Innovaciones en la gestión y calidad de los revestimientos refractarios en la Compañía Sideŕurgica Nacional (Brasil)

The work describes actions carried out in colaboration among the National Steel Company - (CSN)-Brazil and the Interdisciplinary Laboratory of Electrochemistry and Ceramic - LIEC of the Federal University of Sao Carlos Brazil (UFSCar-Brazil), in the area of I&D, for integral management and improvement of the quality and performance of the refractory linings in the sintering areas, blast furnace, hot air pipe lines transferency to the blast furnace, pig-iron ladles, running channels, blast furnaces hearths, torpedo car, etc., as well as, the economic impact generated by the installation of the adopted measures.

Estudio de PMN cerámico dopado con KNbO3 y LiNbO 3 sintetizado por Pechini

PMN belongs to a special class of materials named relaxor ferroelectrics. It has high volumetric efficiency due to its high dielectric constant, which makes it in a perfect material for application in multilayer capacitors. When prepared the columbite route its preparation has many advantages. In this work, the preparations of columbite and PMN were done by Pechini and Partial Oxalate methods, respectively. The effects of the KNbO3 and LiNbO3 dopants added in various concentrations. The idea is founded on the correlations that they have with BaTiO3 y PbTiO3, respectively. The whole process was supervised by TG/DTA, XRD, SEM and determination of the specific surface area of the powders. LiNbO3 carries out the pre-sinterization of the particles, observed by a reduction in the surface area. There are not particle grow, but occur its lengthening. However, for KNbO3 these particle growth, but the agglomerates are softer. The effect produced by the doping during the synthesis of the PMN powder is different from the one produced in the columbite precursor. Pure precursor shows an average particle size of 0,2μm, but the addition of 5,0mol% of dopants carries out the formation of agglomerates close to 4μm. LiNbO 3 addition carries out spherical particles and pre-sinterization, while KNbO3 addition does not change the particles shape.

Estudio de la adición de K+ y LiNbO3 en las propiedades finales del relaxor PMN procesado por mezcla de polvos

PMN ceramic relaxor has been investigated by several researchers and many aspects of this material, like powder morphology, phase decomposition, weight loss during sintering process, densification, between others, still are investigated. PMN powder preparation has been shown more efficient when synthesized by columbite route, however lead addition stage for the PMN powder synthesis remains problematical. Therefore, this work proposes a new association of methodologies, using columbite route and the hydroxide precipitation method. Through use of the powder mixture technique, which permitted to obtain good green and sintered densities, was possible to observe K+ y Li + dopants reduce weight loss in sintering process and change significantly the dielectric properties. Addition of LiNbO3 seeds in conformation stage, which react in a distinct way as a function of the particle size, promotes the formation of differenced grains in the ceramic bulk. Consequently, very different dielectrics properties from conventional PMN ceramic were obtained.

Uso de métodos químicos para obtener polvos cerámicos del sistema (Sn, Ti)O2

The (Sn,Ti)O2, system has a great interest due to its technological applications such as gas sensor and varistor. Although the thermodynamic properties and the kinetics of spinoidal decomposition in this system have been extensively studied, the general properties and applications of SnO2 - TiO2 binary compositions have been not investigated yet in depth. On the other hand, little work has been done to optimize the synthesis methods to obtain (Sn,Ti)O2 cerallmic powders, with pre - determinate physical and chemical characteristics. In this work the ceramic powders has been obtained by coprecipitation and polymeric precursor (Pechini) methods. The different physical chemistry phenomena that occurred during the synthesis were discussed. The (Sn,Ti)O2, ceramic powders were characterized with X- ray diffraction (XRD), thermal analysis (DTA/TG) and scanning electron microscopy (SEM). The knowledge about of steps and variables of synthesis process acquired with development of this work, we permited to obtain (Sn, Ti)O2, nanometers particles to low temperatures: to 450°C for coprecipitation method and to 600°C for Pechini method. The spinodal decomposition that ocurr to 900°C was discussed also.

Degradación y recuperación de varistores de ZnO

In the present work it was studied the main aspect that influences on degradation and physical-chemical properties at grain-boundary region of metal oxide varistors and its consequences on microstructure and nonohmic electric properties. Based on the comprehension of the degradation aspects it was proposed some methodologies to recover the varistors nonohmic properties after being failed with long (2000 μs) and short current pulses (8/20 μs). Our analysis shown that one of the cause of degradation process is related to the lowering of oxygen species amount at grain-boundary region. Therefore, it is possible to re-promote oxygen enrichment of such regions by specific thermal treatments in rich oxygen atmospheres (the best condition found in the present work was temperatures around 900°C for 2 h at an oxygen flux of 15 1/h). The proposed nonohmic properties recovering procedure appear to be valid for all kind metal oxide varistors studied and is very important from technological point of view.

Métodos químicos para obtener varistores basados en SnO2

Synthesis of SnO2 ceramic powders was made by coprecipitation method and polymeric precursor method (Pechini) to obtain Sn-Co-Nb-Ti-Al varistor systems. The particles of the obtained ceramic powder presented nanometric size and SnO2 was the principal crystalline phase in them according to X-ray diffraction results. To determine the behavior of the synthesized samples in front of the thermal treatments, thermal analysis (DTA/TG) were made. Dilatometric studies on previously pressed samples were carried out. The optimal conditions of sintering of this raw material were determined. Microstructures and electric properties of sintered samples were studied using scanning electron microscopy (SEM) and I-V characteristics curves. The samples presented varistor behavior independent of the synthesis method used, with high nonlinearity values as 32. The presence of Al3+ favored the concentration of oxygen vacancies, and the grain growth.

Respuesta eléctrica de películas gruesas del sistema SnO2-TiO2, conformadas con polvos cerámicos obtenidos a través del método pechini

Tin oxide is the compound more used in the gas sensor production, mainly to reduce gases like CO and H2. Their electrical properties are strongly dependent of its surface. For this is of great importance to synthesize nanoscale tin oxide particles to use they later in the films conformation. The synthesis of SnO2-TiO2 nanoparticles by polymeric precursor method is reported in this work. The particles were characterized by DTA/TG, FT-IR, XRD and SEM. Also, the electrical response of thick films measured under oxygen and carbon monoxide atmospheres is was analyzed.

Influencia del TiO2 y Al2O3 sobre las propiedades eléctricas y microestructurales de cerámicas de SnO2 obtenidas por el método Pechini

Tin oxide has wakened up great scientific and technological interest for its potential use in varistors production and as gas sensor. In order to improve the microstructural and electrical properties in SnO varistor ceramics, the influence of differents dopants used, like TiO2 and Al2O3, is under research. The effect of TiO2 and Al2O3 on the properties of Sn-Co-Nb varistor Systems obtained by the Pechini method has been investigated in this work. Characterization of synthesized raw material was performed by X-Ray Diffraction (XRD) and Scanning Electronic Microscopy (SEM). The microstructural and electrical characterization of sintered samples show that the TiO2 favors the grain growth and the Al2O3, contributes to the decrease it, effect that is manifested in the Sn-Co-Nb varistor systems. Breakdown field increase up to 6300V/cm with increasing Al2O3 content and non-linear coefficients with α=22 were obtained.

Anelastic characterization and superconducting properties of RuSr2GdCu2O8+δ

Since the discovery of the high Tc superconductors, many researches have been carried out on the different properties of these materials, especially on the transition temperature into the superconducting state. The rutheno-cuprates belong to a new class of composites, which were synthesized for the first time by Bauernfeind in 1995. Bernhard and collaborators discovered, in 1999, the coexistence of the ferromagnetism and the superconductivity in this phase, which is known as antagonistic phenomenon in the electromagnetism due to spin-charge interactions established in these states. However, the physical nature of the superconducting and magnetic states is still very obscure. The non-stoichiometric (interstitial) oxygen is considered as a possible cause for the non-uniformity of the sample properties. In this paper, results of mechanical spectroscopy in Ru-1212 samples are presented showing complex anelastic spectra, which were attributed to the mobility of the interstitial oxygen atoms in the Ru-1212 lattice.

Effect of airborne particle abrasion protocols on surface topography of Y-TZP ceramic

This study aimed to evaluate Y-TZP surface after different airborne particle abrasion protocols. Seventy-six Y-TZP ceramic blocks (5×4×4) mm3 were sintered and polished. Specimens were randomly divided into 19 groups (n=4) according to control group and 3 factors: a) protocol duration (2 and 4 s); b) particle size (30 μm, alumina coated silica particle; 45 μm, alumina particle; and 145 μm, alumina particle) and; c) pressure (1.5, 2.5 and 4.5 bar). Airborne particle abrasion was performed following a strict protocol. For qualitative and quantitative results, topography surfaces were analyzed in a digital optical profilometer (Interference Microscopic), using different roughness parameters (Ra, Rq, Rz, X-crossing, Mr1, Mr2 and Sdr) and 3D images. Surface roughness also was analyzed following the primer and silane applications on Y-TZP surfaces. One-way ANOVA revealed that treatments (application period, particle size and pressure of particle blasting) provided significant difference for all roughness parameters. The Tukey test determined that the significant differences between groups were different among roughness parameters. In qualitative analysis, the bonding agent application reduced roughness, filing the valleys in the surface. The protocols performed in this study verified that application period, particle size and pressure influenced the topographic pattern and amplitude of roughness.

New methodology for a faster synthesis of SrSnO3 by the modified Pechini method

SrSnO3, a perovskite-type complex oxide, was synthesized by the modified Pechini method using two different precursors, tin chloride and metallic tin. The first one is already traditional in the literature and it claims about 30 days, only for the cleaning of tin citrate aiming at the elimination of the chloride. The second route was developed by our research group and saves time, taking 6 h to complete the synthesis of the resin. The results show that SrSnO3 obtained from the metallic tin show a higher short range order, leading to a band gap value higher than those reported in the literature, besides a meaningful reduction in the formation of SrCO 3, as compared to the one obtained from tin chloride.

Arte em cerâmica e a memória como elemento criativo

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Celeida Tostes: o barro como elemento integrativo na Arte Conteporânea

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Shôjo mangá: de Gengi Monogarati a Miou Takaya

Pós-graduação em Artes - IA

Mulheres recipientes: recortes poéticos do universo feminino nas artes visuais

Pós-graduação em Artes - IA