Faraday Glasses with a Large Size and High Performance

A kind of Faraday glass with a size of 40 mm x 14 mm and 100-300 mm x 25 mm, respectively, was prepared by the melting and casting process, which had neither a Pt particulate nor a bubble or striation. The measurement results showed that the surface homogeneity of the samples was up to +/- 1 x 10-6, the laser threshold reached 10 J/cm2 (1 omega, 3 ns), and the Verdet constants of the glasses were -0.273 min/Oe/cm at 632.8 nm and -0.076 min/Oe/cm at 1064 nm, respectively.

Shear transformation zone volume determining ductile–brittle transition of bulk metallic glasses

Three-point bending experiments were performed on as-cast and annealed samples of Zr52.5Cu17.9Ni14.6Al10Ti5 (Vit105) bulk metallic glasses over a wide range of temperatures varying from room temperature (293 K) to liquid nitrogen temperature (77 K). The results demonstrated that the free volume decrease due to annealing and/or cryogenic temperature can reduce the propensity for the formation of multiple shear bands and hence deteriorate plastic deformation ability. We clearly observed a sharp ductile-to-brittle transition (DBT), across which microscopic fracture feature transfers from micro-scale vein patterns to nano-scale periodic corrugations. Macroscopically, the corresponding fracture mode changes from ductile shear fracture to brittle tensile fracture. The shear transformation zone volume, taking into account free volume, temperature and strain rate, is proposed to quantitatively characterize the DBT behavior in fracture of metallic glasses.

Strain rate-dependent shear band behavior in bulk metallic glasses

In this article, we review our recent advances in understanding the deformation behavior of a typical tough Zr41.2Ti13.8Cu12.5Ni10Be22.5 (Vit 1) bulk metallic glass (BMG), as a model material, under various loading modes and strain rates, focusing particularly on the rate-dependence and formation mechanism of shear-banding. Dynamic and quasi-static mechanical experiments, including plate shear, shear punch and spherical indentation, and continuum as well as atomistic modeling on shear-banding are discussed. The results demonstrate that higher strain rate slows down the annihilation process of free volume, but promotes the free-volume coalescence, which is responsible for the rate-dependent shear banding. The physical origin of shear bands, that is the free volume softening underpinned by irreversible rearrangements of atoms, is unveiled. Finally, some concluding remarks are given.

Luminescent and Mesoporous Europium-Doped Bioactive Glasses (MBG) as a Drug Carrier

Luminescent and mesoporous europium-doped bioactive glasses (MBG:Eu) were successfully synthesized by a two-step acid-catalyzed self-assembly process combined with hydrothermal treatment in an inorganic-organic system. The obtained MBG was performed as a drug delivery carrier to investigate the drug storage/release properties using ibuprofen (IBU) as a model drug. The structural, morphological, textural and optical properties were well characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N-2 adsorption/desorption, and photoluminescence (PL) spectra, respectively. The results reveal that the MBG exhibit the typical ordered characteristics of the hexagonal mesostructure. This composite shows sustained release profile with ibuprofen as the model drug. The IBU-loaded samples still show red luminescence of Eu3+ (D-5(0)-F-7(1, 2)) under UV irradiation, and the emission intensities of Eu3+ in the drug carrier system vary with the released amount of IBU, thus making the drug release be easily tracked and monitored by the change of the luminescence intensity.

Long lasting phosphorescence of Eu2+ in reduced SrO-B2O3 glasses

The blue long-lasting phosphorescence (LLP) phenomenon was observed for Eu2+-doped SrO-B2O3 glasses prepared in the reducing atmosphere. The phosphorescence peaks at about 450 nm due to the 4f5d -> 4f transition of Eu2+. With the doping of different amounts of Eu2+, the concentration-quenching phenomenon was observed for both the LLP and photoluminescence of the glasses, and the critical concentration for the two cases was same, i.e., 0.02 mol% Eu2+. And by the investigation of the TL curves, the content of Eu2+ had an effect on the trap depth of the samples. At last the possible mechanism of the LLP of the samples was suggested.

Long lasting phosphorescence in Eu3+ and Ce3+ co-doped strontium borate glasses

Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of both Eu2+ and Ce3+. The methods of photoluminescence, thermoluminescence and phosphorescence were used to study the samples, and possible mechanism was suggested. The co-doping of Ce3+ ions poisoned the phosphorescence emission of Eu2+ because of the competition to obtain the trapped electron. The phosphorescence of Ce3+ in the sample decays more quickly than that of Eu2+, which is suggested for the reason that the emission energy of Ce3+ is higher or the distance between Ce3+ and electron traps of the glasses is longer.

Near infrared long lasting emission of Yb3+ and its influence on the optical storage ability of Mn2+-activated zinc borosilicate glasses

The near infrared long lasting phosphorescence of Yb3+ is observed in Yb3+ and Mn2+ codoped zinc borosilicate glasses. Compared with the glasses solely activated by Mn2+, when the Yb3+ ion is codoped, the red long lasting phosphorescence of the samples is largely improved in both brightness and persistent time but the photostimulated long lasting phosphorescence is greatly depressed. It is considered that the appearance of the phosphorescence of Yb3+ is due to the alteration of the energy transfer channel; additionally, Yb3+ also changes the trap depth of the glasses with the shallower trap predominating therefrom the red long lasting phosphorescence is improved and the photostimulated long lasting phosphorescence is degraded.

Effect of samarium on Mn activated zinc borosilicate storage glasses

Samarium and manganese co-doped zinc borosilicate storage glasses were prepared by high temperature solid state method. The effect of doping samarium on the defect of Mn activated sample was studied by means of thermoluminescence spectra. It was found that the shallower traps of the sample predominate with the addition of samarium, as a result, the phosphorescence and storage properties of the manganese doped zinc borosilicate glasses were greatly changed.

Hydrogen peroxide biosensor based on sol-gel-derived glasses doped with Eastman AQ polymer

A hydrogen peroxide biosensor based on sol-gel-derived glasses doped with poly(ester sulfonic acid) Eastman AQ 55D was constructed. Thionine (TH), as a mediator, was incorporated in this matrix by electrostatic force between TH+ and the negatively charged sulfonic acid group in Eastman AQ polymer. Performance and characteristics of the sensor were evaluated with respect to response time, sensitivity and storage stability. The enzyme electrode has a sensitivity of 11.36 muA mM(-1) with a detection limit of 5.0 x 10(-7) M H2O2, and the sensor achieved 95% of the steady state current within 20 s. (C) 2001 Elsevier Science B.V. All rights reserved.

Coordination changes in magnesium silicate glasses

Wilding, Martin; Benmore, C.J.; Tangeman, J.A.; Sampath, S., (2004) 'Coordination changes in magnesium silicate glasses', Europhysics Letters 67 pp.212-218 RAE2008

Inorganic glasses, glass-forming liquids and amorphizing solids

Greaves, George; Sen, S., (2007) 'Inorganic glasses, glass-forming liquids and amorphizing solids', Advances in Physics 56(1) pp.1-166 RAE2008