Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37% phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.

Adhesion of Epiphany and AH Plus sealers to human root dentin treated with different solutions

This study evaluated comparatively the adhesion of Epiphany and AH Plus endodontic sealers to human root dentin treated with 1% NaOCl and 1% NaOCl+17% EDTA, using the push-out test. Sixty root cylinders obtained from maxillary canines had the canals prepared and were randomly assigned to 3 groups (n=20), according to root dentin treatment: GI - distilled water (control), GII - 1% NaOCl and GIII - 1% NaOCl+17% EDTA. Each group was divided into 2 subgroups (n=10) filled with either Epiphany or AH Plus. Bond strength push-out test data (kN) were obtained and analyzed statistically by ANOVA and Tukey's post-hoc test. There was statistically significant difference between sealers (AH Plus: 0.78 ± 0.13; Epiphany: 0.61 ± 0.19; p<0.01) and among root dentin treatments (distilled water: 0.58 ± 0.19; 1% NaOCl: 0.71 ± 0.12; 1% NaOCl+17% EDTA: 0.80 ± 0.17; p<0.05). In conclusion, AH Plus sealer presented greater adhesion to dentin than Epiphany, regardless of the treatment of root canal walls.

Effect of insertion method on knoop hardness of high viscous glass ionomer cements

The aim of this study was to assess the Knoop hardness of three high viscous glass ionomer cements: G1 - Ketac Molar; G2 - Ketac Molar Easymix (3M ESPE) and G3 - Magic Glass ART (Vigodent). As a parallel goal, three different methods for insertion of Ketac Molar Easymix were tested: G4 - conventional spatula; G5 - commercial syringe (Centrix) and G6 - low-cost syringe. Ten specimens of each group were prepared and the Knoop hardness was determined 5 times on each specimen with a HM-124 hardness machine (25 g/30 s dwell time) after 24 h, 1 and 2 weeks. During the entire test period, the specimens were stored in liquid paraffin at 37ºC. Significant differences were found between G3 and G1/G2 (two-way ANOVA and Tukey's post hoc test; p<0.01). There was no significant difference in the results among the multiple ways of insertion. The glass ionomer cement Magic Glass ART showed the lowest hardness, while the insertion technique had no significant influence on hardness.

Thermal performance of sisal fiber-cement roofing tiles for rural constructions

Roofing provides the main protection against direct solar radiation in animal housing. Appropriate thermal properties of roofing materials tend to improve the thermal comfort in the inner ambient. Nonasbestos fiber-cement roofing components reinforced with cellulose pulp from sisal (Agave sisalana) were produced by slurry and dewatering techniques, with an optional addition of polypropylene fibers. Nonasbestos tiles were evaluated and compared with commercially available asbestos-cement sheets and ceramic tiles (frequently chosen as roofing materials for animal housing). Thermal conductivity and thermal diffusivity of tiles were determined by the parallel hot-wire method, along with the evaluation of the downside surface temperature. Cement-based components reinforced with sisal pulp presented better thermal performance at room temperature (25ºC), while those reinforced with sisal pulp added by polypropylene fibers presented better thermal performance at 60ºC. Non-asbestos cement tiles provided more efficient protection against radiation than asbestos corrugated sheets.

Análise da pozolanicidade da cinza da casca da castanha do caju pelo método de difratometria de raios X

Atualmente, o aproveitamento de resíduos na construção civil tem sido estimulado, uma vez que esse setor apresenta-se como um dos maiores consumidores de materiais naturais em seus processos e produtos. As cinzas ocupam lugar de destaque entre os resíduos agroindustriais por resultarem de processos de geração de energia. Grande parte dessas cinzas possui atividade pozolânica, podendo ser utilizada como substituto parcial do cimento Portland, resultando numa economia significativa de energia e custo. Este trabalho faz parte de uma pesquisa mais ampla, a qual busca avaliar a viabilidade técnica da cinza da casca da castanha de caju (CCCC) como adição mineral em matrizes de cimento Portland, como também, propor uma metodologia de análise de cinzas agroindustriais. Aplicou-se a técnica de difratometria de raios X para avaliar a reatividade do hidróxido de cálcio pela cinza da casca da castanha de caju em pastas, empregaram-se teores de substituição entre 2,5 e 30,0% e os difratogramas das pastas foram comparados com os das pastas confeccionadas com sílica ativa, executados sobre as mesmas condições de ensaio. Os resultados apontam para a ausência de reatividade pozolânica da CCCC com o cimento Portland.

Swine deep bedding ashes as a mineral additive for cement based mortar

The sustainability of intensive swine production demands alternative destinations for the generated residues. Ashes from swine rice husk-based deep bedding were tested as a mineral addition for cement mortars. The ashes were obtained at 400 to 600ºC, ground and sieved through a 325 mesh sieve (# 0.045 mm). The characterization of the ashes included the determination of the index of pozzolanic activity with lime. The ashes were also tested as partial substitutes of Portland cement. The mortars were prepared using a cement:sand proportion of 1:1.5, and with water/cement ratio of 0.4. Three percentages of mass substitution of the cement were tested: 10, 20 and 30%. Mortar performances were assessed at 7 and 28 days determining their compressive strength. The chosen condition for calcinations at the laboratory scale was related to the maximum temperature of 600ºC since the resulting ashes contained vitreous materials and presented satisfactory values for the pozzolanic index under analysis. The pozzolanic activity indicated promising results for ashes produced at 600ºC as a replacement of up to 30% in cement masses.

Farelo de canola em dietas para o pacu Piaractus mesopotamicus (Holmberg 1987): efeitos sobre o crescimento e a composição corporal

Avaliaram-se os efeitos da inclusão de farelo de canola em dietas de juvenis de pacu (Piaractus mesopotamicus) sobre parâmetros de crescimento e composição corporal. Um total de 192 alevinos (9 a 15g) foram estocados em 24 tanques de cimento, de 100l de capacidade, durante 103 dias. O farelo de canola foi utilizado em quatro proporções: zero; 9,5%; 19% e 38% da dieta, com ou sem farinha de peixe (12%/dieta), totalizando oito tratamentos. A presença de farinha de peixe não afetou os parâmetros de crescimento avaliados. A inclusão de 38% de farelo de canola na dieta diminuiu o ganho de peso dos peixes, valores médios de 28,74g a 50,70g, e piorou a conversão alimentar aparente, de 1,66 para 2,85. A taxa de eficiência protéica também foi menor nos peixes alimentados com 38% de farelo de canola. As várias proporções de farelo de canola das dietas alteraram os teores de umidade, proteína bruta e lipídios dos peixes. A presença da farinha de peixe, nas dietas, somente influiu no teor de lipídios dos peixes alimentados com dietas contendo 9,5% de farelo de canola. Conclui-se que até 19% de farelo de canola pode ser adicionado às dietas de juvenis de pacu, sem que seu desenvolvimento seja prejudicado.

Presence of arsenic in different types of MTA and white and gray Portland cement

Objective. The presence of arsenic in various types of mineral trioxide aggregate (MTA) and Portland cements were evaluated to verify if they comply with the ISO-recommended limit for water-based cements of 2 mg arsenic/kg material. Study design. An amount of 5 mL of hydrochloric acid was added to 2 g each of MTA and Portland cement to be analyzed. After 15 minutes, the material was filtered and the volume of supernatant was diluted with reagent-grade water up to 40 mL. Atomic absorption spectrophotometry readings were performed in triplicate. Results. The following mean values were obtained: CPM (Egeo, Buenos Aires, Argentina) 11.06 mg/kg; CPM sealer (Egeo) 10.30 mg/kg; MTA- Obtura (Angelus, Londrina, PR, Brazil) 0.39 mg/kg; Experimental MTA: 10.30 mg/kg; White MTA- Angelus (Angelus) 1.03 mg/kg; Gray MTA- Angelus (Angelus) 5.91 mg/kg; ProRoot-MTA (Dentsply/Tulsa Dental Specialties, Tulsa, OK) 5.25 mg/kg; Gray Portland cement (Votorantim Cimentos, Cubatao, SP, Brazil): 34.27 mg/kg; and White Portland cement (Cimento Rio Branco, Rio de Janeiro, RJ, Brazil) 0.52 mg/kg. Conclusion. All tested materials presented arsenic in their composition. The form of arsenic was not analyzed nor the toxicity of the arsenic found. Only MTA- Obtura, White MTA- Angelus, and White Portland cement presented arsenic levels below the limit set in the ISO 9917-1 standard. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2008; 106: 909-913)

Asbestose no Brasil: um risco ignorado

É descrito o caso de um trabalhador da indústria de cimento-amianto, portador de quadro de asbestose comprovado clínica, funcional e radialogicamente; trata-se do primeiro caso dessa pneumoconiose descrito na literatura médica brasileira. É chamada a atenção para a possibilidade de que casos dessa doença estejam passando desapercebidos no Brasil, onde é crescente a utilização do amianto pela indústria.

Os gases de efeito de estufa e a problemática da responsabilidade social e ambiental das empresas portuguesas: O caso das cimenteiras

Mestrado em Contabilidade

Reciclagem de pavimentos "in situ" a frio com emulsão betuminosa: a experiência portuguesa

Esta dissertação procura documentar a experiência portuguesa na reciclagem “in situ”, a frio, de pavimentos flexíveis com recurso a emulsões betuminosas, desde a primeira destas obras realizada no nosso país, em 1993, até ao presente. Assim, principia-se por elaborar uma recensão bibliográfica dos temas associados ao assunto central, sendo de seguida expostos os principais conceitos sobre misturas recicladas a frio com emulsão betuminosa e, por último, passadas em revista as normas e especificações técnicas a que devem obedecer, que mais comummente entre nós se aplicam. Numa segunda fase, são examinadas as principais obras que em Portugal se executaram por este processo. Neste âmbito, descrevem-se os vários materiais utilizados nas misturas recicladas: materiais fresados dos pavimentos; materiais correctivos; e ligantes (emulsão betuminosa e cimento). Nos casos em que foi possível obter os elementos necessários a tal, são ainda apresentados os respectivos estudos de formulação. Prossegue-se fazendo a descrição de aspectos relativos ao processo construtivo, tais como, forma de adição do material correctivo, equipamento utilizado na reciclagem do pavimento (máquina recicladora), equipamento de compactação, faseamento dos trabalhos de ocupação da via, tempo de encerramento ao tráfego, etc. Questões relacionadas com o processo de cura e com o desempenho das misturas recicladas a frio com emulsão betuminosa, são também, analisadas. Finalmente, termina-se fazendo um balanço geral de toda a experiência que sobre esta matéria até à data entre nós se adquiriu, extraindo-se dela as conclusões que se afiguraram mais pertinentes.

Degradação do betão por fenómenos de carbonatação: consequências nas armaduras das edificações após anos 50 na cidade de Lisboa

A carbonatação e as suas consequências sobre o betão são do conhecimento do meio científico e técnico, e tem sido analisada há já algumas décadas. A perda do ambiente favorável criado pelo betão em torno das armaduras, provocada pela reacção do dióxido de carbono existente no ar com o hidróxido de cálcio do betão, é o início de um processo que conduz à degradação das estruturas de betão armado. Esta dissertação está estruturada em duas partes fundamentais. Na primeira parte ilustra-se o estado da arte ao desenvolver os temas, directa e indirectamente relacionados com o fenómeno da carbonatação e sua influência sobre as armaduras. Pretendeu-se envolver o conhecimento adquirido, nos temas que vão desde o fabrico do cimento até à sua hidratação, correlacionando as suas características e propriedades. Na segunda parte é analisado o caso de estudo relativo à cidade de Lisboa, pelo esforço de obter algum conhecimento, no que respeita ao fenómeno da carbonatação nas edificações e do respectivo impacto passados mais de 50 anos. Em face do actual estado da arte da edificação e da reabilitação no país, e concretamente na cidade Lisboa, considera-se com sentido de oportunidade o tema desenvolvido. É deste modo possibilitado o conhecimento efectivo da amplitude do fenómeno da carbonatação em alguns edifícios, bem como o estado de degradação da sua estrutura.

Placas de OSB: investigação e estudo laboratorial das suas características de desempenho

A utilização de placas de OSB – Oriented Strand Board está em franca expansão no território nacional e parece ser uma alternativa ecológica e económica aos painéis de derivados de madeira normalmente usados. O OSB é obtido num processo de fabrico resultante da interacção de diversas variáveis, que conferem aos painéis uma vasta gama de aplicações estruturais ou não estruturais (paredes exteriores e interiores, pavimentos, coberturas, componentes de vigas, cofragens, embalagens, móveis, elementos de decoração, etc.). Neste trabalho pretendeu-se investigar, através de pesquisa bibliográfica as características das placas OSB assim como seu processo de fabrico e condicionantes existentes no seu decurso. Em seguida estas foram comparadas com os seus principais concorrentes, o contraplacado e o aglomerado de madeira e cimento. O trabalho experimental realizado teve como objectivo analisar as propriedades de OSB, proveniente do mercado nacional, de acordo com a EN 300:2006 e com os dados recolhidos na pesquisa bibliográfica. Foram executados ensaios de flexão (EN 310:2002), inchamento em espessura (EN 317:2002) e ensaios de flexão após envelhecimento (EN 321:2010). Concluiu-se que o OSB é um material com algumas características de destaque, no entanto a substituição de outros derivados de madeira por este deve ser acompanhada por estudos, principalmente em ambientes húmidos. É importante realçar que este possui modelos com características específicas para determinadas utilizações e ambientes que possibilitam uma optimização do seu comportamento, no entanto, nos ensaios realizados apenas foi utilizado um modelo base de OSB.

Teor crítico de cloretos para iniciação da corrosão do aço no betão

Este trabalho tem como objectivo a determinação do teor crítico de cloretos no betão, ou seja, o teor de cloretos à profundidade da armadura que é necessário para sustentar uma quebra localizada do filme de passivação e, por isso, iniciar a corrosão activa. Uma vez que não existe consenso quanto ao seu valor, este trabalho pretendia dar um contributo no estudo deste parâmetro, utilizando um procedimento que modele realisticamente a corrosão das armaduras em estruturas de betão armado expostas directamente a água do mar. Realizaram-se três séries de testes com cimentos de fontes diferentes. Utilizaram-se varões nervurados e incorporados no betão. Os iões cloreto foram introduzidos por absorção capilar e difusão e a despassivação foi detectada por medição do potencial de corrosão do aço. O teor crítico de cloretos foi determinado em relação à massa de cimento por titulação potenciométrica obtendo-se para a amassadura 1 um intervalo entre 1.0% e 1.6%, para a amassadura 2, um teor entre 0.5% e 0.9% e para a amassadura 3 obtiveram-se teores críticos entre 0.6% e 1.0%. Comparando com o teor máximo de cloretos definido pela norma NP EN 206-1, 0.4%, conclui-se que este valor não é conservador e é um valor para o qual efectivamente ainda não se iniciou a corrosão por cloretos podendo ser utilizado em modelos de previsão do início da corrosão das armaduras. Verificou-se que a não protecção dos varões nas amassaduras, principalmente na amassadura 1, levam a uma maior acessibilidade de oxigénio, provocando “crevice” e corrosão na armadura exposta ao ar, levando a teores críticos de cloretos erróneos. Efectuaram-se registos fotográficos e observações à lupa das armaduras bem como micrografias em MEV e microanálises por dispersão de Raios-X no betão adjacente à armadura. Verificou-se a existência de produtos de corrosão na armadura os quais continham iões cloreto.

Vertebroplastia percutânea por fractura osteoporótica

A Vertebroplastia Percutânea é uma técnica minimamente invasiva relativamente recente, que tem reconhecidas vantagens e aplicações em fracturas compressivas dos corpos vertebrais. Basicamente, consiste na injecção de um Cimento Acrílico no interior do corpo vertebral, e desse modo, minimizar e estabilizar fracturas compressivas dos corpos vertebrais, que são frequentemente de etiologia osteoporótica. Fortemente indicada no tratamento de fracturas incapacitantes, possui como complicação principal o extravasamento do Cimento. Este artigo pretende abordar a técnica, expondo suas indicações, vantagens e complicações mais frequentes. Esta permite reduzir a elevada taxa de morbilidade e impacto económico-social associado à Osteoporose.