Thermoset matrix reinforced with sisal fibers: Effect of the cure cycle on the properties of the biobased composite

Thermoset phenolic composites reinforced with sisal fibers were prepared to optimize the cure step. In the present study, processing parameters such as pressure, temperature, and time interval were varied to control the vaporization of the water generated as a byproduct during the crosslinking reaction. These molecules can vaporize forming voids, which in turn affect the final material properties. The set of results on impact strength revealed that the application of higher pressure before the gel point of the phenolic matrix produced composites with better properties. The SEM images showed that the cure cycle corresponding to the application of higher values of molding pressure at the gel point of the phenolic resin led to the reduction of voids in the matrix. In addition, the increase in the molding pressure during the cure step increased the resin interdiffusion. Better filling of the fiber channels decreased the possibility of water molecules diffusing through the internal spaces of the fibers. These molecules then diffused mainly through the bulk of the thermoset matrix, which led to a decrease in the water diffusion coefficient (D) at all three temperatures (25, 55 and 70 degrees C) considered in the experiments. (C) 2009 Elsevier Ltd. All rights reserved.

Carbon fiber non-crimp multi-axial reinforcement and epoxy mono-component system composite: fatigue behavior

Fiber reinforced polymer composites have been widely applied in the aeronautical field. However, composite processing, which uses unlocked molds, should be avoided in view of the tight requirements and also due to possible environmental contamination. To produce high performance structural frames meeting aeronautical reproducibility and low cost criteria, the Brazilian industry has shown interest to investigate the resin transfer molding process (RTM) considering being a closed-mold pressure injection system which allows faster gel and cure times. Due to the fibrous composite anisotropic and non homogeneity characteristics, the fatigue behavior is a complex phenomenon quite different from to metals materials crucial to be investigated considering the aeronautical application. Fatigue sub-scale specimens of intermediate modulus carbon fiber non-crimp multi-axial reinforcement and epoxy mono-component system composite were produced according to the ASTM 3039 D. Axial fatigue tests were carried out according to ASTM D 3479. A sinusoidal load of 10 Hz frequency and load ratio R = 0.1. It was observed a high fatigue interval obtained for NCF/RTM6 composites. Weibull statistical analysis was applied to describe the failure probability of materials under cyclic loads and fractures pattern was observed by scanning electron microscopy. (C) 2010 Published by Elsevier Ltd.

Evaluation of stitched fabric composite processed by RTM in quasi-static test

Stitched fabrics have been widely studied for potential application in aircraft structures since stitch yarns offer improvements in the out-of-plane mechanical properties and also can save time in the lay up process. The down side of stitch yarns came up in the manufacturing process of fabric in which defects introduced by the needle movement creating fiber-free-zones, fiber breakage and misalignment of fibers. The dry stitched carbon fabric preform has mainly been used in the Resin Transfer Molding (RTM) process which high fiber content is aimed, those defects influence negatively the injection behavior reducing the mechanical properties of final material. The purpose of this research work focused on testing in quasi-static mechanical mode (in-plane tension) of a monocomponent resin CYCOM (R) 890 RTM/carbon fiber anti-symmetric quadriaxial fabric stitched by PE 80Dtex yarn processed by RTM. The evaluation consisted in comparing the scatter of the quasi-static test with the attenuation of ultrasonic maps, which show the path of the resin and possible dry spots considering that interference of yarn in resin flow is detectable in ultrasonic measurement. Microscopic analysis was also considered for further evaluation in case of premature failure. (C) 2011 Published by Elsevier Ltd. Selection and peer-review under responsibility of ICM11

Determination of the photoinduced birefringence and of the refractive index by Brewster method of epoxy resin doped with CdS

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Short-term vs long-term calcium hydroxide therapy after immediate tooth replantation: a histomorphometric study in monkey's teeth

Endodontic treatment is an important step of tooth replantation protocols, but the ideal moment for definitive obturation of replanted teeth has not yet been established. In this study, a histomorphometric analysis was undertaken to evaluate the repair process on immediate replantation of monkeys teeth after calcium hydroxide (CH) therapy for 1 and 6 months followed by root canal filling with a CH-based sealer (Sealapex (R)). The maxillary and mandibular lateral incisors of five female Cebus apella monkeys were extracted, kept in sterile saline for 15 min, replanted and splinted with stainless steel orthodontic wire and composite resin for 10 days. In Group I (control), definitive root canal filling was performed before tooth extraction. In Groups II and III, CH therapy started after removal of splint, and definitive root canal filling was performed 1 and 6 months later, respectively. The animals were euthanized 9 months after replantation, and specimens were processed for histomorphometric analysis. In all groups, epithelial attachment occurred at the cementoenamel junction or very close to this region; the areas of resorption on root surface had small extension and depth and were repaired by newly formed cementum; and the periodontal ligament was organized. Statistical analysis of the scores obtained for the histomorphometric parameters did not show any statistically significant difference (P = 0.1221) among the groups. The results suggests that when endodontic treatment is initiated 10 days after immediate replantation and an antibiotic regimen is associated, definitive root canal filling can be performed after a short-term CH therapy.

Periodontal tissue response to coverage of root cavities restored with resin materials: A histomorphometric study in dogs

Background: the purpose of this study was to histomorphometrically evaluate the response of periodontal tissues covering Class V resin restorations in dogs.Methods: After raising a mucoperiosteal flap, bony defects measuring 5 x 5 mm were created on the buccal aspect of the canines of five dogs followed by cavity preparations on the root surface measuring 3 x 3 x 1 mm. Before repositioning the flap to cover the bone defect, the cavities were restored with composite resin (CR) or resin-modified glass ionomer cement (RMGIC) or were left unrestored as control (C). The dogs were euthanized 90 days after surgery. Specimens comprising the tooth and periodontal tissues were removed, processed routinely, cut into longitudinal serial sections in the bucco-lingual direction, and stained with hematoxylin and eosin (H&E) or Masson's trichrome. The most central sections were selected for histomorphometric analysis.Results: Histomorphometric analysis revealed apical migration of epithelial tissue onto the restorative materials (RMGIC and CR). The C group presented significantly longer connective tissue attachment (P < 0.05) than the RMGIC and CR groups and significantly higher bone regeneration (P < 0.05) compared to the RMGIC group. Histologically, the cervical third (CT) of all groups had the most marked chronic inflammatory infiltrate.Conclusions: Within the limits of this study, it can be concluded that the restorative materials used exhibit biocompatibility; however, both materials interfered with the development of new bone and the connective tissue attachment process.

Retention of oral microorganisms on conventional and resin-modified glass-ionomer cements

A cárie secundária representa problema de saúde pública e socioeconômico no mundo. A restauração de dentes acometidos por cárie pode criar condições favoráveis à proliferação microbiana na superfície do material restaurador ou na interface dente/restauração, criando ambiente propício para o estabelecimento de cárie secundária. O objetivo deste estudo foi avaliar a capacidade de retenção de placa bacteriana em cimentos de ionômero de vidro convencionais (Chelon-Fil e Vidrion R) e modificados por resina (Vitremer e Fuji II LC) e de resina composta híbrida (Z100), utilizada como controle. Nos testes de retenção de microrganismos, in situ, 12 voluntários utilizaram, por 7 dias, placa de Hawley contendo corpos-de-prova de todos os materiais. A seguir, os corpos-de-prova foram transferidos para tubos contendo 2,0 ml de Ringer-PRAS e os microrganismos presentes em sua superfície foram cultivados em placa com ágar-sangue e ágar Mitis Salivarius Bacitracina, os quais foram incubados, a 37ºC, em anaerobiose (90% N2, 10% CO2), por 10 e 2 dias, respectivamente. Os ionômeros modificados por resina retiveram quantidade de bactérias similar àquela mostrada pela resina testada. Os ionômeros modificados por resina também apresentaram menor número de estreptococos do grupo mutans do que a resina e os cimentos ionoméricos convencionais. Os ionômeros de vidro convencionais apresentaram menor número de estreptococos do grupo mutans que a resina, sendo que essa diferença não foi estatisticamente significativa.

Histometric Analysis of Bone Repair in Bone-Implant Interface Using a Polylactic/Polyglycolic Acid Copolymer Associated With Implants in Rabbit Tibia

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of different repair techniques on the accuracy of repositioning the fractured denture base

Objective:This study investigated the efficacy of different techniques for the union of fragments of a denture before repair and on the accuracy of the reposition.Materials and methods:For this study, 20 maxillary dentures made with Lucitone 550 heat-cured resin were used. Points were determined with a scanner on the cusp of the teeth, as a measurement of the segments. After digitisation, each model was exported to the AUTOCAD R 14 program and two-dimensional measurements of the distances between the marked points were made. After the initial analysis, the dentures were fractured into two segments using an impact test machine. For the repair, maxillary dentures were divided into two groups; in the first, the repair was carried out using Kerr's sticky wax and in the second group, Super Bonder was used to join the fragments, with subsequent inclusion of DENTSPLY((R)) Repair Material resin. After the repair, the points of the maxillary dentures were measured again. The numerical values obtained were tabulated to compare the measurements before fracture and after the repair. For statistical analysis, analysis of variance was employed, using a single factor and double factor, followed by the Tukey test with a reliability of 95%.Results:The results demonstrated a statistically significant difference between the materials used to join the dentures for repair, where the dentures were joined with sticky wax presented a larger variation in the distances between the points.Conclusion:The variation in distances between the points is influenced by the agent of repair.

Long-term nano-mechanical properties of biomodified dentin-resin interface components

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

THE EFFECT of DENTIN PRETREATMENT on THE MICROTENSILE BOND STRENGTH of SELF-ADHESIVE RESIN CEMENTS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Hybrid layer thickness and resin tag length of a self-etching adhesive bonded to sound dentin

Objectives: the purpose of this study is to employ optical microscopy to measure the thickness of the hybrid layer and the penetration (tags) of an aggressive self-etching adhesive system into sound dentin.Methods: occtusat cavities were prepared in 40 extracted human posterior teeth. The prepared teeth were randomly assigned to four experimental groups with 10 specimens each. The self-etching adhesive system Adper Prompt L-Pop was applied to the dentin surface as follows: Group 1: cavosurface enamel was etched for 60 s and dentin for 20 s with 35% phosphoric acid get, immediately followed by application of the self -etching adhesive with a brush to the entire cavity for 15 s; Groups 2, 3, and 4: no pre-etching was performed, and the self -etching adhesive was applied to both enamel and dentin for 15, 30 and 45 s, respectively. After curing, the cavities were fitted with composite resin Fittek Z250. Afterwards, the teeth were decalcified and the restorations were carefully removed for later embedding in paraffin. The specimens were serially sectioned at 6 mu m of thickness and sequentially mounted in glass slides. These sections were stained with Brown and Brenn staining for posterior analysis and measurement of the hybrid layer and resin tags on a tight microscope with a micrometric ocular 40/075. The results were submitted to analysis of variance at the 5% level.Results: whenever there was significance, the Tukey test was applied at the 5% level. The specimens receiving application of acid etching before the selfetching. adhesive displayed a larger thickness of the hybrid layer; on the other hand, specimens receiving only application of the self -etching adhesive on dentin for 15, 30 and 45 s exhibited similar thickness of the hybrid layer. As regards the resin tags, no statistically significant differences could be found between the study groups.Conclusions: it could be concluded that the increase in the time of application of the self-etching adhesive Adper Prompt L-Pop did not significantly influence the formation and thickness of hybrid layer, as well as its penetration into the sound dentin surface. (c) 2005 Elsevier Ltd. All rights reserved.

Clinical assessment of postoperative sensitivity in posterior composite restorations

This incidence of postoperative sensitivity was evaluated in resin-based posterior restorations. Two hundred and ninety-two direct restorations were evaluated in premolars and molars. A total of 143 Class I and 149 Class 11 restorations (MO/OD and MOD) were placed in patients ranging in age from 30 to 50 years. After the cavity preparations were completed, a rubber dam was placed, and the preparations were restored using a total-etch system (Prime & Bond NT) and a resin-based restorative material (TPH Spectrum). The patients were contacted after 24 hours and 7, 30 and 90 days postoperatively and questioned regarding the presence of sensitivity and the stimuli that triggered that sensitivity. The Chi-square and Fisher's Exact Test were used for statistical analysis. Evaluation at 24 hours after restorative treatment revealed statistically significant differences among the types of cavity preparations restored and the occurrence of postoperative sensitivity (p=0.0003), with a higher frequency of sensitivity in Class H MOD restorations (26%), followed by Class II MO/DO (15%) and Class I restorations (5%). At 7, 30 and 90 days after restorative treatment, there was a decrease in the occurrence of sensitivity for all groups. The percentage of sensitivity among the groups was not significantly different. This study shows that the occurrence of sensitivity is correlated with the complexity of the restoration.

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.