Effects of water flow on ablation rate and morphological changes in human enamel and dentin after Er:YAG laser irradiation

Purpose: To investigate the laboratory effect of Er:YAG laser on ablation rate and morphological changes in human enamel and dentin with varying water flow. Methods: 23 human third molars were sectioned in mesio-distal and buccal-lingual directions. The slabs were flattened and weighted on an analytical laboratory balance (control). A 4-mm(2) area was demarcated and the samples were randomly assigned into three groups according to water flow employed during the laser irradiation (1.0, 1.5, and 2.0 mL/minute). An Er:YAG laser was used to ablate enamel (80.22-J/cm(2), 300 mJ/4Hz) and dentin (96.26-J/cm(2), 250 mJ/4Hz). After irradiation, the samples were immersed in distilled water for 1 hour and then weighted again. The final mass was obtained and laser-irradiated substrate mass loss was calculated by the difference between the initial and final mass. Afterwards, specimens were prepared for SEM. Results: Data were submitted to ANOVA and Tukey's test (P< 0.05). It was observed that the 2.0 mL/minute resulted in a higher mass loss, 1.0 mL/minute showed a lower mass loss, and 1.5 mL/minute demonstrated intermediate results (P< 0.05). The increase of water flow promoted less melting areas and cracks. Furthermore, dentin was more ablated than enamel. It may be concluded that the water flow of Er:YAG laser and the substrates affected the ablation rate. Among the tested parameters, 2.0 mL/minute improved the ability of ablation in enamel and dentin, with less morphologic surface alteration. (Am J Dent 20 12;25:332-336).

Iron supplementation reduces the erosive potential of a cola drink on enamel and dentin in situ

Iron has been suggested to reduce the erosive potential of cola drinks in vitro. Objective: The aim of this study was to evaluate in situ the effect of ferrous sulfate supplementation on the inhibition of the erosion caused by a cola drink. Material and Methods: Ten adult volunteers participated in a crossover protocol conducted in two phases of 5 days, separated by a washout period of 7 days. In each phase, they wore palatal devices containing two human enamel and two human dentin blocks. The volunteers immersed the devices for 5 min in 150 mL of cola drink (Coca-Cola (TM), pH 2.6), containing ferrous sulfate (10 mmol/L) or not (control), 4 times per day. The effect of ferrous sulfate on the inhibition of erosion was evaluated by profilometry (wear). Data were analyzed by paired t tests (p<0.05). Results: The mean wear (+/- se) was significantly reduced in the presence of ferrous sulfate, both for enamel (control: 5.8 +/- 1.0 mu m; ferrous sulfate: 2.8 +/- 0.6 mu m) and dentin (control: 4.8 +/- 0.8 mu m; ferrous sulfate: 1.7 +/- 0.7 mu m). Conclusions: The supplementation of cola drinks with ferrous sulfate can be a good alternative for the reduction of their erosive potential. Additional studies should be done to test if lower ferrous sulfate concentrations can also have a protective effect as well as the combination of ferrous sulfate with other ions.

Effectiveness of immediate bonding of etch-and-rinse adhesives to simplified ethanol-saturated dentin

This study examined the immediate bond strength of etch-and-rinse adhesives to demineralized dentin saturated with either water or absolute ethanol. The research hypothesis was that there would be no difference in bond strength to dentin between water or ethanol wet-bonding techniques. The medium dentin of 20 third molars was exposed (n = 5). The dentin surface was then acid-etched, left moist and randomly assigned to be saturated via either water wet-bonding (WBT) or absolute ethanol wet-bonding (EBT). The specimens were then treated with one of the following etch-and-rinse adhesive systems: a 3-step, water-based system (Adper Scotchbond Multipurpose, or SBMP) or a 2-step, ethanol/water-based system (Adper Single Bond 2, or SB). Resin composite build-ups were then incrementally constructed. After water storage for 24 h at 37 degrees C, the tensile strength of the specimens was tested in a universal testing machine (0.5 mm/min). Data were analyzed by two-way ANOVA and Tukey's test (alpha = 5%). The failure modes were verified using a stereomicroscope (40x). For both adhesives, no significant difference in bond strength was observed between WBT and EBT (p > 0.05). The highest bond strength was observed for SB, regardless of the bonding technique (p < 0.05). No significant interaction between adhesives and bonding techniques was noticed (p = 0.597). There was a predominance of adhesive failures for all tested groups. The EBT and WBT displayed similar immediate bond strength means for both adhesives. The SB adhesive exhibited higher means for all conditions tested. Further investigations are needed to evaluate long-term bonding to dentin mediated by commercial etch-and-rinse adhesives using the EBT approach.

Fluoride plus CO2 laser against the progression of caries in root dentin

Purpose: To evaluate the effect of a 1.23% acidulated phosphate fluoride (APF) gel combined with CO2 laser in protecting carious root dentin against further cariogenic challenges. Methods: After a 7-day lead-in period, 12 volunteers wore an intraoral palatal device containing four carious root dentin slabs, treated with APF and APF+CO2 or placebo and placebo+CO2. After a 14-day wash-out period, volunteers were crossed-over to the other treatment arm. During both intraoral phases, specimens were submitted to cariogenic challenges and then evaluated for cross-sectional Knoop microhardness. Results: Two-way ANOVA demonstrated that there was significant effect for both main factors: CO2 laser irradiation (P< 0.0001) and gel treatment (P< 0.0001), and that there was no interaction between them (P= 0.4706). Protection of carious root dentin against further cariogenic challenges may be provided by APF fluoride gel and CO2 laser, but no additive benefit was found by combining such strategies. (Am J Dent 2012;25:114-117).

Push-out bond strength and SEM evaluation of a new bonding approach into the root canal

Objective: This study evaluated the performance of different adhesive systems in fiber post placement aiming to clarify the influence of different hydrophobic experimental blend adhesives, and of one commercially available adhesive on the frictional retention during a luting procedure. Material and Methods: One luting agent (70 Wt% BisGMA, 28.5% TEGDMA; 1.5% p-tolyldiethanolamine) to cement fiber posts into root canals was applied with 4 different adhesive combinations: Group 1: The etched roots were rinsed with water for 30 s to remove the phosphoric acid, then rinsed with 99.6% ethanol for 30 s, and blot-dried. A trial adhesive (base to catalyst on a 1: 1 ratio) was used with an experimental luting agent (35% Bis-GMA, 14.37% TEGDMA, 0.5% EDMAB, 0.13% CQ); Group 2: A trial adhesive (base to catalyst on a 1: 2 ratio) was luted as in Group 1; Group 3: One-Step Plus (OSP, Bisco Inc.) following the ethanol bonding technique in combination with the luting agent as in Group 1; Group 4: OSP strictly following the manufacturer's instructions using the luting agent as in Group 1. The groups were challenged with push-out tests. Posted root slices were loaded until post segment extrusion in the apical-coronal direction. Failure modes were analyzed under scanning electron microscopy. Results: Push-out strength was not significantly influenced by the luting agent (p>0.05). No statistically significant differences among the tested groups were found as Group 1 (Exp 1 - ethanol-wet bonding technique)=Group 2 (Exp 2 - ethanol-wet bonding technique)= Group 3 (OSP - ethanol-wet bonding technique)= Group 4 (control, OSP - water-wet bonding technique) (p>0.05). The dominating failure modes in all the groups were cohesive/adhesive failures, which were predominantly observed on the post/luting agent interface. Conclusions: The results of this study support the hypothesis that the proposal to replace water with ethanol to bond fiber posts to the root canal using highly hydrophobic resin is plausible, but this seems to be more the proof of a concept than a clinically applicable procedure.

Influence of Ozone Gas and Ozonated Water Application to Dentin and Bonded Interfaces on Resin-Dentin Bond Strength

Purpose: To assess the influence of ozone gas and ozonated water application to prepared cavity and bonded interfaces on the resin/dentin bond strength of two-step etch-and-rinse adhesive systems (Adper Single Bond 2 [SB2] and XP-Bond [XP]). Materials and Methods: Sixty extracted human third molars were sectioned perpendicularly to their long axes to expose flat occlusal dentin surfaces. In experiment 1, dentin was treated with ozone before the bonding procedure, while in experiment 2, ozone was applied to resin/dentin bonded interfaces. In experiment 1, dentin surfaces were treated either with ozone gas (2100 ppm), ozonated water (3.5 ppm), or distilled water for 120 s, and then bonded with SB2 or XP according to manufacturers' instructions. Hybrid composite buildups were incrementally constructed and the teeth were sectioned into resin-dentin sticks (0.8 mm(2)). In experiment 2, dentin surfaces were first bonded with SB2 or XP, composite buildups were constructed, and bonded sticks obtained. The sticks were treated with ozone as previously described. Bonded sticks were tested under tensile stress at 1 mm/min. Silver nitrate impregnation along the resin/dentin interfaces was also evaluated under SEM. Results: Two-way ANOVA (adhesive and ozone treatment) detected no significant effect for the cross-product interaction and the main factors in the two experiments (p > 0.05), which was confirmed by the photomicrographs. Conclusion: Ozone gas and ozonated water used before the bonding procedure or on resin/dentin bonded interfaces have no deleterious effects on the bond strengths and interfaces.

Delineation of vertebral area on the coronal plane using three-dimensional ultrasonography advanced volume contrast imaging (VCI) Omni view: intrarater reliability and agreement using standard mouse, high definition mouse, and pen-tablet

Objective: To assess the fetal lumbosacral spine by three-dimensional (3D) ultrasonography using volume contrast imaging (VCI) omni view method and compare reproducibility and agreement between three different measurement techniques: standard mouse, high definition mouse and pen-tablet. Methods: A comparative and prospective study with 40 pregnant women between 20 and 34+6 weeks was realized. 3D volume datasets of the fetal spine were acquired using a convex transabdominal transducer. Starting scan plane was the coronal section of fetal lumbosacral spine by VCI-C function. Omni view manual trace was selected and a parallel plane of fetal spine was drawn including interest region. Intraclass correlation coefficient (ICC) was used for reproducibility analysis. The relative difference between three used techniques was compared by chi-square test and Fischer test. Results: Pen-tablet showed better reliability (ICC = 0.987). In the relative proportion of differences, this was significantly higher for the pen-tablet (82.14%; p < 0.01). In paired comparison, the relative difference was significantly greater for the pen-tablet (p < 0.01). Conclusion: The pen-tablet showed to be the most reproductive and concordant method in the measurement of body vertebral area of fetal lumbosacral spine by 3D ultrasonography using the VCI.

In Situ Effect of Dentifrices Associated to CO2 Laser in the Permeability of Eroded Root Dentin

Objective: The aim of this study was to evaluate, through a crossover 2 x 2 in situ trial, the effect of a desensitizing dentifrice associated with CO2 laser irradiation to control the permeability of eroded root dentin. Background data: Facing the increased prevalence of erosive lesion and the need for preventive means to control painful symptoms related to them. Methods: Eighty slabs of bovine root dentin were subjected to initial erosive challenge (citric acid 0.3%, 2 h), followed by a remineralizing period in artificial saliva (24 h). Specimens were then divided according to dentin treatment: desensitizing dentifrice, desensitizing dentifrice + CO2 laser, fluoride anticavity dentifrice. and fluoride anticavity dentifrice + CO2 laser. After a 2-day lead-in period, 10 volunteers wore an intraoral palatal appliance containing four root dentin slabs, in two phases of 5 days each. During the intraoral phase, one side of the appliance was immersed in 0.3% citric acid, and the opposite side was immersed in deionized water, four times a day. One hour after the immersions, all specimens were brushed with dentifrice slurry provided by the researcher. After a 7-day washout period, volunteers were crossed over on the different dentifrice group. Each phase having been completed, the specimens were evaluated for permeability through an optical microscope. Results: Data were analyzed using ANOVA and no significant difference (p = 0.272) was found between the surface treatments performed on bovine root dentin. Conclusions: It can be concluded that fluoride anticavity or desensitizing dentifrice, regardless of the association with the CO2 laser irradiation, was able to control the permeability of eroded root dentin.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS). Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM). Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM. Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Effect of NaF and TiF4 varnish and solution on bovine dentin erosion plus abrasion in vitro

Objectives. This in vitro study aimed to analyze the effect of TiF4 compared to NaF varnishes and solutions, to protect against dentin erosion associated with abrasion. Materials and methods. Bovine dentin specimens were pre-treated with NaF-Duraphat (2.26% F), NaF/CaF2-Duofluorid (5.63% F), experimental-NaF (2.45% F), experimental-TiF4 (2.45% F) and placebo varnishes; NaF (2.26% F) and TiF4 (2.45% F) solutions. Controls remained untreated. The erosive pH cycling was performed using a soft drink (pH 2.6) 4 x 90 s/day and the toothbrushing-abrasion 2 x 10 s/day, in vitro for 5 days. Between the challenges, the specimens were exposed to artificial saliva. Dentin tissue loss was measured profilometrically (mu m). Results. ANOVA/Tukey's test showed that all fluoridated varnishes (Duraphat, 7.5 +/- 1.1; Duofluorid, 6.8 +/- 1.1; NaF, 7.2 +/- 1.9; TiF4, 6.5 +/- 1.0) were able to significantly reduce dentin tissue loss (40.7% reduction compared to control) when compared to placebo varnish (11.2 +/- 1.3), control (11.8 +/- 1.7) and fluoridated (NaF, 9.9 +/- 1.8; TiF4, 10.3 +/- 2.1) solutions (p < 0.0001), which in turn did not significantly differ from each other. Conclusion. All fluoridated varnishes, but not the solutions, had a similar performance and a good potential to reduce dentin tissue loss under mild erosive and abrasive conditions in vitro. Risk patients for erosion and abrasion, especially those with exposed dentin, should benefit from this clinical preventive measure. Further research has to confirm this promising result in the clinical situation.

Back-scattered electron imaging for leakage analysis of four retrofilling materials

This study aimed to evaluate, ex vivo, the nanoleakage in dentinal tubules, the linear infiltration of silver nitrate in the dentin wall/root-end filling material interface, and the presence of gaps in this interface in root-end cavities filled with 4 filling materials. Forty-eight disto-buccal root canals of maxillary molars were instrumented and filled. Retrograde cavities were prepared with ultrasonic points (apical 2 mm). The samples were divided into 2 control groups (n = 4) and 4 experimental groups (n = 10): Group I white mineral trioxide aggregate (MTA); Group II Super EBA; Group III Portland cement; and Group IV Sealer 26. After 1 week, the specimens were subjected to silver nitrate and prepared for SEM (backscattered electrons). In the apical-apical segment, an area with significantly higher leakage was observed for Super EBA, followed by Portland cement, MTA, and Sealer 26 (P = 0.0054). In the medium and cervical segments, all materials showed the same leakage behavior (P = 0.1815 and P = 0.1723, respectively). The linear infiltration at the dentin wall/root-end filling material interface was higher with Super EBA than the other groups. No differences in the percentage of gaps along the 3 mm of dentin wall/root-end filling material interface between the 4 materials were evident (P > 0.05). Nanoleakage occurred mainly in the apical segment of the samples, and Super EBA showed the highest values. The area and linear leakage were lower in the middle and coronal segments, regardless of the root-end filling material. No material perfectly sealed the root-end cavities, which allowed for the leakage occurrence. Microsc. Res. Tech. 75:796800, 2012. (C) 2011 Wiley Periodicals, Inc.

Microtensile bond strength of resin composite to dentin treated with Er:YAG laser of bleached teeth

The objective of this study was to evaluate the influence of Er:YAG laser (lambda = 2.94 mu m) on microtensile bond strength (mu TBS) and superficial morphology of bovine dentin bleached with 16% carbamide peroxide. Forty bovine teeth blocks (7 x 3 x 3 mm(3)) were randomly assigned to four groups: G1- bleaching and Er:YAG irradiation with energy density of 25.56 J/cm(2) (focused mode); G2 - bleaching; G3 - no-bleaching and Er:YAG irradiation (25.56 J/cm(2)); G4 - control, non-treated. G1 and G2 were bleached with 16% carbamide peroxide for 6 h during 21 days. Afterwards, all blocks were abraded with 320 to 600-grit abrasive papers to obtain flat standardized dentin surfaces. G1 and G3 were Er:YAG irradiated. Blocks were immediately restored with 4-mm-high composite resin (Adper Single Bond 2, Z-250-3 M/ESPE). After 24 h, the restored blocks (n = 9) were serially sectioned and trimmed to an hour-glass shape of approximately 1 mm(2) at the bonded interface area, and tested in tension in a universal testing machine (1 mm/ min). Failure mode was determined at a magnification of 100x using a stereomicroscope. One block of each group was selected for scanning electron microscope (SEM) analysis. mu TBS data was analyzed by two-way ANOVA and Tukey test (alpha = 0.05). Mean bond strengths (SD) in MPa were: G1- 32.7 (5.9)(A); G2- 31.1 (6.3)(A); G3- 25.2 (8.3)(B); G4- 36.7 (9.9).(A) Groups with different uppercase letters were significantly different from each other (p < .05). Enamel bleaching procedure did not affect mu TBS values for dentin adhesion. Er:YAG laser irradiation with 25.56 J/cm(2) prior to adhesive procedure of bleached teeth did not affect mu TBS at dentin and promoted a dentin surface with no smear layer and opened dentin tubules observed under SEM. On the other hand, Er:YAG laser irradiation prior to adhesive procedure of non-bleached surface impaired mu TBS compared to the control group.

Push-out strength of root fillings with or without thermomechanical compaction

Carneiro SMBS, Sousa-Neto MD, Rached-Junior FA, Miranda CES, Silva SRC, Silva-Sousa YTC. Push-out strength of root fillings with or without thermomechanical compaction. International Endodontic Journal, 45, 821828, 2012. Abstract Aim To evaluate the influence of thermomechanical compaction (Taggers hybrid technique THT) on the push-out strength of several root filling materials to root dentine. Methodology Root canals of eighty roots in human canines were prepared with the ProTaper system and filled with one of the following materials, using either lateral compaction (LC) (n = 40) or THT (n = 40): AH Plus/gutta-percha (GP) (n = 10), Sealer 26/GP (n = 10), Epiphany SE/Resilon (n = 10) and Epiphany SE/GP (n = 10). Three 2-mm-thick dentine slices were obtained from each third of each root. The root filling in the first slice was subjected to a push-out test to evaluate the bond strength of the materials to intraradicular dentine. Data (in MPa) were analysed using anova and post hoc Tukeys test (P < 0.05). Failure mode was determined at x25 magnification. The other two slices were prepared for scanning electron microscopy (SEM) to examine the surface of the filling materials. Results Lateral compaction (1.34 +/- 1.14 MPa) was associated with a significantly higher bond strength (P < 0.05) than the THT (0.97 +/- 0.88 MPa). AH Plus/GP (2.23 +/- 0.83 MPa) and Sealer 26/GP (1.86 +/- 0.50 MPa) had significantly higher bond strengths than the other materials and differed significantly from each other (P < 0.05). There was a significant difference (P < 0.05) between the coronal (1.36 +/- 1.15 MPa), middle (1.14 +/- 1.05 MPa) and apical thirds (0.95 +/- 0.83 MPa). Considering the technique and root filling material interaction, AH Plus/GP-LC was associated with the highest mean values (2.65 +/- 0.66 MPa) (P < 0.05). Sealer 26/GP-LC (2.10 +/- 0.46 MPa), AH Plus/GP-THT (1.81 +/- 0.78 MPa) and Sealer 26/GP-TH (1.63 +/- 0.44 MPa) had intermediate values that were not significantly different from each other (P > 0.05). Epiphany SE was associated with the lowest mean values (3.70 +/- 0.86 MPa) (P < 0.05), regardless of the root filling technique and type of solid material (cone). Adhesive failures predominated in the specimens filled with Epiphany SE, whilst mixed and cohesive failures were more frequent in those filled with AH Plus and Sealer 26, regardless of the root filling technique. SEM analysis revealed that LC produced a dense and well-compacted filling whilst the use of a hybrid thermomechanical technique resulted in the solid material (GP or Resilon) intermingled within sealer to form a nonhomogenous mass. Conclusion Lateral compaction was associated with higher bond strengths of the materials to intraradicular dentine than a hybrid technique using thermomechanical compaction. The greatest push-out strengths were obtained when the canals were filled with LC of AH Plus and GP cones.

Microhardness of Radicular Dentin Treated with 980-nm Diode Laser and Different Irrigant Solutions

Objective: The aim of this study was to evaluate the microhardness of radicular dentin after treatment with 980-nm diode laser and different irrigant solutions. Background data: There are few reports of the consequences of diode laser irradiation emitted at 980 nm on the mechanical properties of dentin. Methods: Seventy-two single canal, human canines with complete root formation were randomly distributed among three groups (n = 24), according to the irrigant solution used in the biomechanical preparation: distilled water; 1% NaOCl; and, 1% NaOCl + 17% EDTA. These groups subsequently were divided into three subgroups (n = 8), according to the diode laser parameter: no irradiation (control); 1.5W/100 Hz; and 3.0 W/100 Hz. Laser was applied with helicoidal movements for 20 sec. Roots were sectioned in slices and the fragment corresponding to the middle third was submitted to the microhardness test (KHN) at depths of 30, 90, 150, and 300 mu m. Results: ANOVA and Tukey tests showed that the microhardness of the groups irradiated with 1.5 W/100 Hz (49.7 +/- 11.2) and 3.0W/100 Hz (50.6 +/- 11.9) were statistically similar to each other (p > 0.05) and different (p < 0.05) from the non-irradiated group (45.0 +/- 9.7). Higher microhardness values were obtained at 150 mu m (49.2 +/- 11.0) and 300 mu m (52.3 +/- 11.3) which were similar among themselves and different (p < 0.05) only at the depth of 30 mu m (44.4 +/- 10.5). No differences were found among the irrigant solutions (p > 0.05). Conclusions: The microhardness of the radicular dentin increased after irradiation with 980-nm diode laser.

Thermal alteration and morphological changes of sound and demineralized primary dentin after Er:YAG laser ablation

The purpose of this study was to assess the influence of Er:YAG laser pulse repetition rate on the thermal alterations occurring during laser ablation of sound and demineralized primary dentin. The morphological changes at the lased areas were examined by scanning electronic microscopy (SEM). To this end, 60 fragments of 30 sound primary molars were selected and randomly assigned to two groups (n = 30); namely A sound dentin (control) and B demineralized dentin. Each group was divided into three subgroups (n = 10) according to the employed laser frequencies: I4 Hz; II6 Hz, and III10 Hz. Specimens in group B were submitted to a pH-cycling regimen for 21 consecutive days. The irradiation was performed with a 250 mJ pulse energy in the noncontact and focused mode, in the presence of a fine water mist at 1.5 mL/min, for 15 s. The measured temperature was recorded by type K thermocouples adapted to the dentin wall relative to the pulp chamber. Three samples of each group were analyzed by SEM. The data were submitted to the nonparametric Kruskal-Wallis test and to qualitative SEM analysis. The results revealed that the temperature increase did not promote any damage to the dental structure. Data analysis demonstrated that in group A, there was a statistically significant difference among all the subgroups and the temperature rise was directly proportional to the increase in frequency. In group B, there was no difference between subgroup I and II in terms of temperature. The superficial dentin observed by SEM displayed irregularities that augmented with rising frequency, both in sound and demineralized tissues. In conclusion, temperature rise and morphological alterations are directly related to frequency increment in both demineralized and sound dentin. Microsc. Res. Tech., 2011. (c) 2011 Wiley Periodicals, Inc.