Low loss and frequency (1 kHz-1 MHz) independent dielectric characteristics of 3BaO-3TiO(2)-B2O3 glasses

X-ray powder diffraction along with differential thermal analysis carried out on the as-quenched samples in the 3BaO-3TiO(2)-B2O3 system confirmed their amorphous and glassy nature, respectively. The dielectric constants in the 1 kHz-1 MHz frequency range were measured as a function of temperature (323-748 K). The dielectric constant and loss were found to be frequency independent in the 323-473 K temperature range. The temperature coefficient of dielectric constant was estimated using Havinga's formula and found to be 16 ppm K-1. The electrical relaxation was rationalized using the electric modulus formalism. The dielectric constant and loss were 17 +/- 0.5 and 0.005 +/- 0.001, respectively at 323 K in the 1 kHz-1 MHz frequency range which may be of considerable interest to capacitor industry.

Apparent shortening of the Csp(3)-Csp(3) bond analysed via a variable-temperature X-ray diffraction study in racemic 1,1 '-binaphthalene-2,2 '-diyl diethyl bis(carbonate)

Crystal structure determination at room temperature [292 (2) K] of racemic 1,1'-binaphthalene-2,2'-diyl diethyl bis(carbonate), C26H22O6, showed that one of the terminal carbon-carbon bond lengths is very short [Csp(3)-Csp(3) = 1.327 (6) angstrom]. The reason for such a short bond length has been analysed by collecting data sets on the same crystal at 393, 150 and 90 K. The values of the corrected bond lengths clearly suggest that the shortening is mainly due to positional disorder at two sites, with minor perturbations arising as a result of thermal vibrations. The positional disorder has been resolved in the analysis of the 90 K data following the changes in the unit-cell parameters for the data sets at 150 and 90 K, which appear to be an artifact of a near centre of symmetry relationship between the two independent molecules in the space group P (1) over bar at these temperatures. Indeed, the unit cell at low temperature (150 and 90 K) is a supercell of the room-temperature unit cell.

H-1 and F-19 NMR relaxation time studies in (NH4)(2)ZrF6 superionic conductor

H-1 and F-19 spin-lattice relaxation times in polycrystalline diammonium hexafluorozirconate have been measured in the temperature range of 10-400 K to elucidate the molecular motion of both cation and anion. Interesting features such as translational diffusion at higher temperatures, molecular reorientational motion of both cation and anion groups at intermediate temperatures and quantum rotational tunneling of the ammonium group at lower temperatures have been observed. Nuclear magnetic resonance (NMR) relaxation time results correlate well with the NMR second moment and conductivity studies reported earlier.

Electrical Properties of Thermal Evaporated Cd1−xMnxS Nanocrystalline Films

Thin films of Cd1−xMnxS (0<=x<=0.5) were deposited on glass substrates by thermal evaporation. All the films were deposited at 300 K and annealed at 373, 473, and 573 K for 1 h in a high vacuum in the range 10−4 Pa. The as-deposited and the annealed films were characterized for composition, structure, and microstructure by using energy-dispersive X-ray, X-ray diffraction, scanning electron microscopy, and atomic force microscopy (AFM). The electrical properties were studied by Hall effect measurement. Electrical conductivity was studied in the temperature range 190–450 K. AFM studies showed that all the films were in nanocrystalline form with grain size varying in the range between 36 and 82 nm. Grain size studies showed a definite increase with annealing temperature. All the films exhibited wurtzite structure of the host material. The lattice parameter varied linearly with composition, following Vegard's law in the entire composition range. Grain size, electrical conductivity, Hall mobility, carrier concentration, and activation energy varied, exhibiting either maxima or minima at x=0.3.

Generalized survival in step fluctuations

The properties of the generalized survival probability, that is, the probability of not crossing an arbitrary location R during relaxation, have been investigated experimentally (via scanning tunneling microscope observations) and numerically. The results confirm that the generalized survival probability decays exponentially with a time constant tau(s)(R). The distance dependence of the time constant is shown to be tau(s)(R)=tau(s0)exp[-R/w(T)], where w(2)(T) is the material-dependent mean-squared width of the step fluctuations. The result reveals the dependence on the physical parameters of the system inherent in the prior prediction of the time constant scaling with R/L-alpha, with L the system size and alpha the roughness exponent. The survival behavior is also analyzed using a contrasting concept, the generalized inside survival S-in(t,R), which involves fluctuations to an arbitrary location R further from the average. Numerical simulations of the inside survival probability also show an exponential time dependence, and the extracted time constant empirically shows (R/w)(lambda) behavior, with lambda varying over 0.6 to 0.8 as the sampling conditions are changed. The experimental data show similar behavior, and can be well fit with lambda=1.0 for T=300 K, and 0.5 K. Over this temperature range, the ratio of the fixed sampling time to the underlying physical time constant, and thus the true correlation time, increases by a factor of similar to 10(3). Preliminary analysis indicates that the scaling effect due to the true correlation time is relevant in the parameter space of the experimental observations.

Gibbs Energy of Formation of MnO: Measurement and Assessment

Based on the measurements of Alcock and Zador, Grundy et al. estimated an uncertainty of the order of +/- 5 kJ mol(-1) for the standard Gibbs energy of formation of MnO in a recent assessment. Since the evaluation of thermodynamic data for the higher oxides Mn3O4, Mn2O3, and MnO2 depends on values for MnO, a redetermination of its Gibbs energy of formation was undertaken in the temperature range from 875 to 1300 K using a solid-state electrochemical cell incorporating yttria-doped thoria (YDT) as the solid electrolyte and Fe + Fe1-delta O as the reference electrode. The cell can be presented as Pt, Mn + MnO/YDT/Fe + Fe1+delta O, Pt Since the metals Fe and Mn undergo phase transitions in the temperature range of measurement, the reversible emf of the cell is represented by the three linear segments. Combining the emf with the oxygen potential for the reference electrode, the standard Gibbs energy of formation of MnO from alpha-Mn and gaseous diatomic oxygen in the temperature range from 875 to 980 K is obtained as: Delta G(f)(o)/Jmol(-1)(+/- 250) = -385624 + 73.071T From 980 to 1300 K the Gibbs energy of formation of MnO from beta-Mn and oxygen gas is given by: Delta G(f)(o)/Jmol(-1)(+/- 250) = -387850 + 75.36T The new data are in excellent agreement with the earlier measurements of Alcock and Zador. Grundy et al. incorrectly analyzed the data of Alcock and Zador showing relatively large difference (+/- 5 kJ mol(-1)) in Gibbs energies of MnO from their two cells with Fe + Fe1-delta O and Ni + NiO as reference electrodes. Thermodynamic data for MnO is reassessed in the light of the new measurements. A table of refined thermodynamic data for MnO from 298.15 to 2000 K is presented.

1H NMR study of internal motions and quantum rotational tunneling in (CH3)4NGeCl3

(CH3)4NGeCl3 is prepared, characterized and studied using 1H NMR spin lattice relaxation time and second moment to understand the internal motions and quantum rotational tunneling. Proton second moment is measured at 7 MHz as function of temperature in the range 300-77 K and spin lattice relaxation time (T1) is measured at two Larmor frequencies, as a function of temperature in the range 270-17 K employing a homemade wide-line/pulsed NMR spectrometers. T1 data are analyzed in two temperature regions using relevant theoretical models. The relaxation in the higher temperatures (270-115 K) is attributed to the hindered reorientations of symmetric groups (CH3 and (CH3)4N). Broad asymmetric T1 minima observed below 115 K down to 17 K are attributed to quantum rotational tunneling of the inequivalent methyl groups.

Melting of an Anchored Bilayer: Molecular Dynamics Simulations of the Structural Transition in (CnH2n+1NH3)(2)PbI4 (n=12, 14, 16, 18)

The thermally driven Structural phase transition in the organic-inorganic hybrid perovskite (CnH2n+1NH3)(2)PbI4 has been investigated using molecular dynamics (MD) simulations. This system consists of positively charged alkyl-amine chains anchored to a rigid negatively charged PbI4 sheet with the chains organized as bilayers with a herringbone arrangement. Atomistic simulations were performed using ail isothermal-isobaric ensemble over a wide temperature range from 65 to 665 K for different alkyl chain lengths, n = 12, 14, 16, and 18. The simulations are able to reproduce the essential Features of the experimental observations of this system, including the existence of a transition, the linear variation of the transition temperature with alkyl chain length, and the expansion of the bilayer thickness at the transition. By use of the distance fluctuation Criteria, it is Shown that the transition is associated With a Melting of the alkyl chains of the anchored bilayer. Ail analysis of the conformation of the alkyl chains shows increased disorder in the form of gauche defects above due melting transition. Simulations also show that the melting transition is characterized by the complete disappearance of all-trans alkyl chains in the anchored bilayer, in agreement with experimental observations. A conformationally disordered chain has a larger effective cross-sectional area, and above due transition a uniformly tilted arrangement of the anchored chains call no longer be Sustained. At the melt the angular distribution of the orientation of the chains are 110 longer uniform; the chains are splayed allowing for increased space for individual chains of the anchored bilayer. This is reflected in a sharp rise in the ratio of the mean head-to-head to tail-to-tail distance of the chains of the bilayer at the transition resulting in in expansion of the bilayer thickness. The present MD simulations provide a simple explanation as to how changes in conformation of individual alkyl-chains gives rise to the observed increase in the interlayer lattice spacing of (CnH2n+1NH3)(2)PbI4 at the melting transition.

Possible application of carbon nanotube bundles for low temperature sensing

We report on the R-T measurement of carbon nanotube bundles from room temperature down to 1 K. The resistance at a particular temperature depends on the diameter of the bundle. The larger the bundle diameter is, the lower the value of the resistance. The resistance increases with the decrease in temperature as in the case of carbon, carbon glass resistance thermometer, and carbon nanotubes reported in the literature. The rate of the variation of resistance depends on the resistance of the bundle at room temperature which can be explored for the low temperature thermometry. Overall, the resistance and the sensitivity of the bundle depend on the bundle diameter which can be monitored easily.

Study of molecular reorientation and quantum rotational tunneling in tetramethylammonium selenate by H-1 NMR

H-1 NMR spin-lattice relaxation time measurements have been carried out in [(CH3)(4)N](2)SeO4 in the temperature range 389-6.6K to understand the possible phase transitions, internal motions and quantum rotational tunneling. A broad T, minimum observed around 280K is attributed to the simultaneous motions of CH3 and (CH3)(4)N groups. Magnetization recovery is found to be stretched exponential below 72 K with varying stretched exponent. Low-temperature T-1 behavior is interpreted in terms of methyl groups undergoing quantum rotational tunneling. (c) 2007 Elsevier Inc. All rights reserved.

On the low temperature deformation mechanism in polycrystalline cadmium

The thermally activated plastic flow of polycrystalline cadmium was investigated by differentialstress creep tests at 86°K and tensile tests in the temperature range 86°–473°K. The activation energy (0.55 eV) at zero effective stress and the activation volume as a function of effective stress were obtained. It is concluded that intersection of glide and forest dislocations becomes rate controlling for low temperature deformation. The approximate stacking-fault width in cadmium is deduced to be “1.5b”.

Dielectric, pyroelectric and ferroelectric properties of Bi4Ti2.98Nb0.01Ta0.01O12 ceramics

The electrical conductivity and electrical relaxation for ferroelectric Bi4Ti2.98Nb0.01Ta0.01O12 (BTNT) ceramics have been reported in the frequency range 0.1 Hz to 1 MHz and in the 300-550 degrees C temperature range. The electrical data was analyzed in the framework of the dielectric as well as the electric modulus formalisms. The bulk dc conductivity at various temperatures was extracted from the electrical relaxation data. The activation energy associated with the electrical relaxation determined from the electric modulus spectra was found to be 0.93 +/- 0.03 eV, close to that of the activation energy for dc conductivity (1.03 +/- 0.02 eV). It suggests that the movements of oxygen ions are responsible for both ionic conduction as well as the relaxation process. The pyroelectric coefficient was found to be 12 mu C m(-2) K-1 at room temperature which is higher than that of the reported value of pyroelectric coefficient for undoped Bi4Ti3O12 ceramics. (C) 2010 Elsevier B.V. All rights reserved.

Unusual metallic-like transport near the percolation threshold

In multiwall carbon nanotube (MWNT)-polystyrene (PS) composites, a weak temperature dependence of conductivity has been observed at a percolation threshold of 0.4 wt %. The power law [sigma(T)proportional to T-0.3] behavior indicates metallic-like behavior, unlike the usual activated transport for systems near the percolation threshold. The low field positive magnetoconductance follows H-2 dependence, due to the weak localization in disordered metallic systems. The marginal metallic nature of MWNT-PS at percolation threshold is further verified from the negligible frequency dependence of conductivity, in the temperature range of 300 to 5 K. (C) 2010 American Institute of Physics. [doi: 10.1063/1.3455895]

Thermodynamics of GdMnO3 and GdMn2O5 phases determined by the EMF method

Using solid oxide galvanic cells of the type: MnO + Gd2O3 + GdMnO3/O-2/Ni + NiO and Mn3O4 + GdMnO3 + GdMn2O5/O-2/air the equilibrium oxygen pressure for the following reactions :MnO + 1/2Gd(2)O(3) + 1/4O(2) = GdMnO3 1/3Mn(3)O(4) + GdMnO3 + 1/3O(2) = GdMn2O5 was determined in the temperature range from 1073 to 1450 K. From the determined equilibrium oxygen partial pressure the corresponding G i b b s free energy change for these reactions was derived: Delta G(f,GdMnO3)(0) (+/- 425J) 132721(+/ - 2240) +51.91(+/ - 0.81)T Delta G(f,GdMn2O5)(0)(+/- 670J) 121858(+/ - 6176) + 79.52(+/ - 4.83)T From these data, standard G i b b s energies, enthalpies and entropies of formation of GdMnO3 and GdMn2O5 from component oxides and from the elements are derived. Thermodynamic data tables for the two ternary phases are compiled from 298.15 to 1400 K.

Novel Nanocomposites Made of Boron Nitride Nanotubes and a Physical Gel

This article describes successful incorporation of multiwalled boron nitride nanotubes (BNNTs) and various functionalized BNNTs by Lewis bases such as trioctylamine (TOA), tributylamine (TBA), and triphenylphosphine (TPP), etc., in organogels formed by triphenylenevinylene (TPV)-based low molecular weight gelator (LMWG) in toluene and consequent characterization of the resulting gel nanocomposites. Functionalized BNNTs were synthesized first,and the presence of tubular structures with high aspect ratio and increased diameter compared to the starting BNNTs was confirmed by SEM. TEM, and Raman spectroscopy. The micrographs of composites of I and BNNTs showed evidence of wrapping of the gelator molecules on to the BNNT surface presumably brought about by pi-pi stacking and van der Waals interactions, This leads to the formation of densely packed and directionally aligned fibrous networks. Such ``reinforced'' aggregation of the gelator molecules in presence of doped BNNTs led to an increase in the sot-to-gel transition temperature and the solidification temperature of the gel nanocomposites as revealed from differential scanning calorimetry. Rheological investigations of the gel nanocomposites indicate that the flow properties of the resulting materials become resistant to applied stress upon incorporation of even a very low wt % of BNNTs. Finally, the increase in thermal conductivity of the nanocomposite compared to the gelator alone was observed for the temperature range of 0-60 degrees C which may make these composites potentially useful in various applications depending on the choice and the amount of BNNT loading in the composite.