Nucleation and growth of mullite whiskers from lanthanum-doped aluminosilicate melts

Nucleation and growth of mullite whiskers in the La2O3-Al2O3-SiO2 system were investigated in the 1500degrees-1700degreesC temperature range. A differential thermal analysis (DTA) showed that the mullitization temperature decreases from 1350degreesC to 1240degreesC as a result of lanthania doping. In the temperature range of 1250-1500degreesC, most of the mullite grains have an Al2O3/SiO2 = 1.5 composition throughout the ceramic body; however, from 1400degreesC upward, the number of anisotropic grains with the Al2O3/SiO2 = 1.3 composition begins to increase. The concentration of alumina in the composition of the grain-boundary phase decreases as firing temperatures increase. At temperatures > 1500degreesC, alumina grains and whiskers grow on the internal and external surfaces of the ceramic body with the characteristic Al2O3/SiO2 = 1.3 composition. Removal of the mullite whisker layer by acid attack revealed an alumina-rich, rosace-like patterned microstructure correlated with the process of whisker nucleation and growth. In the early stages, whisker growth rates were found to be near 60 mum/h. Experimental evidence pointed to nucleation inside the thin glass layer on the external surface.

Thermal behavior of alpha-(Cu-Al-Ag) alloys

Thermal behavior of alpha-(Cu-Al-Ag) alloys, i.e. alloys with composition less than about 8.5 mass% Al, was studied using differential scanning calorimetry (DSC), differential thermal analysis (DTA), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicated that the presence of silver introduces new thermal events ascribed to the formation of a silver-rich phase and, after addition higher amounts than 8 mass% Ag to the Cu-8 mass% Al alloy it is possible to observe the formation of the gamma(1) phase (Al4Cu9), which is only observed in alloys containing minimum of 9 mass% Al. These results may be attributed to some Ag characteristics and its interaction with Cu and Al.

Ceramic raw materials from the State of Maranhao, Brazil. Part 1: chemical and mineralogical characterization and technological properties of clays from Sao Luis, Rosario, Pinheiro and Mirinzal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Simultaneous solidification of two catalyst wastes and their effect on the early stages of cement hydration

Two catalyst wastes (RNi and RAI) from polyol production were considered as hazardous, due to their respective high concentration of nickel and aluminum contents. This article presents the study, done to avoid environmental impacts, of the simultaneous solidification/stabilization of both catalyst wastes with type II Portland cement (CP) by non-conventional differential thermal analysis (NCDTA). This technique allows one to monitor the initial stages of cement hydration to evaluate the accelerating and/or retarding effects on the process due to the presence of the wastes and to identify the steps where the changes occur. Pastes with water/cement ratio equal to 0.5 were prepared, into which different amounts of each waste were added. NCDTA has the same basic principle of Differential Thermal Analysis (DTA), but differs in the fact that there is no external heating or cooling system as in the case of DTA. The thermal effects of the cement paste hydration with and without waste presence were evaluated from the energy released during the process in real time by acquiring the temperature data of the sample and reference using thermistors with 0.03 A degrees C resolution, coupled to an analog-digital interface. In the early stages of cement hydration retarding and accelerating effects occur, respectively due to RNi and RAl presence, with significant thermal effects. During the simultaneous use of the two waste catalysts for their stabilization process by solidification in cement, there is a synergic resulting effect, which allows better hydration operating conditions than when each waste is solidified separately. Thermogravimetric (TG) and derivative thermogravimetric analysis (DTG) of 4 and 24 h pastes allow a quantitative information about the main cement hydrated phases and confirm the same accelerating or retarding effects due to the presence of wastes indicated from respective NCDTA curves.

Thermal analysis applied in the crystallization study of SrSnO3

SrSnO3 was synthesized by the polymeric precursor method with elimination of carbon in oxygen atmosphere at 250 A degrees C for 24 h. The powder precursors were characterized by TG/DTA and high temperature X-ray diffraction (HTXRD). After calcination at 500, 600 and 700 A degrees C for 2 h, samples were evaluated by X-ray diffraction (XRD), infrared spectroscopy (IR) and Rietveld refinement of the XRD patterns for samples calcined at 900, 1,000 and 1,100 A degrees C. During thermal treatment of the powder precursor ester combustion was followed by carbonate decomposition and perovskite crystallization. No phase transition was observed as usually presented in literature for SrSnO3 that had only a rearrangement of SnO6 polyhedra.

Chemical and spectroscopic studies of a new palladium(II) complex with N-acetyl-L-cysteine

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nanometric Pb1-xLaxTiO3 (x=0, 0.13 and 0.27) powders obtained by the polymeric precursor method

PLT (Pb1-xLaxTiO3, in which x = 0, 0.13 and 0.27) powders were successfully synthesized using the polymeric precursor method, based on the Pechini method. The polymeric precursors were calcined at temperatures ranging from 350 to 500 degrees C for 4 h. X-ray diffraction (XRD) showed the evolution of the crystalline phase starting from the amorphous precursor. Thermogravimetric analyses (TG) and differential thermal analyses (DTA) of the powder precursors showed the influence of the pH on the elimination of organic material. PLT powders have a tendency to form agglomerates, what can be verified by comparing the values of the average particle sizes obtained by Brunauer-Emmett-Teller method, BET (D-BET) with the values of the average crystallite sizes obtained by XRD (D-XRD). (C) 2007 Elsevier Ltd. All fights reserved.

Sewage sludge coke estimation using thermal analysis

The imposition of more stringent legislation by CETESB in the State of So Paulo (Brazil) governing the disposal and utilization of sewage sludge, coupled with the growth in its generation has prompted a drive for alternative uses of sewage sludge. One option that is especially promising, due to its potential to valorize sludge, is its conversion into carbonaceous adsorbents or coke for industrial effluents treatment. Thus, a methodology is presented to estimate the coke produced from the sludge of a sewage treatment station using thermal analysis. The used sewage sludge, which comes from aerobic treatment, was collected in the wastewater treatment station of Barueri, one of the largest of the So Paulo metropolitan area. The sludge samples were collected, dried, ground, and milled until they passed an ABNT 200 sieve. The inert ambient used during its thermal treatment produces inorganic matter and coke as residual materials. Coke formation occurs in the 200-500 A degrees C range and, between 500 and 900 A degrees C, its thermal decomposition occurs. The highest formation of coke occurs at 500 A degrees C.

Influence of polymerization on the synthesis of SrTiO3: Part I. Characteristics of the polymeric precursors and their thermal decomposition

The influence of polymerization on the thermal decomposition of polymeric precursors and phase formation was investigated during synthesis of SrTiO3. The precipitation of polymeric precursor in acetone produced a more thermal stable precursor with lower weight loss during decomposition. This more stable precursor retarded the formation of the SrTiO3 phase. From thermal analysis, XRD and FT-IR the presence of an intermediate phase during decomposition of the precursors was observed. This is a mixed (Sr,Ti) carbonate phase with the proposed composition of Sr2Ti2O5.CO3. © 1995.

Influence of silver additions on the structure and phase transformation of the Cu-13 wt % Al alloy

The influence of silver additions on the structure and phase transformation of the Cu-13 wt % Al alloy was studied by differential thermal analysis, X-ray diffraction, scanning electron microscopy and energy dispersive analysis of X-rays. The results indicate that the presence of silver modifies the phase-stability field, the transition temperature and the structure of the alloy. These effects are more pronounced for silver concentrations up to 8 wt %.

Preparation and characterization of BaBi2Nb2O9(BBN) ceramics synthetized by polymeric precursors method

Pure BBN powders and with addition of 1 and 2 wt% in excess of bismuth were obtained by Pechini Method. The powders calcined at 300°C/4h were analyzed by TG/DTA to study the temperature of organic matter decomposition. A systematic study of calcination temperature and time to the formation of the BBN phase was performed and the phase formation was accompanied by XRD. The calcined powders at 800°C during 2h were analyzed by infrared spectroscopy and by BET. The powders were isostaticaly pressed and sintered at temperatures ranging from 900°C to 1000°C. The ceramics were characterized by XRD to control the crystalline phase and by SEM to analyze the microstructure.

Structural and electrical properties of strontium barium niobate thin films crystallized by conventional furnace and rapid-thermal annealing process

Strontium barium niobate (SBN) thin films were crystallized by conventional electric furnace annealing and by rapid-thermal annealing (RTA) at different temperatures. The average grain size of films was 70 nm and thickness around 500 nm. Using x-ray diffraction, we identified the presence of polycrystalline SBN phase for films annealed from 500 to 700 °C in both cases. Phases such as SrNb2O6 and BaNb2O6 were predominantly crystallized in films annealed at 500 °C, disappearing at higher temperatures. Dielectric and ferroelectric parameters obtained from films crystallized by conventional furnace and RTA presented essentially the same values.

Mechanism of the formation and properties of antimony polyphosphate

Formation of antimony polyphosphate using Sb2O3 and/or (NH4)2HPO4 and NH4H 2PO4 as starting materials has been simulated by thermal analysis technique. The elimination of water and ammonia molecules induced by heating leads to the formation of intermediate ammonium polyphosphate, which subsequently reacts with Sb2O3. Morphologically, vitreous Sb(PO3)3 is composed of plaques having irregular shapes. Infrared spectra and NMR study is consistent with tetrametaphosphate anion arrangement. The compound is thermally unstable and may be recommended as a donor of -O-P-O- linkers in the preparation of special phosphate glasses. © 2005 Akadémiai Kiadó, Budapest.

Effect of thermal treatment under oxygen atmosphere on the superconducting properties of RuSr2GdCu2O8

The discovery of the spatial uniform coexistence of superconductivity and ferromagnetism in rutheno-cuprates, RuSr2GdCu2O8 (Ru-1212), has spurred an extraordinary development in the study of the competition between magnetism and superconductivity. However, several points of their preparation process and characterization that determine their superconductive behavior are still obscure. The improvement of sample preparation conditions involves some thermal treatments in inert atmosphere. The first treatment results in the immediate formation of Sr2GdRuO 6. Using the CuO composition as a precursor, we produced Ru-1212. To turn it metallic and superconductor, besides the previous treatment, a final sinterization is carried out in oxygen flow for several days. Three Ru-1212 samples were produced by varying the last sinterization time (two, four, and six days under oxygen flow). Through measurements of x-ray diffraction, scanning electron microscopy, differential thermal analysis, magnetic susceptibility and mechanical spectroscopy, it was studied the influence of the treatments under oxygen atmosphere on the structural and superconducting properties of the material.

Heating rate and temperature effects on the BaTiO3 formation by thermal decomposition of (Ba,Ti) organic precursors during the Pechini process

Different thermal treatments for the synthesis of BaTiO3 powder obtained through the Pechini method were studied. The synthesis of BaTiO3 starts at 150 °C by the thermal dehydration of organic precursors. The usual inevitable formation of barium carbonate during the thermal decomposition of the precursor could be retarded at lower calcination temperatures and optimized heating rates. The organic precursors were treated at temperatures between 200 and 400 °C. Then, the samples were calcined at 700 and 800 °C for 4 and 2 h, respectively. The resulting ceramic powders were characterized by gravimetric and differential thermal analyses, X-ray powder diffraction and infrared spectroscopy. It was found that depending on the heating rate and final temperature of the thermal treatment, high amounts of BaCO3 and TiO2 could be present due to the high concentration of organics in the final calcination step. © 2007 Elsevier B.V. All rights reserved.