Correlation of the hybrid layer thickness and resin tags length with the bond strength of a self-etching adhesive system.

The objective of this study was to measure the thickness of the hybrid layer (HLT), length of resin tags (RTL) and bond strength (BS) in the same teeth, using a self-etching adhesive system Adper Prompt L Pop to intact dentin and to analyze the correlation between HLTand RTL and their BS. Ten human molars were used for the restorative procedures and each restored tooth was sectioned in mesio-distal direction. One section was submitted to light microscopy analysis of HLT and RTL (400x). Another section was prepared and submitted to the microtensile bond test (0.5 mm/min). The fractured surfaces were analyzed using scanning electron microscopy to determine the failure pattern. Correlation between HLT and RTL with the BS data was analyzed by linear regression. The mean values of HLT, RTL and BS were 3.36 microm, 12.97 microm and 14.10 MPa, respectively. No significant relationship between BS and HLT (R2= 0.011, p>0.05) and between BS and RTL (R2= 0.038) was observed. The results suggested that there was no significant correlation between the HLT and RTL with the BS of the self-etching adhesive to dentin.

Observation of tags and hybrid layer of a single bottle conventional adhesive system and a self-etching adhesive system, on sound dentin.

This experimental light microscopy study investigated the formation of a hybrid layer and resin tags on sound dentin, after utilization of conventional and self-etching adhesive systems. After restorative procedures, the specimens were decalcified in a formic acid and sodium citrate solution, embedded in paraffin, sectioned at 6-microm thickness and stained by the Brown & Brenn method for analysis and measurement by light microscopy (AXIOPHOT) (400x). The results were statistically analyzed by analysis of variance, at a significance level of 5%. Based on the results, it could be concluded that the conventional adhesive allowed the formation of a thicker hybrid layer than the self-etching adhesive, with similar penetration into the dentinal tubules (resin tags).

In vitro surface roughness of different glass ionomer cements indicated for ART restorations

Aim: The aim of this in vitro study was to evaluate the surface roughness of three glass ionomer cements (GICs) indicated for ART restorations. Methods: Ten cylindrical specimens of three commercial glass ionomers cements (Vidrion R - S.S. White, Maxxion R - FGM and Vitromolar DFL) were prepared (n=30) without surface finishing or protection. Twenty-four hours after preparation, the surface roughness measurements were obtained as the mean of three readings of the surface of each specimen by profilometry. The roughness values (Ra, μm) were subjected to one-way ANOVA and Tukey's test (p<0.05). Results: No statistically significant differences were observed between Vidrion R (0.18 ± 0.05) and Vitromolar (0.21 ± 0.05), whereas Maxxion R presented significantly higher roughness values than those of the other materials. Conclusions: It may be concluded that characteristics of particle size and composition of the different GICs affected their surface roughness 24 h after preparation.

Stress distribution in ceramic restorations over natural tooth using finite element analysis. lithium disilicate x aluminum oxide material

Background: Data on stress distribution in tooth-restoration interface with different ceramic restorative materials are limited. The aim of this chapter was to assess the stress distribution in the interface of ceramic restorations with laminate veneer or full-coverage crown with two different materials (lithium dissilicate and densely sintered aluminum oxide) under different loading areas through finite element analysis. Materials and Methods: Six two-dimensional finite element models were fabricated with different restorations on natural tooth: laminate veneer (IPS Empress, IPS Empress Esthetic and Procera AllCeram) or full-coverage crown (IPS e.max Press and Procera AllCeram). Two different loading areas (L) (50N) were also determined: palatal surface at 45° in relation to the long axis of tooth (L1) and perpendicular to the incisal edge (L2). A model with higid natural tooth was used as control. von Mises equivalent stress (σ vM) and maximum principal stress (σ max) were obtained on Ansys software. Results: The presence of ceramic restoration increased σ vM and σ max in the adhesive interface, mainly for the aluminum oxide (Procera AllCeram system) restorations. The full-coverage crowns generated higher stress in the adhesive interface under L1 while the same result was observed for the laminate veneers under L2. Conclusions: Lithium dissilicate and densely sintered aluminum oxide restorations exhibit different behavior due to different mechanical properties and loading conditions. © 2011 Nova Science Publishers, Inc.

Analysis of hybrid layer thickness, resin tag length and their correlation with microtensile bond strength using a total etch adhesive to intact dentin.

The objective of this study was to evaluate the use of a two-step total etch and rinse adhesive, the correlation between the hyybrid layer thickness (HL) and bond strength (BS), and between resin tag length (RT) and bond strength in the same teeth, and also to evaluate the fracture patterns of the tested specimens. Ten human molars were used for the restorative procedure and then sectioned in two halves (mesio-distally). The materials used were Adper Single Bond 2, 3M ESPE, Ultra etch gel, Ultradent and Filtek Z250, 3M ESPE. One half were utilized to measure the HL thickness and RT length through light microscopy analysis (400x), and the other half was subject to a microtensile test to measure the BS. The fractured surfaces were analyzed by scanning electron microscopy and fracture patterns classified. The Pearson correlation test was applied (p = 0.05). The results of the analyses of each specimen then were correlated: mean HL thickness = 4.39 (0.48) microm, mean length of RT = 9.94 (1.69) microm, mean BS = 23.98 (10.24) MPa. A statistically significant correlation between HL thickness and bond strength was found (r = 0.93). The two step etch and rinse adhesive system, showed a strong correlation between HL thickness and bond strength. The most common fractures were adhesive, followed by cohesive in resin.

Influence of the hybrid layer thickness and resin tag length on microtensile bond strength.

The purpose of this study was to evaluate the correlation between the hybrid layer thickness/resin tag length and the microtensile bond strength of conventional two-step adhesive system, when applied to healthy dentinal tissue. After performing the restorative adhesive procedures and tooth extractions, ten specimens were sectioned in the mesiodistal direction. One section was used for microscopic analysis of the resin tag lengths and the hybrid layer thickness, while the other was used for the microtensile bond strength test (0.5 mm/min). The fractured surface was classified according to the fracture pattern, under a stereoscopic microscope at 40x magnification. Data obtained were submitted to analysis using one-way ANOVA and Pearson's Correlation test (alpha=0.05). The means corresponding to the hybrid layer thickness, resin tag lengths and the microtensile test were 2.68 microm, 6.43 microm and 16.23 MPa, respectively. There was no correlation between the means of the values obtained for the microtensile test, and those presented by the hybrid layer (r2=0.40, p>0.05) and resin tags (r2=0.21, p>0.05). The microtensile bond strength of the conventional two-step adhesive system Adper Single Bond 2 did not depend on the thickness of the hybrid layer and length of resin tags.

Influence of cutting instruments and adhesive systems on hybrid layer formation.

Influence of cutting instruments and The aim of this study was to analyze the hybrid layer in noncarious dentin prepared by different cutting instruments and restored with composite resin. The cavities were randomly prepared in 40 specimens using a high-speed diamond bur (KG Sorensen 1013) and an ultrasonic tip (CVDentus C22). The cavities were restored with composite resin by varying the adhesive system between the Adper™ Single Bond (2 x 1 system, primer+adhesive) and the Prompt L-Pop™ (3 x 1 system, self-etching). The restorations were hemisected longitudinally and analyzed in the SEM (Scanning electron microscopy) in order to evaluate the hybrid layer and resinous tags characteristics, using scores ranging from 1 to 6. The Pearson test revealed a high correlation coefficient and good significance levels for both intra- and inter-raters values (r=0.90). The data were statistically analyzed using the Mann-Whitney test (P≤0.05). A larger proportion of regular hybrid layers with numerous tags were observed in the dentin prepared using the high-speed diamond burs and restored with a 2 × 1 adhesive system. Alternatively, the 3 × 1 adhesive system promoted the generation of a thin hybrid layer with few tags. After preparation using an ultrasonic tip revealed few or no tags after the preparation and 2 × 1 or 3 × 1 adhesive system application. The high-speed diamond burs produced a dentin surface that was more favorable to restorative material adhesion than the ultrasonic tips, regardless of the adhesive system used.

Optical characterization of one dental composite resin using bovine enamel as reinforcing filler

The use of composite resins for restorative procedure in anterior and posterior cavities is highly common in Dentistry due to its mechanical and aesthetic properties that are compatible with the remaining dental structure. Thus, the aim of this study was to evaluate the optical characterization of one dental composite resin using bovine enamel as reinforcing filler. The same organic matrix of the commercially available resins was used for this experimental resin. The reinforcing filler was obtained after the gridding of bovine enamel fragments and a superficial treatment was performed to allow the adhesion of the filler particles with the organic matrix. Different optical images as fluorescence and reflectance were performed to compare the experimental composite with the human teeth. The present experimental resin shows similar optical properties compared with human teeth. © 2012 SPIE.

Avaliação de usuários da atenção básica sobre a implantação de protocolo de assistência integral odontológica

Objective: To evaluate the perception of basic attention healthcare users as to the implantation of the Integral Dental Assistance Protocol (PAIO, in Portuguese) and the effect of this program on the oral health condition, oral hygiene, access to and resolubility of the service, in a public basic health unit of João Pessoa-PB. Method: The sample was composed of 32 volunteers, for whom a sixphase intervention was programed: diagnosis of dental needs; resolution of urgencies; restorative interventions; application of promotional measures; evaluation of the health level obtained; and periodic follow-up visits. Data were collected by means of a semistructured interview and a questionnaire, applied before and after PAIO implantation. The interviews were transcribed and analyzed according to the content analysis technique. The effect of PAIO implantation was evaluated by using an increasing scoring system ranging from 1 to 10. The Wilcoxon test was applied with a confidence level of 95%. Results: For the participants that attended the PAIO (n=20), the program contributed to improve oral health condition (100%) and knowledge (100%). The users reported satisfaction (n=12) and had a positive evaluation (n=12), achieved by means of the improvement of oral health condition (n=8), faster and easier access to treatment (n=7), scheduling of dental appoints and warrant of being treated (n=6), welcoming (n=5), motivation for oral care (n=5), and perspective of continuity of PAIO (n=6). The initial evaluation of the users received scores between 5.7 and 7.6. After PAIO implantation, the users' perception was improved (p<0.01), with scores between 9.6 and 9.9. Conclusion: According to the users, the implantation of PAIO contributed to the qualification of health service and oral health care, being a favorable aspect to increase the access to and resolubility of the service.

One-year clinical evaluation of composite restorations in posterior teeth: Effect of adhesive systems

This clinical study assessed the performance of posterior composite resins applied with the Adper™ Single Bond Plus (SB) and Adper ™ Scotchbond SE (SE) adhesive systems and Filtek ™ Supreme Plus composite resin, using modified US Public Health Service criteria. A total of 97 restorations were placed in posterior teeth by two calibrated operators. Application of the materials followed manufacturers' instructions. The restorations were evaluated by two examiners at baseline and after one year. Statistical analyses were conducted using the proportion test at a significance level of 5% (p<0.05). All the restorations evaluated (ie, 100%) received an alpha rating for the criteria of marginal discoloration and marginal integrity at baseline. At one year, for marginal discoloration, 64.6% of SB and 61.2% of SE received an alpha rating. For marginal integrity, 72.9% of SB and 77.6% of SE received an alpha rating. The other restorations received bravo ratings for both criteria. None of the teeth that received the restorative systems presented caries lesions around the restorations. A total of eight teeth presented postoperative sensitivity one week after baseline, five with SB and three with SE; the symptom had disappeared one year later. One year later, composite resin restorations using either adhesive system showed satisfactory clinical performance.

Anterior restorations in bleached teeth: Difficulty establishing the color after bleaching

It is becoming more common for patients to look for cosmetic procedures in dental offices. The search for lost or desired esthetics by patients is increasingly frequent and the professional must be able to meet this demand. To do this, dentists not only need to return the tooth back to its normal functioning state but also promote esthetic excellence. In this context, the association of cosmetic procedures, such as teeth whitening and restorative procedures, such as direct adhesive restorations is very common. The composite resins employed nowadays allow the reproduction of various optical properties of natural teeth. With these composite resins, it is possible to reproduce features such as translucency, opacity and specific features of the dental element, to bring back the esthetic harmony of the smile. This article reports a clinical case demonstrating the placement, in a stratified manner, of composite resins in bleached teeth, as well as the reproduction of optical and natural aspects of the teeth. In order to achieve esthetic and functional success of the restored procedure, it is important to be familiar with the new techniques and new materials in the marketand above all, we must know when and where to use them.

Correlation between hybrid layer thickness, resin tag length and microtensile bond strength of a self-etching adhesive system

The purpose of this study was to evaluate the correlation between the hybrid layer thickness, resin tag length and resin bond strength of a self-etching adhesive system to sound dentin tissue in vivo. After performing restorative procedures and tooth extractions, ten specimens were sectioned in a mesiodistal direction. One dental section was used for light microscope analysis, in which both the resin tag length and hybrid layer thickness were measured, while the other section was analyzed using a microtensile test (0.5 mm/min). The fractured surface of the latter section was characterized using a stereoscopic magnifying glass (40x magnifcation). The results were subject to statistical analysis using the Pearson Correlation Test (a = 0.05). The hybrid layer thickness, resin tag length and resin bond strength mean values were 2.19 microm (0.34), 4.34 microm (0.28) and 9.73 MPa (5,55), respectively. In addition, correlation tests between the resin tag length and the resin bond strength (r=0.014) and also between the hybrid layer thickness and bond strength (r=0.43), showed no statistically significant correlation. The microtensile bond strength of Adper Prompt L Pop self-etching adhesive system does not depend on hybrid layer thickness or resin tag length.

Persistence of epoxy-based sealer residues in dentin treated with different chemical removal protocols

The presence of residual endodontic sealer in the pulp chamber may cause discoloration of the dental crown and interfere with the adhesion of restorative materials. The aim of this study was to compare the efficacy of different solvents in removing residues of an epoxy resin-based sealer (AH Plus) from the dentin walls of the pulp chamber, by scanning electron microscopy (SEM). Forty-four bovine incisor dental crown fragments were treated with 17% EDTA and 2.5% NaOCl. Specimens received a coating of AH Plus and were left undisturbed for 5 min. Then, specimens were divided in four groups (n = 10) and cleaned with one of the following solutions: isopropyl alcohol, 95% ethanol, acetone solution, or amyl acetate solution. Negative controls (n = 2) did not receive AH Plus, while in positive controls (n = 2) the sealer was not removed. AH Plus removal was evaluated by SEM, and a score system was applied. Data were analyzed by Kruskal-Wallis and Dunn tests. None of the solutions tested was able to completely remove AH Plus from the dentin of the pulp chamber. Amyl acetate performed better than 95% ethanol and isopropyl alcohol (p < 0.05), but not better than acetone (p > 0.05) in removing the sealer from dentin. No significant differences were observed between acetone, 95% ethanol, and isopropyl alcohol (p > 0.05). It was concluded that amyl acetate and acetone may be good options for cleaning the pulp chamber after obturation with AH Plus. SCANNING 35:17-21, 2013. © 2012 Wiley Periodicals, Inc. © Wiley Periodicals, Inc.

Effects of dentin dry/moist condition on the immediate adhesive performance of different solvent-based etch-and-rinse adhesivesystems

Purpose: The purpose of this research was to analyze and measure, under optical microscopy, the hybrid layer thickness and resin tags length, as well as the microtensile bond strength of two conventional adhesive systems when applied to dry and moist dentinal substrate. Methods: Thirty-two extracted human molars were randomly distributed into four groups according to the adhesive systems (XP Bond and Prime&Bond 2.1) and moisture condition (dry and moist). In Groups I and II, XP adhesive system was applied on dry and moist dentin, respectively; while Groups III and IV received PB adhesive system, in the same way as was done in Groups I and II, respectively. After adhesive and restorative procedures, all specimens were sectioned along their long axes; one hemi-tooth sample was subjected to the microtensile bond strength test while the other was decalcified and serially sectioned into six micron thick slices and sequentially mounted on glass slides. These sections were stained by the Brown and Brenn method for posterior analysis and measurement of the hybrid layer and resin tags under a light microscope with a micrometric ocular 40/075. Results: Data were analyzed using two-way ANOVA and Tukey's test (α=0.05). For the variable hybrid layer thickness, XP showed no significant differences between dry and moist dentin (5.2 μm and 5.5 μm, respectively), but for PB, hybrid layer was significantly thicker for moist (4.0 μm) than for dry dentin (3.0 μm). For the variable resin tags length XP showed 17.9 μm length for dry dentin and 20.8 μm for moist dentin; PB 11.7 μm for dry and 12.69 μm for moist dentin;there was no significant differences between them, independent of the moisture condition. For the variable microtensile bond strength, XP showed 38.0 MPa for dry dentin and 44.5 MPa for moist dentin; and PB showed 22.7 MPa for dry dentin and 20.8 MPa for dry dentin no significant difference was observed between moist and dry dentin for XP (p=0.2) and PB (p=0.7), but XP was presented significantly higher bond strength values than PB in both moisture conditions (p=0.003 for dry and p=0.002 for moist). Conclusion: The two-step butanol-based etch-and-rinse adhesive XP Bond presented a superior behavior with regard to the hybrid layer thickness, length of resin tags and bond strength to dry and moist dentin substrates when compared with two-step acetone-based adhesive system Prime&Bond2.1. © 2013 Elsevier Ltd.

Effect of light curing modes on mechanical properties of direct and indirect composites

Objective. To evaluate the degree of conversion (DC), flexural strength (FS) and Knoop microhardness (KHN) of direct and indirect composite resins polymerized with different curing systems. Materials and methods. Specimens of direct (Z250, 3M/Espe) and indirect (Sinfony, 3M/Espe) restorative materials were made and polymerized using two light curing units: XL2500 (3M/Espe) and Visio system (3M/Espe). Absorption spectra of both composites were obtained on a FTIR spectrometer in order to calculate the DC. FS was evaluated in a universal testing machine and surface microhardness was performed in a microhardness tester (50gf/15s). DC, FS and KHN data were submitted to two-way ANOVA and Tukey's test (α = 0.05). Results. Z250 showed higher DC, FS and KHN compared with Sinfony when the polymerization was carried out with XL2500 (p < 0.05). However, there is no statistical difference in DC between the materials when Visio was used (p > 0.05). Visio showed higher DC and KHN for Z250 and Sinfony than the values obtained using XL2500 light curing (p < 0.05). For FS, no significant difference between curing units was found (p > 0.05). Conclusion. Even though the Visio system could increase DC and KHN for some direct and indirect composites, compared with the conventional halogen curing unit, a high number of monomers did not undergo conversion during the polymerization. © 2013 Informa Healthcare.