Transparent conducting, aluminium doped zinc oxide thin films (ZnO:Al) were deposited by radio frequency (RF) magnetron sputtering. The RF power was varied from 60 to 350Wwhereas the substrate temperature was kept at 160 °C. The structural, electrical and optical properties of the as-deposited films were found to be influenced by the deposition power. The X-ray diffraction analysis showed that all the films have a strong preferred orientation along the [001] direction. The crystallite size was varied from 14 to 36 nm, however no significant change was observed in the case of lattice constant. The optical band gap varied in the range 3.44-3.58 eV. The lowest resistivity of 1.2×10 -3Vcm was shown by the films deposited at 250 W. The mobility of the films was found to increase with the deposition power.

Transparent conducting thin films by the co-sputtering of ZnO-ITO targets

Transparent and conductive Zn-In-Sn-O (ZITO) amorphous thin films have been deposited at room temperature by the rf magnetron co-sputtering of ITO and ZnO targets. Co-sputtering gives the possibility to deposit multicomponent oxide thin films with different compositions by varying the power to one of the targets. In order to make ZITO films with different Zn content, a constant rf power of 50 W was used for the ITO target, where as the rf power to ZnO target was varied from 25 W to 150 W. The as deposited films showed an increase in Zn content ratio from 17 to 67 % as the power to ZnO target was increased from 25 to 150 W. The structural, electrical and optical properties of the as deposited films are reported. The films showed an average transmittance over 80% in the visible wavelength range. The electrical resistivity and optical band gap of the ZITO films were found to depend on the Zn content in the film. The ZITO films deposited at room temperature with lower Zn content ratios showed better optical transmission and electrical properties compared to ITO film.

Electrical and optical properties of Zn-In-Sn-O transparent conducting thin films

Indium tin oxide (ITO) is one of the widely used transparent conductive oxides (TCO) for application as transparent electrode in thin film silicon solar cells or thin film transistors owing to its low resistivity and high transparency. Nevertheless, indium is a scarce and expensive element and ITO films require high deposition temperature to achieve good electrical and optical properties. On the other hand, although not competing as ITO, doped Zinc Oxide (ZnO) is a promising and cheaper alternative. Therefore, our strategy has been to deposit ITO and ZnO multicomponent thin films at room temperature by radiofrequency (RF) magnetron co-sputtering in order to achieve TCOs with reduced indium content. Thin films of the quaternary system Zn-In-Sn-O (ZITO) with improved electrical and optical properties have been achieved. The samples were deposited by applying different RF powers to ZnO target while keeping a constant RF power to ITO target. This led to ZITO films with zinc content ratio varying between 0 and 67%. The optical, electrical and morphological properties have been thoroughly studied. The film composition was analysed by X-ray Photoelectron Spectroscopy. The films with 17% zinc content ratio showed the lowest resistivity (6.6 × 10 - 4 Ω cm) and the highest transmittance (above 80% in the visible range). Though X-ray Diffraction studies showed amorphous nature for the films, using High Resolution Transmission Electron Microscopy we found that the microstructure of the films consisted of nanometric crystals embedded in a compact amorphous matrix. The effect of post deposition annealing on the films in both reducing and oxidizing atmospheres were studied. The changes were found to strongly depend on the zinc content ratio in the films.

Magnetic field effect on quantum corrections to the low-temperature conductivity in mettalic perovskite oxides

The transport and magnetotransport properties of the metallic and ferromagnetic SrRuO3 (SRO) and the metallic and paramagnetic LaNiO3 (LNO) epitaxial thin films have been investigated in fields up to 55 T at temperatures down to 1.8 K . At low temperatures both samples display a well-defined resistivity minimum. We argue that this behavior is due to the increasing relevance of quantum corrections to the conductivity (QCC) as temperature is lowered; this effect being particularly relevant in these oxides due to their short mean free path. However, it is not straightforward to discriminate between contributions of weak localization and renormalization of electron-electron interactions to the QCC through temperature dependence alone. We have taken advantage of the distinct effect of a magnetic field on both mechanisms to demonstrate that in ferromagnetic SRO the weak-localization contribution is suppressed by the large internal field leaving only renormalized electron-electron interactions, whereas in the nonmagnetic LNO thin films the weak-localization term is relevant.

Magneto-optical Kerr effect in laser-patterned La2/3Sr1/3MnO3 epitaxial thin films

In this study, we have performed magneto-optical Kerr effect (MOKE) measurement on epitaxial La2/3Sr1/3MnO3 thin films containing artificial interfaces created by laser-patterning the SrTiO3 substrate. The observed increase of the resistivity and of the high-field magnetoresistance when measuring the films across the interface arrays are related to the reduction of the magnetization of the interfaces with respect to the rest of the film. As observed by the local MOKE probe, the structural disorder in the manganite film induced by the underlying patterned substrate leads to a large spin disorder responsible for a strong high-field susceptibility of the resistance.

Self-interference of charge carriers in ferromagnetic SrRuO3

We report a systematic study of the low-temperature electrical conductivity in a series of SrRuO3 epitaxial thin films. At relatively high temperature the films display the conventional metallic behavior. However, a well-defined resistivity minimum appears at low temperature. This temperature dependence can be well described in a weak localization scenario: the resistivity minimum arising from the competition of electronic self-interference effects and the normal metallic character. By appropriate selection of the film growth conditions, we have been able to modify the mean-free path of itinerant carriers and thus to tune the relative strength of the quantum effects. We show that data can be quantitatively described by available theoretical models.

Detection and Characterization of Preferential Flow Paths in the Downstream Area of a Hazardous Landfill

We have used surface-based electrical resistivity tomography to detect and characterize preferential hydraulic pathways in the immediate downstream area of an abandoned, hazardous landfill. The landfill occupies the void left by a former gravel pit and its base is close to the groundwater table and lacking an engineered barrier. As such, this site is remarkably typical of many small- to medium-sized waste deposits throughout the densely populated and heavily industrialized foreland on both sides of the Alpine arc. Outflows of pollutants lastingly contaminated local drinking water supplies and necessitated a partial remediation in the form of a synthetic cover barrier, which is meant to prevent meteoric water from percolating through the waste before reaching the groundwater table. Any future additional isolation of the landfill in the form of lateral barriers thus requires adequate knowledge of potential preferential hydraulic pathways for outflowing contaminants. Our results, inferred from a suite of tomographically inverted surfaced-based electrical resistivity profiles oriented roughly perpendicular to the local hydraulic gradient, indicate that potential contaminant outflows would predominantly occur along an unexploited lateral extension of the original gravel deposit. This finds its expression as a distinct and laterally continuous high-resistivity anomaly in the resistivity tomograms. This interpretation is ground-truthed through a litholog from a nearby well. Since the probed glacio-fluvial deposits are largely devoid of mineralogical clay, the geometry of hydraulic and electrical pathways across the pore space of a given lithological unit can be assumed to be identical, which allows for an order-of-magnitude estimation of the overall permeability structure. These estimates indicate that the permeability of the imaged extension of the gravel body is at least two to three orders-of-magnitude higher than that of its finer-grained embedding matrix. This corroborates the preeminent role of the high-resistivity anomaly as a potential preferential flow path.

Sniff nasal inspiratory pressure in patients with chronic obstructive pulmonary disease.

In subjects with normal lung mechanics, inspiratory muscle strength can be reliably and easily assessed by the sniff nasal inspiratory pressure (SNIP), which is the pressure measured in an occluded nostril during a maximal sniff performed through the contralateral nostril. The aim of this study was to assess the validity of the SNIP in patients with chronic obstructive pulmonary disease (COPD), where pressure transmission from alveoli to upper airways is likely to be dampened. Twenty eight patients with COPD were studied (mean forced expiratory volume in one second (FEV1) = 36% of predicted). The SNIP and the sniff oesophageal pressure (sniff Poes) were measured simultaneously during maximal sniffs, and were compared to the maximal inspiratory pressure obtained against an occlusion (MIP). All measurements were performed from functional residual capacity in the sitting position. The ratio SNIP/sniff Poes was 0.80, and did not correlate with the degree of airflow limitation. The ratio MIP/sniff Poes was 0.87, and the ratio SNIP/MIP was 0.97. Inspiratory muscle weakness, as defined by a low sniff Poes, was present in 17 of the 28 patients. A false diagnosis of weakness was made in eight patients when MIP was considered alone, in four when SNIP was considered alone, and in only three patients when MIP and SNIP were combined. We conclude that both the sniff nasal inspiratory pressure and the maximal inspiratory pressure moderately underestimate sniff oesophageal pressure in chronic obstructive pulmonary disease. Although suboptimal in this condition, the sniff nasal inspiratory pressure appears useful to complement the maximal inspiratory pressure for assessing inspiratory muscle strength in patients with chronic obstructive pulmonary disease.

Comprehensive Bridge Deck Deterioration Mapping of Nine Bridges by Nondestructive Evaluation Technologies Final Report, January 2011

The primary objective of this research was to demonstrate the benefits of NDT technologies for effectively detecting and characterizing deterioration in bridge decks. In particular, the objectives were to demonstrate the capabilities of ground-penetrating radar (GPR) and impact echo (IE), and to evaluate and describe the condition of nine bridge decks proposed by Iowa DOT. The first part of the report provides a detailed review of the most important deterioration processes in concrete decks, followed by a discussion of the five NDT technologies utilized in this project. In addition to GPR and IE methods, three other technologies were utilized, namely: half-cell (HC) potential, electrical resistivity (ER), and ultrasonic surface waves (USW) method. The review includes a description of the principles of operation, field implementation, data analysis, and interpretation; information regarding their advantages and limitations in bridge deck evaluations and condition monitoring are also implicitly provided.. The second part of the report provides descriptions and bridge deck evaluation results from the nine bridges. The results of the NDT surveys are described in terms of condition assessment maps and are compared with the observations obtained from the recovered cores or conducted bridge deck rehabilitation. Results from this study confirm that the used technologies can provide detailed and accurate information about a certain type of deterioration, electrochemical environment, or defect. However, they also show that a comprehensive condition assessment of bridge decks can be achieved only through a complementary use of multiple technologies at this stage,. Recommendations are provided for the optimum implementation of NDT technologies for the condition assessment and monitoring of bridge decks.

Development of Performance Properties of Ternary Mixtures and Concrete Pavement Mixture Design and Analysis (MDA): Effect of Paste Quality on Fresh and Hardened Properties of Ternary Mixtures, TPF-5(117), 2012

The purpose of this study was to investigate the effect of cement paste quality on the concrete performance, particularly fresh properties, by changing the water-to-cementitious materials ratio (w/cm), type and dosage of supplementary cementitious materials (SCM), and airvoid system in binary and ternary mixtures. In this experimental program, a total matrix of 54 mixtures with w/cm of 0.40 and 0.45; target air content of 2%, 4%, and 8%; a fixed cementitious content of 600 pounds per cubic yard (pcy), and the incorporation of three types of SCMs at different dosages was prepared. The fine aggregate-to- total aggregate ratio was fixed at 0.42. Workability, rheology, air-void system, setting time, strength, Wenner Probe surface resistivity, and shrinkage were determined. The effects of paste variables on workability are more marked at the higher w/cm. The compressive strength is strongly influenced by the paste quality, dominated by w/cm and air content. Surface resistivity is improved by inclusion of Class F fly ash and slag cement, especially at later ages. Ternary mixtures performed in accordance with their ingredients. The data collected will be used to develop models that will be part of an innovative mix proportioning procedure.

Concrete Pavement Mixture Design and Analysis (MDA): Effect of Aggregate Systems on Concrete Properties, TPF-5(205), 2012

For years, specifications have focused on the water to cement ratio (w/cm) and strength of concrete, despite the majority of the volume of a concrete mixture consisting of aggregate. An aggregate distribution of roughly 60% coarse aggregate and 40% fine aggregate, regardless of gradation and availability of aggregates, has been used as the norm for a concrete pavement mixture. Efforts to reduce the costs and improve sustainability of concrete mixtures have pushed owners to pay closer attention to mixtures with a well-graded aggregate particle distribution. In general, workability has many different variables that are independent of gradation, such as paste volume and viscosity, aggregate’s shape, and texture. A better understanding of how the properties of aggregates affect the workability of concrete is needed. The effects of aggregate characteristics on concrete properties, such as ability to be vibrated, strength, and resistivity, were investigated using mixtures in which the paste content and the w/cm were held constant. The results showed the different aggregate proportions, the maximum nominal aggregate sizes, and combinations of different aggregates all had an impact on the performance in the strength, slump, and box test.

Deep crustal electromagnetic structure of Bhuj earthquake region (India) and its implications

The existence of fluids and partial melt in the lower crust of the seismically active Kutch rift basin (on the western continental margin of India) owing to underplating has been proposed in previous geological and geophysical studies. This hypothesis is examined using magnetotelluric (MT) data acquired at 23 stations along two profiles across Kutch Mainland Uplift and Wagad Uplift. A detailed upper crustal structure is also presented using twodimensional inversion of MT data in the Bhuj earthquake (2001) area. The prominent boundaries of reflection in the upper crust at 5, 10 and 20 km obtained in previous seismic reflection profiles correlate with conductive structures in our models. The MT study reveals 1-2 km thick Mesozoic sediments under the Deccan trap cover. The Deccan trap thickness in this region varies from a few meters to 1.5 km. The basement is shallow on the northern side compared to the south and is in good agreement with geological models as well as drilling information. The models for these profiles indicate that the thickness of sediments would further increase southwards into the Gulf of Kutch. Significant findings of the present study indicate 1) the hypocentre region of the earthquake is devoid of fluids, 2) absence of melt (that is emplaced during rifting as suggested from the passive seismological studies) in the lower crust and 3) a low resistive zone in the depth range of 5-20 km. The present MT study rules out fluidsand melt (magma) as the causative factors that triggered the Bhuj earthquake. The estimated porosity value of 0.02% will explain 100-500 ohm·m resistivity values observed in the lower crust. Based on the seismic velocities and geochemical studies, presence of garnet is inferred. The lower crust consists of basalts - probably generated by partial melting of metasomatised garnet peridotite at deeper depths in the lithosphere - and their composition might be modified by reaction with the spinel peridotites.

Integration of local-scale hydrological and regional-scale geophysical based on a nonlinear Bayesian sequential simulation approach

Significant progress has been made with regard to the quantitative integration of geophysical and hydrological data at the local scale. However, extending the corresponding approaches to the regional scale represents a major, and as-of-yet largely unresolved, challenge. To address this problem, we have developed a downscaling procedure based on a non-linear Bayesian sequential simulation approach. The basic objective of this algorithm is to estimate the value of the sparsely sampled hydraulic conductivity at non-sampled locations based on its relation to the electrical conductivity, which is available throughout the model space. The in situ relationship between the hydraulic and electrical conductivities is described through a non-parametric multivariate kernel density function. This method is then applied to the stochastic integration of low-resolution, re- gional-scale electrical resistivity tomography (ERT) data in combination with high-resolution, local-scale downhole measurements of the hydraulic and electrical conductivities. Finally, the overall viability of this downscaling approach is tested and verified by performing and comparing flow and transport simulation through the original and the downscaled hydraulic conductivity fields. Our results indicate that the proposed procedure does indeed allow for obtaining remarkably faithful estimates of the regional-scale hydraulic conductivity structure and correspondingly reliable predictions of the transport characteristics over relatively long distances.

Stratigraphie, morphodynamique, paléoenvironnements des terrains sédimentaires meubles à forte déclivité du domaine périglaciaire alpin

Dans le contexte d'un climat de plus en plus chaud, une étude « géosystémique » de la répartition du pergélisol dans l'ensemble d'un versant périglaciaire alpin, de la paroi rocheuse jusqu'au glacier rocheux, s'avère primordiale. S'insérant dans cette problématique, ce travail de thèse vise comme objectif général l'étude des versants d'éboulis situés à l'intérieur de la ceinture du pergélisol discontinu selon deux volets de recherche différents : une étude de la stratigraphie et de la répartition du pergélisol dans les éboulis de haute altitude et des processus qui lui sont associés ; une reconstitution de l'histoire paléoenvironnementale du domaine périglaciaire alpin pendant le Tardiglaciaire et l'Holocène. La stratigraphie et la répartition spatiale du pergélisol a été étudiée dans cinq éboulis des Alpes Valaisannes (Suisse), dont trois ont fait l'objet de forages profonds, grâce à la prospection géophysique de détail effectuée à l'aide de méthodes thermiques, de résistivité, sismiques et nucléaires. Les mesures effectuées ont permis de mettre en évidence que, dans les cinq éboulis étudiés, la répartition du pergélisol est discontinue et aucun des versants n'est intégralement occupé par du pergélisol. En particulier, il a été possible de prouver de manière directe que, dans un éboulis, le pergélisol est présent dans les parties inférieures du versant et absent dans les parties supérieures. Trois facteurs de contrôle principaux de la répartition du pergélisol déterminée au sein des éboulis étudiés ont été individualisés, pouvant agir seuls ou de manière combinée : la ventilation ascendante, l'augmentation de la granulométrie en direction de l'aval et la redistribution de la neige par le vent et les avalanches. Parmi ceux-ci, la relation ventilation-granulométrie semble être le facteur de contrôle principal permettant d'expliquer la présence de pergélisol dans les parties inférieures d'un éboulis et son absence dans les parties supérieures. Enfin, l'analyse de la structure des éboulis périglaciaires de haute altitude a permis de montrer que la stratigraphie du pergélisol peut être un élément important pour l'interprétation de la signification paléoclimatique de ce type de formes. Pour le deuxième volet de la recherche, grâce aux datations relatives effectuées à l'aide de l'utilisation conjointe de la méthode paléogéographique et du marteau de Schmidt, il a été possible de définir la chrono-stratigraphie du retrait glaciaire et du développement des glaciers rocheux et des versants d'éboulis des quatre régions des Alpes suisses étudiées (régions du Mont Gelé - Mont Fort, des Fontanesses et de Chamosentse, dans les Alpes Valaisannes, et Massif de la Cima di Gana Bianca, dans les Alpes Tessinoises). La compilation de toutes les datations effectuées a permis de montrer que la plupart des glaciers rocheux actifs étudiés se seraient développés soit juste avant et/ou pendant l'Optimum Climatique Holocène de 9.5-6.3 ka cal BP, soit au plus tard juste après cet évènement climatique majeur du dernier interglaciaire. Parmi les glaciers rocheux fossiles datés, la plupart aurait commencé à se former dans la deuxième moitié du Tardiglaciaire et se serait inactivé dans la première partie de l'Optimum Climatique Holocène. Pour les éboulis étudiés, les datations effectuées ont permis d'observer que leur surface date de la période entre le Boréal et l'Atlantique récent, indiquant que les taux d'éboulisation après la fin de l'Optimum Climatique Holocène ont dû être faibles, et que l'intervalle entre l'âge maximal et l'âge minimal est dans la plupart des cas relativement court (4-6 millénaires), indiquant que les taux d'éboulisation durant la période de formation des éboulis ont dû être importants. Grâce au calcul des taux d'érosion des parois rocheuses sur la base du volume de matériaux rocheux pour quatre des éboulis étudiés, il a été possible mettre en évidence l'existence d'une « éboulisation parapériglaciaire » liée à la dégradation du pergélisol dans les parois rocheuses, fonctionnant principalement durant les périodes de réchauffement climatique rapide comme cela a été le cas au début du Bølling, du Préboréal à la fin de l'Atlantique récent et, peut-être, à partir des années 1980. - In the context of a warmer climate, a « geosystemical » study of the permafrost distribution in a whole alpine periglacial hillslope, from the rockwall to the rockglacier, is of great importance. With respect to this problem, the general objective of this PhD thesis is the global study of talus slopes located within the alpine periglacial belt following two different research axes: the analysis of the internal structure and of the permafrost distribution of high altitude talus slopes and of the related processes; the reconstruction of the palaeoenvironmental history of the alpine periglacial belt during the Lateglacial and the Holocene. The stratigraphy and the permafrost distribution were studied in five talus slopes of the Valais Alps (Switzerland) with the analysis of borehole data (on three of the five talus slopes) and other methods of permafrost prospecting: Electrical Resistivity Tomography (ERT), Refraction Seismic Tomography (RST) and nuclear well logging. The collected data shows that, in all of the studied talus slopes, permafrost distribution is discontinuous and that neither of the hillslopes is integrally characterised by permafrost. In particular, this data proves by direct investigations that, in talus slopes, permafrost is present in the lower parts of the hillslope, whereas it is absent in the upper parts. Permafrost distribution in alpine talus slopes is depending of the combination of almost three controlling factors, whose respective importance is variable: the chimney effect, the increase of grain size downslope and the redistribution of snow by avalanches. Depending on the size of the talus and on topographical and geomorphological heterogeneities, various cases are possible: one dominant controlling factor or the combination of various factors. Nevertheless, it would be an error to consider each controlling factor independently, without considering their relationships. Between these controlling factors, the relationship chimney effect/grain size seems to be the most important factor controlling the presence of permafrost in the lowest part of periglacial talus slopes, and its absence in the upper parts. Finally, the analysis of the talus structure shows that the permafrost stratigraphy may be an important element of interpretation of the palaeoclimatic significance of an alpine talus slope. The second research axe focused on the establishment of a chronology of the Lateglacial glacier retreat and the dating of rockglaciers and talus slopes development in four studied regions of the Swiss Alps (Mont Gelé - Mont Fort, Fontanesses and Chamosentse regions, in the Valais Alps, and the Cima di Gana Bianca Massif, in the Ticino Alps). The compilation of the dates acquired through the combination of the palaeogeographical method and of the Schmidt hammer indicates that most of the investigated active rockglaciers started to evolve during the early phases of the Holocene or, at the latest, after the early-to-mid Holocene Climatic Optimum (ending around 6.3 ka cal BP). For the dated relict rockglaciers, most of them started to evolve in the second half of the Lateglacial, and probably became inactive at the beginning of the Holocene Climatic Optimum. For the investigated talus slopes, the relative dating carried out allowed to show that their surface date from the period included between the Boreal and the end of the Atlantic, pointing out that the rockwall retreat after the end of the Holocene Climatic Optimum was weak, and that the interval between maximal and minimal ages is in most cases relatively short (4-6 millennia). Therefore, the rockwall retreat during the development period of the talus slopes must has been considerable. Thanks to the calculation of rockwall erosion rates based on the volume of talus accumulations for four of the investigated hillslopes, it was possible to find evidences of the existence of "paraperiglacial rockfall phases" related to the permafrost degradation in rockwalls. These phases coincide with rapid climate warming periods, as at the beginning of the Bølling, during the Preboreal or, maybe, since 1980.

Diagnosis of periprosthetic joint infections.

Advances in implant design, surgical technique, peri-operative antimicrobial prophylaxis and laminar airflow operating room environment have made total joint arthroplasty one of the most successful surgical procedures of all times. Orthopaedic implants, however, remain prone to microbial contamination resulting in persistent risk of implant-associated infection. Treatment of infections associated with orthopaedic devices usually requires appropriate surgical intervention combined with a prolonged antimicrobial therapy. The choice of the best possible treatment regimen depends on duration and pathogenesis of infection, stability of the implant, antimicrobial susceptibility of the pathogen and condition of the surrounding soft tissue. In addition towell known diagnostic procedures new promising tools for rapid and correct microbial diagnosis are being developed as correct diagnosis of the responsible micro-organism and this is paramount for successful treatment of prosthetic joint infection.