Micro-raman spectroscopic characterization of a CR-39 detector

Characterization by micro-Raman spectroscopy of polymeric materials used as nuclear track detectors reveals physico-chemical and morphological information on the material's molecular structure. In this work, the nuclear track detector poly(allyl diglycol carbonate), or Columbia Resin 39 (CR-39), was characterized according to the fluence of alpha particles produced by a 226Ra source and chemical etching time. Therefore, damage of the CR-39 chemical structure due to the alpha-particle interaction with the detector was analyzed at the molecular level. It was observed that the ionization and molecular excitation of the CR-39 after the irradiation process entail cleavage of chemical bonds and formation of latent track. In addition, after the chemical etching, there is also loss of polymer structure, leading to the decrease of the group density C-O-C (∼888 cm-1), CH=CH (∼960 cm -1), C-O (∼1110 cm-1), C-O-C (∼1240 cm -1), C-O (∼1290 cm-1), C-O (∼1741 cm -1), -CH2- (∼2910 cm-1), and the main band -CH2- (∼2950 cm-1). The analyses performed after irradiation and chemical etching led to a better understanding of the CR-39 molecular structure and better comprehension of the process of the formation of the track, which is related to chemical etching kinetics. Copyright © 2013 Society for Applied Spectroscopy.

Histologic and biomechanical evaluation of 2 resorbable-blasting media implant surfaces at early implantation times

This study evaluated 3 implant surfaces in a dog model: (1) resorbable-blasting media + acid-etched (RBMa), alumina-blasting + acid-etching (AB/AE), and AB/AE + RBMa (hybrid). All of the surfaces were minimally rough, and Ca and P were present for the RBMa and hybrid surfaces. Following 2 weeks in vivo, no significant differences were observed for torque, bone-to-implant contact, and bone-area fraction occupied measurements. Newly formed woven bone was observed in proximity with all surfaces.

Further investigation of the initial fission-track length and geometry factor in apatite fission-track thermochronology

The external detector method (EDM) is a widely used technique in fission track thermochronology (FTT) in which two different minerals are concomitantly employed: spontaneous tracks are observed in apatite and induced ones in the muscovite external detector. They show intrinsic differences in detection and etching properties that should be taken into account. In this work, new geometry factor values, g, in apatite, were obtained by directly measuring the ρed/ρis ratios and independently determined [GQR]ed/is values through the measurement of projected lengths. Five mounts, two of which were large area prismatic sections and three samples composed of random-orientation pieces have been used to determine the g-values. A side effect of applying EDM is that the value of the initial confined induced fission track, L0, is not measured in routine analyses. The L 0-value is an important parameter to quantify with good confidence the degree of annealing of the spontaneous fission tracks in unknown-age samples, and is essential for accurate thermal history modeling. The impact of using arbitrary L0-values on the inference of sample thermal history is investigated and discussed. The measurement of the L0-value for each sample to be dated using an extra irradiated apatite mount is proposed. This extra mount can be also used for determining the g value as an extension of the ρed/ρis ratio method. Eight apatite samples from crystalline basement, with grains at random orientation, were used to determine the g-values. The results found are statistically in agreement with the values found for apatite samples (from Durango, Mexico) measured in prismatic section and also measured at random orientation. There was no observable variation in efficiency regarding crystal orientation, showing that it is relatively safe using non-prismatic grains, especially in samples with paucity of grains, as it is the case of most basin samples. Implications for the ζ-calibration and for the calibration of the direct (spectrometer-based) fission-track dating are also discussed.

The importance of size-exclusion characteristics of type I collagen in bonding to dentin matrices

The mineral phase of dentin is located primarily within collagen fibrils. During development, bone or dentin collagen fibrils are formed first and then water within the fibril is replaced with apatite crystallites. Mineralized collagen contains very little water. During dentin bonding, acid-etching of mineralized dentin solubilizes the mineral crystallites and replaces them with water. During the infiltration phase of dentin bonding, adhesive comonomers are supposed to replace all of the collagen water with adhesive monomers that are then polymerized into copolymers. The authors of a recently published review suggested that dental monomers were too large to enter and displace water from collagen fibrils. If that were true, the endogenous proteases bound to dentin collagen could be responsible for unimpeded collagen degradation that is responsible for the poor durability of resin-dentin bonds. The current work studied the size-exclusion characteristics of dentin collagen, using a gel-filtration-like column chromatography technique, using dentin powder instead of Sephadex. The elution volumes of test molecules, including adhesive monomers, revealed that adhesive monomers smaller than ∼1000 Da can freely diffuse into collagen water, while molecules of 10,000 Da begin to be excluded, and bovine serum albumin (66,000 Da) was fully excluded. These results validate the concept that dental monomers can permeate between collagen molecules during infiltration by etch-and-rinse adhesives in water-saturated matrices. © 2013 Acta Materialia Inc.

Transdentinal cytotoxicity of experimental adhesive systems of different hydrophilicity applied to ethanol-saturated dentin

The aim of this study was to evaluate the transdentinal cytotoxicity of experimental adhesive systems (EASs) with different hydrophilicity and dentin saturation solutions on odontoblast-like cells. One hundred 0.4-mm-thick dentin discs were mounted in in vitro pulp chambers and assigned to 10 groups. MDPC-23 cells were seeded onto the pulpal side of the discs, incubated for 48 h. The EASs with increasing hydrophilicity (R1, R2, R3 and R4) were applied to the occlusal side after etching and saturation of etched dentin with water or ethanol. R0 (no adhesive) served as controls. R1 is a non-solvated hydrophobic blend, R2 is similar to a simplified etch-and-rinse adhesive system and R3 and R4 are similar to self-etching adhesives. After 24 h, cell metabolism was evaluated by MTT assay (n = 8 discs) and cell morphology was examined by SEM (n = 2 discs). Type of cell death was identified by flow cytometry and the degree of monomer conversion (%DC) was determined by infrared spectroscopy (FTIR) after 10 s or 20 s of photoactivation. Data were analyzed by the Kruskal-Wallis and Mann-Whitney tests (α = 0.05). Dentin saturation with ethanol resulted in higher necrotic cell death ratios for R2, R3 and R4 compared with water saturation, although R2 and R3 induced higher SDH production. Photoactivation for 20 s significantly improved the %DC of all EASs compared with 10 s. A significant positive correlation was observed between the degree of hydrophilicity and %DC. In conclusion, except for R1, dentin saturation with ethanol increased the cytotoxicity of EASs, as expressed by the induction of necrotic cell death. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of artificial aging in marginal adaptation of mixed class V cavities

The aim of this study was to investigate whether the artificial aging by thermal cycling had influenced the marginal adaptation of class V restorations with/without chlorhexidine application in the bond process. Twelve intact human third molars were used. Class V cavity preparations were performed on the buccal surface and the teeth received 35% phosphoric acid-etching procedure (Ultradent Products Inc., South Jordan, Utah, USA). Subsequently, the samples were divided in two groups: Untreated acid-etched dentin and chlorhexidine application as an adjunct in the bond process. The adhesive Single Bond 2 (3M ESPE, St. Paul, MN, USA) was used after 2% chlorhexidine application, and the restorations were performed with FiltekTM Z350 XT (3M ESPE) composite resin. The specimens were submitted to artificial aging by thermal cycling with 3,000 cycles. Analyzes were performed on scanning electron microscopy using replicas of marginal adaptation in percentage of continuous margin before and after the artificial aging. The data were analyzed by paired test and the results showed statistically significant differences in the percentage of continuous margin with/without chlorhexidine treatment before and after thermal cycling. This study concluded that the artificial aging by thermal cycling influenced the marginal adaptation of mixed class V composite restorations.

Effect of final irrigation protocols on microhardness and erosion of root canal dentin

The aim of this study was to evaluate the effect of final irrigation protocols (17% EDTA, BioPure MTAD, SmearClear, and QMiX) on microhardness and erosion of root canal dentin. Fifty roots were sectioned transversely at the cement-enamel junction and each root was sectioned horizontally into 4-mm-thick slices. The samples were divided into five groups (n=10) according to the final irrigation protocol: G1: distilled water (control group); G2: 17% EDTA; G3: BioPure MTAD; G4: SmearClear; and G5: QMiX. The dentin microhardness was then measured with a load of 25 g for 10 s. Initially, the reference microhardness values were obtained for the samples without any etching. The same samples were then submitted to the final irrigation protocols. A new measure was realized and the difference between before and after the procedures was the dentin microhardness reduction. In sequence, the specimens were submitted to SEM analysis to verify the dentinal erosion. The Kruskal Wallis and Dunn tests (α=5%) were used to compare the results. The dentin microhardness decreased for all final irrigation protocols. There was no significant difference between groups 2, 3, 4, and 5 (P>0.05), but this groups presented significant dentin microhardness reduction than G1 (P<0.05). In G2, occurred the highest incidence of dentinal erosion (P<0.05). 17% EDTA, BioPure MTAD, SmearClear, and QMiX promoted significant dentin microhardness reduction. © 2013 Wiley Periodicals, Inc.

Resposta pulpar de dentes de ratos após tratamento capeador direto com sistema adesivo monocomponente ou autocondicionante

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização do mineral zircão através do método de traços de fissão, espectroscopia micro-raman e MEV: geocronologia do grupo Bauru

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo de propriedades físicas de materiais adesivos ortodônticos

Pós-graduação em Ciência dos Materiais - FEIS

Tempo de condicionamento da dentina hígida e afetada por cárie de dentes decíduos e permanentes: efeito na desmineralização do substrato, na produção e na resistência da união resina-dentina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliações clínica e clínica/fotográfica de restaurações adesivas, realizadas em lesões cervicais não cariosas: efeitos dos materiais restauradores, tipos e tempos de avaliação

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação da eficiência de adesão de um cimento resinoso autocondicionante (self-adhesive) sobre esmalte e dentina: efeito termociclagem e condicionamento dental : estudo in vitro

Pós-graduação em Odontologia Restauradora - ICT

Estudo das propriedades mecânicas da interface adesiva criada por sistemas adesivos convencional e autocondicionante, associados ou não ao laser Nd:YAG, utilizando a técnica da nanoindentação

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência adesiva de bráquetes ortodônticos colados com sistemas adesivos convencionais e auto-condicionantes ao esmalte bovino após ciclos térmicos e termomecânicos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)