Mild and severe wear of steels and cast irons in sliding abrasion

This paper presents the results obtained in pin-on-disk test apparatus using glass and alumina as abrasive materials, showing the rates and mechanisms of abrasive wear of 1070 and 52100 steels, and ductile and white cast irons. The test conditions were selected in order to obtain wear rates that correspond to mild and severe abrasion, using different metal hardness-to-abrasive hardness ratios(H/H(A)) and 0.2 or 0.06 mm abrasive grains. The use of bulk Vickers hardness, instead of microhardness, allows a better description of the different abrasion regions. Under severe abrasion, the microcutting mechanism of wear prevailed together with friction coefficients larger than 0.4. On the other hand, when relatively soft abrasives are tested, indentation of abrasive particles followed by its fragmentation, and a creation of a thin deformed layer were the main damage mechanisms, with the friction coefficient lying below 0.4. The abrasive particle size under mild regime is able to change the wear rates in an order of magnitude. (C) 2009 Elsevier B.V. All rights reserved.

Load effect in abrasive wear mechanism of cast iron with graphite and cementite

In this study four irons were casted with different chromium and vanadium contents: 2.66% Cr, 5.01% Cr, 2.51% V and 5.19% V. Their microstructure is composed of: ledeburite, graphite and M(3)C carbides (cementite). Pin-abrasion tests were carried out using fixed alumina abrasive grains at different loads: 1, 2, 4.6 and 10 N. The wear surface and the abrasive paper were examined by scanning electron microscopy for identifying the wear micromechanism. The results reveal that the mass loss increased with the load increase, and the effect of the percentage of chromium on mass loss is inverted when the load is increased from 4.6 to 10 N; for 4.6 N the mass loss decreased when the chromium percentage was increased from 2.66% to 5.01%. Nevertheless, for 10 N the mass loss increased when the chromium percentage was increased. The worn surfaces of the materials tested at 1 N show microcutting caused by the abrasive tip that produces continuous microchips. The worn surfaces and the abrasive paper tested at 10 N show continuous microchips and brittle debris. The results show that high pressures produce a brittle wear mechanism and low pressures produce a more ductile wear micromechanism, for this, the applied pressure defines the dependence between the wear resistance and wear micromechanism. (C) 2009 Elsevier B.V. All rights reserved.

Separation of silica from bauxite via froth flotation

This paper reports an innovative development: concentrating gibbsite via reverse froth flotation in order to obtain a metallurgical-grade bauxite concentrate. Tailings from an industrial plant have undergone attrition scrubbing and desliming; the quartz silica contained in the tailings has undergone flotation. Starch was used as a depressant, and ether-amine as the cationic collector. Optimum pH is around 10.0. In pilot plant scale, a metallurgical-grade concentrate was obtained by assaying 42.3% available alumina with an alumina/insoluble silica mass ratio of 11.1. It contained the gibbsite and the iron and titanium bearing minerals. The concentrate was further upgraded by magnetic separation, leading to 54.0% available alumina, with an alumina/insoluble silica mass ratio of 12.6 at an overall available alumina recovery of 69.3% in the final concentrate (non-magnetic product). (C) 2008 Elsevier Ltd. All rights reserved.

Quantitative analysis of aluminum dross by the Rietveld method

Aluminum white dross is a valuable material principally due to its high metallic aluminum content. The aim of this work is to develop a method for quantitative analysis of aluminum white dross with high accuracy. Initially, the material was separated into four granulometric fractions by means of screening. Two samples of each fraction were obtained, which were analyzed by means of X-ray fluorescence and energy dispersive spectroscopy in order to determine the elements present in the samples. The crystalline phases aluminum, corundum, spinel, defect spinel, diaoyudaoite, aluminum nitride, silicon and quartz low were identified by X-ray diffraction. The quantitative phase analysis was performed by fitting the X-ray diffraction profile with the Rietveld method using the GSAS software. The following quantitative results were found: 77.8% aluminum, 7.3% corundum, 2.6% spinel, 7.6% defect spinel, 1.8% diaoyudaoite, 2.9% aluminum nitride, and values not significant of quartz and silicon.

Interface Energy Measurement of MgO and ZnO: Understanding the Thermodynamic Stability of Nanoparticles

Nanomaterials have triggered excitement in both fundamental science and technological applications in several fields However, the same characteristic high interface area that is responsible for their unique properties causes unconventional instability, often leading to local collapsing during application Thermodynamically, this can be attributed to an increased contribution of the interface to the free energy, activating phenomena such as sintering and grain growth The lack of reliable interface energy data has restricted the development of conceptual models to allow the control of nanoparticle stability on a thermodynamic basis. Here we introduce a novel and accessible methodology to measure interface energy of nanoparticles exploiting the heat released during sintering to establish a quantitative relation between the solid solid and solid vapor interface energies. We exploited this method in MgO and ZnO nanoparticles and determined that the ratio between the solid solid and solid vapor interface energy is 11 for MgO and 0.7 for ZnO. We then discuss that this ratio is responsible for a thermodynamic metastable state that may prevent collapsing of nanoparticles and, therefore, may be used as a tool to design long-term stable nanoparticles.

Relationship between surface segregation and rapid propane electrical response in Cd-doped SnO2 nanornaterials

Controlling the surface properties of nanoparticles using ionic dopants prone to be surface segregated has emerged as an interesting tool for obtaining highly selective and sensitive sensors. In this work, the surface segregation of Cd cations on SnO2 nanopowders prepared by the Pechini`s method was studied by infrared spectroscopy, X-ray diffraction, and specific surface area analysis. We observed that the surface chemistry modifications caused by the surface segregation of Cd and the large specific surface area were closely responsible for a rapid and regular electrical response of 5 mol% Cd-doped SnO2 films to 100 ppm propane and NO, diluted in dry air at relatively low temperature (100 degrees C). (c) 2008 Elsevier B.V. All rights reserved.

Long-term aging of fiber-cement corrugated sheets - The effect of carbonation, leaching and acid rain

This paper studies the performance of fiber-cement corrugated sheets exposed to long-term weathering, exploring the effect of different environments on fiber-cement degradation. Fiber-cement corrugated sheets that had been exposed to weathering, and in place for more than 30-years, were collected from two different Brazilian cities (Sao Paulo and Criciuma). Mechanical properties (MOR, MOE and fracture toughness) were tested on samples removed from the corrugated sheets. Microstructure was evaluated by X-ray diffraction, SEM with EDS analysis, MIP and TG. The results show that the 37-year-old asbestos-cement corrugated sheets from Sao Paulo presented similar characteristics to those of the non-aged asbestos-cement readily available on the market place. Conversely, deterioration of the asbestos-cement from the industrial area of Criciuma is related to acidic attack, along with carbonation and leaching as a consequence of continued exposition to acid rain during several decades. This process resulted in higher porosity and lower mechanical strength, revealing that leaching mechanisms can have important effect on the performance of thin fiber-cement sheets. (c) 2007 Elsevier Ltd. All rights reserved.

Mechanical properties, drying and autogenous shrinkage of blast furnace slag activated with hydrated lime and gypsum

This article reports the characteristics of blast furnace slag (BFS) pastes activated with hydrated lime (5%) and hydrated lime (2%) plus gypsum (6%) in relation to compressive strength, shrinkage (autogenous and drying) and microstructure (porosity, hydrated products). The paste mixtures were characterized using powder X-ray diffraction (XRD), mercury intrusion porosimetry (MIP) and thermogravimetric analysis (TG/DTG). BSF activated with lime and gypsum (LG) results in larger amounts of ettringite when compared with BFS activated with lime (L). Although the porosities of the L and LG mixtures were about the same, there was a greater pore refinement for the BFS activated with lime, with an increase in mesopores volume with age. The presence of ettringite and the higher volumes of macropores cause the compressive strength of BSF activated with hydrated lime plus gypsum to be smaller than that of BFS activated with lime. For both chemical activators, compressive strength developed slowly at early ages. Autogenous and drying shrinkage were greater for the BFS activated with lime, believed to result from the more refined porous structure in comparison with the mixture activated with gypsum plus lime. (c) 2010 Elsevier Ltd. All rights reserved.

Simple and Efficient Access to 3-Ethoxycarbonylpyrroles, Benzofurans, and Naphthofurans

An efficient method was developed for the synthesis of pyrrole and furan derivatives from enamines, phenols, and naphthols. The key steps involve iodocyclization and alumina-induced dehydroiodination reactions.

Squeeze flow as a tool for developing optimized gypsum plasters

This paper presents a rheological investigation of pure gypsum (PG) and a commercial gypsum-lime-filler plaster (CP) using the modified Vicat apparatus and squeeze flow method. The samples were tested at several different intervals after manual or mechanical mixing. The results confirmed squeeze flow to be more sensitive in determining fresh paste behavior than the modified Vicat apparatus. PG set faster when prepared in mechanical mixer than when manually mixed. Conversely, the CP composition presented longer setting when mixed mechanically. The study also included the analysis of two ready-to-use polymer-based products for leveling and rendering (drywall joint compound - DJC; acrylic putty - AP) measured by squeeze flow and compared to the commercial composition. (C) 2008 Elsevier Ltd. All rights reserved.

Chemical-mineralogical characterization of C&D waste recycled aggregates from Sao Paulo, Brazil

This study presents a methodology for the characterization of construction and demolition (C&D) waste recycled aggregates based on a combination of analytical techniques (X-ray fluorescence (XRF), soluble ions, semi-quantitative X-ray diffraction (XRD), thermogravimetric analysis (TCA-DTG) and hydrochloric acid (HCl) selective dissolution). These combined analytical techniques allow for the estimation of the amount of cement paste, its most important hydrated and carbonated phases, as well as the amount of clay and micas. Details of the methodology are presented here and the results of three representative C&D samples taken from the Sao Paulo region in Brazil are discussed. Chemical compositions of mixed C&D aggregate samples have mostly been influenced by particle size rather than the visual classification of C&D into red or grey and geographical origin. The amount of measured soluble salts in C&D aggregates (0.15-25.4 mm) is lower than the usual limits for mortar and concrete production. The content of porous cement paste in the C&D aggregates is around 19.3% (w/w). However, this content is significantly lower than the 43% detected for the C&D powders (< 0.15 min). The clay content of the powders was also high, potentially resulting from soil intermixed with the C&D waste, as well as poorly burnt red ceramic. Since only about 50% of the measured CaO is combined with CO(2), the powders have potential use as raw materials for the cement industry. (C) 2008 Elsevier Ltd. All rights reserved.

DOSES OF INDOLBUTYRIC ACID IN THE ROOTING AND GROWTH OF EUCALYPT CUTTINGS (Eucalyptus urophylla)

This work aimed to evaluate the effect of different concentrations of IBA (indolbutyric acid) in the rooting and growth of Eucalyptus urophylla cuttings. The experimental design used was the randomized blocks, in factorial with an arrangement of split plots, with three concentrations of IBA (2.000; 5.000 and 8.000 mg L(-1)), two ways of the application of plant gowth regulators (paste and powder), and three period of evaluations (30, 45 and 60 days). The experiment was carried out in the Farm Buriti de Prata, an entreprise property of Souza Cruz, in the city of Prata - MG in 2003. After the preparation of the cuttings, patterned in 10 cm of length and 0.8 cm of diameter, those were immersed in mixtures of IBA for 10 seconds, in the forms of dry powder and paste and than planted in plastic tubes contening Plantmax substrate with vermiculite. The cuttings were transported to greenhouse with controled humidity, where they remained for 60 days. The variables studied were: height of plant in the 30(th), 45(th) and 60(th) days after seeding; fresh mass of the aerial part and roots. The IBA applied in powder form as well as in paste form, resulted in an greater seedling growth. To the 60 days, the seedlings presented greater growth, being significantly superior to the heights measured in other times of evaluation. The application of 2.000 mg L(-1) and 5,000 mg L(-1) resulted in significant increases on weight of fresh mass of the aerial part and root system.

ANALYSIS OF PRESSURE FLUCTUATIONS DURING WATER EVAPORATION IN SPOUTED BED

The aim of this work was to study the behaviour of conventional spouted beds during water evaporation and to analyze the pressure fluctuations at the maximum water evaporative capacity for different bed heights and air flow rates. The results showed that spout pressure drop could not indicate the proximity of maximum evaporative capacity; however this condition is denoted by a minimum in fountain height. The standard deviation and amplitude of the pressure fluctuations also showed a minimum point at the maximum water evaporation capacity. The frequency domain analysis of pressure fluctuations revealed that the dry bed has a dominant frequency varying from 6 to 8.2 Hz and that the peak of dominant frequency tends to disappear with the increase in water feed rate.

IDENTIFICATION OF THE STATE OF A WET SPOUTED BED THROUGH TIME-FREQUENCY ANALYSIS OF PRESSURE FLUCTUATION TIME SERIES

The feasibility of detecting instability in wet spouted beds via pressure fluctuation (PF) time-series analyses was investigated. Experiments were carried out in a cylindrical Plexiglas column of diameter 150 mm with a conical base of internal angle 60 degrees, an inlet orifice diameter of 25 mm and glass beads of diameter 2.4 mm. Transducers at several axial positions measured PF time series with incremental addition of aqueous sucrose solutions of different concentrations. Liquid addition affected the spouted bed dynamics, causing irregular spouting, increased voidage in the annulus, increased fountain height, irregular annulus height, channelling, agglomeration, and adhesion of particles to the column walls. Autocorrelations indicated the appearance of periodicities in the PF signals with increasing sucrose addition. Dominant peaks in power-spectral density developed at low frequencies with changing system dynamics. The results indicate that PF signals furnish relevant information on system dynamics, useful for monitoring and control of spouted bed operations such as particle coating and drying of paste-like materials.

Synthesis of (-)-hinokinin by oxidation of (-)-cubebin catalyzed by biomimetic metalloporphyrin catalytic systems

A catalytic system consisting of iron tetraphenylporphyrin supported on an alumina matrix for oxidation of (-)-cubebin with iodosylbenzene or hydrogen peroxide is reported. Conversion of (-)-cubebin is very efficient (100%) with 100% selectivity producing only (-)-hinokinin when iodosylbenzene is used as the oxidant and 70% conversion with 100% selectivity when hydrogen peroxide is the oxidant at room temperature under atmospheric pressure. (c) 2008 Elsevier B.V. All rights reserved.