Síntese, caracterização e estudo das propriedades magnéticas de ortoferritas de lantânio dopadas com manganês

Orthoferrites AFeO3 (A = rare earth) are an important class of perovskite oxides that exhibit weak ferromagnetism. These materials find numerous applications as chemical sensors, cathodes for fuel cells and catalysis, which make them interesting from the standpoint of science and technology. Their structural, electrical and magnetic properties are dependent on many factors such as the preparation method, heat treatment conditions, chemical composition and replacement of cations in sites A and/or B. In this paper, LaFe1-xMnxO3 (0 ≤ x ≤ 1) orthoferrites-type was prepared by Pechini method and Microwave-assisted combustion reaction in order to evaluate the influence of synthesis route on the formation of oxide, as well as the effect of parcial replacement of iron by manganese and heat treatment on the magnetic properties. The precursor powders were calcined at 700°C, 900°C, 1100°C and 1300°C for 4 hours and they were characterized by the techniques: Thermogravimetric analysis (TGA), X ray diffraction (XRD), Refinement by Rietveld method, Scanning electron microscopy (SEM), Reduction temperature programmed (RTP) and Magnetic hysteresis measurements performed at room temperature. According to the XRD patterns, the formation of perovskite phase with orthorhombic structure was observed for the systems where 0 ≤ x ≤ 0.5 and rhombohedral for x = 1. The results also showed a decrease of lattice parameters with the parcial replacement of iron by manganese and consequently a reduction in cell volume. The hysteresis curves exhibited weak ferromagnetism for the systems prepared by both synthesis methods. However, a dependence of magnetization as a function of dopant content was observed for samples produced by Pechini method. As for the systems prepared by combustion reaction, it was found that the secondary phases exert a strong influence on the magnetic behavior

Structural characterization of 0.5PbMg(1/3)Nb(2/3)O(3)-0.5Ba(x)Pb((1-x))TiO(3) powders

The present work reports the effects caused by barium on phase formation, morphology and sintering of lead magnesium niobate-lead titanate (PMN-50PT). Ab initio study of 0.5PbMg(1/3)Nb(2/3)O(3)-0.5Ba(x)Pb((1-x))TiO(3) ceramic powders, with x = 0, 0.20, and 0.40 was proposed, considering that the partial substitution of lead by barium can reestablish the equilibrium of monoclinic-tetragonal phases in the system. It was verified that even for 40 mol% of barium, it was possible to obtain pyrochlore-free PMN-PT powders. The increase of the lattice parameters of PMN-PT doped-powders confirmed dopant incorporation into the perovskite phase. The presence of barium improved the reactivity of the powders, with an average particle size of 120 nm for 40 mol% of barium against 167 mn for the pure sample. Although high barium content (40 mol%) was deleterious for a dense ceramic, contents up to 20 mol% allowed 95% density when sintered at 1100 degrees C for 4 h. (c) 2007 Elsevier Ltd. All rights reserved.

Photoluminescence properties of PZT 52/48 synthesized by microwave hydrothermal method using PVA with template

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A homovalent doping in PMN ceramics by using lithium and scandium cations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The influence of thermal treatment on the preparation of PNM and PMN-PT thin films

Ferroelectric thin films belong to a class of materials with great technological importance in optic fibers, micro-electromechanical systems, and microprocessors and computers memories.The (1-x)PbMg1/3Nb2/3O3(x)PbTiO3 (PMN-PT) thin films, with x=0, 0.1, 0.35 and 0.5, were prepared by Pechini's process and deposited by spin-coating on Si(100), Pt/Ti/SiO2/Si(100) and quartz substrates. The goal of the present paper is to verify the thermal treatment influence on the perovskite phase formation, which is desirable for these applications. The phase formation was analyzed by X-ray diffraction. The film's surface was characterized by atomic force microscopy to analyze the roughness and the homogeneity. The results of this study indicate that the optimum conditions for obtaining the perovskite phase using a Pt/Ti/SiO2/Si(100) substrate, were drying each deposited layer at 140 degreesC (heating plate), and a final thermal treatment at 600 degreesC for 3 h in a closed system with a lead-rich atmosphere. (C) 2003 Elsevier B.V. All rights reserved.

Synthesis of Fine Micro-sized BaZrO3 Powders Based on a Decaoctahedron Shape by the Microwave-Assisted Hydrothermal Method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Lanthanum doped BiFeO3 powders: Syntheses and characterization

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Obtenção da fase peroviskita via microemulsão

Pequenas partículas de fase peroviskita de BaMnO3 foram preparadas por dois métodos: a rota da coprecipitação convencional (RCC) e o método convencional de microemulsão (MCM). As técnicas instrumentais utilizadas para caracterizar as amostras foram: microscopia eletrônica de varredura (SEM), difratometria de raios X (XRD), termogravimetria (TG) e análise térmica diferencial (DTA). A síntese de materiais em sistemas coloidais auto-organizados tem por objetivo aumentar a homogeneidade de tamanho e forma das partículas. Nos últimos anos aumentou a busca por materiais mais uniformes visando o aperfeiçoamento da microestrutura. A rota de microemulsão é um método alternativo para a síntese de materiais porque permite o controle da relação entre as concentrações de água e do tensoativo, (w), o qual controla o tamanho das gotículas de microemulsão denominadas microreatores. Peroviskita pura obtida de microemulsão forma-se em temperatura menor do que a fase precipitada, e resulta.em partículas com distribuição de tamanho mais adequada, de aproximadamente 0,1 mm de diâmetro comparado com a média de 0,5 mm das partículas coprecipitadas.

Efeito da adição simultânea de sementes e dopantes na microestrutura e propriedade dielétrica da cerâmica 0,93 PZN - 0,07 BT

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and electrical properties of SrBi2Nb2O9 thin films prepared by chemical aqueous solution at low temperature

SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates. The dip-coated films were specular and crack-free and crystallized during firing at 700 degrees C. Microstructure and morphological evaluation were followed by grazing incident X-ray diffraction (GIXRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The films exhibited somewhat porous grain structure with rounded grains of about 100 nm. For the electrical measurements, gold electrodes of 300 mu m in diameter were sputter deposited on the top surface, forming a metal-ferroelectric-metal (MFM) configuration. The remanent polarization (P-r) and coercive field (E-c) were 5.6 mu C/cm(2) and 100 kV/cm, respectively. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Influence of the solution pH on the morphological, structural and electrical properties of Bi3.50La0.50Ti3O12 thin films obtained by the polymeric precursor method

Lanthanum-doped Bi4Ti3O12 thin films (BLT) were deposited on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution. The spin-coated films were specular, crack-free and crystalline after annealing at 700 degrees C for 2 h. Crystallinity and morphological evaluation were examined by X ray diffraction (YRD) and atomic force microscopy (AFM). The stability of the formed complex is of extreme importance for the formation of the perovskite phase. Films obtained from acid pH solution present elongated grains around 200 ran in size, whereas films obtained from basic solution present a dense microstructure with spherical grains (100 nm). The dielectric and ferroelectric properties of the BLT films are strongly affected by the solution pH. The hysteresis loops are fully saturated with a remnant polarization and coercive voltage of P-r=20.2 mu C/cm(2) and V-c = 1.35 V and P-r= 15 mu C/cm(2) and V-c = 1.69 V for the films obtained from basic and acid solutions, respectively. (C) 2005 Elsevier B.V. All rights reserved.

Structural effects of Li and K additives on the columbite precursor and 0.9PMN-0.1PT powders

Single-phase perovskite 0.9Pb(Mg1/3Nb2/3)O-3-0.1PbTiO(3) (PMN-PT) powders were prepared by using a Ti-modified columbite precursor (MNT) obtained by the polymeric precursor method. The innovation consists in the preparation of Ti-modified columbite in order to react directly with a stoichiometric amount of PbO to obtain pyrochlore-free PMN-PT powders. It has been shown that titanium oxide forms a solid solution with columbite (MN) and does not affect the obtaining of a single-phase columbite precursor. Thus, a high amount of perovskite phase can be obtained by reaction with PbO at 800 degreesC for 2 h. Effects of K and Li additives on the structure of MNT and PMN-PT were studied. X-ray diffraction studies were carried out to verify the phase formation at each processing step and these data were used for structural refinement by the Rietveld method. Both K and Li additives increase the crystallinity of MNT powders, being this effect more intense for the Li-doped samples. For PMN-PT samples the additives cause an insignificant decrease in the amount of perovskite phase. The morphology of the PMN-PT powder depends on the type of the additive. (C) 2003 Elsevier B.V All rights reserved.

Effect of the heat flux direction on electrical properties of SrBi2Nb2O9 thin films crystallized using a microwave oven

Ferroelectric SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by spin coating onto Pt/Ti/SiO2/Si substrate and crystallized using a domestic microwave oven. It was studied the influence of the heat flux direction and the duration of the thermal treatment on the films crystallization. An element with high dielectric loss, a SiC susceptor, was used to absorb the microwave energy and transfers the heat to the film. Influence of the susceptor position to the sample crystallization was verified, the susceptor was, placed or below the substrate or above the film. The SBN perovskite phase was observed after a thermal treatment at 700 degreesC for 10 min when the susceptor was placed below the substrate and for 30 min when the susceptor was placed above the film. Electrical measurements revealed that the film crystallized at 700 degreesC for 10 min, with the susceptor placed below the film, presented dielectric constant, dielectric loss, remanent polarization and coercive field of, 67, 0.011, 4.2 muC/cm(2) and 27.5 kV/cm, respectively. When the films were crystallized at 700 degreesC for 30 min, with the susceptor placed above the film, the dielectric constant was 115 and the dissipation factor was around of 0.033, remanent polarization and coercive field were 10.8 muC/cm(2) and 170 kV/cm, respectively. (C) 2003 Elsevier B.V. All rights reserved.

Study of Ti-modified columbite route and the effect of lithium doping in 0.9PMN-0.1PT ceramics

The influence of lithium on the structural characteristics of PMN-PT ceramic was studied. The synthesis of PMN-PT powders using this precursor leads to the formation of high amount of perovskite phase. The insertion of Li(+) ions in B-site affects the microstructure because the rise in mass transport changes the mechanical characteristics of sintered ceramic. Higher values of K(m) and T(m) were gotten when lithium is inserted into perovskite phase. Secondary phase was found when lithium content increase beyond 1 mol%, besides the occurrence of transgranular fractures in sintered ceramic. Also, the additive acts increasing the relaxor behavior.

Mechanochemical synthesis of barium titanate

A powder mixture of BaO and TiO2, was mechanochemically treated in a planetary ball mill in an air atmosphere for up to 4 h, using zirconium oxide vial and zirconium oxide balls as the milling medium. Mechanochemical reaction leads to the gradual formation of BaTiO3 phase. Phase evolution during synthesis and changes in powder size and morphology were monitored by XRD, DSC, IR and TEM analysis and it was shown that the formation of BaTiO3 phase was initiated after 60 min. Extended time of milling directed to formation of higher amount of BaTiO3 perovskite phase. Barium titanate with good crystallinity was formed after 240 min sintering without pre-calcination step was performed at 1330 degrees C for 2 It within heating rate 10 degrees C/min. (c) 2005 Elsevier Ltd. All rights reserved.