Lysozyme binding to poly(4-vinyl-N-alkylpyridinium bromide)

The adsorption behavior of polycations at ionic strengths (1) ranging from 0.001 to 0.1 onto silicon wafers was studied by means of ellipsometry, contact angle measurements and atomic force microscopy (AFM). Polycations chosen were bromide salts of poly(4-vinylpyridine) N-alkyl quaternized with linear aliphatic chains of 2 and 5 carbon atoms, QPVP-C2 and QPVP-C5, respectively. Under 1 0.001 the reduction of screening effects led to low adsorbed amounts of QPVP-C2 or QPVP-C5 (1.0 +/- 0.1 mg/m(2)), arising from the adsorption of extended chains. Upon increasing l to 0.1, screening effects led to conformational changes of polyelectrolyte chains ill Solution and to higher adsorbed amount values (1.9 +/- 0.2 mg/m(2)). Advancing contact angle theta(a) measurements performed with water drops onto QPVP-C2 and QPVP-C5 adsorbed layers varied from (45 +/- 2)degrees to (50 +/- 5)degrees, evidencing the exposure of both hydrophobic alkyl groups and charged moieties. The adsorption of lysozyme (LYZ) molecules to QPVP-C5 layers was more pronounced than to QPVP-C2 films. Antimicrobial effect of LYZ bound to QPVP-C2 or QPVP-C5 layers or to Si wafers was evaluated with enzymatic assays using Micrococcus luteus as Substrates. The adsorption behavior of QPVP-C2 and QPVP-C5 at the water-air interface was studied by means Of surface tension measurements. Only QPVP-C5 was able to reduce water Surface tension. Mixtures of LYZ and QPVP-C5 were more efficient in reducing Surface tension than pure LYZ solution, evidencing co-adsorption at liquid-air interface. Moreover, antimicrobial action observed for mixtures of LYZ and QPVP-C5 was more pronounced than that measured for pure LYZ. Hydrophobic interaction between LYZ and QPVP-C5 ill Solution seems to drive the binding and to preserve LYZ secondary structure. (c) 2008 Elsevier Inc. All rights reserved.

Hydrolytic Activity of Free and Immobilized Cellulase

Cellulase is an enzymatic complex which synergically promotes the degradation of cellulose to glucose. The adsorption behavior of cellulase from Trichoderma reesei onto Si wafers or amino-terminated surfaces was investigated by means of ellipsometry and atomic force microscopy (AFM) as a function of temperature. Upon increasing temperature from (24 +/- 1) to (60 +/- 1) degrees C, adsorption of cellulase became faster and more pronounced and the mean roughness of cellulase adsorbed layers increased. In the case of cellulase adsorbed onto Si wafers, Arrhenius`s plot allowed us to estimate the adsorption energy as 24.2 kJ mol(-1). The hydrolytic activity of free cellulase and cellulase immobilized onto Si wafers was tested using cellulose dispersions as substrates. The incubation temperature ranged from (37 +/- 1) to (60 +/- 1) degrees C. The highest efficiency was observed at (60 +/- 1) degrees C. The amount of glucose produced by free cellulase was similar to 20% higher than that obtained from immobilized cellulase. However, immobilizing cellulase onto Si wafers proved to be advantageous because they could be reused six times while retaining their original activity level. Such an effect was attributed to surface hydration, which prevents enzyme denaturation. The hydrolytic activity of cellulase immobilized onto amino-terminated surfaces was slightly lower than that observed for cellulase adsorbed onto Si wafers, and reuse was not possible.

Characteristics of thin cellulose ester films spin-coated from acetone and ethyl acetate solutions

Spin-coated films of cellulose acetate (CA), cellulose acetate propionate (CAP), cellulose acetate butyrate (CAB) and carboxymethylcellulose acetate butyrate (CMCAB) have been characterized by ellipsometry, atomic force microscopy (AFM) and contact angle measurements. The films were spin-coated onto silicon wafers, a polar surface. Mean thickness values were determined by means of ellipsometry and AFM as a function of polymer concentration in solutions prepared either in acetone or in ethyl acetate (EA), both are good solvents for the cellulose esters. The results were discussed in the light of solvent evaporation rate and interaction energy between substrate and solvent. The effects of annealing and type of cellulose ester on film thickness, film morphology, surface roughness and surface wettability were also investigated.

Electrostatic layer-by-layer deposition and electrochemical characterization of thin films composed of MnO(2) nanoparticles in a room-temperature ionic liquid

Thin films of MnO(2) nanoparticles were grown using the layer-by-layer method with poly (diallyldimetylammonium) as the intercalated layer. The film growth was followed by UV-vis, electrochemical quartz crystal microbalance (EQCM), and atomic force microscopy. Linear growth due to electrostatic immobilization of layers was observed up to 30 bilayers, but electrical connectivity was maintained only for 12 MnO(2)/PPDA bilayers. The electrochemical characterization of this film in 1-butyl-2,3-dimethyl-imidazolium (BMMI) bis(trifluoromethanesulfonyl)imide (TFSI) (BMMITFSI) with and without addition of a lithium salt indicated a higher electrochemical response of the nanostructured electrode in the lithium-containing electrolyte. On the basis of EQCM experiments, it was possible to confirm that the charge compensation process is achieved mainly by the TFSI anion at short times (<2 s) and by BMMI and lithium cations at longer times. The fact that large ions like TFSI and BMMI participate in the electroneutrality is attributed to the redox reaction that occurs at the superficial sites and to the high concentration of these species compared to that of lithium cations.

Catalytic properties of thioredoxin immobilized on superparamagnetic nanoparticles

Thioredoxin (Trx1), a very important protein for regulating intracellular redox reactions, was immobilized on iron oxide superparamagnetic nanoparticles previously coated with 3-aminopropyltriethoxysilane (APTS) via covalent coupling using the EDC (1-ethyl-3-{3-dimethylaminopropyl}carbodiimide) method. The system was extensively characterized by atomic force microscopy, vibrational and magnetic techniques. In addition, gold nanoparticles were also employed to probe the exposed groups in the immobilized enzyme based on the SERS (surface enhanced Raman scattering) effect, confirming the accessibility of the cysteines residues at the catalytic site. For the single coated superparamagnetic nanoparticle, by monitoring the enzyme activity with the Ellman reagent, DTNB=5,5`-dithio-bis(2-15 nitrobenzoic acid), an inhibitory effect was observed after the first catalytic cycle. The inhibiting effect disappeared after the application of an additional silicate coating before the AFTS treatment, reflecting a possible influence of unprotected iron-oxide sites in the redox kinetics. In contrast, the doubly coated system exhibited a normal in-vitro kinetic activity, allowing a good enzyme recovery and recyclability. (C) 2011 Elsevier Inc. All rights reserved.

The effect of calcium salts on the viscosity and adsorption behavior of xanthan

The effect of CaCl(2), Ca(NO(3))(2), CaSO(4), CaCO(3) and Ca(3)(PO(4))(2) on the flow behavior of xanthan gum solutions was investigated. Regardless the concentration and type of calcium salt used, xanthan solutions presented pseudoplastic behavior. The soluble salts (CaCl(2) and Ca(NO(3))(2)) induced the disordered state in the xanthan chains at concentration of 1.0 g/L or 10 g/L, decreasing the flow consistency index (K) values. At 100 g/L soluble salts K values were similar to those found for pure xanthan solutions, whereas at the same concentration of insoluble particles the K values increased 20%. The adsorption of xanthan gum onto Si/SiO(2) surfaces in the presence of calcium salts was investigated by ellipsometry and atomic force microscopy (AFM). The adsorbed layer of xanthan onto Si/SiO(2) consisted of two regions: (i) a thin acid resistant sublayer, where xanthan chains were like highly entangled fibers and (ii) a thick upperlayer, whose morphology was calcium salt dependent. (C) 2010 Elsevier Ltd. All rights reserved.

Photocatalyst TiO(2)-Co: the effect of doping depth profile on methylene blue degradation

In this work, we study the effect of doping depth profile on the photocatalytic and surface properties of TiO(2) films. Two thin film layers of TiO(2) (200 nm) and Co (5 nm), respectively, were deposited by physical evaporation on glass substrate. These films were annealed for 1 s at 100 and 400 A degrees C and the Co layer was removed by chemical etching. Atomic force microscopy (AFM) phase images showed changes in the surface in function of thermal treatment. The grazing-incidence X-ray fluorescence (GIXRF) measurements indicated that the thermal treatment caused migration of Co atoms to below the surface, the depths found were between 19 and 29 nm. The contact angle showed distinct values in function of the doped profile or Co surface concentration. The UV-vis spectra presented a red shift with the increasing of thermal treatment. Photocatalytical assays were performed by methylene blue discoloration and the higher activity was found for TiO(2)-Co treated at 400 A degrees C, the ESI-MS showed the fragments formed during the methylene blue decomposition.

Laponite RD/polystyrenesulfonate nanocomposites obtained by photopolymerization

The present paper describes the synthesis and characterization by dynamic light scattering, X-ray diffraction, scanning electron microscopy and atomic force microscopy of Laponite RD/Sodium polystyrenesulfonate nanocomposites obtained by radical photopolymerization initiated by the cationic dye safranine. The presence of the clay mineral does not affect the hydrotropic aggregation of the monomers, but allows a better deaggregation of the initiator molecules, decreasing the quenching of the excited states that leads to the radicals that initiate polymerization. Increasing the amount of clay mineral loading in the polymerization mixture promotes higher monomer conversion and faster polymerization. The size of the nanocomposite particles, measured by light scattering decreases from 400 to 80 nm for clay mineral loadings of 1.0 wt.%. The X-ray diffraction patterns indicate that the clay mineral does not present a regular crystalline structure in the nanocomposite. Atomic force microscopy studies show films of sodium polystyrenesulfonate polymer with embedded Laponite platelets in its structure, forming 1-8 nm height and 25-100 nm diameter aggregates. (C) 2011 Elsevier B.V. All rights reserved.

Electrodeposition and characterization of thin selenium films modified with lead ad-atoms

The deposition and characterization of Se films doped with Pb underpotentially deposited (UPD) ad-atoms was studied in this work. The employed experimental techniques were cyclic voltammetry, chronoamperometry, electrochemical impedance spectroscopy, UV-vis spectroscopy and atomic force microscopy. The initial deposition of Se film by chronoamperometry yielded a thin film composed of approximately 700 layers. The Pb UPD on Se was achieved by chronoamperometry in a potential value previously determined in voltammetric experiments. This deposition yielded a deposition charge of approximately 7.5% of the total one. The film resistance altered from 320 Omega cm(2) for Se to 65 Omega cm(2) for the Se/Pb one. Flat band potential values and number of acceptors and donors were also calculated for both films and the values obtained were + 0.95 and -0.51 V for Se and Se/Pb, respectively. The Se coating presented 1.2 x 10(17) cm(3) acceptors while the Se/Pb one presented 3.2 x 10(17) cm(3) donors. The band gap values for both films were 2.4 eV and 1.9 eV, correspondingly. (C) 2008 Elsevier B.V. All rights reserved.

Biobased films prepared from NaOH/thiourea aqueous solution of chitosan and linter cellulose

In the present study, films based on linter cellulose and chitosan were prepared using an aqueous solution of sodium hydroxide (NaOH)/thiourea as the solvent system. The dissolution process of cellulose and chitosan in NaOH/thiourea aqueous solution was followed by the partial chain depolymerization of both biopolymers, which facilitates their solubilization. Biobased films with different chitosan/cellulose ratios were then elaborated by a casting method and subsequent solvent evaporation. They were characterized by X-ray analysis, scanning electron microscopy (SEM), atomic force microscopy (AFM), thermal analysis, and tests related to tensile strength and biodegradation properties. The SEM images of the biofilms with 50/50 and 60/40 ratio of chitosan/cellulose showed surfaces more wrinkled than the others. The AFM images indicated that higher the content of chitosan in the biobased composite film, higher is the average roughness value. It was inferred through thermal analysis that the thermal stability was affected by the presence of chitosan in the films; the initial temperature of decomposition was shifted to lower levels in the presence of chitosan. Results from the tests for tensile strength indicated that the blending of cellulose and chitosan improved the mechanical properties of the films and that an increase in chitosan content led to production of films with higher tensile strength and percentage of elongation. The degradation study in a simulated soil showed that the higher the crystallinity, the lower is the biodegradation rate.

The processes involved in the Se electrodeposition and dissolution on Au electrode: the H2Se formation

The processes involved in the Se electrodeposition, mainly the one related to the formation of H2Se species on Au electrode in perchloric acid solutions, have been investigated through cyclic voltammetry, electrochemical quartz crystal microbalance (EQCM), rotating ring-disc electrode (RRDE), and atomic force microscopy (AFM) techniques. In the experiments performed with the EQCM, with the potential sweep in the negative direction, the responses for the mass variation were divided in three well-defined potential regions: A (from 1.55 to 0.35 V), B (from 0.35 to -0.37 V), and C (from -0.37 to -0.49 V). It was verified that the following processes can occur, respectively: the species (AuO)(2)H2SeO3 was desorbed during the AuO reduction, the reduction of Se(IV) to Se(0), and the formation of H2Se. When the potential was swept in the positive direction, the responses for the mass variation were divided in four well-defined potential regions: D (from -0.49 to 0.66 V), E (from 0.66 to 0.99 V), F (from 0.99 to 1.26 V), and G (from 1.26 to 1.55 V), and the described processes in these regions were, respectively: the Se deposition and adsorption of water molecules and/or perchlorate ions, the Se dissolution, the Se incorporating mass in the form of HO-Se, and the Au oxidation (all potentials are referred to the Ag/AgCl electrode). Making use of the RRDE, using the collection technique, the formation of H2Se species during the Se electrodeposition was investigated. Therefore, it was confirmed that this species is formed on the disc electrode between -0.3 and -0.55 V vs the Ag/AgCl potential range (collecting the oxidized compound onto the ring electrode). AFM images also indicated that the surface topography of the Se-massive deposit on Au is different from the images registered after the formation of H2Se species, confirming the cathodic stripping of Se.

Physical Vapor Deposited Thin Films of Lignins Extracted from Sugar Cane Bagasse: Morphology, Electrical Properties, and Sensing Applications

The concern related to the environmental degradation and to the exhaustion of natural resources has induced the research on biodegradable materials obtained from renewable sources, which involves fundamental properties and general application. In this context, we have fabricated thin films of lignins, which were extracted from sugar cane bagasse via modified organosolv process using ethanol as organic solvent. The films were made using the vacuum thermal evaporation technique (PVD, physical vapor deposition) grown up to 120 nm. The main objective was to explore basic properties such as electrical and surface morphology and the sensing performance of these lignins as transducers. The PVD film growth was monitored via ultraviolet-visible (UV-vis) absorption spectroscopy and quartz crystal microbalance, revealing a linear relationship between absorbance and film thickness. The 120 nm lignin PVD film morphology presented small aggregates spread all over the film surface on the nanometer scale (atomic force microscopy, AFM) and homogeneous on the micrometer scale (optical microscopy). The PVD films were deposited onto Au interdigitated electrode (IDE) for both electrical characterization and sensing experiments. In the case of electrical characterization, current versus voltage (I vs V) dc measurements were carried out for the Au IDE coated with 120 nm lignin PVD film, leading to a conductivity of 3.6 x 10(-10) S/m. Using impedance spectroscopy, also for the Au IDE coated with the 120 nm lignin PVD film, dielectric constant of 8.0, tan delta of 3.9 x 10(-3)) and conductivity of 1.75 x 10(-9) S/m were calculated at 1 kHz. As a proof-of-principle, the application of these lignins as transducers in sensing devices was monitored by both impedance spectroscopy (capacitance vs frequency) and I versus time dc measurements toward aniline vapor (saturated atmosphere). The electrical responses showed that the sensing units are sensible to aniline vapor with the process being reversible. AFM images conducted directly onto the sensing units (Au IDE coated with 120 nm lignin PVD film) before and after the sensing experiments showed a decrease in the PVD film roughness from 5.8 to 3.2 nm after exposing to aniline.

Cassava bagasse cellulose nanofibrils reinforced thermoplastic cassava starch

Cellulose cassava bagasse nanofibrils (CBN) were directly extracted from a by-product of the cassava starch (CS) industry, viz. the cassava bagasse (CB), The morphological structure of the ensuing nanoparticles was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), presence of other components such as sugars by high performance liquid chromatography (HPLC), thermogravimetric analysis (TGA), and X-ray diffraction (XRD) experiments. The resulting nanofibrils display a relatively low crystallinity and were found to be around 2-11 nm thick and 360-1700 nm long. These nanofibrils were used as reinforcing nanoparticles in a thermoplastic cassava starch matrix plasticized using either glycerol or a mixture of glycerol/sorbitol (1:1) as plasticizer. Nanocomposite films were prepared by a melting process. The reinforcing effect of the filler evaluated by dynamical mechanical tests (DMA) and tensile tests was found to depend on the nature of the plasticizer employed. Thus, for the glycerol-plasticized matrix-based composites, it was limited especially due to additional plasticization by sugars originating from starch hydrolysis during the acid extraction. This effect was evidenced by the reduction of glass vitreous temperature of starch after the incorporation of nanofibrils in TPSG and by the increase of elongation at break in tensile test. On the other hand, for glycerol/sorbitol plasticized nanocomposites the transcrystallization of amylopectin in nanofibrils surface hindered good performances of CBN as reinforcing agent for thermoplastic cassava starch. The incorporation of cassava bagasse cellulose nanofibrils in the thermoplastic starch matrices has resulted in a decrease of its hydrophilic character especially for glycerol plasticized sample. (C) 2009 Elsevier Ltd. All rights reserved.

Modificação estrutural de bentonitas nacionais : caracterização e estudos de adsorção

São apresentados os aspectos teóricos, práticos e bibliográficos envolvidos no desenvolvimento da tese de doutorado intitulada Modificação estrutural de bentonitas nacionais: caracterização e estudos de adsorção. O trabalho consistiu no desenvolvimento de um material adsorvente a partir de bentonitas, do tipo montmorilonitas, modificadas estruturalmente com o objetivo de aumentar sua capacidade de adsorção de poluentes, orgânicos e inorgânicos. O estudo visa incrementar o valor agregado deste recurso mineral e insere-se na área de tratamento de efluentes líquidos usando adsorventes não tradicionais, eficientes e de baixo custo em substituição ao carvão ativado ou às resinas de troca iônica. Foram estudadas as propriedades físicas e químicas; distribuição de tamanho de partículas, área superficial, potenciais eletrocinéticos, capacidade de troca catiônica, composição mineralógica, morfologia superficial e espaçamento basal, bem como as propriedades adsorptivas dos argilominerais não tratados e modificados, não modificadas e pilarizadas respectivamente. Também são discutidos os mecanismos de adsorção envolvidos e o desenvolvimento de um reator contínuo (adsorção em flocos) e de separação sólido/líquido. As modificações estruturais dos argilominerais foram realizadas via homoionização com cloreto de cálcio e posterior intercalação com compostos orgânicos com ação quelante de metais. A FENAN, bentonita obtida pela intercalação com Orto Fenantrolina (OF), foi a que apresentou melhor viabilidade técnica em termos de adsorção, adsorção/dessorção, floculação e de acumulação de poluentes na forma floculada e não floculada. Adicionalmente os estudos de reversibilidade da intercalação revelaram a alta estabilidade da OF na FENAN, em soluções fortemente ácidas, onde aproximadamente 90% da OF permanece ligada à superfície da argila. A quantidade de OF adsorvida na forma de unidades micelares foi de 112 mg por grama de bentonita a pH 8,5 ± 0,5. A caracterização das bentonitas, via difração de Raios X, análise térmica, microscopia eletrônica de varredura e por microscopia de força atômica, revelou que as FENAN possuem um comportamento estrutural muito estável ao longo da seqüência de adsorção/dessorção e que após a adsorção de poluentes inorgânicos, o quelato metálico formado apresenta alta estabilidade dentro da estrutura da organobentonita. A capacidade de acumulação alcançada nas FENAN foi de 110 mg de Cu/g de bentonita, valor superior à de diversos materiais adsorventes alternativos propostos em outros trabalhos similares. Os estudos de acumulação das FENAN floculadas – FENANFLOC, indicaram que a presença de floculante, na quantidade utilizada, não afeta significativamente a capacidade de remoção das bentonitas modificadas. Este comportamento apresentado, permitiu o desenvolvimento do Reator Expandido de Flocos Adsorventes (REFA), cujas características e parâmetros operacionais são discutidos em detalhe. Finalmente, os resultados são discutidos em termos dos fenômenos interfaciais envolvidos e dos potenciais práticos deste novo adsorvente e da nova técnica de adsorção em flocos no REFA.

Modificação de membranas de quitosana por plasma para uso biológico

Chitosan membranes have been modified by plasma, utilizing the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen. The modified membranes by plasma were compared to the unmodified ones. The membranes were characterized by absorption assay, contact angle, atomic force microscopy (AFM). Also, permeability assay of sodium sulfamerazine from such membranes were carried out. Through the absorption assay and contact angle it was possible to obtain information of the wettability of the membranes and what changes the plasma treatment can promote in relation to it. The plasma treatment using oxygen promoted increase of the wetability and swelling while the samples treated with methane decrease of the wetability and swelling. Through the Optical Emission Spectroscopy (OES) it was possible to identify which species were present in the plasma during the treatment. And through the AFM analysis it was possible to observe the changes nanotopography occurred on the surface of the samples. Permeability assay were archived for all treated membranes and compared to no treated ones. Due to that assay it was possible verify which the plasma treatment increased the permeability spectrum of the membranes which has varied from 1,4548 *10-5cm2.min-1 to 2,7713*10-5cm2.min-1. Chitosan membranes with permeability varied are importance in systems drug delivery, to liberate a wide variety of drugs