Faraday Glasses with a Large Size and High Performance

A kind of Faraday glass with a size of 40 mm x 14 mm and 100-300 mm x 25 mm, respectively, was prepared by the melting and casting process, which had neither a Pt particulate nor a bubble or striation. The measurement results showed that the surface homogeneity of the samples was up to +/- 1 x 10-6, the laser threshold reached 10 J/cm2 (1 omega, 3 ns), and the Verdet constants of the glasses were -0.273 min/Oe/cm at 632.8 nm and -0.076 min/Oe/cm at 1064 nm, respectively.