Gelatin-based protonic electrolyte for electrochromic windows

Proton-conducting gel polymer electrolytes based on gelatin plasticized with glycerol and containing acetic acid were investigated, characterized, and applied to electrochromic window. For glycerol contents varying from 7% to 48%, the conductivity of the uniform and predominantly amorphous gel electrolyte was found to follow a Vogel-Tamman-Fulcher behavior with the temperature. Typically, for the electrolyte chosen to make 7 x 2 cm(2) electrochromic smart window with the configuration: glass/fluor-doped tin oxide (FTO)/WO(3)/gelatin electrolyte/CeO(2)-TiO(2)/FTO/glass and containing 28% of glycerol, the conductivities were found to be of the order of 5 x 10(-5) S/cm at room temperature and 3.6 x 10(-4) S/cm at 80 A degrees C. The device was characterized by spectroelectrochemical techniques and was tested up to 10,000 cycles showing a fast coloring/bleaching behavior, where the coloring process was achieved in 10 s and the bleaching in 2 s. The transmission variation at the wavelength of 550 nm was about 15%. The cyclic voltammograms showed a very good reversibility of the cathodic/anodic processes, and the charge density was about 3.5 mC/cm(2). The memory tests showed that the transmittance in the colored state increased by 8% in 90 min after removing the potential.

Agar-based films for application as polymer electrolytes

New types of polymer electrolytes based on agar have been prepared and characterized by impedance spectroscopy, X-ray diffraction measurements, UV-vis spectroscopy and scanning electronic microscopy (SEMI). The best ionic conductivity has been obtained for the samples containing a concentration of 50 wt.% of acetic acid. As a function of the temperature the ionic conductivity exhibits an Arrhenius behavior increasing from 1.1 x 10(-4) S/cm at room temperature to 9.6 x 10(-4) S/cm at 80 degrees C. All the samples showed more than 70% of transparency in the visible region of the electromagnetic spectrum, a very homogeneous surface and a predominantly amorphous structure. All these characteristics imply that these polymer electrolytes can be applied in electrochromic devices. (C) 2009 Elsevier Ltd. All rights reserved.

Optimization of performances of gelatin/LiBF(4)-based polymer electrolytes by plasticizing effects

Gelatin is a cheap and abundant natural product with very good biodegradation properties and can be used to obtain acetic acid or LiClO(4)-based gel polymer electrolytes (GPEs) with high ionic conductivity and good stability. This article presents results of GPEs obtained by the plasticization of gelatin and addition of LiBF(4), where the optimization of the system was achieved by using a factorial design type 22 with two variables: glycerol and LiBF(4). From this analysis it was stated that the effect of glycerol as a plasticizer on the ionic conductivity results is much more important than the effect obtained by varying the lithium salt content or the effect of the interaction of both variables. Also all the samples were characterized by X-ray diffraction measurements, UV-vis-NIR spectroscopy and scanning electron microscopy (SEM) and impedance spectroscopy. The ionic conductivity results of all analyzed samples as a function of temperature obey predominantly an Arrhenius relationship and the samples are stable up to 160 degrees C. Good conductivity results combined with transparency and good adhesion to the electrodes have shown that gelatin-based GPEs are very promising materials to be used as solid electrolytes in electrochromic devices. (C) 2009 Elsevier Ltd. All rights reserved.

Plasticized pectin-based gel electrolytes

Pectin is a natural polymer present in plants and, as all natural polymers has biodegradation properties. Chemically, pectin is a polysaccharide composed of a linear chain of 1 -> 4 linked galacturonic acids, which is esterified with methanol at 80%. The pectin-based gel electrolytes in a transparent film form were obtained by a plasticization process with glycerol and addition of LiClO(4). The films showed good ionic conductivity results, which increased from 10(-5) S/cm for the samples with 37 wt.% of glycerol to 4.7 x 10(-4) S/cm at room temperature for the sample with 68 wt.% of glycerol. The electrochemical behaviors of the samples were studied by electrochemical impedance spectroscopy (EIS), and Nyquist graphs are showed and discussed. The obtained pectin-based samples also presented good adherence to the glass, flexibility, homogeneity (SEM) and transparency (about 70% in the vis) properties. They are good candidates to be applied as gel electrolytes in electrochromic devices. (C) 2009 Elsevier Ltd. All rights reserved.

Encapsulation of single hMSCs in polyelectrolyte shells

The main objective of this Thesis was to encapsulate single viable cells within polyelectrolyte films using the Layer-by-Layer (LbL) technique. Most of the experiments used human mesenchymal stem cells (MSCs) whose characteristics (capacity of selfrenewal and potential to differentiate into several types of cells) make them particularly interesting to be used in biomedical applications. Also, most of the experiments used alginate (ALG) as the anionic polyelectrolyte and chitosan (CHI) or poly(allylamine hydrochloride) (PAH) as the cationic polyelectrolyte. Hyaluronic acid (HA) was also tested as an anionic polyelectrolyte. At the beginning of the work, the experimental conditions necessary to obtain the encapsulation of individual cells were studied and established. Through fluorescence microscopy visualization by staining the cell nucleus and using polyelectrolytes conjugated to fluorescent dyes, it was possible to prove the obtainment of capsules containing one single cell inside. Capsules aggregation was an observed problem which, despite the efforts to design an experimental process to avoid this situation (namely, by playing with cell concentration and different means of re-suspending and stirring the cells), was not completely overcome. In a second part of the project, single cells were encapsulated within polyelectrolyte layers made of CHI/ALG, PAH/ALG and PAH/HA and their viability was evaluated through the resazurin reduction assay and the Live/Dead assay. In these experiments, during the LbL process, polyelectrolyte solutions were used at a concentration of 1mg/mL based on literature. In general, the viability of the encapsulated cells was shown to be very low/absent. Then, as a consequence of the lack of viability of cells encapsulated within polyelectrolyte layers, the LbL technique was applied in cells growing adherent to the surface of cell culture plates. The cells were cultured like in a sandwich, between the surface of the cell culture dish and the polyelectrolyte layers. Also here, the polyelectrolyte solutions were used at a concentration of 1mg/mL during the LbL process. Surprisingly, cell viability was also absent in these systems. A systematic study (dose-effect study) was performed to evaluate the effect of the concentration of the individual polyelectrolytes (ALG, CHI and PAH were studied) in cell viability. Experiments were performed using cells growing adherent to the surface of cell culture plates. The results pointed out that a very high (cytotoxic) concentration of polyelectrolytes had been in use. Also, in general, PAH was much more cytotoxic than CHI, whereas ALG was the less cytotoxic polyelectrolyte. Finally, using alginate and chitosan solutions with adequate concentrations (low concentrations: 50ng/mL and 1μg/mL), the encapsulation of single viable cells was again attempted. Once again, the encapsulated cells were not shown to be viable. In conclusion, the viability of the encapsulated cells is not only dependent on the cytotoxic characteristics (or combined cytotoxic characteristics) of the polyelectrolytes but it seems that, when detached from the culture plates, the cells become too fragile and lose their viability very easily.

Gene delivery using dendrimer/pDNA complexes immobilized in electrospun fibers using the layer-by-layer technique

Tissue engineering is an important branch of regenerative medicine that uses cells, materials (scaffolds), and suitable biochemical and physicochemical factors to improve or replace specific biological functions. In particular, the control of cell behavior (namely, of cell adhesion, proliferation and differentiation) is a key aspect for the design of successful therapeutical approaches. In this study, poly(lactic-co-glycolic acid) (PLGA) fiber mats were prepared using the electrospinning technology (the fiber diameters were in the micrometer range). Furthermore, the electrospun fiber mats thus formed were functionalized using the layer-by- layer (LbL) technique with chitosan and alginate (natural and biodegradable polyelectrolytes having opposite charges) as a mean for the immobilization of pDNA/dendrimer complexes. The polyelectrolyte multilayer deposition was confirmed by fluorescence spectroscopy using fluorescent-labeled polyelectrolytes. The electrospun fiber mats coated with chitosan and alginate were successfully loaded with complexes of pDNA and poly(amidoamine) (PAMAM) dendrimers (generation 5) and were able of releasing them in a controlled manner along time. In addition, these mats supported the adhesion and proliferation of NIH 3T3 cells and of human mesenchymal stem cells (hMSCs) in their surface. Transfection experiments using a pDNA encoding for luciferase showed the ability of the electrospun fiber mats to efficiently serve as gene delivery systems. When a pDNA encoding for bone morphogenetic protein-2 (BMP-2) was used, the osteoblastic differentiation of hMSCs cultured on the surface of the mats was promoted. Taken together, the results revealed that merging the electrospinning technique with the LbL technique, can be a suitable methodology for the creation of biological active matrices for bone tissue engineering.

Produção de enzimas quitosanolíticas utilizando Paenibacillus ehimensis e Paenibacillus chitinolyticus para obtenção de quitoologossacarídeos

The acquisition of oligosaccharides from chitosan has been the subject of several studies in the pharmaceutical, biochemical, food and medical due to functional properties of these compounds. This study aimed to boost its production of chitooligosaccharides (COS) through the optimization of production and characterization of chitosanolytic enzymes secreted by microorganisms Paenibacillus chitinolyticus and Paenibacillus ehimensis, and evaluating the antioxidant potential of the products obtained. In the process of optimizing the production of chitosanase were employed strategies Fractional Factorial Experimental Design and Central Composite Rotatable Design. The results identified the chitosan, peptone and yeast extract as the components that influenced the production of chitosanase by these microorganisms. With the optimization of the culture media was possible to obtain an increase of approximately 8.1 times (from 0.043 to 0.35 U.mL U.mL-1) and 7.6 times (from 0.08 U.mL-1 to 0.61 U.mL-1) in the enzymatic activity of chitosanase produced by P. chitinolyticus and P. ehimensis respectively. Enzyme complexes showed high stability in temperature ranges between 30º and 55º C and pH between 5.0 and 9.0. Has seen the share of organic solvents, divalent ions and other chemical agents on the activity of these enzymes, demonstrating high stability of these crude complexes and dependence of Mn2+. The COS generated showed the ability of DPPH radical scavenging activity, reaching a maximum rate of scavenging of 61% and 39% when they were produced with enzymes of P. ehimensis and P. chitinolyticus respectively. The use of these enzymes in raw form might facilitate its use for industrial applications

Produção e caracterização de quitooligossacarídeos produzidos pelo fungo Metarhizium anisopliae e avaliação da citotoxicidade em células tumorais

Chitosan is a natural polymer, biodegradable, nontoxic, high molecular weight derived from marine animals, insects and microorganisms. Oligomers of glucosamine (GlcN) and N-acetylglucosamine (GlcNAc) have interesting biological activities, including antitumor effects, antimicrobial activity, antioxidant and others. The alternative proposed by this work was to study the viability of producing chitooligosaccharides using a crude enzymes extract produced by the fungus Metarhizium anisopliae. Hydrolysis of chitosan was carried out at different times, from 10 to 60 minutes to produce chitooligosaccharides with detection and quantification performed by High Performace Liquid Chromatography (HPLC). The evaluation of cytotoxicity of chitosan oligomers was carried out in tumor cells (HepG2 and HeLa) and non-tumor (3T3). The cells were treated for 72 hours with the oligomers and cell viability investigated using the method of MTT. The production of chitosan oligomers was higher for 10 minutes of hydrolysis, with pentamers concentration of 0.15 mg/mL, but the hexamers, the molecules showing greater interest in biological properties, were observed only with 30 minutes of hydrolysis with a concentration of 0.004 mg/mL. A study to evaluate the biological activities of COS including cytotoxicity in tumor and normal cells and various tests in vitro antioxidant activity of pure chitosan oligomers and the mixture of oligomers produced by the crude enzyme was performed. Moreover, the compound with the highest cytotoxicity among the oligomers was pure glucosamine, with IC50 values of 0.30; 0.49; 0.44 mg/mL for HepG2 cells, HeLa and 3T3, respectively. Superoxide anion scavenging was the mainly antioxidant activity showed by the COS and oligomers. This activity was also depending on the oligomer composition in the chitosan hydrolysates. The oligomers produced by hydrolysis for 20 minutes was analyzed for the ability to inhibit tumor cells showing inhibition of proliferation only in HeLa cells, did not show any effect in HepG2 cells and fibroblast cells (3T3)

Estudo da permeação em membranas quitosana

This study proposes to do a study on the mathematical modeling of permeation of films based on chitosan. To conduct the study were obtained membranes with various compositions: a virtually pure membrane-based chitosan; one of chitosan associated with poly (ethylene oxide (PEO). The membranes of pure chitosan were treated with plasma in atmospheres of oxygen, argon and methane. The various types of films were characterized as to its permeation regarding sufamerazina sodium. In the process of mathematical modeling were compared the standard method of obtaining the coefficient of permeation recital straight down the slope of the plot obtained by extinction / time with a the integration process of numerical permeability rate will be calculated from the spectroscopy UV

Modificação de membranas de quitosana por plasma para uso biológico

Chitosan membranes have been modified by plasma, utilizing the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen. The modified membranes by plasma were compared to the unmodified ones. The membranes were characterized by absorption assay, contact angle, atomic force microscopy (AFM). Also, permeability assay of sodium sulfamerazine from such membranes were carried out. Through the absorption assay and contact angle it was possible to obtain information of the wettability of the membranes and what changes the plasma treatment can promote in relation to it. The plasma treatment using oxygen promoted increase of the wetability and swelling while the samples treated with methane decrease of the wetability and swelling. Through the Optical Emission Spectroscopy (OES) it was possible to identify which species were present in the plasma during the treatment. And through the AFM analysis it was possible to observe the changes nanotopography occurred on the surface of the samples. Permeability assay were archived for all treated membranes and compared to no treated ones. Due to that assay it was possible verify which the plasma treatment increased the permeability spectrum of the membranes which has varied from 1,4548 *10-5cm2.min-1 to 2,7713*10-5cm2.min-1. Chitosan membranes with permeability varied are importance in systems drug delivery, to liberate a wide variety of drugs

Formulação de pastas cimentícias com adição de suspensões de quitosana para cimentação de poços de petróleo

Primary cementing is one of the main operations in well drilling responsible for the mechanical stability and zonal isolation during the production of oil. However, the cement sheath is constantly under mechanical stresses and temperature variations caused by the recovery of heavy oil. In order to minimize fracture and wear of the cement sheath, new admixtures are developed to improve the properties of Portland cement slurries and avoid environmental contamination caused by leaking gas and oil. Polymers with the ability to form polymeric films are candidates to improve the properties of hardened cement slurries, especially their fracture energy. The present study aimed at evaluating the effect of the addition of a chitosan suspension on cement slurries in order to improve the properties of the cement and increase its performance on heavy oil recovery. Chitosan was dissolved in acetic ac id (0.25 M and 2 M) and added to the formulation of the slurries in different concentrations. SEM analyses confirmed the formation of polymeric films in the cementitious matrix. Strength tests showed higher fracture energy compared to slurries without the addition of chitosan. The formation of the polymeric films also reduced the permeability of the slurry. Therefore, chitosan suspensions can be potentially used as cementing admixtures for heavy oil well applications

Utilização de nanosílica como aditivo estendedor para pastas cimentantes de baixa densidade destinadas à cimentação de poços petrolíferos

Cementing operations are conducted at different times of the well s life and they have high importance, because the functions are fundamental to keep good properties during a long life of the well, such as, maintain the mechanical stability of the well, to promote the isolation hydraulic and support the tubing. In some situations, the rocky zones have low fractures pressures and require the use of lightweight slurries to prevent the hydrostatic pressure in the formation is greater than the pressure of fracture. There are three ways to reduce the density of cement slurries: exterders water additives, microspheres and foamed slurries. The most used extender water additive is sodium bentonite, which is a clay with a good capacity of water absorption and expansion of its volume, the main disadvantage of this additive is the reduction of the strength. Currently, the use of nanoscale particles has received special attention, mainly because they get new functionalities. Following this trend, this paper aims to use a colloidal solution of nano-silica as an exterders water additives for use in oil wells. Slurries were designed with fixed 13lb/gal density and concentration of nano silica 0.1 gpc; 0.4 gpc; 0.7 and 1gpc, the influence of nano-silica was studied at these levels in isolation and combined varying concentrations of CaCl2,. Tests including rheology, stability, strength, thickening time, porosity and permeability. Besides the API tests, microstructural characterizations were performed after 28 days of the slurries, X-ray diffraction (XRD) and scanning electron microscopy (SEM)

Efeito do tratamento por plasma na proliferação de fibroblastos e esterilização de membranas de quitosana

Chitosan is being studied for use as dressing due their biological properties. Aiming to expand the use in biomedical applications, chitosan membranes were modified by plasma using the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen (H2). The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle, surface energy and water absorption test. Biological Tests were also performed, such as: test sterilization and proliferation of fibroblasts (3T3 line). Through SEM we observed morphological changes occurring during the plasma treatment, the formation of micro and nano-sized valleys. MFA was used to analyze different roughness parameters (Ra, Rp, Rz) and surface topography. It was found that the treated samples had an increase in surface roughness and sharp peaks. Methane plasma treatment decreased the hydrophilicity of the membranes and also the rate of water absorption, while the other treatments turned the membranes hydrophilic. The sterilization was effective in all treatment times with the following gases: Ar, N2 and H2. With respect to proliferation, all treatments showed an improvement in cell proliferation increased in a range 150% to 250% compared to untreated membrane. The highlights were the treatments with Ar 60 min, O2 60 min, CH4 15 min. Observing the results of the analyzes performed in this study, it appears that there is no single parameter that influences cell proliferation, but rather a set of ideal conditions that favor cell proliferation

Formulação e caracterização de pastas espumadas por incorporação de ar e estabilizantes minerais

Cementing operations may occur at various stages of the life cycle of an oil well since its construction until its definitive abandonment. There are some situations in which the interest zones are depleted or have low fracture pressure. In such cases, the adoption of lowdensity cement slurries is an efficient solution. To this end, there are basically three ways to reduce the density of cement slurries: using microspheres, water extending additives or foamed cement. The objective of this study is to formulate, to study and to characterize lowdensity foamed cement, using an air entrainment surfactant with vermiculite or diatomite as water extenders and stabilizers. The methodology consists on preparation and evaluation of the slurries under the American Petroleum Institute (API) and the Brazilian Association of Technical Standards (ABNT) guidelines. Based on calculated densities between 13 and 15 ppg (1.559 and 1.799 g/cm3), the slurries were prepared with fixed surfactant concentration, varying the concentrations of vermiculite and diatomite and were compared with the base slurries. The results of plastic viscosity, yield point and gel strength and the compressive strength for 24 h showed that the slurries presented suitable rheology and mechanical strength for cementing operations in oil wells, and had their densities reduced between 8.40 and 11.89 ppg (1.007 and 1.426 g/cm3). The conclusion is that is possible, under atmospheric conditions, to obtain light weighted foamed cement slurries with satisfactory rheological and mechanical properties by means of air entrainment and mineral additions with extenders and stabilizers effects. The slurries have great potential for cementing operations; applicability in deep wells, in low fracture gradient formations and in depleted zones and bring cost savings by reducing the cementing consumption

Nanopartículas de alginato como sistema de liberação para o herbicida clomazone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)