Early Bone Healing and Biomechanical Fixation of Dual Acid-Etched and As-Machined Implants with Healing Chambers: An Experimental Study in Dogs

Purpose: To evaluate the biomechanical fixation, bone-to-implant contact (BIC), and bone morphology of screw-type root-form implants with healing chambers with as-machined or dual acid-etched (DAE) surfaces in a canine model. Materials and Methods: The animal model included the placement of machined (n = 24) and DAE (n = 24) implants along the proximal tibiae of six mongrel dogs, which remained in place for 2 or 4 weeks. Following euthanasia, half of the specimens were subjected to biomechanical testing (torque to interface failure) and the other half were processed for histomorphologic and histomorphometric (%BIC) assessments. Statistical analyses were performed by one-way analysis of variance at the 95% confidence level and the Tukey post hoc test for multiple comparisons. Results: At 4 weeks, the DAE surface presented significantly higher mean values for torque to interface failure overall. A significant increase in %BIC values occurred for both groups over time. For both groups, bone formation through the classic appositional healing pathway was observed in regions where intimate contact between the implant and the osteotomy walls occurred immediately after implantation. Where contact-free spaces existed after implantation (healing chambers), an intramembranous-like healing mode with newly formed woven bone prevailed. Conclusions: In the present short-term evaluation, no differences were observed in BIC between groups; however, an increase in biomechanical fixation was seen from 2 to 4 weeks with the DAE surface. INT J ORAL MAXILLOFAC IMPLANTS 2011;26:75-82

Bioglass Associated With Leukocyte-Poor Platelet-Rich Plasma in the Rabbit Maxillary Sinus: Histomorphometric, Densitometric, and Fractal Analysis

The objective of the present study was to evaluate the outcomes of autogenous bone graft (AB) and bioglass (BG) associated or not with leukocyte-poor platelet-rich plasma (LP-PRP) in the rabbit maxillary sinus (MS) by histomorphometric and radiographic analysis. Twenty rabbits divided into 2 groups (G1, G2) were submitted to sinus lift surgery. In G1, 10 MS were grafted with AB and 10 MS were grafted with BG. In G2, 10 MS were grafted with AB + LP-PRP and 10 MS were grafted with BG + LP-PRP. After 90 days, the animals were killed and specimens were obtained, x-rayed, and submitted to histomorphometric, radiographic bone density (RD) and fractal dimension analysis. Radiographic bone density mean values (SD), expressed as aluminum equivalent in mm, of AB, BG, AB + LP-PRP, and BG + LP-PRP groups were 1.79 (0.31), 2.04 (0.39), 1.61 (0.28), and 1.53 (0.30), respectively. Significant differences (P < 0.05) were observed between BG and AB, and BG + PRP and BG. Fractal dimension mean values were 1.48 (0.04), 1.35 (0.08), 1.44 (0.04), and 1.44 (0.06), respectively. Significant differences were observed between BG and AB, and AB + LP-PRP and BG. Mean values for the percentage of bone inside MS were 63.30 (8.60), 52.65 (10.41), 55.25 (7.01), and 51.07 (10.25), respectively. No differences were found. No correlations were observed among percentage of bone, RD and FD. Histological analysis showed that MS treated with AB presented mature and new bone formation. The other groups showed minor bone formation. Within the limitations of this study, the results indicated that at a 90-day time end point, AB yielded better results than AB + LP-PRP, BG, and BG + LP-PRP and should be considered the primary material for MS augmentation.

Comparison between embossed digital imaging and unprocessed film-based radiography in detecting periodontal bone defects: an in vitro study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of Combined Digital Imaging Parameters on Endodontic File Measurements

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Hardness of heat-polymerized acrylic resins after disinfection and long-term water immersion

Statement of the problem. In selecting a disinfectant for dental prostheses, compatibility between the disinfectant and the type of denture base material must be considered to avoid adverse effects on the hardness of the acrylic resin.Purpose. This study investigated the hardness of 2 denture base resins after disinfection and long-term water immersion.Material and methods. Thirty-two disk-shaped specimens (13 mm in diameter and 8 mm thick) were fabricated from each resin (Lucitone 550 and QC-20), polished, stored in water at 37degreesC for 48 hours, and submitted to hardness tests (Vickers hardness number [VHN]) before disinfection. Disinfection methods included scrubbing with 4% chlorhexidine gluconate for 1 minute, immersion for 10 minutes in I of the tested disinfectant Solutions (n=8) (3.78% sodium perborate, 4% chlorhexidine gluconate, or 1% sodium hypochorite), and immersion in water for 3 minutes. The disinfection procedures were repeated 4 times, and 12 hardness measurements were made on each specimen. Control specimens (not disinfected) were stored in water for 56 minutes. Hardness tests (VHN) were also performed after 15, 30, 60, 90, and 120 days of storage in water. Statistical analyses of data were conducted with a repeated measures 3-way analysis of variance (ANOVA) and Tukey post-hoc test (alpha=.05).Results. Mean values +/- SD for Lucitone 550 (16.52 +/- 0.94 VHN) and QC-20 (9.61 +/- 0.62 VHN) demonstrated a significant (P<.05) decrease in hardness after disinfection, regardless of material and disinfectant solutions used (Lucitone 550: 15.25 +/- 0.74; QC-20: 8.09 +/- 0.39). However, this effect was reversed after 15 days of storage in water. Both materials exhibited a continuous increase (P<.05) in hardness values for up to 60 days of water storage, after which no significant change was observed.Conclusion. Within the limitations of this in vitro study, QC-20 and Lucitone 550 specimens exhibited significantly lower hardness values after disinfection regardless of the disinfectant solution used.

Effect of microwave irradiation and water storage on the viscoelastic properties of denture base and reline acrylic resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of long-term water immersion on the fracture toughness of denture base and reline resins

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The Effect of Splint Material Rigidity in Implant Impression Techniques

Purpose This in vitro study compared the dimensional accuracy of two impression techniques Duralay splinted impression copings (D) and metal splinted impression copings (M) for implant supported pros theses Materials and Methods A master cast with four parallel implant abutment analogs and a passive framework were fabricated Vinyl polysiloxane impression material was used for all impressions with a metal stock tray Two groups (D and M) were tested (n = 5) The measurement method employed was just one titanium screw tightened to the framework Each group s measurements were analyzed using software that received the images of a video camera coupled to a stereomicroscope at X100 magnification The results were analyzed statistically (t test) Results The mean values of abutment/framework interface gaps were master cast = 32 mu m (SD 2), group D = 165 mu m (SD 60), and group M = 69 mu m (SD 36) There was a statistically significant difference between the D and M groups (P <= 001) Conclusion Under the limitations of this study, it could be suggested that a more accurate working cast can be fabricated using metal splinted impression copings INT J ORAL MAXILLOFAC IMPLANTS 2010 25 1153-1158

Comparison of impression techniques and materials for implant-supported prosthesis

Purpose: To investigate, in vitro, the dimensional accuracy of two impression techniques (squared impression copings and squared impression copings sandblasted and coated with impression adhesive) made of vinyl polysiloxane and polyether impression materials. Materials and Methods: A master cast (control group) with four parallel implant abutment analogs, a passive framework, and a custom aluminum tray was fabricated. Four groups (n = 5 each group) were tested: squared Impregum (SI), squared Express (SE), sandblasted adhesive squared Impregum (ASI), and sandblasted adhesive squared Express (ASE). The measurement method employed was just one titanium screw tightened to the framework. A stereomicroscope was used to evaluate the fit of the framework by measuring the size of the gap between the abutment and the framework. The results were analyzed statistically. Results: The mean values for the abutment/framework interface gaps were: master cast, 31.63 mu m (SD 2.16); SI, 38.03 mu m (SD 9.29); ASI, 46.80 mu m (SD 8.47); SE, 151.21 mu m (SD 22.79); and ASE, 136.59 mu m (SD 29.80). No significant difference was detected between the SI or ASI techniques and the master cast. No significant difference was detected between the SE and ASE techniques. Conclusion: Within the limitations of this study, it can be concluded that Impregum Soft medium consistency was the best impression material and the impression technique did not influence the accuracy of the stone casts. INT J ORAL MAXILLOFAC IMPLANTS 2010;25:771-776

Comparison of the Accuracy of Plastic and Metal Stock Trays for Implant Impressions

Purpose: This in vitro study evaluated the dimensional accuracy of two impression techniques (tapered and splinted) with two stock trays (plastic and metal) for implant-supported prostheses. Materials and Methods: A master cast with four parallel abutment analogs and a passive framework were fabricated. Polyvinyl siloxane impression material was used for all impressions with two metal stock trays and two plastic stock trays (closed and open trays). Four groups (tapered plastic, splinted plastic, tapered metal, and splinted metal) and a control group (master cast) were tested (n = 5 for each group). After the framework was seated on each of the casts, one abutment screw was tightened, and the marginal gap between the abutment and framework on the other side was measured with a stereomicroscope. The measurements were analyzed with the Kruskal-Wallis one-way analysis of variance on ranks test followed by the Dunn method. Results: The mean values (+/- standard deviations) for the abutment/framework interface gaps were: master cast, 32 +/- 2 mu m; tapered metal, 44 +/- 10 mu m; splinted metal, 69 +/- 28 mu m; tapered plastic, 164 +/- 58 mu m; splinted plastic, 128 +/- 47 mu m. No significant difference was detected between the master cast, tapered metal, and splinted metal groups or between the tapered and splinted plastic groups. Conclusions: In this study, the rigidity of the metal stock tray ensured better results than the plastic stock tray for implant impressions with a high-viscosity impression material (putty). Statistically similar results were obtained using tapered impression copings and splinted squared impression copings. The tapered impression copings technique and splinted squared impression copings technique with a metal stock tray produced precise casts with no statistically significant difference in interface gaps compared to the master cast. INT J ORAL MAXILLOFAC IMPLANTS 2012;27:544-550.

Comparative assessment of the flow rate of root canal sealers

OBJETIVO: Este estudo avaliou o escoamento do Acroseal, AH Plus, Endomethasone N, Sealapex e ActiV GP de acordo com a especificação ISO 6876/2001. METODOLOGIA: Um volume de 0,05 mL do cimento manipulado de acordo com as recomendações do fabricante foi colocado numa placa de vidro. Aos 180±5 s após o início da espatulação, uma segunda placa de vidro foi colocada sobre o cimento, seguida por um peso de massa de 100 g para fazer um total de 120±2 g. Dez minutos após o começo da manipulação o peso foi removido e o valor do diâmetro do disco de cimento foi mensurado. A média de 3 mensurações para cada cimento foi tomada como o escoamento do material. Os dados foram comparados estatisticamente pelos testes ANOVA e Tukey. RESULTADOS: Os escoamentos obtidos foram: Acroseal 21.,4 mm, AH Plus 22,72 mm, ActiV GP 24,90 mm, Endomethasone N 18,76 mm e Sealapex 25,15 mm. CONCLUSÃO: Apenas o Endomethasone N não se enquadrou na especificação ISO a qual requer que o cimento tenha um diâmetro não inferior a 20 mm. O Sealapex alcançou o melhor escoamento, mas não foi estatisticamente diferente do Activ GP e AH Plus (P>0,05).

Influence of light guide tip used in the photo-activation on degree of conversion and hardness of one nanofilled dental composite

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of different dental composite resins on the polymerization process

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In Vitro Study of Fracture Load and Fracture Pattern of Ceramic Crowns: A Finite Element and Fractography Analysis

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A Thermal Investigation of Dental Bleaching In Vitro

Objective: Our goal was to investigate the surface temperature variations in the cervical region via infrared thermography, as well as the temperature within the pulp chamber via thermocouples, of mandibular incisors when subjected to dental bleaching using two different 35% hydrogen peroxide gels, red (HP) and green (HPM), when activated by halogen light (HL) and LED light.Background Data: Temperatures increases of more than 5.5 degrees C are considered to be potentially threatening to pulp vitality, while those higher than 10 degrees C can result in periodontal injury.Materials and Methods: Tooth samples were randomly divided into four groups (n = 10 each), according to the bleaching agent and catalyst light source used.Results: Mean values and standard deviations of the temperature increases inside the pulp chamber in the HL groups were 4.4 degrees +/- 2.1 degrees C with HP, and 4.5 degrees +/- 1.2 degrees C with HPM; whereas in the groups using LED light, they were 1.4 degrees +/- 0.3 degrees C for HP, and 1.5 degrees +/- 0.2 degrees C for HPM. For the root surfaces, the maximum temperature increases in the groups irradiated with HL were 6.5 degrees +/- 1.5 degrees C for HP, and 7.5 degrees +/- 1.1 degrees C with HPM; whereas in the groups irradiated with LED light, they were 2.8 degrees +/- 0.7 degrees C with HP, and 3 degrees +/- 0.8 degrees C with HPM. There were no statistically significant differences in pulp and surface temperature increases between the groups using different gels, although the mean temperature increases were significantly higher for the groups irradiated with HL when compared with those irradiated with the LED light (p < 0.05 with Tukey's test).Conclusion: LED light may be safe for periodontal and pulp tissue when using this method, but HL should be used with care.