Adhesive Bonding of Resin Composite to Various Ni-Cr Alloy Surfaces Using Different Metal Conditioners and a Surface Modification System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Composite surfaces after finishing and polishing techniques

Purpose: To evaluate the effect of finishing and polishing techniques on surface roughness of resin-based composites (RBCs). Materials and Methods: Forty specimens of each material were cured under Mylar strips and immersed in artificial saliva for 1 wk. Samples were tested with a profilometer to obtain baseline average surface roughness (Ra). Specimens of both RBCs were then finished and polished according to four techniques: (1) Sof-Lex disks; (2) Sof-Lex disks followed by Prisma Gloss; (3) Enhance points; (4) Enhance points followed by Prisma Gloss application. New readings of the roughness pattern were carried out and the difference of post-polishing and baseline values were analyzed. Results: ANOVA test (alpha= 0.05) did not show differences between materials (P= 0.9393) nor interaction effects (P= 0.3094), but significant difference among the finishing/polishing techniques were detected (P= 0.0157). Tukey's test showed that the smoothest surface was obtained when the specimens were treated by Sof-Lex followed by Prosma Gloss polishing paste; and the worst results were obtained after using Enhance points alone.

Effect of dentin conditioning time on nanoleakage

Objectives: To study the nanoleakage pattern in the dentin hybrid layer by using different dentin adhesives. The null hypotheses tested in this study were: 1) dentin conditioning time does not affect nanoleakage within the hybrid layer; 2) the type of dentin adhesive used does not affect nanoleakage. Methods: Standardized Class V cavities were prepared in 30 intact human molars on the buccal and lingual surfaces. The specimens were randomly assigned to 2 total-etch dentin adhesives (OptiBond SOLO Plus [OPS, Kerr] and One-Step [ONS, BISCO Inc]) and 2 self-etch dentin adhesives (Clearfil SE Bond [CSE, Kuraray] and Adper Prompt L-Pop [APL, 3M ESPE]). The specimens were etched or conditioned for 15 seconds, 30 seconds or 60 seconds. Upon restoration of the Class V cavities with the proprietary resin composite, the specimens were isolated with nail polish except for a 2.0-mm rim around the restoration, and they were immersed in 50 wt% ammoniacal silver nitrate solution (pH=9.5) for 24 hours followed by 8 hours of immersion in photo-developing solution to reduce the silver ions to metallic silver. The specimens were fixed, dehydrated and processed for FESEM and TEM. Silver penetration was measured along the cervical wall, and data were analyzed with Kruskal-Wallis non-parametric tests at a significance level of 95%. Results: There were no statistically significant differences among the experimental groups for the factor conditioning time (p>0.926). There were significant differences for the variable dentin adhesive (p<0.0001). The least amount of nanoleakage within the hybrid layer occurred with CSE, while ONS resulted in the greatest penetration of silver ions. The adhesives OPS and APL ranked in the intermediary subset. Under TEM, all adhesives resulted in some degree of nanoleakage within the hybrid layer. Both spotted/reticular and water-tree nanoleakage patterns were observed. Significance: Longer conditioning times did not increase nanoleakage within the hybrid layer. Nanoleakage varied with the type of adhesive used.

Measurement of shrinkage of composite resin by laser speckle contrast analysis

The aim of this study was to evaluate the shrinkage of a microhybrid dental composite resin photo-activated by one LED with different power densities by means of speckle technique. The dental composite resin Filtek (TM) Z-250 (3M/ESPE) at color A(2) was used for the samples preparation. Uncured composite was packed in a metallic mold and irradiated during 20 s from 100 to 1000 mW cm(-2). For the photo-activation of the samples, it was used a LED prototype (Light Emission Diode) with wavelength centered at 470 nm and adjustable power density until 1 W cm(-2). The speckle patterns obtained from the bottom composite surfaces were monitored using a CCD camera without lens. The speckle field is recorded in a digital picture and stored by CCD camera as the carrier of information on the displacement of the tested surface. The calculated values were obtained for each pair of adjacent patterns and the changes in speckle contrast as a function of time were obtained from six repeated measurements. The speckle contrasts obtained from the bottom surface with 100 mW cm(-1) were smaller than those than the other power densities. The higher power densities provided the higher shrinkage.

Surfactin reduces the adhesion of food-borne pathogenic bacteria to solid surfaces

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

GLOBAL DYNAMICS IN THE POINCARE BALL of THE CHEN SYSTEM HAVING INVARIANT ALGEBRAIC SURFACES

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Streptococcus mutans Biofilm Adhesion on Composite Resin Surfaces After Different Finishing and Polishing Techniques

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Glacially striated, soft sediment surfaces on late Paleozoic tillite at São Luiz do Purunã, PR

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of oxygen flow on crystallization and morphology of PLZT thin films

PLZT thin films were prepared by a dip coating process using Pechini's method, also known as polymeric precursor method. The PLZT solution was obtained from a mixture of the individual cation solutions and the process to prepare each solution is based on metallic citrate polymerization. The viscosity of the PLZT solution was adjusted at 40 cP while the ionic concentration was adjusted at 0.1 M. PLZT solutions were deposited on silicon (100) and platinum coated silicon (100) substrates with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with a heating rate of 1 degreesC/min up to 300 degreesC and 5 degreesC/min up to 650 degreesC in order to obtain homogeneous and cracks free films. The influence of oxygen flow on crystallization and morphology of PLZT (9/65/35) thin film is discussed. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Effect of variations in annealing temperature and metallic cations on nanostructured molybdate thin films

Crystalline molybdate thin films were prepared by the complex polymerization method. The AMoO(4) (A = Ca, Sr, Ba) films were deposited onto Si wafers by the spinning technique. The Mo-O bond in the AMoO(4) structure was confirmed by FTIR spectra. X-ray diffraction revealed the presence of crystalline scheelite-type phase. The mass, size, and basicity of A(2+) cations was found to be dependent on the intrinsic characteristics of the materials. The grain size increased in the following order: CaMoO4 < SrMoO4 < BaMoO4. The emission band wavelength was detected at around 576 nm. Our findings suggest that the material's morphology and photoluminescence were both affected by the variations in cations (Ca, Sr, or Ba) and in the thermal treatment.

Aço inox bactericida

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrochemical behavior of metallic chromium in chloride media

The electrochemical behavior of metallic chromium in aqueous solutions containing chloride ions at different pH was studied by means of open-circuit potential vs. time measurements, cyclic voltammetry and electrochemical impedance spectroscopy. The composition of the surface oxides was analyzed by XPS. For solutions with pH<3 the formation of a passive layer occurs via a dissolution/precipitation process while for pH>3 the mechanism changes. XPS analysis revealed that Cr2O3 basically constitutes the passive layer.