Compositional and structural changes at the anodic surface of thermally poled soda-lime float glass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Degradation of the surface of a metasilicate glass due to atmosphere moisture

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Radionuclide concentrations in raw and purified phosphoric acids from Brazil and their processing wastes: implications for radiation exposures

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and evaluation of an experimental luting glass ionomer cement to be used in dentistry

The aim of this paper is to compare the fluoride-releasing and mechanical properties of an experimental luting glass ionomer cement, which has a modified composition and a commercial luting cement. The experimental powder was obtained by sol-gel process and then, it was used to prepare the experimental cements. The properties of cement pastes, such as setting time and working time, microhardness and diametral tensile strength were determined. Fluoride release from GICs was evaluated at time intervals of 1, 7, 14, 21 and 28 days in deionized water. Atomic force microscopy (AFM) analyses showed that the surface of the experimental cements is more homogeneous than commercial GICs. The mechanical properties and the measure of liberation of fluoride of the two cements were influenced by ratio powder:liquid and chemical composition of the precursor powders. Experimental cements released less fluoride than commercial cements. However, this liberation was more constant during the analyzed period. Thus, the results obtained in this study indicated that the composition of the experimental powder modified by the niobium can lead the formation of the polysalt matrix with good mechanical properties. In other words, we can say that experimental powder offered considerable promise for exploitation in dental field.

SnO2 nanoparticles functionalized in amorphous silica and glass

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Polycyclic aromatic hydrocarbons (PAHs) in raw cane sugar (rapadura) in Brazil

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Pump excited state absorption in holmium-doped fluoride glass

The primary excited state absorption processes relating to the (5)I(6) -> (5)I(7) 3 mu m laser transition in singly Ho(3+)-doped fluoride glass have been investigated in detail using time-resolved fluorescence spectroscopy. Selective laser excitation of the (5)I(6) and (5)I(7) energy levels established the occurrence of two excited state absorption transitions from these energy levels that compete with previously described energy transfer upconversion processes. The (5)I(7) -> (5)I(4) excited state absorption transition has peak cross sections at 1216 nm (sigma(esa)=2.8x10(-21) cm(2)), 1174 nm (sigma(esa)=1x10(-21) cm(2)), and 1134 nm (sigma(esa)=7.4x10(-22) cm(2)) which have a strong overlap with the (5)I(8) -> (5)I(6) ground state absorption. on the other hand, it was established that the excited state absorption transition (5)I(6) -> (5)S(2) had a weak overlap with ground state absorption. Using numerical solution of the rate equations, we show that Ho(3+)-doped fluoride fiber lasers employing pumping at 1100 nm rely on excited state absorption from the lowest excited state of Ho(3+) to maintain a population inversion and that energy transfer upconversion processes compete detrimentally with the excited state absorption processes in concentrated Ho(3+)-doped fluoride glass. (c) 2008 American Institute of Physics.

Color tunability of intense upconversion emission from Er3+-Yb3+ co-doped SiO2-Ta2O5 glass ceramic planar waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Refractive index changes in photochromic SbPO4-WO3 glass by exposure to band-gap radiation

We report photoinduced photo-darkening in SbPO4-WO3 glass by exposure to 532 nm light with a power density of 143 mW/cm(2). The time of exposure was varied between 0 and 256 min following which visible photo-darkening, peaking at 850 nm was observed. Spectrophotometer measurement of absorption was performed for both treated and untreated regions of the sample. Time exposure to below band-gap light results in a single exponent Gaussian absorption function over an exceptionally wide range of wavelengths (500 nm-1600 nm), with a 1/e width of 647.5 nm. Kramers-Kronig transform of the change in the absorption indicates a negative local change in the refractive index. The dispersed refractive index change at 1550 nm, Delta n, is calculated to be similar to -5 x 10(-8). The peak absorption increases with time of exposure and the photo-darkening remains irreversible at room temperature. Crown Copyright (C) 2010 Published by Elsevier B.V. All rights reserved.

Plasmonic Coupling in Er3+:Au Tellurite Glass

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural study of thin films prepared from tungstate glass matrix by Raman and X-ray absorption spectroscopy

Thin films were prepared using glass precursors obtained in the ternary system NaPO(3)-BaF(2)-WO(3) and the binary system NaPO(3)-WO(3) with high concentrations of WO(3) (above 40% molar). Vitreous samples have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. Several structural characterizations were performed by Raman spectroscopy and X-ray Absorption Near Edge Spectroscopy (XANES) at the tungsten L(I) and L(III) absorption edges. XANES investigations showed that tungsten atoms are only sixfold coordinated (octahedral WO(6)) and that these films are free of tungstate tetrahedral units (WO(4)). In addition, Raman spectroscopy allowed identifying a break in the linear phosphate chains as the amount of WO(3) increases and the formation of P-O-W bonds in the films network indicating the intermediary behavior of WO(6) octahedra in the film network. Based on XANES data, we suggested a new attribution of several Raman absorption bands which allowed identifying the presence of W-O and W=O terminal bonds and a progressive apparition of W-O-W bridging bonds for the most WO(3) concentrated samples (above 40% molar) attributed to the formation of WO(6) clusters. (C) 2008 Elsevier B.V. All rights reserved.

Structural Investigations of Glass Ceramics in the Ga2S3-GeS2-CsCl System

Transparent glass ceramics have been prepared in the Ga2S3-GeS2-CsCI pseudoternary system appropriate heat treatment time and temperature. In situ X-ray diffraction at the heat treatment temperature and Cs-133 and Ga-71 solid-state nuclear magnetic resonance have been performed in function of annealing time to understand the crystallization process. Both techniques have evidenced the nucleating agent role played by gallium with the formation of Ga2S3 nanocrystals. on the other hand, cesium is incorporated very much later into the crystallites during the ceramization. Moreover, the addition of CsCl, which is readily integrated into the glassy network, permits us to shift the optical band gap toward shorter wavelength. Thus, new glass ceramics transmitting in the whole visible range up to 11.5 mu m have been Successfully synthesized from the (Ga2S3)(35)-(GeS2)(25)-CsCl40 base glass composition.

Occurrence of toxigenic Escherichia coli in raw milk cheese in Brazil

Pesquisou-se a ocorrência de Escherichia coli toxigênica, em queijo produzido com leite não pasteurizado, na Região Centro Oeste do Brazil. Foram utilizados 50 queijos adquiridos em diferentes supermercados. As amostras isoladas foram classificadas por sorogrupo, avaliadas em relação à sensibilidade para 13 agentes antimicrobianos e submetidas à reação em cadeia da polimerase para a presença de genes característicos de E. coli verotoxigênica (VTEC) e enterotoxigênica (ETEC). E. coli foi recuperada em 48(96,0%) dos queijos. Foram identificados os sorogrupos O125 (6,0%), O111 (4,0%), O55 (2,0%) e O119 (2,0%). Três (6,0%) amostras de E. coli foram classificadas como VTEC e uma (2,0%) como ETEC. Os maiores índices de resistência foram verificados para: cefalotina (60,0%), ácido nalidíxico (40,0%), doxiciclina (33,0%), tetraciclina (31,0%) e ampicilina (29,0%).

Synthesis and Structural Studies of Er3+ Containing Lead Cadmium Fluoroborate Glasses and Glass-Ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Glass transitions and state diagram for freeze-dried pineapple

Glass transition temperature of freeze-dried pineapple conditioned by adsorption at various water activities at 25 degreesC was determined by differential scanning calorimetry (DSC). High moisture content samples corresponding to water activities higher than 0.9, obtained by liquid water addition, were also analysed. The DSC traces showed a well-visible shift in baseline at the glass transition temperature (T(g)). Besides, no ice formation was observed until water activity was equal to 0.75. For water activities lower than 0.88, the glass transition curve showed that T(g) decreased with increasing moisture content and the experimental data could be well-correlated by the Gordon-Taylor equation. For higher water activities, this curve exhibited a discontinuity, with suddenly increasing glass transition temperatures approaching a constant value that corresponds to the T(g) of the maximally freeze-concentrated amorphous matrix. The unfreezable water content was determined through melting enthalpy dependence on the sample moisture content.