Effect of Ta2O5 doping on the electrical properties of 0.99SnO(2)center dot 0.01CoO ceramic

The effect of Ta2O5 doping in 0.99SnO(2). 0.01CoO on the microstructure and electrical properties of this ceramic were analyzed in this study. The grain size was found to decrease from 6.87 mu m to 5.68 mu m when the Ta2O5 concentration increased from 0.050 to 0.075 mol%. DC electrical characterization showed a dramatic increase in the current loss and decrease in the non-linear coefficient with the increase of the Ta2O5 concentration. The conduction mechanism is by thermionic emission and the potential barriers are of Schottky type, separated by a thin film. (C) 2000 Kluwer Academic Publishers.

Effect of Fe2O3 doping on the electrical properties of a SnO2 based varistor

The effect of Fe2O3 addition on the densification and electrical properties of the (0.9895 - x) SnO2 + 0.01CoO + 0.005Nb(2)O(5) + xFe(2)O(3) system, where x = 0.005 or 0.01, was considered in this study. The samples were sintered at 1300degreesC for 2 h. Microstructure analysis by scanning electron microscopy showed that the effect of Fe2O3 addition is to decrease the SnO2 grain size. J x E curves indicated that the system exhibit a varistor behavior and the effect of Fe2O3 is to increase both, the non-linear coefficient (alpha) and the breakdown voltage (E-r). Considering the Schottky thermionic emission model the potential height and width were estimated. Small amount addition of Fe2O3 to the basic system increases both the potential barrier height and width. (C) 2002 Kluwer Academic Publishers.

Mapping QTLs for aluminum tolerance in maize

Aluminum toxicity is one of the major constraints for plant development in acid soils, limiting food production in many countries. Cultivars genetically adapted to acid soils may offer an environmental compatible solution, providing a sustainable agriculture system. The aim of this work was to identify genomic regions associated with Al tolerance in maize, and to quantify the genetic effects on the phenotypic variation. A population of 168 F-3:4 families derived from a cross between two contrasting maize inbred lines for Al tolerance was evaluated using the NSRL and RSRL parameters in nutrient solution containing toxic level of aluminum. Variance analyses indicated that the NSRL was the most reliable phenotypic index to measure Al tolerance in the population, being used for further QTL mapping analysis. RFLP and SSR markers were selected for bulked segregant analysis, and additional SSR markers, flanking the polymorphisms of interest, were chosen in order to saturate the putative target regions. Seven linkage groups were constructed using 17 RFLP and 34 SSR markers. Five QTLs were mapped on chromosomes 2, 6 and 8, explaining 60% of the phenotypic variation. QTL(4) and marker umc043 were located on chromosomes 8 and 5, close to genes encoding for enzymes involved in the organic acids synthesis pathways, a widely proposed mechanism for Al tolerance in plants. QTL(2) was mapped in the same region as Alm2, also associated with Al tolerance in maize. In addition, dominant and additive effects were important in the control of this trait in maize.

The effect of EU3+ ion doping concentration in Gd2O3 fine spherical particles

This work reports on the preparation of Gd2O3, cubic system, with spherical particles, narrow size distribution, whether or not doped with 1-5 at.% of Eu3+ and the influence of Eu3+ concentration on optical and morphological properties. Average diameter and size distribution particle analyses were performed for all samples from SEM results. Doped samples were also investigated by luminescence spectroscopy and emission kinetic measurements. All oxide samples present a particle average diameter distribution range from 110 to 150 nm and a decrease of particle average diameter with the presence of Eu3+. The particle size decrease is almost the same for all samples with different doping ion concentration. Therefore, the presence of doping ion may be inhibiting particle growth after the nucleation process. From spectroscopic studies, the doping ion distribution in the surface of oxide samples can be considered homogeneous because concentration quenching is not observed, as well as a significant difference among the calculated lifetime for each sample. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Influence of Zn2+ co-doping ion on Eu3+-O2- associate luminescence in Sr2SiO4

This work reports on the study about the luminescence behavior of Eu3+-O2- associates in Sr2SiO4 doped with Eu3+, or simultaneously doped with Eu3+ and Zn2+ ions, where the Zn2+ doping ion acts as a charge compensating agent. Both Sr2SiO4:Eu3+ and Sr2SiO4:Eu3+,Zn2+ emission spectra show two types D-5(0)-->F-7(0) type transitions, one type related to Eu3+ in the Sr2+ Site, at 577 and 580 nm and the other one related to Eu3+-O2- associates, at 574 nm. Excitation spectra present two CT bands at 275 and 324 nm related to each emission center, respectively. Comparing the relative intensities between the emission spectra, the 0-->0 transition at 574 nm assigned to Eu3+-O2- associates in the Sr2SiO4:Eu3+ emission spectrum is much more intense than the same transition in the Sr2SiO4:Eu3+,Zn2+ emission spectrum. Moreover, in the Sr2SiO4:Eu3+ excitation spectrum, the intensity ratio between the CT band related to the Eu3+-O2- emission center and Eu3+ F-7-->L-5(6) transition is also larger than in the Sr2SiO4:Eu3+,Zn2+ one. Therefore, the presence of Zn2+ species provides an extra charge compensating mechanism, which decreases the formation of Eu3+-O2- associates. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Study of Ti-modified columbite route and the effect of lithium doping in 0.9PMN-0.1PT ceramics

The influence of lithium on the structural characteristics of PMN-PT ceramic was studied. The synthesis of PMN-PT powders using this precursor leads to the formation of high amount of perovskite phase. The insertion of Li(+) ions in B-site affects the microstructure because the rise in mass transport changes the mechanical characteristics of sintered ceramic. Higher values of K(m) and T(m) were gotten when lithium is inserted into perovskite phase. Secondary phase was found when lithium content increase beyond 1 mol%, besides the occurrence of transgranular fractures in sintered ceramic. Also, the additive acts increasing the relaxor behavior.

Magnetic doping in Zn7-xMxSb2O12 spinels (M = Ni and Co)

In this article we present a concise report on our studies on the magnetic behavior and structural arrangements of the inverse spinel Zn7-xMxSb2O12 system (M = Ni, Co). Studies on the temperature dependence of the magnetization (M) of several samples in this system showed the occurrence of a spin-glass-like state in temperatures around 10 K. The capability of this system to hold magnetic ions in either octahedral and/or tetrahedral positions is responsible for the occurrence of competing ferromagnetic and antiferromagnetic interactions. This condition is likely to cause the appearance of the observed spin-glass-like behavior. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Mullite whiskers grown from erbia-doped aluminum hydroxide-silica gel

Mullite whiskers and anisotropic grains that were derived from erbia-doped aluminum hydroxide-silica gel were studied. Firing 3.0-mol%-erbia-doped isostatically pressed pellets at 1600 degrees C for 1.0-8.0 h resulted in a high surface concentration of mullite whiskers. Their c-axes were aligned preferentially along the pellet surface; the maximum length was 50 mu m, and the maximum aspect ratio was 23. The pellet surface was fully covered by mullite whiskers, and small anisotropic grains with a low aspect ratio were observed in the bulk. The voids that were observed in the fracture surfaces were covered fully by mullite whiskers. The large number of voids resulted in an apparent density of 1.60 g/cm(3) in the sintered pellets. The molar ratio of alumina to silica in the whiskers was in the range of 1.30-1.45 tan average value of 1.31), regardless of whether the alumina/silica powder compositions were mixed in a 3:2 or 2:1 ratio.

Mutagenic activity in waste from an aluminum products factory in Salmonella/microsome assay

The mutagenic activity of waste material originating from an aluminum products factory was determined by the Salmonella/microsome assay, using the bacterial strains TA100, TA98 and YG1024. The material was obtained by sweeping the factory floor at the end of the work shift. Organic compounds were extracted by ultrasound for 30 min in dichloromethane or 70% ethanol. After evaporation of solvent, these extracts were dissolved in dimethylsulfoxide, and tested for the mutagenic activity at varying concentrations. All the extracts from the factory had mutagenic activity, especially in the YG1024 strain, suggesting the presence of aromatic amines, later confirmed by chemical analysis. The TA98 strain also showed mutagenic activity, though it did not exhibit the highest mutagenicity index observed with the YG1024 strain. In TA100, mutagenic activity was not observed. This study should serve as an alert to management and those who are occupationally exposed, and as a warning that this type of waste should not be discarded in the environment without any control. (C) 2004 Elsevier Ltd. All rights reserved.

INHIBITION OF BOVINE BRAIN ACETYLCHOLINESTERASE BY ALUMINUM

We report the in vitro inhibitory effect of very low concentrations of aluminum salts (IC50 = 4.1 X 10(-12)M) on bovine brain acetylcholinesterase (AChE). The enzymatic assays were performed using acetylcholine bromide in a buffered pH 7.4 solution at 37 degrees C. The relevant enzyme interacting species is the Al3+ ion, whose concentrations were fixed at pM levels by a citrate metal ion buffer system. The IC50 demonstrates that Al3+ is a potent inhibitor of AChE.

Zeta potential and doping in polyaniline dispersions

Polyaniline (PAni) has been classified as an intractable polymer, particularly in its conducting form, the emeraldine salt (ES). Therefore one can consider the mixture of water and PAni as a suspension. The conducting form of PAni can be obtained by a doping process known as acid doping, in which a strong acid turns PAni from its insulating form, the emeraldine base (EB), into the conducting form, the emeraldine salt. With the objective of establishing a correlation between the doping level and the zeta potential of polyaniline dispersions, polyaniline + HCl aqueous suspensions were prepared. Positive zeta potential values for the various suspensions of PAni showed that it acquired positive charges after the doping process. It was also observed an increase in zeta potential values as HCl concentration increased, which could be correlated to UV-visible spectra of PAni suspensions.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Improvement of the corrosion resistance of polysiloxane hybrid coatings by cerium doping

Polysiloxane hybrid films were deposited on stainless steel by dip-coating using a sol prepared by hydrolytic co-polycondensation of tetraethoxysilane (TEOS) and 3-methacryloxy propyltrimethoxysilane (MPTS), followed by radical polymerization of methacrylic moieties. The TEOS/MPTS ratio was chosen equal to 2 and the Ce/Si ratio varied between 0.01 and 0.1. The effects of cerium concentration and valence (Ce(III) and Ce (IV)) on the structural features of polysiloxane films were studied by X-ray photoelectron spectroscopy (XPS) and (29)Si nuclear magnetic resonance (NMR). The corrosion protection of stainless steel by the hybrid coatings was investigated by XPS, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves, after immersion in saline and acid solutions. The NMR results have shown for Ce(IV) doped films a high degree of polycondensation of up to 89%. Electrochemical analysis has evidenced that hybrid films with the lowest Ce concentration act as an efficient diffusion barrier by increasing the corrosion resistance and reducing the current densities up to 3 orders of magnitude compared to bare stainless steel. The analysis of structural effects induced by Ce(III) and Ce(IV) species, performed by XPS, indicates that the improved corrosion protection of Ce(IV) doped films might be mainly related to the enhanced polymerization of siloxane groups. (C) 2010 Elsevier B.V. All rights reserved.