Magnetic field dependent magnetization of a conducting plasticized poly(aniline) film

We report magnetic data of free standing films of poly( aniline) (PANI) protonated with a plasticizing di-ester of succinic acid. The data have been obtained using the electron spin resonance (ESR) technique at two different frequencies, X-band (9.4 GHz) and Q-band ( 34 GHz), on one hand, and by magnetization measurements in broad ranges of temperatures and magnetic fields on the other hand. All the data can be explained assuming a transition as a function of temperature from delocalized magnetic moments in the valence band to localized positive polarons in several antiferromagnetically correlated bands. By increasing the magnetic field, the magnetic properties are affected in several ways. An intra-band admixture of states occurs; it contributes to increase the spins' localization and finally promotes an antiferromagnetic-metamagnetic transition.

Impedance spectroscopy analysis of TiO(2) thin film gas sensors obtained from water-based anatase colloids

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of the fluorination of DLC film on the corrosion protection of aluminum alloy (AA 5052)

It is presented a study conducted on the physical and electrochemical properties of fluorinated a-C:H films deposited onto a commercial aluminum alloy (AA 5052). The coatings were deposited from mixtures of 91% of acetylene and 9% of argon by plasma immersion ion implantation and deposition technique, PIIID. Total gas pressure was 44 Pa and deposition time (t(dep)) was varied from 300 to 1200 s. The depositing plasmas were generated by the application of radiofrequency power (13.56 MHz, 100W) to the upper electrode and high voltage negative pulses (2400 V. 300 Hz) to the sample holder. Fluorine was incorporated in a post-deposition plasma treatment (13.56 MHz, 70W, 13 Pa) generated from sulfur hexafluoride atmosphere. Chemical structure and composition of the films were investigated using infrared reflectance/absorbance spectroscopy and X-ray photoelectron spectroscopy. The corrosion resistance of the layers was determined by electrochemical impedance spectroscopy (EIS) in a 3.5% NaCl solution, at room temperature. Films presented good adhesion to the substrates and are classified as hydrogenated amorphous carbon (a-C:H) with oxygen traces. Fluorine was detected in all the samples after the post-deposition treatment being its proportion independent on the deposition time. Film thickness presented different tendencies with t(dep), revealing the variation of the deposition rate as a function of the deposition time. Such fluorinated a-C:H films improved the corrosion resistance of the aluminum surface. In a general way the corrosion resistance was higher for films prepared with lower deposition times. The variation of sample temperature with t(dep) was found to be decisive for the concentration of defects in the films and, consequently, for the performance of the samples in electrochemical tests. Results are interpreted in terms of the energy delivered to the growing layer by ionic bombardment. (C) 2010 Elsevier B.V. All rights reserved.

Electrooxidation and determination of dopamine using a Nafion (R)-cobalt hexacyanoferrate film modified electrode

The electrocatalysis of dopamine has been studied using a cobalt hexacyanoferrate film (CoHCFe)-modified glassy carbon electrode. Using a rotating disk CoHCFe-modified electrode, the reaction rate constant for dopamine was found to be 3.5 x 105 cm(3) mol(-1) s(-1) at a concentration of 5.0 x 10(-5) mol L-1. When a Nafion (R) film is applied to the CoHCFe-modified electrode surface a high selectivity for the determination of dopamine over ascorbic acid was obtained. The analytical curve for dopamine presented linear dependence over the concentration range from 1.2 x 10(-5) to 5.0 x 10(-4) mol L-1 with a slope of 23.5 mA mol(-1) L and a linear correlation coefficient of 0.999. The detection limit of this method was 8.9 x 10(-6) mol L-1 and the relative standard deviation for five measurements of 2.5 x 10(-4) mol L-1 dopamine was 0.58%.

Study of the Electrochemical Behavior of Histamine Using a Nafion (R)-Copper(II) Hexacyanoferrate Film-Modified Electrode.

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

HMDSO plasma polymerization and thin film optical properties

Thin films were deposited from hexamethyldisiloxane (HMDSO) in a glow discharge supplied with radiofrequency (rf) power. Actino-metric optical emission spectroscopy was used to follow trends in the plasma concentrations of the species SiH (414.2 nm), CH (431.4 nm), CO (520.0 nm), and H (656.3 nm) as a function of the applied rf power (range 5 to 35 W). Transmission infrared spectroscopy (IRS) was employed to characterize the molecular structure of the polymer, showing the presence of Si-H, Si-O-Si, Si-O-C and C-H groups. The deposition rate, determined by optical interferometry, ranged from 60 to 130 nm/min. Optical properties were determined from transmission ultra violet-visible spectroscopy (UVS) data. The absorption coefficient α, the refractive index n, and the optical gap E04 of the polymer films were calculated as a function of the applied power. The refractive index at a photon energy of 1 eV varied from 1.45 to 1.55, depending on the rf power used for the deposition. The absorption coefficient showed an absorption edge similar to other non-crystalline materials, amorphous hydrogenated carbon, and semiconductors. For our samples, we define as an optical gap, the photon energy E04 corresponding to the energy at an absorption of 104 cm-1. The values of E04 decreased from 5.3 to 4.6 as the rf power was increased from 5 to 35 W. © 1995.

Analytical chemistry in a liquid film/droplet

The measurement of nitrogen dioxide at the parts-perbillion level is described. The experimental arrangement consists of two optical fibers placed on opposite sides of and in contact with a liquid film (14-57 μL in volume) supported on a U-shaped wire guide and two tubular conduits (one of which constitutes the means for the delivery of the liquid), light from a green (555 nm) light-emitting diode enters the liquid film, composed of Griess-Saltzman reagent. The transmitted light is measured by a referenced photodetection arrangement. Sample gas flows past the droplet at a low flow rate (typically 0.10-0.25 L/min). The response is proportional to the sampling period and the analyte concentration. The limit of detection for this nonoptimized arrangement is estimated to be <10 ppb by volume for a 5 min sample. Some unusual characteristics are observed. The initial absorbance, when most of the analyte/reaction product is still near the surface, is higher than that when the content of the droplet is fully mixed. The signal depends on the sample flow rate in a nonmonotonic fashion, first increasing and then decreasing with increasing sampling rate; the specific chemistry involved in the collection and determination of NO2 may be responsible.

Shelf life extension of individually film-wrapped mangoes

Mangoes cv. Keitt were individually sealed in a heat-shrinkable polyolefin film (D-955) and a low-density polyethylene film (LDPE), stored for 0-5 weeks at 12°C and 17°C, and then ripened unwrapped at 22°C. Weight loss of packaged mangoes was significantly lower than that of the non-wrapped control. A sensory panel ranked the mangoes for overall eating quality and appearance. D-955 and LDPE film-sealed mangoes and control had shelf lives of 33, 15 and 7 days at 12°C and 17,10 and 7 days at 17°C, respectively.

Dosimetry and cost of imaging osseointegrated implants with film-based and computed tomography

Thermoluminescent dosimeters were used to measure radiation doses at craniofacial sites in a tissue-equivalent phantom during film-based multidirectional tomography with the Tomax Ultrascan (Incubation Industries, Ivyland, Pa.) and during computed tomography with the Elscint Excel 2400 (Elscint Corp., Tel Aviv, Israel). Mean absorbed doses for presurgical mandibular and maxillary canine and molar implant assessments were converted to equivalent doses, which were then multipied by published weighting factors and summed to give effective doses. The computed tomgraphy device consistently delivered higher doses than the Tomax Ultrascan to all anatomic locations; the differences were most pronounced when only one or two implant sites were evaluated. The reasons for the dose disparities are considered both anatomically and procedurally. A survey of examination cost revealed film-based multidirectional tomography to be less expensive than computed tomography.

Approximate solution for non-Darcy transient film condensation in a porous medium

The problem of non-darcian transient film condensation adjacent to a vertical flat plate embedded in a porous medium has been considered. The governing equation for the boundary layer thickness was obtained by an integral method and solved approximately by the method of integral relations. It is shown that the results are in good agreement with those obtained exactly by the method of characteristics.

Approximate solution for non-darcy transient film condensation in a porous medium

The problem of non-darcian transient film condensation adjacent to a vertical flat plate embedded in a porous medium has been considered. The governing equation for the boundary layer thickness was obtained by an integral method and solved approximately by the method of integral relations. It is shown that the results are in good agreement with those obtained exactly by the method of characteristics.

Oxidative dissolution of covellite by Thiobacillus ferrooxidans

Oxidation of research-grade covellite was investigated in respirometric and growth experiments with Thiobacillus ferrooxidans. Covellite was directly oxidized by T. ferrooxidans in respirometric experiments, but the pH of mineral salts medium increased to prohibitively high values because of high sulfide concentrations. In glycine-H 2SO 4 buffered medium the pH remained steady and the oxygen uptake activity of T. ferrooxidans was not inhibited. In cultures growing with covellite as the sole source of energy, the pH increased to about 4. Redox potential increased to 500-600 mV during bacterial oxidation of covellite in the presence and absence of additional Fe 2+, whereas it remained mostly at about 350 mV in abiotic control. Jarosite was a major solid-phase product in T. ferrooxidans cultures. The solubilization of copper from covellite in inoculated flasks was higher than that obtained in control flasks and was not enhanced in the presence of additional Fe 2+.The sample also contained bornite (Cu 5FeS 4) which released iron in solution under all experimental conditions. Accumulation of S 0 was apparent only in inoculated covellite samples. © 1997 Elsevier B.V. All rights reserved.

Oxidative dissolution of chalcopyrite by Thiobacillus ferrooxidans

The oxidative dissolution of research-grade chalcopyrite was characterized in respirometric and growth experiments with Thiobacillus ferrooxidans. In respirometric experiments with chalcopyrite, the pH of mineral salts medium increased to values that inhibited the oxygen uptake activity of T. ferrooxidans. In glycine-H 2SO 4 buffered medium the pH remained stable and oxygen uptake was not inhibited. In cultures growing with chalcopyrite as the sole source of energy, pH changes were only minor during the incubation. The redox potential values increased to about 600 mV during the bacterial oxidation of chalcopyrite in the presence and absence of additional Fe 2+, while they remained at about 350 mV in abiotic control flasks. Iron in chalcopyrite was solubilized and oxidized to Fe 3+ by T. ferrooxidans. In the abiotic controls, by comparison, less iron was solubilized and it remained as Fe 2+. Jarosite was a major solid- phase product in T. ferrooxidans cultures. The solub'flization of copper from chalcopyrite in inoculated flasks was enhanced in the presence of additional Fe 2+.Accumulation of S 0, reflecting partial oxidation of the S-entity of chalcopyrite, was apparent from the x-ray diffraction analysis of solid residues from the inoculated flasks as well the abiotic controls. © 1997 Elsevier B.V. All rights reserved.

Matching fields of a long superconducting film

We obtain the vortex configurations, the matching fields, and the magnetization of a superconducting film with a finite cross section. The applied magnetic field is normal to this cross section, and we use the London theory to calculate many of its properties, such as the local magnetic field, the free energy, and the induction for the mixed state. Thus previous similar theoretical works, done for an infinitely long superconducting film, are recovered here, in the special limit of a very long cross section. ©1999 The American Physical Society.