High specific surface area LaFeCo perovskites-Synthesis by nanocasting and catalytic behavior in the reduction of NO with CO

LaFe(1-x)CO(x)O(3) perovskites were conventionally or nanocasting synthesized. The nanocasting involved the preparation of a micro-mesoporous carbon mould using a Silica Aerosil 200 and a carbon source. Then, perovskites were carbon cast at 800 degrees C. The solids were characterized by XRD, N(2) sorption, FTIR, TGA/DTG, SEM and TEM. N(2) sorption evidenced that the nanocast perovskites did not show significant intraparticle porosity in despite of their enhanced (30-50 m(2)/g) specific surface area (SSA). Nevertheless, TEM images, XRD and Rietveld refinement data showed that the solids are constituted at least by 97 wt% of perovskite phase and by agglomerates smaller than 100 nm constituted by crystallites of about 6 nm. TGA/DTG results demonstrated carbon oxidation during the perovskite formation, thus eliminating the template effect and facilitating the occurrence of sintering, which limited the SSA increase. The nanocast perovskites were more active in the reduction of NO than the uncast ones, behavior that was attributed to the increase in their SSA that allows the exposure of a higher number of accessible active sites. However, the perovskite composition and the presence of impurities can reduce the effect of the improvement of the textural properties. The nanocast perovskites also showed high thermal and catalytic stability, corroborating their potential as catalysts for the studied reaction. (C) 2009 Elsevier B.V. All rights reserved.

Preparation and structural characterization of rare-earth doped lead lanthanum zirconate titanate ceramics

A new preparation route towards rare-earth (RE) doped polycrystalline lead lanthanum zirconate titanate (PLZT) ceramics (RE = Y(3+), Nd(3+), Yb(3+)), based on the use of doped lanthanum oxide or zirconia, is reported. Structural characterization by X-ray powder diffraction reveals that secondary phase formation can be substantially diminished in comparison to conventional preparation methods. The distribution of the rare-earth dopants was investigated as a function of concentration by static (207)Pb spin echo NMR spectra, using Fourier Transformation of Carr-Purcell-Meiboom-Gill spin echo trains. For the Nd- and Yb-doped materials, the interaction of the (207)Pb nuclei with the unpaired electron spin density results in significant broadening and shifting of the NMR signal, whereas these effects are absent in the diamagnetic Y(3+) doped materials. Based on different concentration dependences of the NMR lineshape parameters, we conclude that the structural role of the Nd(3+) dopants differs significantly from that of Yb(3+). While the Nd(3+) ions appear to be statistically distributed in the PLZT lattice, incorporation of Yb(3+) into PLZT appears to be limited by the appearance of doped cubic zirconia as a secondary phase. (C) 2009 Elsevier Masson SAS. All rights reserved.

Glass-to-Vitroceramic Transition in the Yttrium Aluminoborate System: Structural Studies by Solid-State NMR

The crystallization of laser glasses in the system (B(2)O(3))(0.6){(Al(2)O(3))(0.4-y)(Y(2)O(3))(y)} (0.1 <= y <= 0.25) doped with different levels of ytterbium oxide has been investigated by X-ray powder diffraction, differential thermal analysis, and various solid-state NMR techniques. The homogeneous glasses undergo major phase segregation processes resulting in crystalline YBO(3), crystalline YAI(3)(BO(3))(4), and residual glassy B(2)O(3) as the major products. This process can be analyzed in a quantitative fashion by solid-state (11)B, (27)Al, and (89)Y NMR spectroscopies as well as (11)B{(27)Al} rotational echo double resonance (REDOR) experiments. The Yb dopants end up in both of the crystalline components, producing increased line widths of the corresponding (11)B, (27)Al, and (89)Y NMR resonances that depend linearly on the Yb/Y substitution ratio. A preliminary analysis of the composition dependence suggests that the Yb(3+) dopant is not perfectly equipartitioned between both crystalline phases, suggesting a moderate preference of Yb to substitute in the crystalline YBO(3) component.

Bendadaite, a new iron arsenate mineral of the arthurite group

Bendadaite, ideally Fe(2+)Fe(2)(3+)(AsO(4))(2)(OH)(2 center dot).4H(2)O, is a new member of the arthurite group It was found as a weathering product of arsenopyrite on a single hand specimen from the phosphate pegmatite Bendada. central Portugal (type locality) Co-type locality is the granite pegmatite of La via do Almerindo (Almerindo mine), Linopolis, Divmo das Laranjeiras county, Minas Gerais, Brazil Further localities are the Vein Negra mine, Copiapo province, Chile, mid-East, Bou Azzer district, Morocco, and Para Inferida yard, Fenugu Sibirt mine, Gonnosfanadiga, Medio Campidano Province, Sardinia. Italy Type bendadaite occurs as blackish green to dark brownish tufts (<0 1 mm long) and flattened radiating aggregates. in intimate association with an intermediate member of the scorodite-mansfieldite series It is monoclinic. space group P2(l/c). with a = 10 239(3) angstrom. b = 9 713(2) angstrom, c = 5 552(2) angstrom. beta = 94 11(2)degrees. = 550 7(2) angstrom(3). Z = 2 Electron-microprobe analysis yielded (wt %). CaO 0 04, MnO 0 03. CuO 006, ZnO 004. Fe(2)O(3) (total) 43 92, Al(2)O(3) 115. SnO(2) 0 10, As(2)O(5) 43 27. P(2)O(5) 1 86, SO(3) 0.03 The empirical formula is (Fe(0 52)(2+)Fe(0 32)(3+)rectangle(0 16))(Sigma 1 00)(Fe(1 89)(3+)Al(0 11))(Sigma 2 00)(As(1 87)P(0 13))(Sigma 2 00)O(8)(OH)(2 00) 4H(2)O based. CM 2(As,P) and assuming ideal 80, 2(OH), 4H2O and complete occupancy of the ferric on site by Fe(3+) and Al Optically, bendadaite is biaxial, positive, 2V(est) = 85+/-4 degrees, 2V(eale) = 88 degrees, with alpha 1 734(3). 13 1 759(3), 7 1 787(4) Pleochrosim is medium strong X pale reddish brown. Y yellowish brown, Z dark yellowish brown. absorption Z > V > X, optical dispersion weak, r > v. Optical axis plane Is parallel to (010), with X approximately parallel to a and Z nearly parallel to c Bendadaite has vitreous to sub-adamantine luster, is translucent and non-fluorescent It is brittle, shows irregular fracture and a good cleavage parallel to 1010} 3 15 0 10 g/cm(3), 3 193 g/cm3 (for the empirical formula) The five strongest powder diffraction lines [d in angstrom (I)(hkl] are 10 22 (10)(100), 7 036 (8)(110), 4 250 (5)(11 I), 2 865 (4)(311), 4 833 (3)(020,011) The d spacings are very similar to those of its Zn analogue, ojelaite The crystal structure of bendadaite was solved and refined using a crystal from the co-type locality with the composition (Fe(0 95)(2+)rectangle(0 05))(Sigma 1 00)(Fe(1 80)(3+)Al(0 20))Sigma(2 00)(As(1 48)P(0 52))(Sigma 2 00)O(8)) (OH)(2) 4H(2)O (R = 16%) and confirms an arthurite-type atomic arrangement

Brumadoite, a new copper tellurate hydrate, from Brumado, Bahia, Brazil

Brumadoite, ideally Cu(2)Te(6+)O(4)(OH)(4)center dot 5H(2)O, is a new mineral from Pedra Preta mine, Serra das Eguas, Brumado, Bahia, Brazil. It occurs as microcrystalline aggregates both on and, rarely, pseudomorphous after coarse-grained magnesite, associated with mottramite and quartz. Crystals are platy, subhedral, 1-2 mu m in size. Brumadoite is blue (near RHS 114B), has a pale blue streak and a vitreous lustre. It is transparent to translucent and does not fluoresce. The empirical formula is (Cu(2.90)Pb(0.04)Ca(0.01))(Sigma 2.95) (Te(0.93)(6+)Si(0.05))(Sigma 0.98)O(3.92)(OH)(3.84)center dot 5.24H(2)O. Infrared spectra clearly show both (OH) and H(2)O. Microchemical spot tests using a KI Solution show that brumadoite has tellurium in the 6(+) state. The mineral is monoclinic, P2(1)/m or P2(1). Unit-cell parameters refined from X-ray powder data are a 8.629(2) angstrom, b 5.805(2) angstrom, c 7.654(2) angstrom, beta 103.17(2)degrees, V 373.3(2) angstrom(3), Z = 2. The eight strongest X-ray powder-diffraction lines [d in angstrom, (l),(hkl)] are: 8.432,(100),(100); 3.162,(66),((2) over bar 02); 2.385,(27),(220); 2.291,((1) over bar 12),(22); 1.916,(11),(312); 1.666,(14),((4) over bar 22,114); 1.452,(10), (323, 040); 1.450,(10),(422,403). The name is for the type locality, Brumado, Bahia, Brazil. The new mineral species has been approved by the CNMNC (IMA 2008-028).

Footemineite, the Mn-analog of atencioite, from the Foote mine, Kings Mountain, Cleveland County, North Carolina, USA, and its relationship with other roscherite-group minerals

Footemineite, ideally Ca2Mn2+square Mn22+Be4(PO4)(6)(OH)(4)-6H(2)O, triclinic, is a new member of the roscherite group. It occurs on thin fractures crossing quartz-microcline-spodumene pegmatite at the Foote mine, Kings Mountain, Cleveland County, North Carolina, U.S.A. Associated minerals are albite, analcime, eosphorite, siderite/rhodochrosite, fairfieldite, fluorapatite, quartz, milarite, and pyrite. Footemineite forms prismatic to bladed generally rough to barrel-shaped crystals up to about 1.5 mm long and I mm in diameter. Its color is yellow, the streak is white, and the luster is vitreous to slightly pearly. Footemineite is transparent and non-fluorescent. Twinning is simple, by reflection, with twin boundaries across the length of the crystals. Cleavage is good on {0 (1) over bar1}) and {100}. Density (calc.) is 2.873 g/cm(3). Footemineite is biaxial (-), n(alpha) = 1.620(2), n(beta) = 1.627(2), n(gamma) = 1.634(2) (white light). 2V(obs) = 80 degrees, 2V(calc) = 89.6 degrees. Orientation: X boolean AND b similar to 12 degrees, Y boolean AND c similar to 15 degrees, Z boolean AND a similar to 15 degrees. Elongation direction is c, dispersion: r > v or r < v, weak. Pleochroism: beta (brownish yellow) > alpha = gamma (yellow). Mossbauer and IR spectra are given. The chemical composition is (EDS mode electron microprobe, Li and Be by ICP-OES, Fe3+:Fe2+ y Mossbauer, H2O by TG data, wt%): Li2O 0.23, BeO 9.54, CaO 9.43, SrO 0.23, BaO 0.24, MgO 0.18, MnO 26.16, FeO 2.77, Fe2O3 0.62, Al2O3 0.14, P2O5 36.58, SiO2 0.42, H2O 13.1, total 99.64. The empirical formula is (Ca1.89Sr0.03Ba0.02)Sigma(1.94)(Mn-0.90(2+)square(0.10))Sigma(1.00)(square 0.78Li0.17Mg0.05) Sigma(1.00)(Mn3.252+Fe0.432+ Fe0.093+Al0.03)Sigma(3.80) Be-4.30(P5.81Si0.08O24)[(OH)3.64(H2O)0.36]Sigma(4.00)center dot 6.00H(2)O . The strongest reflection peaks of the powder diffraction pattern [d, angstrom (1, %) (hkl)] are 9.575 (53) (010), 5.998 (100) (0 (1) over bar1), 4.848 (26) (021), 3.192 (44) (210), 3.003 (14) (0 (2) over bar2), 2.803 (38) ((1) over bar 03), 2.650 (29) ((2) over bar 02), 2.424 (14) (231). Single-crystal unit-cell parameters are a = 6.788(2), b = 9.972(3), c = 10.014(2) A, (x = 73.84(2), beta = 85.34(2), gamma = 87.44(2)degrees,V = 648.74 angstrom(3), Z = 1. The space group is P (1) over bar. Crystal structure was refined to R = 0.0347 with 1273 independent reflections (F > 2(5). Footemineite is dimorphous with roscherite, and isostructural with atencioite. It is identical with the mineral from Foote mine described as ""triclinic roscherite."" The name is for the Foote mine, type locality for this and several other minerals.

Persistent luminescence of Eu(2+) and Dy(3+) doped barium aluminate (BaAl(2)O(4):Eu(2+),Dy(3+)) materials

Polycrystalline Eu(2+) and Dy(3+) doped barium aluminate materials, BaAl(2)O(4):Eu(2+),Dy(3+), were prepared with solid state reactions at temperatures between 700 and 1500 degrees C. The influence of the thermal treatments on the stability, homogeneity and structure as well as to the UV-excited and persistent luminescence of the materials was investigated by X-ray powder diffraction, SEM imaging and infrared spectroscopies as well as by steady state luminescence spectroscopy and persistent luminescence decay curves, respectively. The IR spectra of the materials prepared at 250, 700, and 1500 degrees C follow the formation of BaAl(2)O(4) composition whereas the X-ray powder diffraction of compounds revealed how the hexagonal structure was obtained. The morphology of the materials at high temperatures indicated important aggregation due to sintering. The luminescence decay of the quite narrow Eu(2+) band at ca. 500 nm shows the presence of persistent luminescence after UV irradiation. The dopant (Eu(2+)) and co-clopant (Dy(3+)) concentrations affect the crystallinity and luminescence properties of the materials. (C) 2009 Elsevier B.V. All rights reserved.

Structural Investigation of MFe(2)O(4) (M = Fe, Co) Magnetic Fluids

Ferrites of the type M(II)Fe(2)O(4) (M = Fe and Co) have been prepared by the traditional coprecipitation method. These ferrites were modified by the adsorption of fatty acids derived from soybean and castor oil and were then dispersed in cyclohexane, providing very stable magnetic fluids, readily usable in nonpolar media. The structural properties of the ferrites and modified ferrites as well as the magnetic fluids were characterized by XRD (X-ray powder diffraction), TEM (transmission electron microscopy), DRIFTS (diffusion reflectance infrared Fourier transform spectroscopy), FTMR (Fourier transform near-infrared), UV-vis, normal Raman spectroscopy, and surface-enhanced Raman scattering (SERS). XRD and TEM analysis have shown that the magnetic nanoparticles (nonmodified and modified) present diameters in the range of 10-15 nm. DRIFTS measurements have shown that the carboxylate groups of soybean and castor oil fatty acids adsorb on the ferrite surface, forming three different structures: a bridging bidentate, a bridging monodentate, and a bidentate chelate structure. The FTIR and Raman spectra of nonmodified Fe(3)O(4) and CoFe(2)O(4) nanoparticles have shown that the number of observed phonons is not compatible with the expected O(h)(7) symmetry, since IR-only active phonons were observed. in the Raman spectra and vice versa. SERS measurements of a CoFe(2)O(4) thin film on a SERS-active gold electrode at different applied potentials made possible the assignment of the signals near 550 and 630 cm(-1) to Co-O motions and the signals near 470 and 680 cm(-1) to Fe-O motions.

Compatibility studies between captopril and pharmaceutical excipients used in tablets formulations

Captopril (CAP) was the first commercially available angiotensine-converting enzyme (ACE) inhibitor. In the anti-hypertensive therapy is considered the selected drug has to be therapeutically effective together with reduced toxicity. CAP is an antihypertensive drug currently being administered in tablet form. In order to investigate the possible interactions between CAP and excipients in tablets formulations, differential scanning calorimetry (DSC) and thermogravimetric (TG) analysis completed by X-ray powder diffraction (XRPD) and Fourier transform infrared spectroscopy (FTIR) were used for compatibility studies. A possible drug-excipient interaction was observed with magnesium stearate by DSC technique.

Characterization of banana, sugarcane bagasse and sponge gourd fibers of Brazil

In recent times, increasing attention has been paid to the use of renewable resources particularly of plant origin keeping in view the ecological concerns, renewability and many governments passing laws for the use of such materials. On the other hand, despite abundant availability of lignocellulosic materials in Brazil, very few attempts have been made about their utilization, probably due to lack of sufficient structure/property data. Systematic studies to know their properties and morphology may bridge this gap while leading to value addition to these natural materials. Chemical composition, X-ray powder diffraction, and morphological studies and thermal behavior aspects in respect of banana, sugarcane bagasse sponge gourd fibers of Brazilian origin are presented. Chemical compositions of the three fibers are found to be different than those reported earlier. X-ray diffraction patterns of these three fibers exhibit mainly cellulose type I structure with the crystallinity indices of 39%, 48% and 50% respectively for these fibers. Morphological studies of the fibers revealed different sizes and arrangement of cells. Thermal stability of all the fibers is found to be around 200 degrees C. Decomposition of both cellulose and hemicelluloses in the fibers takes place at 300 degrees C and above, while the degradation of fibers takes place above 400 degrees C. These data may help finding new uses for these fibers. (C) 2009 Elsevier B.V. All rights reserved.

Local Structure and Photochromic Response in Ormosils Containing Dodecatungstophosphoric Acid

Two hybrid materials based on dodecatungstophosphoric acid (HPW) dispersed in ormosils modified with 3-aminopropiltrietoxysilane (APTS) or with N-(3-(trimethoxysilyl)-propyl)-ethylene-diamine (TSPEN) show reversible photochromic response induced by irradiation in the 200-390 nm UV range. A set of solid-state nuclear magnetic resonance (NMR) techniques was used to analyze the structural properties of the main components of these hybrids (the HPW polyanion, the inorganic matrix, and the organic functionalities). For the ormosils, the use of (29)Si NMR, {(1)H}-(29)Si cross-polarization, and {(1)H}-(29)Si HETCOR revealed a homogeneous distribution of silicon species Q ``, T(2), and T(3) for the APTS hybrid, contrasting with the separation of T(3) species in the TSPEN hybrid. The combination of (31)P NMR, {(1)H}-(31)P cross-polarization and (31)P-{(1)H} spin-echo double resonance (SEDOR) revealed the dispersion of the HPW ions in the ormosil, occupying sites with a high number of close protons (>50). Differences in the molecular dynamics at room temperature, inferred from SEDOR experiments, indicate a state of restricted mobility of the HPW ion and the surrounding molecular groups in the TSPEN hybrid. This behavior is consistent with the presence of more amino groups in the TSPEN, acting as chelating groups to the HPW ion. This hybrid, with the strong chelate interaction of the diamine group, shows the most intense photochromic response, in agreement with the charge transfer models proposed to explain the photochromic effect. Electronic reflectance spectroscopy in irradiated samples revealed the presence of one-electron and two-electron reduced polyanions. The one-electron reduced species could be detected also by (31)P NMR spectroscopy immediately after UV irradiation.

Caracterização espectroscópica de peixe do período cretáceo (Bacia do Araripe)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo de coprólito da bacia sedimentar do Araripe por meios de espectroscopia FT-IR e difração de Raios-X

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

New palladium(II) complexes with pyrazole ligands Part II. Synthesis, spectral and thermal studies, and antitumor evaluation

This study describes the synthesis, IR, (1)H, and (13)C{(1)H} NMR spectroscopic as well the thermal characterization of the new palladium(II) pyrazolyl complexes [PdCl(2)(HmPz)(2)] 1, [PdBr(2)(HmPz)(2)] 2, [PdI(2)(HmPz)(2)] 3, [Pd(SCN)(2)(HmPz)(2)] 4 {HmPz = 4-methylpyrazole}. The residues of the thermal decomposition were identified as Pd(0) by X-ray powder diffraction. From the initial decomposition temperatures, the thermal stability of the complexes can be ordered in the sequence: 1 > 2 > 4 a parts per thousand 3. The cytotoxic activities of the complexes and the ligand were investigated against two murine cancer cell lines: mammary adenocarcinoma (LM3) and lung adenocarcinoma (LP07) and compared to cisplatin under the same experimental conditions.

Mono- and dinuclear palladium(II) compounds containing N,S donor ligands - Synthesis, characterization and thermal behavior

Synthesis, spectroscopic characterization and thermal analysis of the compounds [Pd-2(dmba)(2)(mu-NCO)(mu-2-qnS)] (1), [Pd-2(dmba)(2)(mu-NCO)(mu-8-qnS)] (2), [Pd(2-qnS)(2)] (3) and [Pd(8-qn(S))2] (4) (dmba=N,N-dimethylbenzylamine; 2-qnS=2-quinolinethiolate; 8-qnS=8-quinolinethiolate) are described. The thermal decomposition of these compounds occurs in four consecutive steps and the final decomposition products were identified as Pd(0) by X-ray powder diffraction. The thermal stability order of the complexes is 4 > 3 > 1 > 2.