Study on nanohardness of helium-implanted 4H-SiC

The hardness of 4H-SiC, which was high-temperature (500 K) helium-Implanted to fluences of 3 x 10(16) Ions cm(-2) and subsequently thermally annealed at the temperature ranging from 773 to 1273 K, was studied by nanoindentation It is found that the hardness of the implanted 4H-SiC increases at the first, then decreases, and then increases again with increasing annealing tempeature in the temperature range of 500-1273 K, and significant increase in hardness is observed at 773 K. The behavior is ascribed to the changes of the density, length, and tangling of the covalent Si-C bond through the recombination of point defects, clustering of He-vacancy, and growth of helium bubbles during the thermal annealing

Structural and optical properties of 6H-SiC helium-implanted at 600 K

Single crystals of 6H-SiC were implanted at 600 K with 100 key He ions to three successively fluences and subsequently annealed at different temperatures ranging from 873 to 1473 K in vacuum. The recovery of lattice damage was investigated by different techniques including Rutherford backscattering spectrometry in channeling geometry, Raman spectroscopy and Fourier transform infrared spectroscopy. All three techniques showed that the damage induced by helium ion implantation in the lattice is closely related to the fluence. Rutherford backscattering spectrometry/channeling data on high temperature implantations suggest that for a fluence of 3 x 10(16) He+/cm(2), extended defects are created by thermal annealing to 1473 K. Apart from a well-known intensity decrease of scattering peaks in Raman spectroscopy it was found that the absorbance peak in Fourier transform infrared spectroscopy due to the stretching vibration of Si-C bond shifted to smaller wave numbers with increasing fluence, shifting back to larger wave numbers with increasing annealing temperature. These phenomena are attributed to different lattice damage behavior induced by the hot implantation process, in which simultaneous recovery was prevailing. (C) 2010 Elsevier B.V. All rights reserved.

Enhanced nucleation of Ag nanoparticles by vacancy-type defects in Ar-ions implanted spinel

Vacancy-type defects are introduced into magnesium aluminate spine] (MgAl2O4 (1 1 0)) by Ar-ions implantation, and then Ag-ions are implanted into the depth rich in vacancy-type defects. The ultraviolet-visible spectrometry (UV-VIS) and positron annihilation spectroscopy (PAS) are used to study the influence of vacancy-type defects on nucleation of Ag nanoparticles. After introduction of vacancy-type defects the pronounced increase of surface plasmon resonance (SPR) absorbance intensity indicates that defects enhance the nucleation of Ag nanoparticles. The PAS results reveal that vacancy-type defects provide pre-nucleating centers for Ag nanoparticles nucleation and growth. (C) 2010 Elsevier B.V. All rights reserved.

Color center formation in silica glass induced by high energy Fe and Xe ions

Silica glass samples were implanted with 1.157 GeV Fe-56 and 1.755 GeV Xe-136 ions to fluences range from 1 x 10(11) to 3.8 x 10(12) ions/cm(2). Virgin and irradiated samples were investigated by ultraviolet (UV) absorption from 3 to 6.4 eV and photoluminescence (PL) spectroscopy. The UV absorption investigation reveals the presence of various color centers (E' center, non-bridging oxygen hole center (NBOHC) and ODC(II)) appearing in the irradiated samples. It is found that the concentration of all color centers increase with the increase of fluence and tend to saturation at high fluence. Furthermore the concentration of E' center and that of NBOHC is approximately equal and both scale better with the energy deposition through processes of electronic stopping, indicating that E' center and NBOHC are mainly produced simultaneously from the scission of strained Si-O-Si bond by electronic excitation effects in heavy ion irradiated silica glass. The PL measurement shows three emissions peaked at about 4.28 eV (alpha band), 3.2 eV (beta band) and 2.67 eV (gamma band) when excited at 5 eV. The intensities of alpha and gamma bands increase with the increase of fluence and tend to saturation at high fluence. The intensity of beta band is at its maximum in virgin silica glass and it is reduced on increasing the ions fluence. It is further confirmed that nuclear energy loss processes determine the production of alpha and gamma bands and electronic energy loss processes determine the bleaching of beta band in heavy ion irradiated silica glass. (c) 2009 Elsevier B.V. All rights reserved.

predicting upgrade project defects based on enhancement requirements: an empirical study

Chinese Acad Sci, ISCAS Lab Internet Software Technologies