Kinetics of formalization of poly(vinyl acetate)

Kinetic information on the formation of poly(vinyl formal) by the reaction of poly(vinyl acetate) and formaldehyde in presence of aqueous acid has been derived from the spectroscopic analysis of polymer samples after different periods of reaction. The hydroxyl content of poly(vinyl formal) is found to be nearly independent of reaction time and only slightly affected by temperature while the fall of acetate content and the increase in formal content are most rapid in the initial period and are largely influenced by temperature. The rate expression formulated on the assumption that the formalization reaction is of first order with respect to both poly(vinyl acetate) and formaldehyde explains the observed variation of polymer composition with reaction time. The activation energy for the reaction is found to be 17.3 kcal/mol.

Metal chelates in vinyl polymerization. I. Ferric dipivaloylmethide as an initiator

The behavior of the chelate, ferric dipivaloylmethide, Fe(DPM)3, in vinyl polymerization systems was investigated. The polymerization was found to be of free-radical nature. The rate of polymerization was proportional to the square root of the concentration of the chelate. The monomer exponent was close to 1.5 for the Fe(DPM)3-initiated polymerization of styrene and methyl methacrylate. The kinetic and transfer constants and activation energies for these systems have been evaluated. Spectral studies revealed the possibility of a complex formation between the chelate and the monomer. A kinetic scheme for the Fe(DPM)3-initiated polymerization is derived based on this initial complex formation.

Metal chelates in vinyl polymerization. II. Mechanism of initiation by Fe(DPM)3

The nature of the interaction between the unsaturated monomer and the chelate, Fe(DPM)3, is studied in detail. The interaction is found to occur only in solution. The stoichiometry of interaction and the equilibrium constant are evaluated. With the help of spectral evidence, attempts are made to point out the specific sites of interaction.

One-Pot Synthesis of beta-Amino/beta-Hydroxy Selenides and Sulfides from Aziridines and Epoxides

Diaryl disulfides and diselenides undergo facile cleavage on treatment with rongalite (sodium hydroxymethanesulfinate) to generate the corresponding thiolate and selenolate species in Situ, which effect the ring opening of aziridines and epoxides in a regioselective manner. A simple, mild, cost-effective protocol has been developed to prepare beta-amino and beta-hydroxy sulfides and selenides in a one-pot operation.

Encapsulation and release of rifampicin using poly(vinyl pyrrolidone)-poly (methacrylic acid) polyelectrolyte capsules

Poly(vinyl pyrrolidone) and poly(methacrylic acid) multilayer capsules based on hydrogen bonding have been prepared by the layer-by-layer approach and used to encapsulate and release rifampicin, an antituberculosis drug. Removal of silica core using a buffer of ammonium fluoride and hydrofluoric acid at about pH 3 was found to produce better capsules than hydrofluoric acid alone. An eight-layered capsule had a wall thickness of 20 rim. Maximum encapsulation was found to be about 86 mu g at 40 degrees C with 1 +/- 0.2 x 10(6) capsules. Release studies showed a burst kind of release and maximum release was obtained above pH 7 where the capsules disintegrate rapidly thereby releasing the drug in a short period. Interactions studies with Mycobacterium smegmatis showed that the capsules were cytocompatible and the released drug functioned with the same efficacy as the free drug.

Poly (vinyl alcohol) hydrogel membrane as electrolyte for direct borohydride fuel cells

A direct borohydride fuel cell (DBFC) employing a poly (vinyl alcohol)hydrogel membrane electrolyte (PHME) is reported. The DBFC employs an AB(5) Misch metal alloy as anode and a goldplated stainless steel mesh as cathode in conjunction with aqueous alkaline solution of sodium borohydride as fuel and aqueous acidified solution of hydrogen peroxide as oxidant. Room temperature performances of the PHME-based DBFC in respect of peak power outputs; ex-situ cross-over of oxidant, fuel,anolyte and catholyte across the membrane electrolytes; utilization efficiencies of fuel and oxidant, as also cell performance durability are compared with a similar DBFC employing a NafionA (R)-117 membrane electrolyte (NME). Peak power densities of similar to 30 and similar to 40 mW cm(-2) are observed for the DBFCs with PHME and NME, respectively. The crossover of NaBH4 across both the membranes has been found to be very low. The utilization efficiencies of NaBH4 and H2O2 are found to be similar to 24 and similar to 59%, respectively for the PHME-based DBFC; similar to 18 and similar to 62%, respectively for the NME-based DBFC. The PHME and NME-based DBFCs exhibit operational cell potentials of similar to 1 center dot 2 and similar to 1 center dot 4 V, respectively at a load current density of 10 mA cm(-2) for similar to 100 h.

Composition of aqueous solutions in equilibrium with sulfides and oxides of iron at 3500°C

Solutions of potassium chloride (pH-buffered and 1-molat) equilibrated at 350°C with pyrrhotite, pyrite, and magnetite contained approximately 1 millimole of reduced sulfur and less than 0.1 millimole of oxidized sulfur per kilogram. Similar solutions equilibrated with pyrite, magnetite, and hematite contained approximately 1 millimole of reduced sulfur, but 3 to 6 millimoles of oxidized sulfur per kilogram. Both types of solutions contained less than 0.1 millimole of iron per kilogram at pH ≥ 6 and approximately 100 millimoles per kilogram at pH 2.

Seawater Durability of Epoxy/Vinyl Ester Reinforced with Glass/Carbon Composites

Seawater aging response was investigated in marine-grade glass/epoxy, glass/vinyl ester, carbon/epoxy and carbon/vinyl ester composites with respect to water uptake, interlaminar shear strength, flexural strength, tensile strength, and tensile fracture surface observations. The reduction of mechanical properties was found to be higher in them initial stages which showed saturation in the longer durations of seawater immersion. The flexural strength and ultimate tensile strength (UTS) dropped by about 35% and 27% for glass/epoxy, 22% and 15% for glass/vinyl ester, 48% and 34% for carbon/epoxy 28%, and 21% carbon/vinyl ester composites respectively. The water uptake behavior of epoxy-based composites was inferior to that of the vinyl system.

Reaction of beta-haloenones with tetrathiomolybdate: Synthesis of vinyl disulfides

beta -Haloenones react readily with benzyltriethylammonium tetrathiomolybdate to form the corresponding vinyl disulfides in good yields.

Vinyl radical induced Michael additions: Total synthesis of (±)-seychellene

A new strategy for the total synthesis of (±)-seychellene which involves (i) a regiospecific construction of a bicyclo(2.2.2)octene moiety having a methyl group at the bridgehead and (ii) a vinyl radical induced intramolecular Michael addition is described.

A kinetic investigation of thermal degradation of poly(vinyl formals)

Several samples of poly(vinyl formal) having the same vinyl alcohol content (8–9%) but varying contents of vinyl acetate (6–22%) and vinyl formol (70–85%) were prepared and subjected to thermogravimetric analysis, in air and nitrogen atmospheres, employing both isothermal and dynamic methods. Kinetic parameters determined from both the isothermal and dynamic TGA data are compared. The activation energy is seen to be largely dependent on the degree of conversion, implying a complex degradation reaction. The activation energy is also much less for degradation in air than in nitrogen, which can be explained by a reaction with oxygen-producing structures favoring degradation. The activation energy is less sensitive to variation in polymer composition for degradation in air than in nitrogen. Thus, in the dynamic process, the activation energy value decreases (from 36 to 23 kcal/mole) with increasing acetate content (from 6 to 22%) in nitrogen atmosphere, while in air the activation energy value increases only moderately (from 21 to 27 kcal/mole) with increasing acetate content (from 6 to 22%). The order of reaction is nearly unity, irrespective of the composition of the polymer, both in air and nitrogen.

A kinetic investigation of thermal degradation of poly(vinyl formals)

Several samples of poly(vinyl formal) having the same vinyl alcohol content (8–9%) but varying contents of vinyl acetate (6–22%) and vinyl formol (70–85%) were prepared and subjected to thermogravimetric analysis, in air and nitrogen atmospheres, employing both isothermal and dynamic methods. Kinetic parameters determined from both the isothermal and dynamic TGA data are compared. The activation energy is seen to be largely dependent on the degree of conversion, implying a complex degradation reaction. The activation energy is also much less for degradation in air than in nitrogen, which can be explained by a reaction with oxygen-producing structures favoring degradation. The activation energy is less sensitive to variation in polymer composition for degradation in air than in nitrogen. Thus, in the dynamic process, the activation energy value decreases (from 36 to 23 kcal/mole) with increasing acetate content (from 6 to 22%) in nitrogen atmosphere, while in air the activation energy value increases only moderately (from 21 to 27 kcal/mole) with increasing acetate content (from 6 to 22%). The order of reaction is nearly unity, irrespective of the composition of the polymer, both in air and nitrogen.