Surface-mediated selective photocatalytic aerobic oxidation reactions on TiO2 nanofibres

N-doped TiO2 nanofibres were observed to possess lower aerobic oxidation activity than undoped TiO2 nanofibres in the selective photocatalytic aerobic oxidation of enzylamine and 4-methoxybenzyl alcohol. This was attributed to the reduction free energy of O2 adsorption in the vicinity of nitrogen dopant sites, as indicated by density functional theory (DFT) calculations when three-coordinated oxygen atoms are substituted by nitrogen atoms. It was found that the activity recovered following a controlled calcination of the N-doped NFs in air. The dependence of the conversion of benzylamine and 4-methoxybenzyl alcohol on the intensity of light irradiation confirmed that these reactions were driven by light. Action spectra showed that the two oxidation reactions are responsive to light from the UV region through to the visible light irradiation range. The extended light absorption wavelength range in these systems compared to pure TiO2 materials was found to result from the formation of surface complex species following adsorption of reactants onto the catalysts' surface, evidenced by the in situ IR experiment. Both catalytic and in situ IR results reveal that benzaldehyde is the intermediate in the aerobic oxidation of benzylamine to N-benzylidenebenzylamine process.

Heterojunctions between amorphous and crystalline niobium oxide with enhanced photoactivity for selective aerobic oxidation of benzylamine to imine under visible light

The formation of heterojunctions between two crystals with different band gap structures, acting as a tunnel for the unidirectional transfer of photo-generated charges, is an efficient strategy to enhance photocatalytic performance in semiconductor photocatalysts. The heterojunctions may also promote the photoactivity in the visible-light-response of any surface complex catalysts by influencing the transfer of photo-generated electrons. Herein, Nb2O5 microfibers, with a high surface area of interfaces between an amorphous phase and crystalline phase, were designed and synthesised by the calcination of hydrogen-form niobate while controlling the crystallization The photoactivity of these microfibers towards selective aerobic oxidation reactions was investigated. As predicted, the Nb2O5 microfibres containing heterojunctions exhibited the highest photoactivity. This could be due to the band gap difference between the amorphous phase and the crystalline phase, which shortened the charge mobile distance and improved the efficiency.

Continuous Distribution Kinetics for Photopolymerization of Alkyl Methacrylates

The photopolymerization of methyl,ethyl,butyl, and hexyl methacrylates in solution was studied. The effect of initial initiator and monomer concentrations on the time evolution of polymer concentration (M) over bar (n) and PDI was examined. The reversible chain addition and beta-scission, and primary radical termination steps were included in the mechanism along with the classical steps. The rate equations were derived using continuous distribution kinetics and solved numerically to fit the experimental data. The regressed rate coefficients compared well with the literature data. The model predicted the instantaneous increase in (M) over bar (n) and PDI to steady state values. The rate coefficients exhibited a linear increase with the size of alkyl chain of the alkyl methacrylates.

Crystallization kinetics of SrBi2B2O7 glasses by non-isothermal methods

Transparent glasses of SrBi2B2O7 (SBBO) were fabricated via the conventional melt-quenching technique. The amorphous and the glassy nature of the as-quenched samples were, respectively, confirmed by X-ray powder diffraction (XRD) and differential scanning calorimetry (DSC). The glass transition (T (g)) and the crystallization parameters [crystallization activation energy (E (cr)) and Avrami exponent (n)] were evaluated under non-isothermal conditions using DSC. There was a close agreement between the activation energies for the crystallization process determined by Augis and Bennet and Kissinger methods. The variation of local activation energy [E (c)(x)] that was determined by Ozawa method, decreased with the fraction of crystallization (x). The Avrami exponent (n(x)) increased with the increase in fraction of crystallization (x) suggesting that there was a change over in the crystallization process from the surface to the bulk.

Anomalous reaction-diffusion as a model of nonexponential DNA escape kinetics

We show that data from recent experiments carried out on the kinetics of DNA escape from alpha-hemolysin nanopores [M. Wiggin, C. Tropini, C. T. Cossa, N. N. Jetha, and A. Marziali, Biophys. J. 95, 5317 (2008)] may be rationalized by a model of chain dynamics based on the anomalous diffusion of a particle moving in a harmonic well in the presence of a delta function sink. The experiments of Wiggin found, among other things, that the occasional occurrence of unusually long escape times in the distribution of chain trapping events led to nonexponential decays in the survival probability, S(t), of the DNA molecules within the nanopore. Wiggin ascribed this nonexponentiality to the existence of a distribution of trapping potentials, which they suggested was theresult of stochastic interactions between the bases of the DNA and the amino acids located on the surface of the nanopore. Based on this idea, they showed that the experimentally determined S(t) could be well fit in both the short and long time regimes by a function of the form (1+t/tau)(-alpha) (the so called Becquerel function). In our model, S(t) is found to be given by a Mittag-Leffler function at short times and by a generalized Mittag-Leffler function at long times. By suitable choice of certain parameter values, these functions are found to fit the experimental S(t) even better than the Becquerel function. Anomalous diffusion of DNA within the trap prior to escape over a barrier of fixed height may therefore provide a second, plausible explanation of the data, and may offer fresh perspectives on similar trapping and escape problems.

Kinetics and mechanism of hot corrosion of γ-Y 2Si 2O 7 in thin-film Na 2SO 4 molten salt

γ-Y 2Si 2O 7 is a promising candidate material both for hightemperature structural applications and as an environmental/thermal barrier coating material due to its unique properties such as high melting point, machinability, thermal stability, low linear thermal expansion coefficient (3.9×10 -6/K, 200°-1300°C), and low thermal conductivity (<3.0 W/ṁK above 300°C). The hot corrosion behavior of γ-Y 2Si 2O 7 in thin-film molten Na 2SO 4 at 850°-1000°C for 20 h in flowing air was investigated using a thermogravimetric analyzer (TGA) and a mass spectrometer (MS). γ-Y 2Si 2O 7 exhibited good resistance against Na 2SO 4 molten salt. The kinetic curves were well fitted by a paralinear equation: the linear part was caused by the evaporation of Na2SO4 and the parabolic part came from gas products evolved from the hotcorrosion reaction. A thin silica film formed under the corrosion scale was the key factor for retarding the hot corrosion. The apparent activation energy for the corrosion of γ-Y 2Si 2O 7 in Na 2SO 4 molten salt with flowing air was evaluated to be 255 kJ/mol.

Cyclic-oxidation behavior of Ti3SiC2-base material at 1100°c

The cyclic-oxidation behavior of Ti3SiC2-base material was studied at 1100°C in air. Scale spallation and weight loss were not observed in the present tests and the weight gain would just continue if the experiments were not interrupted. The present results demonstrated that the scale growth on Ti3SiC2-base material obeyed a parabolic rate law up to 20 cycles. It then changed to a linear rate with further increasing cycles. The scales formed on the Ti3SiC2base material were composed of an inward-growing, fine-grain mixture of Ti022 + SiO2 and an outward-growing, coarse-grain TiO2. Theoretical calculations show that the mismatch in thermal expansion coefficients between the inner scale and Ti3SiC2-base matrix is small. The outer TiO2 layer was under very low compressive stress, while the inner TiO2 + SiO2 layer was under tensile stress during cooling. Scale spaliation is, therefore, not expected and the scale formed on Ti3SiC2-base material is adherent and resistant to cyclic oxidation.

Kinetics of photocatalytic reduction of NO by CO with Pd2+-Ion-Substituted Nano-TiO2

The objective of the present study is to develop the reaction mechanism and kinetics of photoreduction of NO by CO. For this purpose, the reactions were conducted in the presence of Pd-ion-substituted nano-TiO2, Ti1-xPdxO2-delta, which was synthesized via a solution combustion method. The photocatalytic activity was investigated with unsubstituted TiO2, 1% Pd/TiO2(imp), and Ti1-xPdxO2-delta (where x = 0.05-0.3). No appreciable NO conversion was observed over unsubstituted TiO2, although, despite competitive adsorption of NO and CO on the Pd2+ sites, there was a significant reduction of NO over Ti1-xPdxO2-delta. The kinetic model showed that the enhanced catalytic activity is due to the NO photodissociation at the oxide-ion vacancy.

Hydrocarbon oxidation and three-way catalytic activity on a single step directly coated cordierite monolith: High catalytic activity of Ce0.98Pd0.02O2−δ

Catalytic activity of cordierite honeycomb by a completely new coating method for the oxidation of major hydrocarbons in exhaust gas is reported here. The new coating process consists of (a) dipping and growing γ-Al2O3 on cordierite by combustion of monolith dipped in the aqueous solution of Al(NO3)3 and oxalyldihydrazide (ODH) (or glycine) at 600 °C and active catalyst phase Ce0.98Pd0.02O2−δ on γ-Al2O3-coated cordierite again by combustion of monolith dipped in the aqueous solution of ceric ammonium nitrate, ODH and 1.2 × 10−3 M PdCl2 solution at 500 °C. Weight of active catalyst can be varied from 0.02 wt% to 2 wt% which is sufficient but can be loaded even up to 12 wt% by repeating dip dry combustion. Adhesion of catalyst to cordierite surface is via oxide growth, which is very strong. ‘HC’ oxidation over the monolith catalyst is carried out with a mixture having the composition, 470 ppm of both propene and propane and 870 ppm of both ethylene and acetylene with the varying amount of O2. Three-way catalytic test is done by putting hydrocarbon mixture along with CO (10 000 ppm), NO (2000 ppm) and O2 (15 000 ppm). Below 350 °C full conversion is achieved. In this method, handling of nano-material powder is avoided.

Kinetics of Pressureless Infiltration of Al-Mg Melts into Porous Alumina Preforms

Effective “hydrodynamic” radii governing infiltration kinetics of reactive Al-Mg melts into alumina preforms were found to be three orders of magnitude smaller than the average pore size of the packed bed and also smaller compared with the kinetics for a nonreactive system. A sinusoidal capillary model was developed to predict flow kinetics within the packed bed. For the reactive system, two factors were ascribed for additional melt retardation: (1) different intrinsic wettabilities of the two liquids on alumina, thereby leading to significantly different “effective” local contact angles; and (2) local solute depletion from the meniscus, which was incorporated as a time-dependent contact angle.

'Wet N2O oxidation' process and interface state density characterization of nanoscale nitrided SiO2 for flash memory application

In this paper we first present the 'wet N2O' furnace oxidation process to grow nitrided tunnel oxides in the thickness range 6 to 8 nm on silicon at a temperature of 800 degrees C. Electrical characteristics of MOS capacitors and MOSFETs fabricated using this oxide as gate oxide have been evaluated and the superior features of this oxide are ascertained The frequency response of the interface states, before and after subjecting the MOSFET gate oxide to constant current stress, is studied using a simple analytical model developed in this work.

Kinetics of enzymatic synthesis of geranyl butyrate by transesterification in various supercritical fluids

The transesterification of methyl butyrate, ethyl butyrate and butyl butyrate to geranyl butyrate was investigated in supercritical carbon dioxide. The effect of chain length of the butyrate on the rate of transesterification was investigated. The initial rates followed the trend: ethyl butyrate < butyl butyrate < methyl butyrate. The transesterification of butyl butyrate to geranyl butyrate in various supercritical fluids such as ethylene, methane, ethane was also examined. The initial rate of transesterification of butyl butyrate in different supercritical fluids followed the order: ScCO2 < ScC2H6 < ScC2H4 < ScCH4. The highest initial rate was obtained in supercritical methane and the reasons for this observation were proposed. The Ping-Pong Bi-Bi model with inhibition by both acid and alcohol was used to model the experimental data and determine the kinetics of the reaction. (C) 2010 Elsevier B.V. All rights reserved.