Electrical measurements in doped zirconia-ceria ceramics

Zirconia-ceria powders with 12 mol % of CeO2 doped with 0.3 mol% of iron, copper, manganese and nickel oxides were synthesized by the conventional mixed oxide method. These systems were investigated with regard to the sinterability and electrical properties. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. Small amount of dopant such as iron reduces sintering temperature by over 150degreesC and more than 98% of tetragonal phase was retained at room temperature in samples sintered at 1450degreesC against 1600degreesC to stabilize the tetragonal phase on pure ZrO2-CeO2 system. The electrical conductivity was measured using impedance spectroscopy and the results were reported. The activation energy values calculated from the Arrhenius's plots in the temperature range of 350-700degreesC for intragrain conductivities are 1.04 eV.

Renewable drops electrochemical sensor for sulfide ions detection

The design and characteristics of a novel electrochemical system, which uses a drop as a renewable electroanalytical sensor, are described. This article describes the performance of the electrochemical system, the coupling of the experimental arrangement with flow injection technique and a demonstration of its applicability for the measurement of sulfide. The method is based on renewable drops of ferricyanide ions, buffered by borate. The ferrocyanide ions, product of the reaction between ferricyanide and sulfide ions, are oxidized on a platinum microelectrode and the current measured is related to sulfide concentration. The measurements can be done in continuous or static flow mode. In continuous mode, the detection limit is 5.0 x 10(-5) mol L-1.

Effect of thermal treatment temperature on the crystallinity and morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate thin films (LiTaO3) with (50:50) stoichiometry were prepared by spin coating method using a polymeric organic solution. The films were deposited on silicon (100) substrates with 4 layers. The substrates were previously cleaned and then the solution of lithium tantalate was deposited by adjusting the speed at 5000 rpm. The thin films deposited were thermally treated from 350 to 600degreesC for 3 hours in order to study the influence of the thermal treatment temperature on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction (XRD) results showed that the films are polycrystalline and secondary phases free. The thickness of films was observed by scanning electron microscopy (SEM). The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by thermal treatment.

A disposaable electrochemical sensor for the rapid determination of levodopa

Levodopa (L-dopa), the biological precursor of catecholamines, is the most widely prescribed drug in the treatment of Parkinson's disease. The present work presents a proposal for the application of a gold screen-printed electrode an electrochemical sensor for monitoring L-dopa in stationary solution and a flow system. Using the electrooxidation of L-dopa at +0.63 V in acetate buffer pH 3.0 on a gold screen-printed electrode it is possible to obtain a linear calibration curve from 9.9 x 10(-5) to 1.2 x 10(-3) mol L-1 and a detection limit of 6.8 x 10(-5) mol L-1. Under amperometric conditions (E-app = 0.8 V; flow rate = 14.1 ml, min(-1); pH 3.0), an analytical calibration graph for L-dopa was obtained from 1.0 x 10(-6) mol L-1 6.6 x 10(-4) mol L-1 with a detection limit of 9.9 x 10(-7) mol L-1. The method was successfully applied to the determination of L-dopa in commercial dosage forms without any pre-treatment. (c) 2005 Elsevier B.V. All rights reserved.

Analysis of aromatic amines in surface waters receiving wastewater from a textile industry by liquid chromatographic with electrochemical detection

A high performance liquid chromatography ( HPLC) method with electrochemical detection (ED) was developed for the determination of benzidine, 3,3-dimethylbenzidine, o-toluidine and 3,3-dichlorobenzidine in the wastewater of the textile industry. The aromatic amines were eluted on a reversed phase column Shimadzu Shimpack C-18 using acetonitrile + ammonium acetate (1 x 10(-4) mol L-1) at a ratio 46: 54 v/v as mobile phase, pumped at a flow rate of 1.0 mL min(-1). The electrochemical oxidation of the aromatic amines exhibits well-defined peaks at a potential range of +0.45 to +0.78 V on a glassy carbon electrode. Optimum working potentials for amperometric detection were from 0.70 V to +1.0 V vs. Ag/AgCl. Analytical curves for all the aromatic amines studied using the best experimental conditions present linear relationship from 1 x 10(-8) mol L-1 to 1.5 x 10(-5) mol L-1, r = 0.99965, n = 15. Detection limits of 4.5 nM (benzidine), 1.94 nM (o-toluidine), 7.69 nM (3,3-dimethylbenzidine), and 5.15 nM (3,3-dichlorobenzidine) were achieved, respectively. The detection limits were around 10 times lower than that verified for HPLC with ultra violet detection. The applicability of the method was demonstrated by the determination of benzidine in wastewater from the textile industry dealing with an azo dye processing plant.

Barium strontium titanate nanocrystalline thin films prepared by soft chemical method

Barium strontium titanate (Ba0.65Sr0.35TiO3) nanocrystalline thin films, which were produced by the soft chemical method, were crystallized at low temperature using a domestic microwave oven. A SiC susceptor were used to absorb the microwave energy and rapidly transfer the heat to the film. Low microwave power and short time have been used. The films obtained are crack-free, well-adhered, and fully crystallized. The microstructure displayed a polycrystalline nature with nanograin size. The metal-BST-metal structure of the thin films treated at 700 degrees C show food electric properties. The ferroelectric nature of the BST35 thin film was indicated by buttertly- shaped C-V curves. The capacitance-frequency curves reveal that the dielectric constant may reach a value up to 800 at 100kHz. The dissipation factor was 0.01 at 100kHz. The charge storage density as function of applied voltage graph showed that the charge storage densities are suitable for use in trench type 64 Mb ( 1-5 mu C/cm(2) and 265 Mb (2-11 mu C/cm(2)) DRAMs. (C) 2007 Elsevier Ltd. All rights reserved.

Effect of preannealing on the morphology of LiTaO3 thin films prepared from the polymeric precursor method

Lithium tantalate (LiTaO3) thin films with 50:50 stoichiometry were deposited on silicon (100) substrates with two layers by the spin coating method using a polymeric organic solution. In order to study the influence of preannealing on the crystallinity, microstructure, grain size and roughness of the final film, two annealing procedures, slow preannealing and fast preannealing, were used. X-ray diffraction (XRD) results showed that LiTaO3 thin films are polycrystalline. It was observed by scanning electron microscopy (SEM) that the thin film, which had been thermally treated using slow preannealing, was characterized by a dense and homogeneous surface. The atomic force microscopy (AFM) studies showed that the roughness is strongly influenced by preannealing temperature. (C) 2003 Elsevier B.V. All rights reserved.

Effect of oxygen atmosphere on the morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate (LiTaO3) thin films with (50:50) stoichiometry were prepared using polymeric organic solution. The 5-layered films were deposited on silicon (100) substrates by spin coating method. The coated substrates were thermally treated at 500degreesC for 3 h under several oxygen atmospheres in order to study the influence of oxygen flow on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction results showed that an oxygen flow of 100 cm(3)/min leads to LiTaO3 thin films with higher crystallinity, without preferential orientation. It was observed by scanning electron microscopy (SEM) that the thickness of thin films decreases when the oxygen flow increases. The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by oxygen flow.

Anodic oxidation of formaldehyde on Pt-modified SnO2 thin film electrodes prepared by a sol-gel method

Pt-modified SnO2 electrodes were prepared onto titanium substrates in the form of thin films of similar to2 mum at different temperatures in the range from 200 to 400degreesC. Surface morphology was examined by scanning electron microscopy (SEM). It was found that Pt-SnO2 sol-gel layers are significantly rough and have a low porosity. X-ray diffraction (XRD) studies showed that the films consist of Pt nanoparticles with average size varying from about 5 to 10 nm, depending on the preparation temperature, and amorphous tin oxide. X-ray photoelectron spectroscopy (XPS) was employed to determine the superficial composition of the electrodes and demonstrated the presence of Sn4+ in all the samples. XPS spectra of the Pt 4f electrons showed the presence of Pt in the zero-valence state as well as in ionic forms. The general electrochemical behavior was characterized by cyclic voltammetry in 1 mol l(-1) HClO4 and the electrocatalytic activity towards the oxidation of formaldehyde was investigated by potential sweeps and chronoamperometry. The results obtained show that the Pt-SnO2/Ti system exhibits a significant catalytic activity for the oxidation of formaldehyde, with an onset potential below 0.1 V. (C) 2004 Elsevier Ltd. All rights reserved.

Determination of acetaldehyde in fuel ethanol by high-performance liquid chromatography with electrochemical detection

The cyclic voltammetric behavior of acetaldehyde and the derivatized product with 2,4-dinitrophenylhydrazine (DNPHi) has been studied at a glassy carbon electrode. This study was used to optimize the best experimental conditions for its determination by high-performance liquid chromatographic (HPLC) separation coupled with electrochemical detection. The acetaldehyde-2,4-dinitrophenyl.hydrazone (ADNPH) was eluted and separated by a reversed-phase column, C-18, under isocratic conditions with the mobile phase containing a binary mixture of methanol/LiCl(aq) at a concentration of 1.0 x 10(-3) M (80:20 v/v) and a flow rate of 1.0 mL min(-1). The optimum condition for the electrochemical detection of ADNPH was +1.0 V vs. Ag/AgCl as a reference electrode. The proposed method was simple, rapid (analysis time 7 min) and sensitive (detection limit 3.80 mu g L-1) at a signal-to-noise ratio of 3:1. It was also highly selective and reproducible [standard deviation 8.2% +/- 0.36 (n = 5)]. The analytical curve of ADNPH was linear over the range of 3-300 mg L-1 per injection (20 mu L), and the analytical recovery was > 99%.

Dielectric and fatigue properties of Pb(Zr0.53Ti0.47)O-3 thin films prepared from oxide precursors method

Fatigue is an important problem to be considered if a ferroelectric film is used for non-volatile memory devices. In this phenomena, the remanent polarization and coercive field properties degrades in cycles which increase in hysteresis loops. The reasons have been attributed to different mechanisms such as a large voltage applied on ferroelectric film in every reading process in Ferroelectric Random Access Memory (FeRAM) or memories for digital storage in computer, grain size effects and others. The aim of this work is to investigate the influence of the crystallization kinetics on dielectric and ferroelectric properties of the Pb(Zr0.53Ti0.47)O-3 thin films prepared by an alternative chemical method. Films were crystallized in air on Pt/Ti/SiO2/Si substrates at 700 degrees C for 1 hour, in conventional thermal annealing (CTA), and at 700 degrees C for 1 min and 700 degrees C 5 min, using a rapid thermal annealing (RTA) process. Final films were crack free and presented an average of 750 nm in thickness. Dielectric properties were studied in the frequency range of 100 Hz - 1 MHz. All films showed a dielectric dispersion at low frequency. Ferroelectric properties were measured from hysteresis loops at 10 kHz. The obtained remanent polarization (P-r) and coercive field (E-c) were 3.7 mu C/cm(2) and 71.9 kV/cm respectively for film crystallized by CTA while in films crystallized by RTA these parameters were essentially the same. In the fatigue process, the P, value decreased to 14% from the initial value after 1.3 x 10(9) switching cycles, for film by CTA, while for film crystallized by RTA for 5 min, P, decreased to 47% from initial value after 1.7 x 10(9) switching cycles.

Luminescence properties of Eu(3+)- and Mg(2+)-doped LiTaO(3) obtained via the polymeric precursor method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Theoretical investigation of the electronic structure and absorption spectra of carbon cluster nanotubes

Electronic and optical properties of recently discovered single-shell carbon cluster nanotubes are studied through a semiempirical INDOCI method. The calculations are performed within the cluster model and include up to 196 atoms. The trend of the forbidden band gap with the number of carbon atoms (Cn n = 60, 10, 140) for a fixed diameter is analyzed. With increasing n the band gap decreases, as expected. The tubule, with diameter of 7.2Å (as C60-Buckyball) is predicted to be a metal or a narrow-gap semiconductor. The calculated absorption spectra of the clusters show a characteristic strong peak around 40,000 cm-1. Other features of the calculated UV-visible absorption spectra are discussed. © 1994.

LiNbO3 thin films prepared from a polymeric precursor method

LiNbO3 thin films were prepared from polymeric precursor method by dip coating. The precursor films, deposited on Si(111) substrates, were heat-treated from 400°C to 900°C in order to study the heat treatment influence on the crystallinity and microstructure of the final film. The X-ray diffraction patterns showed, in particular, that these films crystallize at low temperature (450°C) and present no preferential orientation. The scanning electron microscopy studies showed that the film microstructure is strongly influenced by the annealing temperature. © 1997 Trans Tech Publications.

Structural and surface morphology characterizations of oriented LiNbO3 thin films grown by polymeric precursor method

Polymeric precursor solution was used to deposit LiNbO3 thin films by dip coating on sapphire substrates. The effects of processing variables, such as heat treatment conditions and number of deposited layers, on crystallinity and morphology of the final films were investigated. X-ray diffraction patterns show the oriented growth of the films. The rocking curves, obtained around the (006) LiNbO3 peak, revealed that the shape peak and the FWHM value were influenced by the processing variables. According to these parameters, some films presented very homogeneous dense and smooth surfaces, as shown by the SEM and AFM studies.