Synthesis and Characterization of Au@Pt Nanoparticles with Ultrathin Platinum Overlayers

Gold-core platinum-shell (Au@Pt) nanoparticles with ultrathin platinum overlayers, ranging from submonolayer to two monolayers of platinum atoms, were prepared at room-temperature using a scalable, wet-chemical synthesis route. The synthesis involved the reduction of chloroauric acid with tannic acid to form 5 nm (nominal dia.) gold nanoparticles followed by addition of desired amount of chloroplatinic acid and hydrazine to form platinum overlayers with bulk Pt/Au atomic ratios (Pt surface coverages) corresponding to 0.19 (half monolayer), 0.39 (monolayer), 0.58 (1.5 monolayer) and 0.88 (2 monolayers). The colloidal particles were coated with octadecanethiol and phase-transferred into chlroform-hexane mixture to facilitate sample preparation for structural characterization. The structure of the resultant nanoparticles were determined to be Au@Pt using HRTEM, SAED, XPS, UV-vis and confirmed by cyclic voltammetry (CV) studies. Monolayers of octadecanethiol coated Au@Pt nanoparticles were self-assembled at an air-water interface and transfer printed twice onto a gold substrate to form bilayer films for electrochemical characterization. Electrochemical activity on such films was observed only after the removal of the octadecanethiol ligand coating the nanoparticles, using a RF plasma etching process. The electrochemical activity (HOR, MOR studies) of Au@Pt nanoparticles was found to be highest for particles having a two atom thick platinum overlayer. These nanoparticles can significantly enhance platinum utilization in electrocatalytic applications as their platinum content based activity was three times higher than pure platinum nanoparticles.

PREPARATION AND CHARACTERIZATION OF A MULTICYLINDER MICROELECTRODE COUPLED WITH A CONVENTIONAL GLASSY-CARBON ELECTRODE AND ITS APPLICATION TO THE DETECTION OF DOPAMINE

A multi-cylinder microelectrode coupled with a conventional glassy carbon disc electrode (MCM/GC) was prepared and characterized using cyclic voltammetry and chronoamperometry. It was demonstrated that in the same way as one observed a steady-state current at closely spaced microelectrodes when redox recycling takes place, the same effect can be obtained with the MCM/GC device. The experimental results obtained with K3Fe(CN)6 solutions were compared with a previously developed theory. Further, it was demonstrated that with a carbon fibre MCM/GC device, the voltammetric behaviour of dopamine is greatly improved by virtue of redox recycling, hence giving high sensitivity. The steady-state collection current was linearly related to dopamine concentration in the range 1 X 10(-4) to 5 x 10(-7) Mol l-1, and the detection limit was 2 x 10(-7) mol l-1. The influence of coexisting ascorbic acid was also investigated. This device was applied successfully in the determination of dopamine hydrochloride in pharmaceutical preparations.

Fabrication of Electrochemical Sensors for the Determination of Pharmaceuticals

Voltammetric sensors are an important class of electrochemical sensors in which the analytical information is obtained from the measurement of current obtained as a result of electrochemical oxidation/reduction.This current is proportional to the concentration of the analyte.Chemically modified electrodes(CMEs) have great significance as important analytical tools for the electrochemical determination of pharmaceuticals.The modification of electrode results in efficient determination of electro-active biomolecules at very lower potential without its major interferences.The operation mechanism of CMEs depends on the properties of the modifier materials that are used to promote selectivity towards the target analytes.Modified electrodes can be prepared by deposition of various compounds such as organic compounds ,conducting polymers,metal oxides,etc. on the various electrode surfaces.The thesis presents the development ,electrochemical characterization and analytical application studies of eight voltammetric sensors developed for six drugs viz.,Ambroxol,Sulfamethoxazole,PAM Chloride, Lamivudine,Metronidazole and Nimesulide.The modification techniques adopted as part of the present work include Multiwalled Carbon Nanotube(MWCNT) based modification.Electropolymerisation and Gold Nanoparticle (AuNP) based modifications.

Synthesis, Characterization, and Electrocatalytic Activity toward Methanol Oxidation of Carbon-Supported Pt(x)-(RuO(2)-M)(1-x) Composite Ternary Catalysts (M = CeO(2), MoO(3), or PbO(x))

Carbon-supported platinum is commonly used as an anode electrocatalyst in low-temperature fuel cells fueled with methanol. The cost of Pt and the limited world supply are significant barriers for the widespread use of this type of fuel cell. Moreover, Pt used as anode material is readily poisoned by carbon monoxide produced as a byproduct of the alcohol oxidation. Although improvements in the catalytic performance for methanol oxidation were attained using Pt-Ru alloys, the state-of-the-art Pt-Ru catalyst needs further improvement because of relatively low catalytic activity and the high cost of noble Pt and Ru. For these reasons, the development of highly efficient ternary platinum-based catalysts is an important challenge. Thus, various compositions of ternary Pt(x)-(RuO(2)-M)(1-x)/C composites (M = CeO(2), MoO(3), or PbO(x)) were developed and further investigated as catalysts for the methanol electro-oxidation reaction. The characterization carried out by X-ray diffraction, energy-dispersive X-ray analysis, transmission electron microscopy, X-ray photoelectron spectroscopy, and cyclic voltammetry point out that the different metallic oxides were successfully deposited on the Pt/C, producing small and well-controlled nanoparticles in the range of 2.8-4.2 nm. Electrochemical experiments demonstrated that the Pt(0.50)(RuO(2)-CeO(2))(0.50)/C composite displays the higher catalytic activity toward the methanol oxidation reaction (lowest onset potential of 207 mV and current densities taken at 450 mV, which are 140 times higher than those at commercial Pt/C), followed by the Pt(0.75)(RuO(2)-MoO(3))(0.25)/C composite. In addition, both of these composites produced low quantities of formic acid and formaldehyde when compared to a commercially available Pt(0.75)-Ru(0.25)/C composite (from E-Tek, Inc.), suggesting that the oxidation of methanol occurs mainly by a pathway that produces CO(2) forming the intermediary CO(ads).

Development of an electrochemical sensor based on nanostructured hausmannite-type manganese oxide for detection of sodium ions

The preparation and electrochemical characterization of hausmannite-type manganese oxide to use as a sensing material for sodium ion is described. This paper reports a new via synthetic to obtain of the hausmannite-type manganese oxide and its application in the construction of modified electrode as a voltammetric sensor. The electrochemical activity of hausmannite-type manganese oxide is controlled by intercalation/deintercalation of the sodium ions within the oxide lattice. The detection is based on the measurement of anodic current generated by oxidation of MnIII-MnIV at electrode surface. The best electrochemical response was obtained for a sensor composition of 20% (w/w) hausmannite oxide in the paste, a TRIS buffer solution of pH 6.0-7.0 and a scan rate of 50 mV s-1. A sensitive linear voltammetric response for sodium ions was obtained in the concentration range of 2.01 × 10 -5-2.09 × 10-4 mol L-1 with a slope of 355 μA L mmol-1 and a detection limit of 7.50 × 10 -6 mol L-1 using cyclic voltammetry. The use of hausmannite has significantly improved the selectivity of the sensor compared to the birnessite-type manganese oxide modified electrode. Under the working conditions, the proposed method was successfully applied to determination of sodium ions in urine samples. © 2013 Elsevier B.V.

Electrochemical sensor for ranitidine determination based on carbon paste electrode modified with oxovanadium (IV) salen complex

The preparation and electrochemical characterization of a carbon paste electrode modified with the N,N-ethylene-bis(salicyllideneiminato)oxovanadium (IV) complex ([VO(salen)]) as well as its application for ranitidine determination are described. The electrochemical behavior of the modified electrode for the electroreduction of ranitidine was investigated using cyclic voltammetry, and analytical curves were obtained for ranitidine using linear sweep voltammetry (LSV) under optimized conditions. The best voltammetric response was obtained for an electrode composition of 20% (m/m) [VO(salen)] in the paste, 0.10 mol L- 1 of KCl solution (pH 5.5 adjusted with HCl) as supporting electrolyte and scan rate of 25 mV s- 1. A sensitive linear voltammetric response for ranitidine was obtained in the concentration range from 9.9 × 10- 5 to 1.0 × 10- 3 mol L- 1, with a detection limit of 6.6 × 10- 5 mol L- 1 using linear sweep voltammetry. These results demonstrated the viability of this modified electrode as a sensor for determination, quality control and routine analysis of ranitidine in pharmaceutical formulations. © 2013 Published by Elsevier B.V.

Electrochemical investigation of the voltammetric determination of hydrochlorothiazide using a nickel hydroxide modified nickel electrode

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrochemical performance of carbon gels with variable surface chemistry and physics

This study describes the electrochemical characterization of N-doped carbon xerogels in the form of microspheres and of carbon aerogels with varied porosities and surface oxygen complexes. The interfacial capacitance of N-doped carbon xerogels decreased with increased micropore surface area as determined by N2 adsorption at −196 °C. The interfacial capacitance showed a good correlation with the areal NXPS concentration, and the best correlation with the areal concentration of pyrrolic or pyridonic nitrogen functionalities. The gravimetric capacitance decreased with greater xerogel microsphere diameter. The interfacial capacitance of carbon aerogels increased with higher percentage of porosity as determined from particle and true densities. The interfacial capacitance showed a linear relationship with the areal oxygen concentration and with the areal concentrations of CO- and CO2-evolving groups.

Successful functionalization of superporous zeolite templated carbon using aminobenzene acids and electrochemical methods

A novel and selective electrochemical functionalization of a highly reactive superporous zeolite templated carbon (ZTC) with two different aminobenzene acids (2-aminobenzoic and 4-aminobenzoic acid) was achieved. The functionalization was done through potentiodynamic treatment in acid media under oxidative conditions, which were optimized to preserve the unique ZTC structure. Interestingly, it was possible to avoid the electrochemical oxidation of the highly reactive ZTC structure by controlling the potential limit of the potentiodynamic experiment in presence of aminobenzene acids. The electrochemical characterization demonstrated the formation of polymer chains along with covalently bonded functionalities to the ZTC surface. The functionalized ZTCs showed several redox processes, producing a capacitance increase in both basic and acid media. The rate performance showed that the capacitance increase is retained at scan rates as high as 100 mV s−1, indicating that there is a fast charge transfer between the polymer chains formed inside the ZTC porosity or the new surface functionalities and the ZTC itself. The success of the proposed approach was also confirmed by using other characterization techniques, which confirmed the presence of different nitrogen groups in the ZTC surface. This promising method could be used to achieve highly selective functionalization of highly porous carbon materials.

Synthesis and characterization of nanocomposites based on PANI and carbon nanostructures prepared by electropolymerization

Nanocomposites based on polyaniline (PANI) and carbon nanostructures (CNSs) (graphene (G) and multiwall carbon nanotubes (MWCNTs)) were prepared by in situ electrochemical polymerization. CNSs were inserted into the PANI matrix by dispersing them into the electrolyte before the electropolymerization. Electrochemical characterization by means of cyclic voltammetry and steady state polarization were performed in order to determine conditions for electro- polymerization. Electro-polymerization of the PANI based nanocomposites was carried out at 0.75 V vs. saturated calomel electrode (SCE) for 40 and 60 minutes. The morphology and structural characteristics of the obtained nanocomposites were studied by scanning electron microscopy (SEM) and Raman spectroscopy, while thermal stability was determined using thermal gravimetric analysis (TGA). According to the morphological and structural study, fibrous and porous structure of PANI based nanocomposites was detected well embedding both G and MWCNTs. Also, strong interaction between quinoidal structure of PANI with carbon nanostructures via π–π stacking was detected by Raman spectroscopy. TGA showed the increased thermal stability of composites reinforced with CNSs, especially those reinforced with graphene.

Synthesis and Thermophysical Properties of Ether Functionalized Sulfonium Ionic Liquids as Potential Electrolytes for Electrochemical Applications

During this work, a novel series of hydrophobic room temperature ionic liquids (ILs) based on five ether functionalized sulfonium cations bearing the bis(trifluoromethyl)sulfonylimide, [NTf2]- anion were synthesized and characterized. Their physicochemical properties, such as density, viscosity and ionic conductivity, electrochemical window along with thermal properties including phase transition behavior and decomposition temperature, have been measured. All of these ILs showed large liquid range temperature, low viscosity and good conductivity. Additionally, by combining DFT calculations along with electrochemical characterization it appears that these novel ILs show good electrochemical stability windows, suitable for the potential application as electrolyte materials in electrochemical energy storage devices.

Study of the Electrochemical, Physical and Morphological Characteristics of Anode Catalysts for Perfluorosulfonic Acid (PFSA) Membrane Water Electrolysers

A number of supported and un-supported Oxygen Evolution Reaction (OER) iridium based electrocatalysts for Polymer Electrolyte Membrane Water Electrolysis (PEMWE) were synthesized using a polyol method. The electrocatalysts and the supports were characterized using a wide range of physical and electrochemical characterization methods. The effect of morphological characteristics of the OER electrocatalyst and the support on the OER activity was studied. The results of this thesis contribute to the existing research to reduce the cost of PEMWE by enhancing the utilization of precious metal for OER electrocatalysis. Iridium electrocatalysts supported on antimony tin oxide (Ir/ATO) were synthesized using the polyol method with two different heating techniques: conventional and microwave-irradiation. It was shown that the physical morphology and electrochemical properties of Ir/ATO synthesized with the two heating methods were comparable. However, the microwave irradiation method was extremely faster than the conventional heating method. Additionally, the effect of heat treatment (calcination temperature) on the morphology and OER activity of Ir/ATO synthesized electrocatalyst with the conventional polyol method. It was found that the iridium electrocatalyst synthesized with the polyol method, consisted of 1-5 nm particles, possessed an amorphous structure, and contained iridium with an average oxidation state of less than +4. Calcining the catalyst at temperatures more than 400 ºC and less than 700ºC: 1) increased the size of the iridium particles to 30 nm, 2) changed the structure of iridium particles from amorphous to crystalline, 3) increased the iridium oxidation state to +4 (IrO2), 4) reduced the electrochemically active surface area by approximately 50%, and 5) reduced the OER activity by approximately 25%; however, it had no significant effect on the physical and chemical morphology of the ATO support. Moreover, potential support metal carbides and oxides including: Tantalum Carbide (TaC), Niobium Oxide (Nb2O5), Niobium Carbide (NbC), Titanium Carbide (TiC), Tungsten Carbide (WC) and Antimony-doped Tin Oxide (ATO, Sb2O5-SnO2), were characterized, and used as support for the iridium OER electrocatalysts. TaC was found to be a promising support, and increasing its surface area by 4% improved the OER performance of the final supported catalyst by approximately 50%.

In-situ one-step hydrothermal synthesis of a lead germanate-graphene composite as a novel anode material for lithium-ion batteries

Lead germanate-graphene nanosheets (PbGeO3-GNS) composites have been prepared by an efficient one-step, in-situ hydrothermal method and were used as anode materials for Li-ion batteries (LIBs). The PbGeO3 nanowires, around 100–200 nm in diameter, are highly encapsulated in a graphene matrix. The lithiation and de-lithiation reaction mechanisms of the PbGeO3 anode during the charge-discharge processes have been investigated by X-ray diffraction and electrochemical characterization. Compared with pure PbGeO3 anode, dramatic improvements in the electrochemical performance of the composite anodes have been obtained. In the voltage window of 0.01–1.50 V, the composite anode with 20 wt.% GNS delivers a discharge capacity of 607 mAh g−1 at 100 mA g−1 after 50 cycles. Even at a high current density of 1600 mA g−1, a capacity of 406 mAh g−1 can be achieved. Therefore, the PbGeO3-GNS composite can be considered as a potential anode material for lithium ion batteries.

Pd Supported on Titanium Nitride for Efficient Ethanol Oxidation

The excellent metal support interaction between palladium (Pd) and titanium nitride (TiN) is exploited in designing an efficient anode material. Pd-TN, that could be useful for direct ethanol fuel cell in alkaline media. The physicochemical and electrochemical characterization of the Pd-TiN/electrolyte interface reveals an efficient oxidation of ethanol coupled with excellent stability of the catalyst under electrochemical conditions. Characterization of the interface using in situ Fourier transform infrared spectroscopy (in situ FITR) shows the production CO2 at low overvoltages revealing an efficient cleaving of the C-C bond. The performance comparison of Pd supported on TiN (Pd-TiN) with that supported on carbon (Pd-C) clearly demonstrates the advantages of TiN support over carbon. A positive chemical shift of Pd (3d) binding energy confirms the existence of metal support interaction between pd and TiN, which in turn helps weaken the Pd-CO synergetic bonding interaction. The remarkable ability of TiN to accumulate -OH species on its surface coupled with the strong adhesion of Pd makes TiN an active support material for electrocatalysts.

Growth of Polypyrrole-Horseradish Peroxidase Microstructures for H2O2 Biosensor

Conducting polymer microstructures for enzymatic biosensors are developed by a facile electrochemical route. Horseradish peroxide (HRP)-entrapped polypyrrole (PPy) films with bowl-shaped microstructures are developed on stainless steel (SS 304) substrates by a single-step process. Potentiodynamic scanning/cyclic voltammetry is used for generation of PPy microstructures using electrogenerated oxygen bubbles stabilized by zwitterionic surfactant/buffer N-2-hydroxyethylpiperazine N-2-ethanesulfonic acid as soft templates. Scanning electron microscopic images reveal the bowl-shaped structures surrounded by cauliflower-like fractal PPy films and globular nanostructures. Raman spectroscopy reveals the oxidized nature of the film. Sensing properties of PPy-HRP films for hydrogen peroxide (H2O2) are demonstrated. Electrochemical characterization of the sensor films is done by linear sweep voltammetry (LSV) and amperometry. LSV results indicated the reduction of H2O2 and linearity in response of the sensing film. The amperometric biosensor has a performance comparable to those in the literature with advantages of hard-template free synthesis procedure and a satisfactory sensitivity value of 12.8 mu A/(cm(2) . mM) in the range of 1-10 mM H2O2.