvious optical amplification was realized at 1300 nm wavelength when excited at 808 and 980 nm, respectively.

Transparent colloid containing upconverting nanocrystals: An alternative medium for three-dimensional volumetric display

We report an alternative medium of transparent upconverting colloid containing lanthanide ion doped NaYF4 nanocrystals for three-dimensional (3D) volumetric display. The colloids exhibit tunable upconversion luminescence with a wide spectrum of colors by adjusting the doping concentrations of the nanocrystals and the compositions of the colloids. Our preliminary experimental result indicates that an upconverting colloid-based 3D volumetric display using a convergent, near infrared laser beam to induce a localized luminescent spot near the focus is technically feasible. Therefore arbitrary 3D objects can be created inside the upconverting colloid by use of computer controlled 3D scanning systems. (C) 2008 Optical Society of America

Novel Bi-doped glasses for broadband optical amplification

Broadband infrared luminescence is observed in various Bi-doped oxide glasses prepared by conventional melting-quenching technique. The absorption spectrum of the Bi-doped germanium oxide glass consists of five broad peaks at below 370, 500, 700, 800 and 1000 nm. The fluorescence spectrum exhibits a broad peak at about 1300 nm with full width at half maximum (FWHM) of more than 300 nm when excited by an 808 nm laser diode. The fluorescence lifetime at room temperature decreases with increasing Bi2O3 concentration. Influence of the glass composition and melting atmosphere on the fluorescence lifetime and luminescent intensity is investigated. The mechanism of the broadband infrared luminescence is suggested. The product of stimulated emission cross-section and lifetime of the Bi-doped aluminophosphate glass is about 5.0 X 10(-24) cm(2) s. The glasses might be promising for applications in broadband optical fiber amplifiers and tunable lasers. (c) 2007 Elsevier B.V. All rights reserved.

用于波导放大器的Er^3＋／Yb^3＋共掺磷酸盐玻璃的性能研究

通过优化熔融条件和玻璃组份，成功开发出一种新的Er^3+／Yb^3+共掺磷酸盐玻璃，其在沸水和熔盐中均表现出很好的化学稳定性。通过分析室温下Er^3+／Yb^3+共掺磷酸盐玻璃的吸收光谱，计算得到了Er^3+离子在波长1533nm处的峰值发射截面和杜得-奥菲而特强度参数；其中Er^3+离子在波长1533nm处的峰值发射截面为0．72×10^20cm^2，大于Schott的IOG1玻璃中Er^3+离子的峰值发射截面0．67×10^-20cm^2。通过改变离子交换的条件，获得了1．55μm单模光波导的制作条件

KMgF3及KMgF3：Eu^2＋晶体的射线辐照效应

KMgF3F Eu晶体中Eu^3＋→Eu^2＋的转换率在低浓度掺杂时接近100％，完全转换的饱和掺杂摩尔分数为0．29％．实验条件下，KMgF，晶体的X射线1h辐照损伤可在约100h后恢复；KMgF3：Eu^2＋晶体经X射线辐照后，360nm锐峰发射强度略有降低．不同剂量的γ射线辐照，KMgF3晶体热释光曲线的各个温度峰强度变化明显不同，即使小剂量辐照，造成的损伤也较难恢复，如γ射线辐照剂量为10^3Gy时，辐照损伤的恢复时间约需30d．KMgF3：Eu^2＋晶体360nm锐峰发射强度随γ射线辐照剂量增大

不同退火气氛下γ-LiAlO2形貌和结构研究

研究了温度梯度法生长的γ-LiAlO2晶体在1100℃下富Li气氛和空气中退火处理后的表面形貌、表面结构以及吸收光谱。发现γ-LiAlO2晶体的抛光面在1100℃空气中退火后变为粗糙面，X射线衍射(XRD)分析表明此粗糙面为单相的LiAl5O8。而γ-LiAlO2晶体的抛光面在1100℃富Li气氛中处理后几乎没有变化。同时对不同气氛下热处理的γ-LiAlO2晶体进行了光谱分析，确认了晶片中196nm的吸收峰是由Li空位引起的。

新型衬底材料γ-LiAlO2热稳定性研究

研究了温度梯度法生长的γ-LiAlO2晶体在1100℃不同气氛处理的热稳定性。借助扫描电子显微镜和X射线衍射分析发现：1100℃／10h真空和空气处理后的样品表面分别形成了均匀微孔状和岛状LiAl5O8多晶；而富Li气氛处理后样品表面仍然光滑且仍为LiAlO2。用Leitz大视场显微镜观察重新抛光后样品内部宏观缺陷，发现空气和真空处理后样品缺陷增多，分别为岛状和条纹状缺陷；而富Li气氛处理后样品中缺陷明显减少。对比不同气氛处理的4块样品吸收光谱，确认了真空和空气处理产生的196nm吸收峰可能是Li空位吸收

Efficient laser oscillation of Yb : Y3Al5O12 single crystal grown by temperature gradient technique

Low-threshold and highly efficient continuous-wave laser performance of Yb:Y3Al5O12 (Yb:YAG) single crystal grown by a temperature gradient technique (TGT) was achieved at room temperature. The laser can be operated at 1030 and 1049 nm by varying the transmission of the output coupler. Slope efficiencies of 57% and 68% at 1049 and 1030 nm, respectively, were achieved for 10 at. % Yb:YAG sample in continuous-wave laser-diode pumping. The effect of pump power on the laser emission spectrum of both wavelengths is addressed. The near-diffraction-limited beam quality for different laser cavities was achieved. The excellent laser performance indicates that TGT-grown Yb:YAG crystals have very good optical quality and can be potentially used in high-power solid-state lasers.

Optical spectroscopy of Yb3Al5O12 single crystal

Yb3Al5O12 single crystal has been grown by Czochralski (CZ) method. The absorption spectrum was investigated at low temperature and the electronic energy levels for F-2(5/2) multiplet of Yb3+ in YbAG was proposed. The up-conversion emission of the crystal under 940 nm diode pumping and the X-ray excited luminescence (XEL) features of the crystal were also studied. (c) 2005 Elsevier B.V. All rights reserved.

Broadband infrared luminescence of bismuth-doped borosilicate glasses

We prepare bismuth-doped borosilicate glasses and the luminescence properties in infrared wavelength region are investigated. Transmission spectrum, fluorescence spectrum and fluorescence decay curve are measured. The glasses exhibit a broad infrared luminescence peaking at 1340nm with the full width at half maximum of about 205nm, and lifetime of 273 mu s when excited by an 808-nm laser diode. The glasses are promising materials for broadband optical amplifiers and tunable lasers.

Growth and properties of ZnO thin film on beta-Ga2O3(100) substrate by pulsed laser deposition

Zinc oxide (ZnO) thin films were grown on the beta-Ga2O3 (100) substrate by pulsed laser deposition (PLD). X-ray diffraction (XRD) indicated that the ZnO films are c-axis oriented. The optical and electrical properties of the films were investigated. The room temperature Photoluminescence (PL) spectrum showed a near band emission at 3.28 eV with two deep level emissions. Optical absorption indicated a visible exciton absorption at room temperature. The as-grown films had good electrical properties with the resistivities as low as 0.02 Omega cm at room temperature. Thus, beta-Ga2O3 (100) substrate is shown to be a suitable substrate for fabricating ZnO film. (c) 2006 Elsevier B.V. All rights reserved.

Cr^3＋：Al2O3透明多晶陶瓷光谱特性分析

对透光性良好的Cr^3＋：Al2O3透明多晶陶瓷的光谱性能进行了研究，其吸收光谱中吸收峰与单晶红宝石相一致，按吸收光谱和Tanabe-Sugano能级图，算出其晶场强度参数Dq及Racah参数B分别为1792cm^-1，689cm^-1，Dq／B=2．6，陶瓷中Cr^3＋离子所处格位的晶体场强比单晶弱一些，但Cr^3＋：Al2O3透明陶瓷仍属于强场晶体材料；当Cr^3＋掺杂浓度到达0．8wt％时，陶瓷的发射谱仍保持较好的R线发射；随Cr^3＋掺杂浓度的增大，激发峰位发生“红移”．在Cr^3＋：Al2O3透